The hydrophobic silica aero-gels were prepared by copolymerization under ambient pressure, and sol-gel two-step catalysis.Tetraethoxysilane (TEOS) was used as precursor, methacrylic propenyl trimethoxy silane (KH-570) was used as modifier and ethanol (EtOH) was used as solvent.To establish the reaction mechanism and confirm the preparation process steps, in-situ IR was used to monitor the process on line.The pore size distribution, microstructure, surface functional groups and thermal stability were investigated with SEM, BET, FTIR and TG-DSC.The results showed that silica aero-gels modified with KH-570 exhibited good hydrophobic performance with surface area of 877.17 m2·g-1.This material was composed of accumulated spherical nano-particles.The particle size was in the range of 10—50 nm and the pore size was 1.9—2.5 nm.It was typical nano-mesoporous material.
Key words: 疏水性, 二氧化硅, 共聚法, 常压干燥
摘要:
以正硅酸乙酯为原料,应用溶胶-凝胶两步催化,甲基丙烯酸基丙基三甲氧基硅烷作为改性剂,无水乙醇为溶剂,共聚法常压下制备疏水性SiO2气凝胶。运用原位红外在线监测反应历程,确定制备工艺步骤。运用N2吸附仪、扫描电镜、红外光谱、TG-DSC对SiO2气凝胶孔径分布、形貌、表面官能团及热稳定性进行分析。结果表明,经甲基丙烯酸基丙基三甲氧基硅烷改性的SiO2气凝胶疏水性能良好,疏水的耐温性可达到407℃,比表面积为877.17 m2·g-1, 由球形纳米颗粒堆积而成,颗粒尺寸范围在10~50 nm,孔径集中分布在1.9疏水性, 二氧化硅, 共聚法, 常压干燥
ZHENG Wenzhi, CHEN Li, HUANG Xianghua, CHEN Yao. Preparation and characterization of hydrophobic silica aero-gels by co-precursor method[J]. CIESC Journal, 2011, 62(1): 248-254.
郑文芝, 陈砺, 黄湘桦, 陈姚. 共聚法制备疏水性SiO2气凝胶 [J]. 化工学报, 2011, 62(1): 248-254.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://hgxb.cip.com.cn/EN/
https://hgxb.cip.com.cn/EN/Y2011/V62/I1/248
ZHOU Hongjun;YIN Guoqiang;LIN Xuan;GE Jianfang
Nonisothermal crystallization of PP/PP-g-NH2/nano-SiO2 composites
Synthesis of core-shell polyacrylate emulsion containing fluorine and silicon and surface properties of latex films
Morphology and moisture-retaining property of post hybridized membrane of electrospun PVA nanofibers
Preparation of polyethylene glycol/silicon dioxide phase change materials
Silica nanotubes synthesized from TEOS with ammonium D,L-tartrate as template and their characterization
Preparation and performance of nano-SiO2 composite coating