摘要：

采用修饰多层LB 膜的方法制备导电聚合物聚3〖DK〗,4-乙烯二氧噻吩/聚苯乙烯磺酸（PEDOT-PSS）/十八胺（ODA）及硬脂酸(SA)复合层状有序膜。实验表明，PEDOT-PSS纳米粒子对单分子层具有包裹作用，形成了稳定的复合单分子膜； 二次离子质谱（SIMS）和小角X

关键词: 导电聚合物；聚FONT-FAMILY: Calibri,sans-serif, mso-bidi-font-size: 11.0pt, mso-bidi-font-family: 宋体, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, mso-fareast-font-family: 宋体, mso-hansi-font-family: 宋体">3,4-FONT-FAMILY: 宋体, mso-bidi-font-size: 11.0pt, mso-ascii-font-family: Calibri, mso-bidi-font-family: 宋体, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA">乙烯二氧噻吩聚苯乙烯磺酸；膜；

Abstract:

A Langmuir-Blodgett (LB）inducing method was firstly used to prepare single layer and multilayer conducting composite PEDOT-PSS film.The film-forming ability of ionization ODA and ODA-SA monolayer spread on PEDOT-PSS nanoparticles subphase and the behavior of ODA/PEDOT-PSS assembly particles on pure water were firstly investigated.The results indicated that PEDOT-PSS nanoparaticles in subphase packed the ionization monolayer to form stable complex Langmuir film was formed at air/water interface.It was found that the best film-forming conditions for composite film were as follows: distinct interface was formed between ODA and PEDOT-PSS layer and single layer thickness of PEDOT-PSS was about 23 nm, which was well in accordance with the size of PEDOT-PSS nanoparticles.Different structures were designed to test the conductive ability of these composite films and a varible range hopping（VRH）model was used to explain the film conductive mechanism.The results indicated that a 3D-VRH model explained well of transferring of charge carrier in multilayer film.

Key words: 导电聚合物；聚FONT-FAMILY: Calibri,sans-serif, mso-bidi-font-size: 11.0pt, mso-bidi-font-family: 宋体, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, mso-fareast-font-family: 宋体, mso-hansi-font-family: 宋体">3,4-FONT-FAMILY: 宋体, mso-bidi-font-size: 11.0pt, mso-ascii-font-family: Calibri, mso-bidi-font-family: 宋体, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA">乙烯二氧噻吩聚苯乙烯磺酸；膜；