Formation of aluminum corrosion sensitive film on optical fiber and its corrosion performance
• 表面与界面工程 • Previous Articles Next Articles
QIU Zhigang;LUO Ya’nan;SONG Shizhe
Online:
Published:
邱志刚;雒娅楠;宋诗哲
天津大学材料学院,天津 300072;材料腐蚀与防护国家重点实验室,辽宁 沈阳 110016
Abstract: In this paper, with the technology of vacuum sputter, pure aluminum corrosion sensitive film was directly deposited on the core of optical fiber with its clad removed.Metallographic microscope and scanning electron microscope (SEM) were used to analyze the structure of the film.The thickness of the pure aluminum corrosion sensitive film was about 14.65 μm, and the film was distributed evenly and firmly bonded with the fiber core.Galvanostatic step and electrochemical impedance spectroscopy (EIS) were used to evaluate the corrosion resistance in NaCl solution with different concentrations (0.001—0.1 mol8226;L-1).The result showed that the corrosion resistance of the aluminum film was similar to that of industrial pure aluminum in NaCl solution with the concentration less than 0.1 mol8226;L-1.But the EIS data showed that there were holes on the film surface.
QIU Zhigang;LUO Ya’nan;SONG Shizhe.
邱志刚;雒娅楠;宋诗哲 . 光纤上铝腐蚀敏感膜的形成和腐蚀行为 [J]. CIESC Journal.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://hgxb.cip.com.cn/EN/
https://hgxb.cip.com.cn/EN/Y2006/V57/I7/1622