CIESC Journal ›› 2009, Vol. 60 ›› Issue (8): 2137-2140.
Previous Articles
HU Wenbin;CUI Yingde;YIN Guoqiang;Duncan J Macquarrie;LIAO Liewen;CHEN Xunjun
Online:
Published:
胡文斌;崔英德;尹国强;Duncan J Macquarrie;廖列文;陈循军
Abstract:
The direct synthesis of templated super-microporous silica with spherical and cylindrical shapes was achieved in a water/acetonitrile/n-dodecylamine system, using 3-mercaptopropyltrimethoxysilane and 3-trifluoromethyltrimethylsilane as co-template.The benefits of this system to prepare such silicas were high surface area, much enhanced wall thickness, and consequently to greater structural stability.The particles obtained from this route were spherical and cylindrical.The sample was characterized by using N2 adsorption /desorption, XRD, FTIR,SEM , TG-DSC and 13C CP MAS NMR methods,and the process of the direct preparation was given.
Key words: 超微孔SiO2, 球状和柱状, 硅烷
超微孔SiO2,
摘要: 以常用的十二烷基胺为模板剂,首次以3-巯丙基-三甲氧基硅烷和三氟甲基三甲基硅烷为共模板剂,在乙氰-水溶剂中,合成了高比面积、高热稳定性、具有球状和柱状新颖形貌的超微孔分子筛,并用氮气吸附脱咐,XRD,FT-IR,SEM和TG-DSC等对其结构进行了表征,推测了合成过程.
关键词: 超微孔SiO2, 球状和柱状, 硅烷
HU Wenbin, CUI Yingde, YIN Guoqiang, Duncan J Macquarrie, LIAO Liewen, CHEN Xunjun. Direct synthesis and characterization of super-microporous SiO2 with spherical and cylindrical shapes[J]. CIESC Journal, 2009, 60(8): 2137-2140.
胡文斌, 崔英德, 尹国强, Duncan J Macquarrie, 廖列文, 陈循军. 含有球状和柱状超微孔SiO2的一步合成与表征 [J]. 化工学报, 2009, 60(8): 2137-2140.