Iron Arene Salts as Initiators for Thermal Curing of Epoxides by Photo-catalysis

WANG Tao; LI Baoshan; YU Meng; WAN Pinyu   

  1. DepartmentofChemistry,BeijingUniversityofChemicalTechnology,Beijing100029,China
  • Received:1900-01-01 Revised:1900-01-01 Online:2005-04-28 Published:2005-04-28
  • Contact: WANG Tao

PDF (PC)

203

被引次数

1

摘要： [Cyclopentadien-Fe-naphthalene]BF4(CFN) and [cyclopentadien-Fe-anisole]BF4(CFA) thermal cationic initiators for the curing of epoxide E44 and GGE were investigated. CFN brought out the curing of E44 at 89.1℃ and that of GGE at 148.7℃. However, CFA had much less thermal initiating activity under 300℃. Under UV radiation for short time, the thermal initiating activities of CFN and CFA were enhanced obviously. It was observed that the initiating onset temperature decreased and the evolved heat of the curing increased. Both CFN and CFA can carrv out the polvmerization of E44 and GGE near 85℃ and 112℃ by UV radiation.

关键词: 铁有机化合物;热加工技术;环氧化物;光学催化剂

Abstract: [Cyclopentadien-Fe-naphthalene]BF4(CFN) and [cyclopentadien-Fe-anisole]BF4(CFA) thermal cationic initiators for the curing of epoxide E44 and GGE were investigated. CFN brought out the curing of E44 at 89.1℃ and that of GGE at 148.7℃. However, CFA had much less thermal initiating activity under 300℃. Under UV radiation for short time, the thermal initiating activities of CFN and CFA were enhanced obviously. It was observed that the initiating onset temperature decreased and the evolved heat of the curing increased. Both CFN and CFA can carrv out the polvmerization of E44 and GGE near 85℃ and 112℃ by UV radiation.

Key words: thermal initiators, photo-catalyses, epoxide

版权所有 © 2019 《化工学报》编辑部
北京市东城区青年湖南街13号（100011）
电话：010-64519489，010-64519362，010-64519485，010-64519490，010-64519451
E-Mail：hgxb@cip.com.cn
京ICP备12046843号-7
京公网安备 11010102001995号
本系统由北京玛格泰克科技发展有限公司设计开发