调控炭化过程优化煤基硬炭负极储钠性能
|
郭行,韩纹莉,董晓玲,李文翠
|
Adjusting carbonization process to optimize sodium storage performance of coal-based hard carbon anode
|
Hang GUO,Wenli HAN,Xiaoling DONG,Wencui LI
|
|
表2 炭化后样品的结构信息
|
Table 2 Structure information of the samples after carbonization
|
|
Sample | SBET/(m2·g-1) | d002/nm | Lc /nm | La /nm | AG/AD | 元素含量(质量分数)/% |
---|
C | N | H | O |
---|
XJM-1-3-60 | 44.35 | 0.371 | 1.17 | 3.68 | 0.37 | 96.27 | 0.36 | 0.30 | 3.07 | XJM-2-3-60 | 14.50 | 0.368 | 1.15 | 3.51 | 0.28 | 97.51 | 0.24 | 0.20 | 2.05 | XJM-2-3-130 | 29.93 | 0.368 | 1.18 | 3.51 | 0.28 | 96.27 | 0.25 | 0.28 | 3.20 | XJM-2-3-20 | 3.17 | 0.373 | 1.14 | 3.37 | 0.27 | 97.99 | 0.31 | 0.19 | 1.51 | XJM-2-1-60 | 10.55 | 0.370 | 1.16 | 3.51 | 0.33 | 97.25 | 0.25 | 0.20 | 2.30 | XJM-2-5-60 | 9.41 | 0.369 | 1.15 | 3.30 | 0.25 | 96.81 | 0.27 | 0.16 | 2.76 |
|
|
|