加氢含硫污水管道冲蚀临界特性的电化学测试

化工学报 ›› 2009, Vol. 60 ›› Issue (3): 691-695.

加氢含硫污水管道冲蚀临界特性的电化学测试

偶国富;曹海彬;朱祖超;王艳萍;包金哲

浙江理工大学机械与自动控制学院

出版日期:2009-03-05 发布日期:2009-03-05

Determination of critical erosion-corrosion properties of hydrocracker sulfur-containing waste water pipe by electrochemical method

OU Guofu;CAO Haibin;ZHU Zuchao;WANG Yanping;BAO Jinzhe

Online:2009-03-05 Published:2009-03-05

摘要/Abstract

摘要：

利用旋转式单相流冲蚀实验装置模拟加氢空冷器管道系统的工况条件，采用电化学测试方法，研究20^#碳钢在含硫污水中的冲蚀临界特性。利用电子扫描电镜（SEM）表征试件表面腐蚀产物保护膜的微观形貌。结果表明：实验条件下，20^#碳钢腐蚀产物保护膜的厚度约为30～40 μm，使腐蚀产物膜发生冲蚀破坏的介质临界流速约为8.03 m·s^-1。

关键词:

加氢裂化, 含硫污水, 冲蚀, 临界特性, 电化学测试方法

Abstract:

The operation condition of the air cooler pipeline system of hydrocracker was simulated by a rotary single-phase erosion experimental device. The critical erosion-corrosion properties of 20^# steel pipe in sulfur-containing waste water was determined by using the electrochemical method. The micro-morphology of the protective corrosion product film was analyzed by scanning electron microscopy (SEM). Under experimental conditions, the thickness of the protective corrosion product film was 30—40 μm， and the critical flow velocity that caused erosion-corrosion of the protective corrosion product film of 20^#steel was about 8.03 m·s^-1.

Key words:

加氢裂化, 含硫污水, 冲蚀, 临界特性, 电化学测试方法

偶国富, 曹海彬, 朱祖超, 王艳萍, 包金哲. 加氢含硫污水管道冲蚀临界特性的电化学测试 [J]. 化工学报, 2009, 60(3): 691-695.

OU Guofu, CAO Haibin, ZHU Zuchao, WANG Yanping, BAO Jinzhe. Determination of critical erosion-corrosion properties of hydrocracker sulfur-containing waste water pipe by electrochemical method[J]. CIESC Journal, 2009, 60(3): 691-695.

[1]	蒋奔, 翟明, 任建行, 马世恒, 申长雨. 纤维增强塑料注射充模过程中纤维对模具的冲蚀磨损模拟[J]. 化工学报, 2018, 69(7): 3174-3180.
[2]	陈俊森, 彭冲, 方向晨, 周志明. NiMo/HY催化剂上四氢萘加氢裂化反应网络与热力学平衡分析[J]. 化工学报, 2018, 69(2): 709-717.
[3]	金浩哲1，偶国富1，李鹏轩2. 基于相似理论的REAC出口弯管冲蚀瞬态特性[J]. 化工学报, 2011, 62(S2): 124-130.