V2O5@CeO2核壳微球结构的脱硝催化剂制备及其抗硫性能

doi:10.11949/j.issn.0438-1157.20161421

摘要/Abstract

摘要：

利用静电自组装法制备了V₂O₅@CeO₂核壳微球结构，并负载在TiO₂上。考察了分散剂六偏磷酸钠（SHP（对表面zeta电位的影响，采用扫描电镜（SEM（、投射电镜（TEM（观察了核壳结构的形貌，并在固定床上进行了脱硝性能测试，并通过比表面积（BET（、氨气吸附漫反射（in situ DRIFTS（等进行表征。结果表明：SHP使纳米颗粒表面带负电，且一定范围内SHP浓度越高，zeta电位越大；含质量分数1%V₂O₅、5% CeO₂的催化剂，在260~400℃间具有80%以上的脱硝效率，对比了该核壳结构与传统浸渍法制备催化剂的抗硫抗水性，烟气中含15%（体积分数（H₂O，SO₂含量较低时，脱硝性能优于传统浸渍法制备的催化剂。

关键词: 静电自组装, 核壳结构, SCR脱硝, 硫中毒

Abstract:

V₂O₅@CeO₂ core-shell microspheres are prepared by electrostatic self-assembly technique and supported on TiO₂. Influences of dispersant (SHP) on zeta potential are investigated. Morphology of obtained microspheres are observed by TEM and FESEM and the catalytic performance for the selective catalytic reduction of NO_x with NH₃ (NH₃-SCR) was investigated in a fixed-bed stainless steel reactor. The catalysts are characterized by BET and in situ DRIFTS analysis of NH₃ adsorption. The results show that the nanoparticle surface is negatively charged by dispersant (SHP) and within a certain range, the higher the concentration of SHP is, the greater the zeta potential are. Catalysts with mass fraction of 1% V₂O₅ and 5% CeO₂ show high activity with the NO_x conversion over 80% from 260 to 400℃. Compared with catalysts prepared by the traditional impregnation method, the core-shell catalysts present higher SO₂ and H₂O resistance at low SO₂ concentration. When the flue gas contains 571 mg·m^-3 SO₂ and 15%(vol) H₂O, the NO_x conversion can be maintained at a high level of 80% after 7 hours.

Key words: electrostatic self-assembly, core-shell, SCR deNO_x, SO₂ resistance

中图分类号:

O643.36

赵栗, 肖睿, 曾德望. V₂O₅@CeO₂核壳微球结构的脱硝催化剂制备及其抗硫性能[J]. 化工学报, 2017, 68(4): 1373-1380.

ZHAO Li, XIAO Rui, ZENG Dewang. Preparation and SO₂-resistance of V₂O₅@CeO₂ core-shell microspheres for SCR deNO_x[J]. CIESC Journal, 2017, 68(4): 1373-1380.

