摘要：

采用浓HNO₃和H₂O₂对原始CMSs进行表面修饰，使其团聚现象得到改善；以氧化后CMSs作为结构基团，采用垂直沉积法实现CMSs的自组装，得到CMSs薄膜。考察了溶剂、悬浮液pH值、悬浮液浓度和反应温度对自组装的影响。采用场发射扫描电子显微镜和原子力显微镜对产物进行表征分析，结果表明，以NaOH溶液为溶剂配制悬浮液、悬浮液浓度为2%（质量）、pH=13、温度为50

关键词: 碳微球, 修饰, 自组装

Abstract:

To improve the dispersibility of carbon microspheres (CMSs), their surfaces were first oxidized by a mixture of concentrated HNO₃ and H₂O₂.Then oxidized-CMSs were self-assembled by vertical deposition, and the effects of solvent, pH value of the suspension, suspension concentration and reaction temperature on self-assembly were investigated.The morphologies of all samples were characterized by field emission scanning electron microscopy and atomic force microscopy.The results showed that the CMSs film with more ordered and denser structure was obtained using NaOH solution as solvent for preparing suspension, at suspension concentration of 2%（mass）, pH of 13 and deposition temperature of 50℃.The sample showed good reflection of light with uniform color, which indicated the formation of uniform CMSs film.