分散聚合法合成含有环氧基的无孔超顺磁性微球及其表征

马志亚; 官月平; 刘先桥; 刘会洲   

  1. State Key Laboratory of Biochemical Engineering, Laboratory of Separation Science and Engineering, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100080, China
  • 收稿日期:1900-01-01 修回日期:1900-01-01 出版日期:2005-04-28 发布日期:2005-04-28
  • 通讯作者: 马志亚

Preparation and Characterization of Non-porous Superparamagnetic Microspheres with Epoxy Groups by Dispersion Polymerization

MA Zhiya; GUAN Yueping; LIU Xianqiao; LIU Huizhou   

  1. State Key Laboratory of Biochemical Engineering, Laboratory of Separation Science and Engineering, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100080, China
  • Received:1900-01-01 Revised:1900-01-01 Online:2005-04-28 Published:2005-04-28
  • Contact: MA Zhiya

PDF (PC)

271

被引次数

1

摘要： Non-porous superparamagnetic polymer microspheres with epoxy groups were prepared by dispersion polymerization of glycidyl methacrylate (GMA) in the presence of magnetic iron oxide (Fe3O4) nanoparticles coated with oleic acid. The polymerization was carried out in the ethanol/water medium using polyvinylpyrrolidone (PVP) and 2,2’-azobisisobutyronitrile (AIBN) as stabilizer and initiator, respectively. The magnetic microspheres obtained were characterized with scanning electron microscopy (SEM), vibrating sample magnetometry (VSM) and Fourier transform infrared spectroscopy (FTIR). The results showed that the magnetic microspheres had an average size of-1μm with superparamagnetic characteristics. The saturation magnetization was found to be 4.5emu..g-1. There was abundance of epoxy groups with density of 0.028 mmol·g^-1 in microspheres. The magnetic PGMA microspheres have extensive potential uses in magnetic bioseparation and biotechnology.

关键词: 超顺磁性;微球体;环氧聚合物;分散聚合;生物技术;乙烯聚合物;聚苯乙烯

Abstract: Non-porous superparamagnetic polymer microspheres with epoxy groups were prepared by dispersion polymerization of glycidyl methacrylate (GMA) in the presence of magnetic iron oxide (Fe3O4) nanoparticles coated with oleic acid. The polymerization was carried out in the ethanol/water medium using polyvinylpyrrolidone (PVP) and 2,2’-azobisisobutyronitrile (AIBN) as stabilizer and initiator, respectively. The magnetic microspheres obtained were characterized with scanning electron microscopy (SEM), vibrating sample magnetometry (VSM) and Fourier transform infrared spectroscopy (FTIR). The results showed that the magnetic microspheres had an average size of-1μm with superparamagnetic characteristics. The saturation magnetization was found to be 4.5emu..g-1. There was abundance of epoxy groups with density of 0.028 mmol·g^-1 in microspheres. The magnetic PGMA microspheres have extensive potential uses in magnetic bioseparation and biotechnology.

Key words: polyglycidyl methacrylate, magnetic polymer microsphere, dispersion polymerization, epoxy groups

版权所有 © 2019 《化工学报》编辑部
北京市东城区青年湖南街13号（100011）
电话：010-64519489，010-64519362，010-64519485，010-64519490，010-64519451
E-Mail：hgxb@cip.com.cn
京ICP备12046843号-7
京公网安备 11010102001995号
本系统由北京玛格泰克科技发展有限公司设计开发