参考文献 30

[1]	赵兵. 燃煤锅炉烟气中一氧化氮排放浓度测量[J]. 资源节约与环保, 2014, (2):27-27.ZHAO B. Measurement of concentration of NO in flue gas of coal-fired boiler[J]. Resources Economization & Environment Protection, 2014, (2):27-27.
[2]	闫志勇, 高翔, 吴杰, 等. V2O5-WO3-MoO3/TiO2催化剂制备及NH3选择性还原NOx的试验研究[J]. 动力工程学报, 2007, 27(2):282-286.YAN Z Y, GAO X, WU J, et al. Experimental study on preparation of V2O5-WO3-MoO3/TiO2 catalysts and selective reduction of NOx with NH3[J]. Journal of Power Engineering, 2007, 27(2):282-281.
[3]	GAO Y, LUAN T, LV T, et al. Performance of V2O5-WO3-MoO3/TiO2 catalyst for selective catalytic reduction of NOx by NH3[J]. Chinese Journal of Chemical Engineering, 2013, (1):1-7.
[4]	PENG Y, LI K, LI J. Identification of the active sites on CeO2-WO3 catalysts for SCR of NOx with NH3:an in situ IR and Raman spectroscopy study[J]. Applied Catalysis B Environmental, 2013, s140/141(2):483-492.
[5]	SHISHKIN A, CARLSSON P A, HÄRELIND H, et al. Effect of preparation procedure on the catalytic properties of Fe-ZSM-5 as SCR catalyst[J]. Topics in Catalysis, 2013, 56(9/10):567-575.
[6]	BLAKEMAN P G, BURKHOLDER E M, CHEN H Y, et al. The role of pore size on the thermal stability of zeolite supported Cu SCR catalysts[J]. Catalysis Today, 2014, 231(8):56-63.
[7]	王龙飞, 张亚平, 郭婉秋, 等. WO3/TiO2-ZrO2脱硝催化剂制备及其NH3活化机理[J]. 化工学报, 2015, 66(10):3903-3910.WANG L F, ZHANG Y P, GUO W Q, et al. Preparation of WO3/TiO2-ZrO2 catalyst for selective catalytic reduction and mechanism of NH3 activation[J]. CIESC Journal, 2015, 66(10):3903-3910.
[8]	BERNHARD A M, PEITZ D, ELSENER M, et al. Catalytic urea hydrolysis in the selective catalytic reduction of NOx:catalyst screening and kinetics on anatase TiO2 and ZrO2[J]. Catal. Sci. Technol., 2013, 3(4):942-951.
[9]	XU Z, ZHAO H, WEI Y, et al. Self-assembly template combustion synthesis of a core-shell CuO@TiO2-Al2O3, hierarchical structure as an oxygen carrier for the chemical-looping processes[J]. Combustion & Flame, 2015, 162(8):3030-3045.
[10]	DU C, SU J, LUO W, et al. Graphene supported Ag@Co core-shell nanoparticles as efficient catalysts for hydrolytic dehydrogenation of amine boranes[J]. Journal of Molecular Catalysis A Chemical, 2014, s383/384(3):38-45.
[11]	ZHANG L, ZHANG D, ZHANG J, et al. Design of meso-TiO2@MnOx-CeOx/CNTs with a core-shell structure as DeNOx catalysts:promotion of activity, stability and SO2-tolerance.[J]. Nanoscale, 2013, 5(20):9821-9.
[12]	SHEN J, HU Y, LI C, et al. Layer-by-layer self-assembly of graphene nanoplatelets[J]. Langmuir the ACS Journal of Surfaces & Colloids, 2009, 25(11):6122-8.
[13]	李丽, 胡中爱, 杨玉英, 等. MnO2/NiCo2O4的静电自组装合成及其电化学性能[J]. 物理化学学报, 2014, 30(5):899-907.LI L, HU Z A, YANG Y Y, et al. Synthesis of a MnO2/NiCo2O4 composite by electrostatic self-assembly and its electrochemical performance[J]. Acta Physico-Chimica Sinica, 2014, 30(5):899-907.
[14]	黄怡, 李梅. 用层层自组装法制备PS/SnO2核壳微球[J]. 材料导报, 2006, 20(10):143-146.HUANG Y, LI M. Preparation of PS/SnO2core-shell microspheres by layer-by-layer assembly technique[J]. Materials Review, 2006, 20(10):143-146.
[15]	XIANG Y, LU S, JIANG S P. ChemInform abstract:layer-by-layer self-assembly in the development of electrochemical energy conversion and storage devices from fuel cells to supercapacitors[J]. Chemical Society Reviews, 2013, 44(4):7291-7321.
