Preparation and property of high specific surface solid base catalyst based on LiAl-LDH /C hybrid precursor

doi:10.11949/0438-1157.20201682

Abstract

Abstract:

A series of LiAl-CO₃-LDH/C hybrid composite precursors were prepared by a novel separate nucleation and aging steps we developed previously, glucose molecules were introduced as carbon source during the crystallization process of LDHs nuclei to fabricate LDHs/C hybrid composite precursor with controlled composition and structure. LiAl composite oxide based solid base catalyst with high specific surface area was obtained by topological transformation of precursors and removal of amorphous carbon components under high temperature treatment. Using XRD, FT-IR, BET, TEM, SEM, CO₂-TPD and other characterization methods, the composition, structure, texture properties and surface basicity of the catalyst were studied in detail. Knoevenagel condensation reaction of benzaldehyde and ethyl cyanoacetate was used as the probe reaction to investigate the alkali catalytic performance of the prepared catalyst. The results indicate that molar ratio of glucose to Al³⁺, hydrothermal temperature and calcination temperature are the main factors affecting the activity of catalysts, and higher hydrothermal temperature or calcination temperature has negative impact on the exposure of basic sites. The LiAl-MMO-150-3-500 catalyst, calcinated at 500℃ with the molar ratio of glucose to Al³⁺ was 3 in the corresponding precursor, has a surface area of about 229 m²·g^-1, the total basic sites of about 855 μmol·g^-1 based on phenol adsorption method, and thus exhibits the highest catalytic performance with the conversion of benzaldehyde reach up to 88.21% under our experimental conditions.

Key words: layered double hydroxides, hybrid precursor, high specific surface areas, solid base catalyst, Knoevenagel condensation reaction

摘要：

采用成核-晶化隔离法制备LiAl-CO₃-LDHs晶核，在LDHs晶核晶化的过程中引入葡萄糖分子作为碳源，构筑组成和结构可调的LDHs/C型杂化复合前体。通过高温处理，实现前体的结构拓扑转变及无定形碳组分的去除，得到高比表面积的LiAl复合金属氧化物型固体碱催化剂。采用XRD、FT-IR、BET、TEM、SEM、CO₂-TPD等表征手段对催化剂的组成、结构、织构性能、表面碱性进行了详细研究，并以苯甲醛和氰基乙酸乙酯间的Knoevenagel缩合反应为探针反应系统地研究了催化剂的碱催化性能。研究结果表明，LDHs/C杂化前体制备过程中葡萄糖与金属离子的摩尔比、水热晶化温度以及焙烧温度是影响催化剂活性的主要因素，晶化温度和焙烧温度的提升不利于碱性位的充分暴露。在150℃的水热晶化温度下，葡萄糖与Al³⁺的摩尔比为3时的杂化复合前体经500℃焙烧得到的LiAl-MMO-150-3-500固体催化剂比表面积高达229 m²·g^-1，苯酚吸附测得催化剂的总碱量为855 μmol·g^-1，对苯甲醛的转化率高达88.21%。

关键词: 层状双金属氢氧化物, 杂化前体, 高比表面积, 固体碱催化剂, Knoevenagel缩合反应

CLC Number:

TQ 131.1

SONG Yihui, LEI Zhiyi, FAN Guoli, YANG Lan, LIN Yanjun, LI Feng. Preparation and property of high specific surface solid base catalyst based on LiAl-LDH /C hybrid precursor[J]. CIESC Journal, 2021, 72(6): 3084-3094.

宋奕慧, 雷志轶, 范国利, 杨兰, 林彦军, 李峰. 基于LiAl-LDH/C杂化前体制备高比表面固体碱催化剂及其催化性能研究[J]. 化工学报, 2021, 72(6): 3084-3094.

