CIESC Journal ›› 2003, Vol. 54 ›› Issue (2): 273-276.
Previous Articles Next Articles
LU Chunmei;ZHAO Jianli;HAN Kuihua
Online:
Published:
路春美;赵建立;韩奎华
Abstract: The microstructure of the raw,calcined,and desulfurized samples of shell and limestone was detected and analyzed by SEM.Their ability of capturing SO2 was verified by using LCT-2 thermobalance and the high temperature tube reactor.The results showed that the better pore structure and smaller gas diffusion resistance of shell were in favor of the inner reaction for SO2 gas.Shell had higher calcium utilization ratio than that of limestone especially under the conditions of high reaction temperature and the increased reaction time.The bigger difference of the inner structure was found in the reaction of sulfation after calcination and direct sulfation.In direct sulfation, the reaction was restrained because of the bad pore connectivity, while the former reaction took place with good pore connectivity.
Key words: 贝壳, 石灰石, 微观结构, 扫描电镜, 固硫特性
贝壳,
关键词: 贝壳, 石灰石, 微观结构, 扫描电镜, 固硫特性
LU Chunmei, ZHAO Jianli, HAN Kuihua. MICROSTRUCTURAL CHARACTERISTICS OF SHELL AND LIMESTONE AS BURNING COAL SULFUR SORBENT[J]. CIESC Journal, 2003, 54(2): 273-276.
路春美, 赵建立, 韩奎华. 贝壳和石灰石作为燃煤固硫剂的微观结构特性 [J]. 化工学报, 2003, 54(2): 273-276.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://hgxb.cip.com.cn/EN/
https://hgxb.cip.com.cn/EN/Y2003/V54/I2/273
QIAO Chunzhen;WANG Baoli;XIAO Yunhan
Activity decline of Ca-based CO2 absorbent in repetitive calcination-carbonation
Scale-inhibiting mechanism of phosphono carboxylic acid on CaCO3
Surface structure of blended coals during pyrolysis