Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials

摘要/Abstract

摘要： The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction(XRD),N₂ adsorption-desorption studies,transmission electron microscopy(TEM)and surface morphology analysis(SEM),surface acid(NH₃-TPD),reducibility properties(TPR),X-ray energy dispersive spectrometer(EDS)and thermogravimetric analysis(TG/DTG).A l/La composite mesoporous material were synthesized with n(Al):n(La)=70:1.0,80℃ of reaction temperature,20 h of reaction time,12 h of crystallization time,650℃ of calcination temperature.The specific surface area of the sample is 273.90 m²·g^-1,with the average diameter 5.642 nm and pore volume 0.2354 cm³·g^-1.The samples have mesoporous structure and its particles are similar to a worm-shaped tubular structure.The influence of calcination temperature on the surface physical and chemical properties of Al/La composited mesoporous materials was examined,and the results showed that the acid strength was increased but the amount of acidic sites is decreased as the calcination temperature increased.It was found that the sample calcined at 650℃ had appropriate acid content,acid strength and better reducibility.

关键词: Al/La composite oxides, mesoporous material, synthesis, characterization

Abstract: The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction(XRD),N₂ adsorption-desorption studies,transmission electron microscopy(TEM)and surface morphology analysis(SEM),surface acid(NH₃-TPD),reducibility properties(TPR),X-ray energy dispersive spectrometer(EDS)and thermogravimetric analysis(TG/DTG).A l/La composite mesoporous material were synthesized with n(Al):n(La)=70:1.0,80℃ of reaction temperature,20 h of reaction time,12 h of crystallization time,650℃ of calcination temperature.The specific surface area of the sample is 273.90 m²·g^-1,with the average diameter 5.642 nm and pore volume 0.2354 cm³·g^-1.The samples have mesoporous structure and its particles are similar to a worm-shaped tubular structure.The influence of calcination temperature on the surface physical and chemical properties of Al/La composited mesoporous materials was examined,and the results showed that the acid strength was increased but the amount of acidic sites is decreased as the calcination temperature increased.It was found that the sample calcined at 650℃ had appropriate acid content,acid strength and better reducibility.

Key words: Al/La composite oxides, mesoporous material, synthesis, characterization

宋伟明, 左春玲, 邓启刚. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. CIESC Journal, 2011, 19(1): 70-75.

SONG Weiming, ZUO Chunling, DENG Qigang. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. , 2011, 19(1): 70-75.