Figures/Tables 14

References 37

1	乜贞, 伍倩, 卜令忠, 等. 国内外盐湖锂资源开发利用进展[J]. 中国盐业, 2015, (24): 45-50.
	Nie Z, Wu Q, Bu L Z, et al. Development and utilization of salt lake lithium resources at home and abroad [J]. China Salt Industry, 2015, (24): 45-50.
2	宋彭生, 李武, 孙柏, 等. 盐湖资源开发利用进展[J]. 无机化学学报, 2011, 27(5): 801-815.
	Song P S, Li W, Sun B, et al. Recent development on comprehensive utilization of salt lake resources[J]. Chinese Journal of Inorganic Chemistry, 2011, 27(5): 801-815.
3	王志国. 盐湖锂资源开发利用与研究进展[J]. 广州化工, 2011, 39(7): 23-24, 38.
	Wang Z G. Research progress on development and utilization of lithium resource[J]. Guangzhou Chemical Industry, 2011, 39(7): 23-24, 38.
4	宋彭生. 盐湖及相关资源开发利用进展[J]. 盐湖研究, 2000, 8(1): 1-16.
	Song P S. Comprehensive utilization of salt lake and related resources[J]. Journal of Salt Lake Research, 2000, 8(1): 1-16.
5	马钥德. 我国盐湖资源概况[C]//中国化工学会无机盐学术年会, 2003.
	Ma Y D. Overview of salt lake resources in China[C]// Annual Meeting of Inorganic Salts of China Chemical Industry Association. 2003.
6	张苏江, 崔立伟, 孔令湖, 等. 国内外锂矿资源及其分布概述[J]. 有色金属工程, 2020, 10(10): 95-104.
	Zhang S J, Cui L W, Kong L H, et al. Summarize on the lithium mineral resources and their distribution at home and abroad[J]. Nonferrous Metals Engineering, 2020, 10(10): 95-104.
7	柴文帅. 新冠疫情影响下的全球锂资源供需情况分析[J]. 新材料产业, 2020, (4): 46-50.
	Chai W S. Analysis of global lithium resource supply and demand under the influence of COVID-19 [J]. Advanced Materials Industry, 2020, (4): 46-50.
8	王翘楚, 孙鑫, 郝瀚, 等. 锂的城市矿产利用: 前景、挑战及政策建议[J]. 科技导报, 2020, 38(15): 6-15.
	Wang Q C, Sun X, Hao H, et al. Urban mining of lithium: prospects, challenges and policy recommendations[J]. Science & Technology Review, 2020, 38(15): 6-15.
9	张苏江, 张彦文, 张立伟, 等. 中国锂矿资源现状及其可持续发展策略[J]. 无机盐工业, 2020, 52(7): 1-7.
	Zhang S J, Zhang Y W, Zhang L W, et al. Present situation and sustainable development strategy of China's lithium resources[J]. Inorganic Chemicals Industry, 2020, 52(7): 1-7.
10	张润泽. 锂——战略性新兴资源的关键[J]. 世界有色金属, 2020(11): 259-260.
	Zhang R Z. Lithium—key to strategic emerging resources[J]. World Nonferrous Metals, 2020(11): 259-260.
11	汪明泉. 柴达木盆地一里坪盐湖富锂卤水成因研究[D]. 北京: 中国地质大学(北京), 2020.
	Wang M Q. Origin of lithium-rich brine in Yiliping salt lake, Qaidam basin[D]. Beijing: ChinaUniversity of Geosciences, 2020.
12	陈玉明, 陈喜峰, 赵宏军, 等. 南美“锂三角”战略地位日益凸显[N]. 中国矿业报, 2020-4-29(1).
	Chen Y M, Chen X F, Zhao H J, et al. The strategic position of “Lithium Triangle” in South America is increasingly prominent[N]. China Mining News, 2020-4-29(1).
13	Brindley G W, Kikkawa S. Thermal behavior of hydrotalcite and of anion-exchanged forms of hydrotalcite[J]. Clays and Clay Minerals, 1980, 28(2): 87-91.
14	Reichle W T. Catalytic reactions by thermally activated, synthetic, anionic clay minerals[J]. Journal of Catalysis, 1985, 94(2): 547-557.
15	Cavani F, Trifirò F, Vaccari A. Hydrotalcite-type anionic clays: preparation, properties and applications[J]. Catalysis Today, 1991, 11(2): 173-301.
16	魏彤, 王谋华, 魏伟, 等. 固体碱催化剂[J]. 化学通报, 2002, 65(9): 594-600.
	Wei T, Wang M H, Wei W, et al. The investigation status and development trend of solid base catalysts[J]. Chemistry, 2002, 65(9): 594-600.
17	Sideris P J, Nielsen U G, Gan Z H, et al. Mg/Al ordering in layered double hydroxides revealed by multinuclear NMR spectroscopy[J]. Science, 2008, 321(5885): 113-117.
18	Wang Q, O'Hare D. Recent advances in the synthesis and application of layered double hydroxide (LDH) nanosheets[J]. Chemical Reviews, 2012, 112(7): 4124-4155.
19	沈家骢. 超分子层状结构: 组装与功能[M]. 北京: 科学出版社, 2005.
	Shen J C, et al. Supramolecular Layer Structure: Assembly and Function[M]. Beijing: Science Press, 2005.