[16]	唐雪萍. 纳米V2O5/活性焦催化剂的制备[D]. 武汉:武汉科技大学, 2012.TANG X P. Preparation of nano V2O5/AC catalyst[D]. Wuhan:Wuhan University of Science and Technology, 2012.
[17]	潘国梁, 贾晓斌, 魏惠华, 等. 药用微乳伪三元相图的几种制备方法比较研究[J]. 中国药房, 2006, 17(1):21-23.PAN G L, JIA X B, WEI H H, et al. Comparison among several preparation methods for pseudoternary phase diagrams of pharmaceutical microemulsions[J]. China Pharmacy, 2006, 17(1):21-23.
[18]	宋晓岚, 邱冠周, 杨振华, 等. 水相介质中纳米CeO2的分散行为[J]. 稀有金属, 2005, 29(2):167-172.SONG X L, QIU G Z, YANG Z H, et al. Dispersion behavior of nanometer CeO2 in aqueous medium[J]. Chinese Journal of Rare Metals, 2005, 29(2):167-172.
[19]	张亚平, 郭婉秋, 王龙飞, 等. V2O5-CeO2/TiO2-ZrO2催化剂表征及NH3还原NOx性能[J]. 催化学报, 2015, 36(10):1701-1710.ZHANG Y P, GUO W Q, WANG L F, et al. Characterization and activity of V2O5-CeO2/TiO2-ZrO2catalysts for NH3-selective catalytic reduction of NO[J]. Gastroenterology, 2015, 142(5):S-45.
[20]	TING C, BIN G, HE L, et al. In situ DRIFTS study of the mechanism of low temperature selective catalytic reduction over manganese-iron oxides[J]. Chinese Journal of Catalysis, 2014, 35:294-301.
[21]	THIRUPATHI B, SMIRNIOTIS P G. Nickel-doped Mn/TiO2, as an efficient catalyst for the low-temperature SCR of NO with NH3:catalytic evaluation and characterizations[J]. Journal of Catalysis, 2012, 288(4):74-83.
[22]	QIAN L, HUA C G, PING L, et al. In situ IR studies of selective catalytic reduction of NO with NH3 on Ce-Ti amorphous oxides[J]. Chinese Journal of Catalysis, 2014, 35:1289-1298.
[23]	王强, 谭成玉. 一种高山红景天成分FT-IR和FT-Raman光谱的研究[J]. 光散射学报, 2000, 12(1):30-32.WANG Q, TAN C Y. Studies on the FT-IR and FT -Raman spectra of a compound from Rhodiola sachalinensis A. Bor.[J]. Chinese Journal of Light Scattering, 2000, 12(1):30-32.
[24]	车勇, 李松涛, 张永清, 等. 酸枣不同部位的红外光谱分析[J]. 林产化学与工业, 2012, 32(2):117-120.CHE Y, LI S T, ZHANG Y Q, et al. Analysis of different part of Z. jujuba. var. spinosa by Fourier transform infrared spectroscopy[J]. Chemistry and Industry of Forest Products, 2012, 32(2):117-120.
[25]	QI G, YANG R T, CHANG R. MnOx-CeO2 mixed oxides prepared by co-precipitation for selective catalytic reduction of NO with NH3 at low temperatures[J]. Applied Catalysis B:Environmental, 2004, 51(2):93-106.
[26]	RAMIS G, LARRUBIA M A. An FT-IR study of the adsorption and oxidation of N-containing compounds over Fe2O3/Al2O3 SCR catalysts[J]. Journal of Molecular Catalysis A:Chemical, 2004, 215(1):161-167.
[27]	KOEBEL M, MADIA G, RAIMONDI F, et al. Enhanced reoxidation of vanadia by NO2 in the fast SCR reaction[J]. Journal of Catalysis, 2002, 209(1):159-165.
[28]	XIONG Y, TANG C, YAO X, et al. Effect of metal ions doping (M=Ti4+, Sn4+) on the catalytic performance of MnOx/CeO2 catalyst for low temperature selective catalytic reduction of NO with NH3[J]. Applied Catalysis A:General, 2015, 495:206-216.
[29]	UNDERWOOD G M, MILLER T M, GRASSIAN V H. Transmission FT-IR and Knudsen cell study of the heterogeneous reactivity of gaseous nitrogen dioxide on mineral oxide particles[J]. The Journal of Physical Chemistry A, 1999, 103(31):6184-6190.
[30]	KANTCHEVA M. Identification, stability, and reactivity of NOx species adsorbed on titania-supported manganese catalysts[J]. Journal of Catalysis, 2001, 204(2):479-494.