参考文献

1 Ribeiro, C.M., Conceicao, F.L., Lopes, J.M., “Comparative study of Al-MCM materials prepared at room temperature with different aluminium sources and by some hydrothermal methods”, Micropor. Mesopor. Mater., 92 (2), 270-285 (2006).
2 Chen, L., Liu, X.Q., “π-Complexation mesoporous adsorbents Cu-MCM-48 for ethylene-ethane separation”, Chin. J. Chem. Eng.,16 (4), 570-574 (2008).
3 Younghun, K., Pil, K., Changmook, K., Jongheop, Y., “Comparison of mesoporous aluminas synthesized using stearic acid and its salts”, Kor. J. Chem. Eng., 22 (2), 321-327 (2005).
4 Alieh, K., Hamid, R. A., Matin, P., “Production of syngas by CO₂ reforming on M_xLa_1-xNi_0.3Al_0.7O₃-d (M = Li, Na, K) Catalysts”, Ind. Eng. Chem. Res., 47 (16), 5892-5898 (2008).
5 Kenneth, A.B., Linjie, H., Josephine, M.H., “Controlled pore opening of Ni/Al₂O₃ using chemical vapor deposition in a fluidized bed reactor”, Ind. Eng. Chem. Res., 46 (2), 684-690 (2007).
6 Naik, B., Prasad, V.S., Ghosh, N.N., “Development of a simple aqueous solution based chemical method for synthesis of mesoporous γ-alumina powders with disordered pore structure”, J. Porous Mater., 17 (1), 115-121 (2010).
7 Wang, A.M., Zhou C., Wang, H., Shen, S.B., Xue, J.Y., Ouyang, P.K., “Covalent assembly of penicillin acylase in mesoporous silica based on macromolecular crowding theory”, Chin. J. Chem. Eng., 15 (6),788-790 (2007).
8 May, M., Navarrete, J., Asomoza, M., Gomez, R., “Tailored mesoporous alumina prepared from different aluminum alkoxide precursors”, J. Porous Mater., 14 (2), 159-164 (2007).
9 Suzuki, N., Yamauchi, Y., “One-step synthesis of hierarchical porous γ-alumina with high surface area”, J. Sol Gel Sci. Technol., 53 (2),428-433 (2010).
10 Zhang, Y., Liang, H., Zhao, C.Y., Liu, Y., “Macroporous alumina monoliths prepared by filling polymer foams with alumina hydrosols”, J. Mater. Sci., 44 (3), 931-938 (2009).
11 Pavese, M., Biamino, S., “Mesoporous alumina obtained by combustion synthesis without template”, J. Por. Mater., 16 (1), 59-64 (2009).
12 Kim, P., Joo, J.B., Kim, H., Kim, W., Kim, Y., Song, I.K., Yi, J., “Preparation of mesoporous Ni-alumina catalyst by one-step sol-gel method: Control of textural properties and catalytic application to the hydrodechlorination of o-dichlorobenzene”, Catal. Lett., 104 (1),3-8 (2005).
13 Niu, J.R., Liu, W., Dai, H.X., He, H., Zi, X.H., Li, P.H., “Preparation and characterization of highly active nanosized strontium-doped lanthanum cobaltate catalysts with high surface areas”, Chin. Sci. Bull., 51 (14), 1673-1681 (2006).
14 Jeon, J.K., Kim, C.,J., Park, Y.K., Ihm, S.K., “Catalytic properties of potassiumor lanthanum-promoted Co/γ-Al₂O₃ catalysts in carbon monoxide hydrogenation”, Kor. J. Chem. Eng., 21 (2), 365-369 (2004).
15 Dupeyrat, C.B., Ortega, F.M., Ganne, M., “Methane catalytic combustion on La-based perovskite type catalysts in high temperature isothermal conditions”, Appl. Catal. A, 206, 205-215 (2001).
16 Antoninho, V., Neftali, V.C., Luiz, F.D.P., “Synthesis of Ni nanoparticles in microporous and mesoporous Al and Mg oxides”, Micropor. Mesopor. Mater., 68 (1), 151-157 (2004).
17 Hussam, H., Ibrahim, P.K., Raphael, O.I., “Reforming of isooctane over Ni-Al₂O₃ catalysts for hydrogen production: Effects of catalyst preparation method and nickel loading”, Energy Fuels, 21 (2),570-580 (2007).
18 Zhang, Z.X., Bai, P., Xu, B.J., Yan, Z.F., “Synthesis of mesoporous alumina TUD-1 with high thermostability”, J. Por. Mater., 13,245-250 (2006).
19 Kim, Y., Lee, B., Jongheop, Y., “Effect of framework or textural nanoporosity on the bulk morphology of mesoporous aluminas”, Kor. J. Chem. Eng., 24 (4), 679-682 (2007).
20 Bhattacharyya, S., Gabashvili, A., Perkas, N., “Sonochemical insertion of silver nanoparticles into two-dimensional mesoporous alumina”, J. Phys. Chem. C., 111, 11161-11167 (2007).
21 Zhang, G., Li, L., Zhang, X., Yuan, F.L., Guang, H.Z., Fu, H.G., “The effect of La₂O₃ and gelatinization aid on the thermostability of active Al₂O₃ ”, J. Natural Sci. Heilongjiang University, 20 (2), 106-110 (2003). (in Chinese)
22 Yang, L.N., Joo, J.B., Kim, Y.J., Oh, S., Kim, N.D., Jongheop, Y., “Synthesis of superacidic mesoporous alumina and its application in the dehydration of glycerol”, Kor. J. Chem. Eng., 25 (5), 1014-1017 (2008).

