大孔二氧化硅膜上纳米碳纤维层结构化催化剂载体的制备

CIESC Journal

• REACTION KINETICS, CATALYSIS • 上一篇下一篇

大孔二氧化硅膜上纳米碳纤维层结构化催化剂载体的制备

刘平乐^a; L.Lefferts^b

^aCollege of Chemical Engineering, Xiangtan University, Xiangtan 411105, China
^b Faculty of Science and Technology, IMPACT, University of Twente, P. O. Box 217, 7500 AE Enschede, The Netherlands

收稿日期:1900-01-01 修回日期:1900-01-01 出版日期:2006-06-28 发布日期:2006-06-28
通讯作者: 刘平乐

Preparation of Carbon Nano-fiber Washcoat on Porous Silica Foam as Structured Catalyst Support

LIUPingle^a; L.Lefferts^b

a College of Chemical Engineering, Xiangtan University, Xiangtan 411105, China
b Faculty of Science and Technology, IMPACT, University of Twente, P. O. Box 217, 7500 AE Enschede, The Netherlands

Received:1900-01-01 Revised:1900-01-01 Online:2006-06-28 Published:2006-06-28
Contact: LIU Pingle

摘要/Abstract

摘要： This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene spheres are assembled on porous disk substrate by vacuum filtration or evaporation. The polystyrene template is annealed slightly above the glass transition temperature in order to strengthen the colloidal crystal and ensure interconnection of the spheres so as to obtain porous materials with open structure. Following the treatment of hexde-cyltrimethylammonium bromide, the polystyrene template is filled with silica colloidal solution, which solidifies in the cavities. Then the polystyrene particles are removed by calcination at 843K, leaving behind porous silica foam. Scanning electron microscopy images demonstrate that silica foam has uniform and open structured pores. Nickel particles were deposited on porous silica foam layer by the dipping method and porous carbon nano-fiber washcoat was prepared by catalytic decomposition of ethene over small nickel particles.

关键词: sphere template;colloidal crystal;silica foam;carbon nano-fiber;washcoat

Abstract: This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene spheres are assembled on porous disk substrate by vacuum filtration or evaporation. The polystyrene template is annealed slightly above the glass transition temperature in order to strengthen the colloidal crystal and ensure interconnection of the spheres so as to obtain porous materials with open structure. Following the treatment of hexde-cyltrimethylammonium bromide, the polystyrene template is filled with silica colloidal solution, which solidifies in the cavities. Then the polystyrene particles are removed by calcination at 843K, leaving behind porous silica foam. Scanning electron microscopy images demonstrate that silica foam has uniform and open structured pores. Nickel particles were deposited on porous silica foam layer by the dipping method and porous carbon nano-fiber washcoat was prepared by catalytic decomposition of ethene over small nickel particles.

Key words: sphere template, colloidal crystal, silica foam, carbon nano-fiber, washcoat

刘平乐, L.Lefferts. 大孔二氧化硅膜上纳米碳纤维层结构化催化剂载体的制备[J]. CIESC Journal.

LIUPingle, L.Lefferts. Preparation of Carbon Nano-fiber Washcoat on Porous Silica Foam as Structured Catalyst Support[J]. .

参考文献

1    Hoogenraad, M.S., “Growth and utilization of carbon nano fibers”, Ph.D. Thesis, Utrecht Univ., The Nether-lands (1995).
2    Pham-Huu, C., Keller, N., Ehret, G., Charbonniere, L., Ziessel, R., Ledoux, M., “Carbon nanofiber supported palladium catalyst for liquid-phase reactions”, J. Mol. Catal. A Chem., 170, 155—163(2001).
3    Planeix, J.M., Coustel, N., Coq, B., Brotons, V., Kumb-har, P.S., Dutartre, R., Geneste, P., Bernier, P., Ajayan, P.M., “Application of carbon nanotubes as supports in heterogeneous catalysis”, J. Am. Chem. Soc., 116,     7935—7936(1994).
4    Jarrah, N., van Ommen, J.G., Lefferts, L., “Development of monolith with a carbon-nanofiber-washcoat as a structured catalyst support in liquid phase”, Catal. Today, 79/80, 29—33(2003).
5    Jarrah, N., Van Ommen, J.G., Lefferts, L., “Growing a carbon nano-fiber layer on a monolith support: Effect of nickel loading and growth conditions”, J. Mater. Chem., 14, 1590—1597(2004).
6    Denkov, N.D., Velev, O.D., Kralchevsky, P.A., Ivanov, I.B., Yoshimura, H., Nagayama, K., “Mechanism of formation of two-dimensional crystals from latex parti-cles on substrates”, Langmuir, 8, 3183—3190(1992).
7    Denkov, N.D., Velev, O.D., Kralchevsky, P.A., Ivanov, I.B., Yoshimura, H., Nagayama, K., “2-Dimensional crystallization”, Nature, 361, 26(1993).
8    Dimitrov, A.S., Nagayama, K., “Continuous convective assembling of fine particles into two-dimensional arrays on solid surfaces”, Langmuir, 12, 1303—1311(1996).
9    Pusey, P.N., van Megen, W., Bartlett, P., Ackerson, B.J., Rarity, J.G., Underwood, S.M., “Structure of crystals of hard colloidal spheres”, Phys. Rev. Lett., 63, 2753(1989).
10    Zhu, J., Li, M., Rogers, R., Meyer, W., Ottewill, R.H., STS-73 Space Shuttle Crew, Russel, W.B., Chaikin, P.M., “Crystallization of hard-sphere colloids in micro-gravity”, Nature, 387, 883(1997).
11    Velev, O.D., Jede, T.J., Lobo, R.F., Lenhoff, A.M., “Mi-crostructured porous silica obtained via colloidal crystal templates”, Chem. Mater., 10, 3597—3602(1998).
12    Ottewill, R.H., “Colloid stability and instability: Order disorder”, Langmuir, 5, 4—9(1989).

大孔二氧化硅膜上纳米碳纤维层结构化催化剂载体的制备

Preparation of Carbon Nano-fiber Washcoat on Porous Silica Foam as Structured Catalyst Support

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics

本文评价