湿式催化氧化/膜过滤组合工艺膜过滤机理

doi:10.3969/j.issn.0438-1157.2013.05.020

化工学报 ›› 2013, Vol. 64 ›› Issue (5): 1642-1650.DOI: 10.3969/j.issn.0438-1157.2013.05.020

湿式催化氧化/膜过滤组合工艺膜过滤机理

李晓祎, 吴嗣骏, 孙德智

北京林业大学水体污染源控制技术北京市重点实验室, 北京 100083

收稿日期:2012-07-30 修回日期:2012-09-04 出版日期:2013-05-05 发布日期:2013-05-05
通讯作者: 孙德智
作者简介:李晓祎(1988-),女,硕士研究生。
基金资助:
国家自然科学基金项目(50978029)。

Filtration mechanism of membranes in combination of catalytic wet air oxidation and membrane filtration

LI Xiaoyi, WU Sijun, SUN Dezhi

Beijing Key Laboratory for Source Control Technology of Water Pollution, Beijing Forestry University, Beijing 100083, China

Received:2012-07-30 Revised:2012-09-04 Online:2013-05-05 Published:2013-05-05
Supported by:
supported by the National Natural Science Foundation of China(50978029).

摘要/Abstract

摘要： 采用湿式催化氧化/膜过滤组合工艺,以Mo-Zn-Al-O粉末作为催化剂降解阳离子红GTL模拟染料废水,探讨在膜过滤过程中平均孔径为0.1 μm的微滤和0.022 μm的超滤聚偏氟乙烯(PVDF)中空纤维膜的过滤机理。实验结果表明,两种膜过滤组合工艺对染料的降解效果均优于单独湿式催化氧化,0.01 MPa恒压条件下运行120 min后微滤和超滤的膜通量分别衰减了26.63%和16.48%,其原因是粉末催化剂可在微滤膜孔内部沉积形成中间阻塞过滤,后在表面形成滤饼层;而在超滤膜表面仅形成滤饼层。通过实验结果对膜阻力进行计算,可知在相同反应过程后微滤膜产生的不可逆阻力大于超滤膜。在不同反应条件下,催化剂的沉积量与膜阻力呈现线性相关。

关键词: 湿式催化氧化, 膜过滤, 粉末催化剂, 微滤, 超滤

Abstract: The treatment of simulated cationic red GTL dye wastewater was conducted by coupling technology of catalytic wet air oxidation(CWAO)with membrane filtration, using Mo-Zn-Al-O as catalyst.The filtration mechanism of polyvinylidene fluoride hollow fiber microfiltration(MF)membranes with average pore size 0.1 μm and ultrafiltration(UF)membranes with average pore size 0.022 μm was investigated.It was found that the degradation efficiency of hybrid system was superior to CWAO with single process.Under 0.01 MPa pressure for 120 min the fluxes of MF and UF declined 26.63% and 16.48%, respectively.The reason for flux decline of microfiltration membrane was considered to be the blocking of pores and the formation of cake layer on the membrane surface by deposited catalyst powder, while that of ultrafiltration was dominated by cake layer formation.The experimental results showed that the irreversible resistance in microfiltration was larger than that in ultrafiltration after the same process.Under different operation conditions, a linear relationship could be obtained between the filtration resistance and specific deposit.

Key words: catalytic wet air oxidation, membrane filtration, powder catalyst, microfiltration, ultrafiltration

中图分类号:

X505

李晓祎, 吴嗣骏, 孙德智. 湿式催化氧化/膜过滤组合工艺膜过滤机理[J]. 化工学报, 2013, 64(5): 1642-1650.

LI Xiaoyi, WU Sijun, SUN Dezhi. Filtration mechanism of membranes in combination of catalytic wet air oxidation and membrane filtration[J]. CIESC Journal, 2013, 64(5): 1642-1650.

