Abstract: 4A-type zeolite molecular sieve was synthesized by the hydrothermal method，hydrochloric acid leaching and caustic soda alkaline leaching of coal gangue of Inner Mongolia. 4A- type zeolite molecular sieve was characterized by X-ray diffraction (XRD)，scanning electron microscopy (SEM)，and Fourier transform infrared spectroscopy (FT-IR). The optimum conditions were: roasting temperature 720 ℃，roasting time 1 h，acid leaching time 2.5 h，rotating speed 220 r/min，water bath temperature 95 ℃，aging temperature 25℃，aging time 30 min，crystallization temperature 100 ℃，crystallization time 14 h.

Key words: 4A-type zeolite molecular sieve, coal gangue, hydrothermal method, hydrochloric acid leaching, caustic soda alkaline leaching

摘要： 研究了以内蒙古地区的煤矸石为原料，利用盐酸酸浸法、烧碱碱浸法和水热合成法制备4A 分子筛，设计了工艺流程，考察了反应条件对4A分子筛结构和形貌的影响，并利用X射线衍射仪（XRD）、电镜扫描仪（SEM） 及傅里叶转换红外光谱仪（FT-IR）等测试手段对其进行了表征。结果表明最佳条件为煤矸石煅烧温度为720 ℃，煅烧时间为1 h，酸浸时间为2.5 h，转速为220 r/min，水浴温度为95 ℃，烧碱碱浸时间为5 h，碱浸温度为25 ℃，合成4A 分子筛的陈化温度为25 ℃，陈化时间为1 h，晶化温度为100 ℃，晶化时间为14 h，进行比较后得到了符合结构、形貌较优的4A分子筛产品。

关键词: 4A分子筛, 煤矸石, 酸浸法, 碱浸法, 水热法