CIESC Journal ›› 2005, Vol. 56 ›› Issue (12): 2434-2439.
Previous Articles Next Articles
WU Yusheng;YU Haiyan;YANG Yihong;BI Shiwen
Online:
Published:
吴玉胜;于海燕;杨毅宏;毕诗文
Abstract: In order to stabilize the particle size of Al(OH)3 production in sodium aluminate solution, a systematic study of the effects and mechanism of additives on agglomeration and nucleation in seed precipitation was made. The result indicated that some appropriate additive at certain concentration could significantly decrease the fine particle content, enhance the agglomeration process, and effectively restrain the secondary nucleation process. For instance, additive I33 at 40 ml8226;L-1 decreased the content of particles less than 30 μm by 26.1% and increases the mean particle size by 21.08 μm. The crystal morphology showed that the additives could accelerate the inter-growth of crystals.
Key words: 铝酸钠溶液, 氢氧化铝, 附聚, 二次成核, 添加剂
摘要: 研究了添加剂I3、I32和I33对铝酸钠溶液分解过程附聚和二次成核的影响,探讨了其作用机理,并利用电子显微镜(SEM)对产品的结晶形貌进行了观察.结果表明,添加剂的应用促进了不同颗粒间附聚的进行,提高了附聚颗粒的临界半径,并有效抑制了二次成核的发生.添加剂I33在40 ml8226;L-1时,附聚产物小于30 μm的细粒子个数分数降低26.1%,平均粒度增加21.08 μm(相对空白样).晶体形貌分析表明,添加剂促进了晶体间的交互生长.
关键词: 铝酸钠溶液, 氢氧化铝, 附聚, 二次成核, 添加剂
WU Yusheng, YU Haiyan, YANG Yihong, BI Shiwen. Effects of additives on agglomeration and secondary nucleation in seed precipitation in sodium aluminate solution[J]. CIESC Journal, 2005, 56(12): 2434-2439.
吴玉胜, 于海燕, 杨毅宏, 毕诗文. 添加剂对铝酸钠溶液晶种分解过程附聚及二次成核的影响 [J]. 化工学报, 2005, 56(12): 2434-2439.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://hgxb.cip.com.cn/EN/
https://hgxb.cip.com.cn/EN/Y2005/V56/I12/2434
Preparation of hexagonal plate nano-aluminum trihydrate by hypergravity-carbonation
Infrared spectrum of aluminate solutions with collector
Effects of additives on preparation and use of calcium sorbent for SO2 removal
LU Chenxing;XIAO Qingmin;DONG Xiaoyan
Refolding of denatured carbonic anhydrase assisted by amide and refolding kinetics
YANG Lianwei;YAO Guangchun;WANG Dongshu
Depositing copper on carbon fiber and influence of carbon fiber to interface of Cf/Cu composite