参考文献 18

[1]	Ma H, Zhuo Q, Wang B.Characteristics of CuO-MoO3-P2O5 catalyst and its catalytic wet oxidation(CWO)of dye wastewater under extremely mild conditions[J].Environmental Science and Technology, 2007, 41:7491-7496
[2]	Liu Yan(刘琰), Sun Dezhi(孙德智).Preparation and activity of Fe2O3-CeO2 /γ-Al2O3 catalyst for catalytic wet peroxide oxidation of dye wastewater[J].Journal of Chemical Industry and Engineering(China)(化工学报), 2006,57(10):2303-2308
[3]	Li W, Zhao S, Qi B, et al.Fast catalytic degradation of organic dye with air and MoO3:Ce nanofibers under room condition[J].Applied Catalysis B:Environmental,2009, 92:333-340
[4]	Yuan M, Wang S, Wang X, et al.Removal of organic dye by air and macroporous ZnO/MoO3/SiO2 hybrid under room conditions[J].Applied Surface Science, 2011, 257:7913-7919
[5]	Wu J M, Wen W.Catalyzed degradation of azo dyes under ambient conditions[J].Environmental Science and Technology, 2010, 44:9123-9127
[6]	Xu Yin(许银), Sun Dezhi(孙德智).Preparation and activity of Mn-Zn-Al-O catalyst for catalytic wet air oxidation under room conditions[J].CIESC Journal(化工学报), 2012,63:1415-1421
[7]	Hua B, Jiang A, Guo L, et al.Photocatalytic membrane reactor for degradation of acid red B wastewater[J].Chemical Engineering Journal, 2010, 156:571-577
[8]	Joanna G D, Sylwia M, Antoni W Morawski.Integration of photocatalysis with membrane processes for purification of water contaminated with organic dyes[J].Catalysis Today, 2010, 156:295-300
[9]	Rahul A Damodara, et al.Coupling of membrane separation with photocatalytic slurry reactor for advanced dye wastewater treatment[J].Separation and Purification Technology, 2010, 76:64-71
[10]	Mozia S.Photocatalytic membrane reactors(PMRs)in water and wastewater treatment:a review[J].Separation and Purification Technology, 2010, 73:71-91
[11]	Chong M N, Jin B,Chow C W K, Saint C.Recent developments in photocatalytic water treatment technology:a review[J].Water Research, 2010, 44:2997-3027
[12]	Xu Y, Li X Y, Sun D Z, et al.Degradation of cationic red GTL by catalytic wet air oxidation over Mo-Zn-Al-O catalyst under room temperature and atmospheric pressure[J].Environmental Science and Technology, 2012, 46:2856-2863
[13]	Jawor A, Hoek E M V.Removing cadmium ions from water via nanoparticle enhanced ultrafiltration[J].Environmental Science and Technology, 2010, 44:2570-2576
[14]	Psoch C, Schiewer S.Resistance analysis for enhanced wastewater membrane filtration[J].Journal of Membrane Science, 2006, 280:284-297
[15]	Zhang Guoliang, Zhang Jiwei, Wang Ling, Meng Qin, et al. Fouling mechanism of low-pressure hollow fiber membranes used in separating nanosized photocatalysts[J].Journal of Membrane Science, 2012, 389:532-543
[16]	Zhong Z, Xing W, Jin W, Xu N.Adhesion of nanosized nickel catalysts in the nanocatalysis/UF system[J].AIChE Journal, 2007, 53:1204-1210
[17]	Luo M L, Zhao J Q, Tang W,Pu C S.Hydrophilic modification of poly(ether sulfone)ultrafiltration membrane surface by self-assembly of TiO2 nanoparticles[J].Applied Surface Science, 2005,249:76-84
[18]	Xi W,Geissen S U.Separation of titanium dioxide from photocatalytically treated water by cross-flow microfiltration[J].Water Research,2001,35:1256-1262

湿式催化氧化/膜过滤组合工艺膜过滤机理

Filtration mechanism of membranes in combination of catalytic wet air oxidation and membrane filtration

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 18

相关文章 15

编辑推荐

Metrics

本文评价

[1]	孙敏, 贾辉, 秦卿雯, 王琦, 郭子楠, 罗艳茹, 王捷. 电阻抗成像原位在线监测超滤膜污染行为研究[J]. 化工学报, 2022, 73(4): 1754-1762.
[2]	张兰河, 汪露, 李梓萌, 唐宏, 郭静波, 贾艳萍, 张明爽. 电极超滤膜生物反应器处理阴离子表面活性剂废水[J]. 化工学报, 2022, 73(10): 4679-4691.
[3]	王开珍, 王书浩, 李韵浩, 周勇, 高从堦. 原位合成法制备高通量聚砜超滤膜及其性能研究[J]. 化工学报, 2021, 72(3): 1712-1721.
[4]	王文广, 谭明, 孙小寒, 杨兴涛, 张晓东, 张杨, 赵洪武. 基于海水淡化中试的超滤膜清洗工艺及机理[J]. 化工学报, 2020, 71(S2): 289-296.
[5]	蔡媛媛,郭百涛,邢卫红,高从堦. 面向健康产业应用需求的膜技术与膜材料[J]. 化工学报, 2020, 71(7): 2921-2932.
[6]	赵学辉, 李晓乐, 刘洋, 胡岩, 许青, 张宏伟. KMnO₄溶液pH调控对PVDF膜物化性能和污染行为影响[J]. 化工学报, 2020, 71(5): 2401-2412.
[7]	薛爱莲, 周守勇, 蔡健健, 李梅生, 张艳, 赵宜江. 温敏性PVDF/PGS-g-PNIPAM纳米复合超滤膜的制备和性能[J]. 化工学报, 2020, 71(3): 1380-1389.
[8]	许浩, 顾凯锋, 李韵浩, 周勇, 高从堦. 低截留分子量聚醚砜超滤膜[J]. 化工学报, 2019, 70(5): 1999-2006.
[9]	郝松泽, 张宏伟, 吴云, 王捷. 双金属催化滤料生物滤池处理效果及对膜污染影响研究[J]. 化工学报, 2019, 70(11): 4377-4386.
[10]	刘蕾, 任继巍, 刘鑫露, 郑兆娟, 李鑫, 欧阳嘉. 亚硫酸氢镁预处理麦秆废液中同步分离木质素磺酸盐和低聚木糖的方法研究[J]. 化工学报, 2018, 69(8): 3678-3685.
[11]	周丰, 黄慧敏, 钱飞跃, 沈耀良, 周晓吉, 李欣, 夏雪. 碳纳米管负载层结构对复合膜分离性能的影响研究[J]. 化工学报, 2018, 69(5): 2318-2326.
[12]	孙雪飞, 高勇强, 赵颂, 张文, 王志, 王晓琳. 胍基聚合物接枝改性制备抗菌抗污染超滤膜[J]. 化工学报, 2018, 69(11): 4869-4878.
[13]	张锐, 李敏, 周天旭, 彭宏伟, 郭旭虹. 新型温敏超滤膜处理印染废水的研究[J]. 化工学报, 2018, 69(11): 4910-4917.
[14]	陈奕山, 蔡逸丰, 张铭, 薛凡, 顾天宇, 陈献富, 邱鸣慧, 范益群. 多孔陶瓷膜用于碳量子点的分离与纯化[J]. 化工学报, 2018, 69(10): 4284-4291.
[15]	薛娟琴, 王森, 韩小龙, 王玉琪, 李继定. 氧化石墨烯改性PVDF超滤膜制备及分离性能[J]. 化工学报, 2017, 68(9): 3466-3473.