热塑性弹性体SBS的接枝改性研究

CIESC Journal

热塑性弹性体SBS的接枝改性研究

张权,施用晞,王洪澎,李洋,黎渝

北京化工学院,北京化工学院,北京化工学院,北京化工学院,北京化工学院北京100029 ,北京100029 ,北京100029 ,北京100029 ,北京100029

出版日期:1992-08-25 发布日期:1992-08-25

GRAFT MODIFICATION OF THERMOPLASTIC ELASTOMER SBS

Zhang Quan, Shi yongxi, Wang Hongpeng, Li Yang and Li Yu (Beijing Institute of Chemical Technology, Beijing 100029)

Online:1992-08-25 Published:1992-08-25

摘要/Abstract

摘要： <正>1引言由于SBS化学组成及其结构的待点,将它作为粘合剂,比一般合成橡胶粘合剂更具独特之处.然而由于SBS大分子内缺少极性基团,使得SBS粘合剂与聚氯乙烯、聚氨酯和金属等材料的粘接效果不够理想,为改善其粘接性,国内外学者对其进行了接枝改性的研究.

Abstract: Due to its chemical composition and structure SBS has unique adhesive function. However, in the absence of polar group in SBS macromolecules, its adhesion to metal is weak. In this paper, SBS was melted and reacted with maleic anhydride (MAH), methyl methacrylate (MMA) and the mixture of MAH and MMA to improve its adhesion to metal, The results show that the strength of adhesion to alumimium of SBS adhesives modified by melting reaction with the mixture of MAH and MMA is stronger than those of SBS modified by MAH or MMA separately. Besides, the melting reaction had an notable effect on the formation of microphase segregation structure of SBS.

张权,施用晞,王洪澎,李洋,黎渝. 热塑性弹性体SBS的接枝改性研究 [J]. CIESC Journal.

Zhang Quan, Shi yongxi, Wang Hongpeng, Li Yang and Li Yu (Beijing Institute of Chemical Technology, Beijing 100029). GRAFT MODIFICATION OF THERMOPLASTIC ELASTOMER SBS[J]. .