重力下水道中混凝土的微生物诱导腐蚀及防护涂层

M. Valix1, D. Zamri1, H. Mineyama1, W.H. Cheung1, J. Shi1, H. Bustamante2   

  1. 1 School of Chemical and Biomolecular Engineering, The University of Sydney, NSW 2006, Australia 2 Sydney Water Corporation, PO Box 399 Parramatta, NSW 2124, Australia
  • 收稿日期:2012-02-06 修回日期:2012-02-27 出版日期:2012-06-28 发布日期:2012-02-27

Microbiologically induced corrosion of concrete and protective coatings in gravity sewers

M. Valix1, D. Zamri1, H. Mineyama1, W.H. Cheung1, J. Shi1, H. Bustamante2   

  1. 1 School of Chemical and Biomolecular Engineering, The University of Sydney, NSW 2006, Australia 2 Sydney Water Corporation, PO Box 399 Parramatta, NSW 2124, Australia
  • Received:2012-02-06 Revised:2012-02-27 Online:2012-06-28 Published:2012-02-27

摘要： Microbiologically induced corrosion of concrete (MICC) and its protective coatings has a high economic impact on sewer maintenance and rehabilitation. A better understanding of the micro-organisms and the biogenic acids that are generated in the sewer is essential in controlling the corrosion of concrete pipes and protective coatings. The role of succession of micro-organisms growth in the corrosion of concrete and protective coatings was evaluated in this study. Examination of various sewer pipe materials exhibiting various extents of degradation, including concrete, cement based and epoxy based coating revealed the presence of both organic and biogenic sulphuric acids. This reflects the activity of fungi and the thiobacilli strains. Organism growth and metabolism were strongly related to the substrate pH. Fungi were found to grow and metabolise organic acids at pH from 2.0-8.0. Whilst the thiobacilli strains grew and generated sulphuric acids at pH below 3.0. The successive growth of the organisms provides an important bearing in developing improved strategies to better manage sewers.

关键词: concrete, microbiologically induced corrosion, fungi, bacteria

Abstract: Microbiologically induced corrosion of concrete (MICC) and its protective coatings has a high economic impact on sewer maintenance and rehabilitation. A better understanding of the micro-organisms and the biogenic acids that are generated in the sewer is essential in controlling the corrosion of concrete pipes and protective coatings. The role of succession of micro-organisms growth in the corrosion of concrete and protective coatings was evaluated in this study. Examination of various sewer pipe materials exhibiting various extents of degradation, including concrete, cement based and epoxy based coating revealed the presence of both organic and biogenic sulphuric acids. This reflects the activity of fungi and the thiobacilli strains. Organism growth and metabolism were strongly related to the substrate pH. Fungi were found to grow and metabolise organic acids at pH from 2.0-8.0. Whilst the thiobacilli strains grew and generated sulphuric acids at pH below 3.0. The successive growth of the organisms provides an important bearing in developing improved strategies to better manage sewers.

Key words: concrete, microbiologically induced corrosion, fungi, bacteria

版权所有 © 2019 《化工学报》编辑部
北京市东城区青年湖南街13号（100011）
电话：010-64519489，010-64519362，010-64519485，010-64519490，010-64519451
E-Mail：hgxb@cip.com.cn
京ICP备12046843号-7
京公网安备 11010102001995号
本系统由北京玛格泰克科技发展有限公司设计开发