电子束固化水性聚氨酯丙烯酸酯的制备及性能

徐海涛，朱令干，廖建华，梁红波，熊磊   

  1. 南昌航空大学材料学院，江西 南昌 330063
  • 收稿日期:2011-10-16 修回日期:2011-11-26 出版日期:2012-04-05 发布日期:2012-04-05
  • 通讯作者: 徐海涛

Synthesis and properties of electron beam curing waterborne polyurethane acrylate

XU Haitao，ZHU Linggan，LIAO Jianhua，LIANG Hongbo，XIONG Lei   

  1. School of Materials，Nanchang Hangkong University，Nanchang 330063，Jiangxi，China
  • Received:2011-10-16 Revised:2011-11-26 Online:2012-04-05 Published:2012-04-05

PDF (PC)

798

被引次数

10 | 3

摘要： 研究了一种制备水性聚氨酯丙烯酸酯的新方法，通过在扩链剂分子结构中组装离子基团来改善亲水性，解决了聚氨酯丙烯酸酯与水难相溶的问题。采用这种方法制备了一种聚氨酯丙烯酸酯产物，使用FTIR和1H NMR对产物结构进行了表征。对产物与水的储存稳定性、黏度、电子束固化行为及固化后性能进行了研究。结果表明，分散乳液储存稳定性好，经电子束固化后性能(如硬度、附着力、光泽度、柔韧性、热稳定性)优良。

关键词: 水性聚氨酯丙烯酸酯, 扩链剂, 电子束固化

Abstract: A new preparation method of waterborne polyurethane acrylate was developed.With this method the hydrophilicity of polyurethane acrylate was improved by assembling ionic groups on the molecular structure of chain extender, and the immiscibility of polyurethane acrylate with water was resolved.The polyurethane acrylate prepared by this method was characterized by Fourior-transformed infrared spectroscopy（FTIR)and 1H nuclear magnetic resonance（1H NMR).Its stability with water, viscosity, electron beam curing behavior and cured properties were studied.The results showed that the as-prepared product had water storage stability and the emulsion particle sizes decreased with increasing water content in the range from 0.50 to 0.75.The product properties cured by electron beam, such as thermal stability, hardness, adhesion, gloss, flexibility were excellent.

Key words: waterborne polyurethane acrylate, chain extender, electron beam curing

中图分类号: 

版权所有 © 2019 《化工学报》编辑部
北京市东城区青年湖南街13号（100011）
电话：010-64519489，010-64519362，010-64519485，010-64519490，010-64519451
E-Mail：hgxb@cip.com.cn
京ICP备12046843号-7
京公网安备 11010102001995号
本系统由北京玛格泰克科技发展有限公司设计开发