[1]	宋伟明, 刘星, 荆涛, 邓启刚. 介孔分子筛Al-MCM-41接枝三丁基氯化锡的表征及催化性能[J]. Chinese Journal of Chemical Engineering, 2012, 20(5): 900-905.
[2]	程健, 郭烈锦, 许世森, 张瑞云, 李晨. 薄姆石合成亚微米γ-偏铝酸锂[J]. Chinese Journal of Chemical Engineering, 2012, 20(4): 776-783.
[3]	宁张磊, 常志东, 李文军, 孙长艳, 张经华, 刘洋 . 溶剂热法制备一维锶磷灰石纳米棒及其发光性能研究[J]. CIESC Journal, 2012, 20(1): 89-94.
[4]	孙晓英, 赵雪冰, 杜伟, 刘德华. Kinetics of Formic Acid-autocatalyzed Preparation of Performic Acid in Aqueous Phase[J]. CIESC Journal, 2011, 19(6): 964-971.
[5]	刘少友, 陆建平, 冯庆革, 唐文华. Effect of Ethanol on Synthesis and Electrochemical Property of Mesoporous Al-doped Titanium Dioxide via Solid-state Reaction [J]. CIESC Journal, 2011, 19(4): 674-681.
[6]	纪永军, 杨建国. Synthesis of Methyl Isopropyl Ketone and Diethyl Ketone over Ni-Na/ZrO₂-MnO₂-ZnO Catalyst [J]. CIESC Journal, 2011, 19(4): 656-656-660.
[7]	杨革, 张营, 白艳芬. Purification and Characterization of a Nonylphenol(NP)-degrading Enzyme from Bacillus cereus.Frankland [J]. CIESC Journal, 2011, 19(4): 644-648.
[8]	程翔, 叶杰旭, 孙德智, 陈爱燕. Influence of Synthesis Temperature on Phosphate Adsorption by Zn-Al Layered Double Hydroxides in Excess Sludge Liquor[J]. CIESC Journal, 2011, 19(3): 391-396.
[9]	霍亚坤, 丁文明, 黄霞, 徐静年, 赵梦华. Fluoride Removal by Lanthanum Alginate Bead: Adsorbent Characterization and Adsorption Mechanism[J]. CIESC Journal, 2011, 19(3): 365-370.
[10]	潘崇根, 李瑛, 蒋文, 刘化章. Effects of Reaction Conditions on Performance of Ru Catalyst and Iron Catalyst for Ammonia Synthesis[J]. CIESC Journal, 2011, 19(2): 273-277.
[11]	朱杰, 崔宇, NAWAZ Zeeshan, 王垚, 魏飞. In situ Synthesis of SAPO-34 Zeolites in Kaolin Microspheres for a Fluidized Methanol or Dimethyl Ether to Olefins Process[J]. CIESC Journal, 2010, 18(6): 979-987.
[12]	王石泉, 李国华, 杜国栋, 江雪娅, 冯传启, 郭再平, KIM Seung-Joo. Hydrothermal Synthesis of Molybdenum Disulfide for Lithium Ion Battery Applications[J]. CIESC Journal, 2010, 18(6): 910-913.
[13]	肖丰, 都健, 刘琳琳, 栾国颜, 姚平经. Simultaneous Optimization of Synthesis and Scheduling of Cleaning in Flexible Heat Exchanger Networks[J]. CIESC Journal, 2010, 18(3): 402-411.
[14]	王艳, 龚磊, 李延斌, 卫芝贤. Combustion Synthesis of La_0.8Sr_0.2MnO₃ and Its Effect on HMX Thermal Decomposition[J]. CIESC Journal, 2010, 18(3): 397-401.
[15]	段云霞, 陈涛, 陈洵, 王靖宇, 赵学明. Enhanced Riboflavin Production by Expressing Heterologous Riboflavin Operon from B.cereus ATCC14579 in Bacillus subtilis[J]. CIESC Journal, 2010, 18(1): 129-136.