V₂O₅@CeO₂核壳微球结构的脱硝催化剂制备及其抗硫性能

Preparation and SO₂-resistance of V₂O₅@CeO₂ core-shell microspheres for SCR deNO_x

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 30

相关文章 15

编辑推荐

Metrics

本文评价

[1]	李勇, 高佳琦, 杜超, 赵亚丽, 李伯琼, 申倩倩, 贾虎生, 薛晋波. Ni@C@TiO₂核壳双重异质结的构筑及光热催化分解水产氢[J]. 化工学报, 2023, 74(6): 2458-2467.
[2]	夏青, 徐宇兴, 周运成, 纪雪倩, 冯海兰, 王鹏飞, 谭强强. 核壳结构米粒状FeS₂/C纳米材料制备及储锂性能研究[J]. 化工学报, 2021, 72(5): 2849-2856.
[3]	孙克宁, 陈谦, 聂明明, 侯瑞君. 重整催化剂的抗硫性能研究进展[J]. 化工学报, 2020, 71(9): 4131-4140.
[4]	宋刘斌, 蒋鹏, 肖忠良, 周乘风, 黎安娴, 池振振. 核壳结构正极材料界面设计与性能研究[J]. 化工学报, 2019, 70(7): 2426-2438.
[5]	刘皓, 张天巍, 夏登友, 梁强, 王淮斌. 凝胶型核壳结构粉体抑制A类火的有效性研究[J]. 化工学报, 2019, 70(4): 1652-1660.
[6]	牛立博, 刘辰, 马苑媛, 张慧玲, 白国义. 核壳结构镍基纳米催化剂的制备及其在肉桂醛加氢反应中的性能[J]. 化工学报, 2017, 68(11): 4161-4168.
[7]	冯纪璐, 齐军茹, 翁静宜, 刘倩茹, 曹静, 程萌. 大豆7S球蛋白与葡聚糖共价键合纳米凝胶的制备与表征[J]. 化工学报, 2016, 67(9): 4020-4026.
[8]	廖永进, 张亚平, 余岳溪, 李娟, 郭婉秋, 汪小蕾. MnO_x/WO₃/TiO₂低温选择性催化还原NO_x机理的原位红外研究[J]. 化工学报, 2016, 67(12): 5031-5039.
[9]	周威, 傅和青, 颜财彬, 陈焕钦. 改性纳米SiO₂/聚氨酯-含氟丙烯酸酯无皂乳液合成及其胶膜性能表征[J]. 化工学报, 2013, 64(6): 2291-2299.
[10]	陈　丹，舒　婷，廖世军. 核壳结构低铂催化剂：设计、制备及核的组成及结构的影响[J]. 化工进展, 2013, 32(05): 1053-1059.
[11]	黄森，肖新颜，潘季荣. 纳米SiO₂/聚氨酯-含氟丙烯酸酯杂化乳液的合成与表征[J]. 化工学报, 2012, 63(4): 1301-1307.
[12]	郭泓雨, 崔洁铭, 孙德林, 周健. 温敏性两亲嵌段共聚物相行为的耗散粒子动力学模拟[J]. 化工学报, 2012, 63(11): 3707-3715.
[13]	李磊，苏碧云，詹国雄，刘祥. Beta沸石合成研究进展[J]. 化工进展, 2012, 31(11): 2465-2469.
[14]	郑细鸣, 万灵书, 仰云峰, 徐志康. 聚丙烯微孔膜荷负电表面的构建与阻抗蛋白质吸附性能[J]. 化工学报, 2011, 62(6): 1633-1640.
[15]	马英子, 肖新颜. 核壳型纳米SiO₂/含氟聚丙烯酸酯复合乳液的合成与表征 [J]. 化工学报, 2011, 62(4): 1143-1149.