20	Miyata S, Kumura T, Hattori H, et al. Physico-chemical properties and structure of magnesia-alumina[J]. Nippon Kagaku Zassi, 1971, 92(6): 514-519.
21	Taylor H F W. Crystal structures of some double hydroxide minerals[J]. Mineralogical Magazine, 1973, 39(304): 377-389.
22	Zou L, Xiang X, Fan J, et al. Single-source precursor to complex metal oxide monoliths with tunable microstructures and properties: the case of Mg-containing materials[J]. Chemistry of Materials, 2007, 19(26): 6518-6527.
23	Xiang X, Hima H I, Wang H, et al. Facile synthesis and catalytic properties of nickel-based mixed-metal oxides with mesopore networks from a novel hybrid composite precursor[J]. Chemistry of Materials, 2008, 20(3): 1173-1182.
24	张毅. 镁基水滑石紫外阻隔材料的制备及在聚丙烯中的应用[D]. 北京: 中国科学院大学(中国科学院青海盐湖研究所), 2019.
	Zhang Y. Preparation of manganese-based layered double hydroxides UV shielding material and its application in polypropylene[D]. Beijing: University of Chinese Academy of Sciences, 2019.
25	阿旦春, 肖学英, 文静, 等. 氢氧化镁煅烧工艺和原料配比对氯氧镁水泥抗压强度的影响[J]. 盐湖研究, 2020, 28(3): 85-92.
	A D C, Xiao X Y, Wen J, et al. Influence of calcining process of magnesium hydroxide and raw material ratio on compressive strength of MOC based on orthogonal experiment[J]. Journal of Salt Lake Research, 2020, 28(3): 85-92.
26	绪连萧. 混合离子溶液中镁、锂分离与提取的反应-分离耦合方法的研究[D]. 北京: 北京化工大学, 2016.
	Xu L X. Research on separation and extraction Mg/Li from mixed ionic solutions with reaction-separation coupling technique[D]. Beijing: Beijing University of Chemical Technology, 2016.
27	雷志轶. 新型高比表面固体碱催化剂制备、结构及其性能研究[D]. 北京: 北京化工大学, 2009.
	Lei Z Y. Investigations on synthesis, structure and properties of new-style high-surface-area solid base catalyst[D]. Beijing: Beijing University of Chemical Technology, 2009.
28	高志. 金属加氢催化剂活性位的精细调控及其催化生物质平台分子转化性能[D]. 北京: 北京化工大学, 2018.
	Gao Z. Fine control of active sites of metal hydrogenation catalysts and their performance for catalytic transformation of biomass platform molecules[D]. Beijing: Beijing University of Chemical Technology, 2018.
29	Gao Z, Yang L, Fan G L, et al. Promotional role of surface defects on carbon-supported ruthenium-based catalysts in the transfer hydrogenation of furfural[J]. ChemCatChem, 2016, 8(24): 3769-3779.
30	Titulaer M K, Jansen J B H, Geus J W. The quantity of reduced nickel in synthetic takovite: effects of preparation conditions and calcination temperature[J]. Clays Clay Miner., 1994, 42: 249-258.
31	Marezio M, Remeika J P. Polymorphism of LiMO₂ compounds and high‐pressure single‐crystal synthesis of LiBO₂ [J]. J. Chem. Phys., 1966, 44(19): 3143-3144.
32	段雪, 张法智. 插层组装与功能材料[M]. 北京: 化学工业出版社, 2007.
	Duan X, Zhang F Z. Intercalation Assembly and Functional Materials [M]. Beijing: Chemical Industry Press, 2007.
33	Gregg S J, Sing K S W. Adsorption, Surface Area and Porosity[M]. 2nd ed. New York: Academic Press, 1982.
34	田部浩三. 新固体酸和碱及其催化作用[M]. 郑禄彬, 译. 北京: 化学工业出版社, 1992.
	Tanabe Kozo. New Solid Acids and Bases and Their Catalytic Properties[M]. Zheng L B, trans. Beijing: Chemical Industry Press, 1992.
35	雷经新, 石秋杰. 固体碱催化剂在有机合成中的应用及进展[J]. 化工时刊, 2005, 19(2): 49-53.
	Lei J X, Shi Q J. Application and progress of solid base catalysts in organicsynthesis[J]. Chemical Industry Times, 2005, 19(2): 49-53.
36	辛勤. 固体催化剂研究方法[M]. 北京: 科学出版社, 2004.
	Xin Q. Solid Catalyst Research Methods [M]. Beijing: Science Press, 2004.
37	Zhang M, Zhao Y, Liu Q, et al. A La-doped Mg-Al mixed metal oxide supported copper catalyst with enhanced catalytic performance in transfer dehydrogenation of 1-decanol[J]. Dalton Transactions (Cambridge, England), 2016, 45(3): 1093-1102.

