Abstract: Acrylamide/2-acrylamido alkane sulfonic acid hydrophobic associating copolymers were synthesized by micellar copolymerization. Effects of hydrophobe content, polymer concentration, salinity and surfactant on rheological behavior of copolymers were investigated and the conformation of polymers in solution was studied by means of environmental scanning electronic microscopy and dynamic light scattering. The experimental results showed that in the dilute regime the hydrophobic parts could interact intramolecularly, while in the regime where the polymer concentration was higher than the critical association concentration, intermolecular hydrophobic association became predominant. Within the limit of the solubility, the critical association concentration of the polymer decreased with the increase of the salinity. The experimental results of the solution conformation indicated the presence of the three-dimensional network structure in deionized water and the size of the mesh in the network varied with the polymer concentration. In NaG1 solution, above the critical association concentration, an increase in polymer concentration enhanced the intermolecular association and also enlarged the hydrodynamic radius. It would result in the imorovement of the thickening power of polvmers.

Key words: hydrophobic associating polymer, salt tolerance, viscosity, conformation

摘要： Acrylamide/2-acrylamido alkane sulfonic acid hydrophobic associating copolymers were synthesized by micellar copolymerization. Effects of hydrophobe content, polymer concentration, salinity and surfactant on rheological behavior of copolymers were investigated and the conformation of polymers in solution was studied by means of environmental scanning electronic microscopy and dynamic light scattering. The experimental results showed that in the dilute regime the hydrophobic parts could interact intramolecularly, while in the regime where the polymer concentration was higher than the critical association concentration, intermolecular hydrophobic association became predominant. Within the limit of the solubility, the critical association concentration of the polymer decreased with the increase of the salinity. The experimental results of the solution conformation indicated the presence of the three-dimensional network structure in deionized water and the size of the mesh in the network varied with the polymer concentration. In NaG1 solution, above the critical association concentration, an increase in polymer concentration enhanced the intermolecular association and also enlarged the hydrodynamic radius. It would result in the imorovement of the thickening power of polvmers.

关键词: 合成方法;化学性质;防水聚合物;粘性;晶体