后处理对改性聚氨酯系中空纤维膜压力响应行为的影响

刘海亮,肖长发,胡晓宇,刘美甜   

  1. 天津工业大学中空纤维膜材料与膜过程省部共建国家重点实验室培育基地,天津 300160
  • 收稿日期:2011-06-07 修回日期:2012-01-07 出版日期:2012-04-05 发布日期:2012-04-05
  • 通讯作者: 肖长发

Effect of post-treatment on pressure-responsive behavior of modified polyurethane based hollow fiber membrane

LIU Hailiang, XIAO Changfa, HU Xiaoyu, LIU Meitian   

  1. State Key Laboratory of Hollow Fiber Membrane Materials and Processes,Tianjin Polytechnic University,Tianjin 300160,China
  • Received:2011-06-07 Revised:2012-01-07 Online:2012-04-05 Published:2012-04-05

摘要: 采用熔融纺丝制得改性聚氨酯系中空纤维膜,通过测试水通量随压力的变化研究了拉伸、热处理温度和热处理时间对改性聚氨酯系中空纤维膜压力响应行为的影响。结果表明,所得膜可发生明显的压力响应行为,且拉伸倍数越大,膜的强度越大,压力响应行为越精确;随热处理温度升高,膜的支撑性变差,压力响应行为变弱;随热处理时间延长,膜形变回复率变低,压力响应行为减弱。

关键词: 压力响应行为, 聚氨酯, 中空纤维膜, 后处理, 熔融纺丝

Abstract: Modified polyurethane(PU)based hollow fiber membranes were prepared by the melt-spinning method.Influences of drawing, heat-treatment temperature and heat-treatment time on the pressure-responsive behavior were studied by the relationships between water flux and test pressure.The results showed that the hollow fiber membranes exhibited obvious pressure-responsive behavior.With increasing theoretical draw ratio,the strength of the membrane was greater and the pressure-responsive behavior was stronger.While, membrane pore size on inner surface and mean pore size became larger, the pure water flux(PWF)increased, the porosity first increased then slightly decreased.With increasing heat-treatment temperature, membrane support became worse and the pressure-responsive behavior became weaker.While, membrane pore size became smaller, the PWF and porosity of membrane increased and then decreased.With extending heat-treatment times, the deformation-recovery ratio of membrane diminished and the pressure-responsive behavior became weaker.The PWF and porosity of membrane first increased, then decreased, finally achieved stability.

Key words: pressure-responsive behavior, polyurethane, hollow fiber membrane, post-treatment, melt-spinning