Samples	hkl	d / nm	a / nm	c / nm	D_a / nm	D_c / nm
LiAl-LDHs-150-0	(003) (110)	0.7360 0.1466	0.2932	2.208	35.37	30.26
LiAl-LDHs-150-1	(003) (110)	0.7725 0.1474	0.2948	2.318	14.41	6.994
LiAl-LDHs-150-3	(003) (110)	0.7583 0.1471	0.2942	2.2749	12.82	5.567
LiAl-LDHs-150-4	(003) (110)	0.7730 0.1475	0.2950	2.319	19.21	4.503
LiAl-LDHs-160-3	(003) (110)	0.7814 0.1530	0.3060	2.344	13.39	5.932
LiAl-LDHs-180-3	(003) (110)	0.7729 0.1521	0.3042	2.319	17.07	6.222

Samples	hkl	d / nm	a / nm	c / nm	D_a / nm	D_c / nm
LiAl-LDHs-150-0	(003) (110)	0.7360 0.1466	0.2932	2.208	35.37	30.26
LiAl-LDHs-150-1	(003) (110)	0.7725 0.1474	0.2948	2.318	14.41	6.994
LiAl-LDHs-150-3	(003) (110)	0.7583 0.1471	0.2942	2.2749	12.82	5.567
LiAl-LDHs-150-4	(003) (110)	0.7730 0.1475	0.2950	2.319	19.21	4.503
LiAl-LDHs-160-3	(003) (110)	0.7814 0.1530	0.3060	2.344	13.39	5.932
LiAl-LDHs-180-3	(003) (110)	0.7729 0.1521	0.3042	2.319	17.07	6.222

Samples	Specific area/(m²·g^-1)	Total volume/(ml·g^-1)	Optimum pore size/nm
LiAl-MMO-150-0-500	123	0.2170	3.9
LiAl-MMO-150-1-500	225	1.0168	14.0
LiAl-MMO-150-3-500	229	0.8962	7.2
LiAl-MMO-150-4-500	241	1.2230	12.0
LiAl-MMO-160-3-500	206	0.5393	9.7
LiAl-MMO-180-3-500	178	1.0440	9.5
LiAl-MMO-150-3-400	232	0.9421	65
LiAl-MMO-150-3-700	94	0.6095	20.1

Samples	Specific area/(m²·g^-1)	Total volume/(ml·g^-1)	Optimum pore size/nm
LiAl-MMO-150-0-500	123	0.2170	3.9
LiAl-MMO-150-1-500	225	1.0168	14.0
LiAl-MMO-150-3-500	229	0.8962	7.2
LiAl-MMO-150-4-500	241	1.2230	12.0
LiAl-MMO-160-3-500	206	0.5393	9.7
LiAl-MMO-180-3-500	178	1.0440	9.5
LiAl-MMO-150-3-400	232	0.9421	65
LiAl-MMO-150-3-700	94	0.6095	20.1

Samples	Number of base sites/(μmol of phenol·g^-1)	Density of base sites/(μmol of phenol·m^-2)
LiAl-MMO-150-0-500	306	2.49
LiAl-MMO-150-1-500	635	2.82
LiAl-MMO-150-3-500	855	3.74
LiAl-MMO-150-4-500	800	3.32
LiAl-MMO-160-3-500	730	3.54
LiAl-MMO-180-3-500	635	3.57
LiAl-MMO-150-3-400	582	2.51
LiAl-MMO-150-3-700	308	3.28