热引发前线聚合法固化脂环族环氧树脂

doi:10.3969/j.issn.0438-1157.2014.08.059

摘要/Abstract

摘要： 采用热引发前线聚合（TFP）方法固化了脂环族环氧树脂（221树脂），研究了固化剂用量、预热温度和反应器倾斜角度等因素对聚合前线的推动速率和前线温度的影响，并利用FTIR、DSC、TG等手段对固化物结构和热性能进行了表征。研究结果表明，固化剂用量越大或预热温度越高，引发前线聚合反应所需的时间越短，前线推动速率V_f 越快，前线最高温度T_max 越高，达到最高前线温度所需时间越短；试管倾斜一定角度后，下行前线方向发生偏离，V_f有所下降；FTIR测试结果表明，采用TFP法得到的环氧固化物与采用传统热固化工艺得到的固化物有相似的红外吸收，DSC和TG测试结果表明前线聚合产物具有更高的玻璃化温度和更好的热稳定性。

关键词: 前线聚合, 环氧树脂, 固化, 推动速率, 热性能

Abstract: The method of thermal frontal polymerization (TFP) was used to cure the selected alicyclic epoxy resin. The effect of the factors, including amount of curing agent, preheating temperature and tilt angle of reactor, on frontal velocity and frontal temperature was investigated. The structure and thermal properties of the cured products were characterized with FTIR, DSC and TG analysis. The results showed that both frontal velocity V_f and maximum frontal temperature T_max increased with increasing amount of curing agent or preheating temperature, while initiation time and the time needed to reach the highest frontal temperature decreased. When the reactor tilted, the heading direction of the descending front would drift, and frontal velocity would tend to slow down. The analysis of FTIR spectrum indicated that the products obtained by the TFP method exhibited similar infrared absorption as compared to that of the products prepared by the traditional thermal curing method. DSC and TG results revealed that the products obtained by the TFP method had higher glass transition temperature and better thermal stability.

Key words: frontal polymerization, epoxy resin, curing, heading velocity, thermal properties

中图分类号:

TQ264.1

周建萍, 赵海芳, 伍辉儒, 刘志雷, 贾仕君. 热引发前线聚合法固化脂环族环氧树脂[J]. 化工学报, 2014, 65(8): 3283-3289.

ZHOU Jianping, ZHAO Haifang, WU Huiru, LIU Zhilei, JIA Shijun. Alicyclic epoxy resin cured by thermal frontal polymerization[J]. CIESC Journal, 2014, 65(8): 3283-3289.

参考文献 29

[1]	Li Guilin (李桂林). Epoxy Resin and Epoxy Coating (环氧树脂与环氧涂料)[M]. Beijing: Chemical Industry Press, 2003:1-5
[2]	Yan Qingzhi (燕青芝), Su Xintai (宿新泰), Guo Changchun (郭昌纯). Recent developments of self-propagating frontal polymerization [J]. Progress in Chemistry (化学进展), 2005, 17(6): 1081
[3]	Chechilo N M, Khvililitskii R J, Enikolopyan N S. On the phenomenon of polymerization reaction spreading[J]. Dokl Akad Nauk SSSR, 1972, 204: 1180
[4]	Szalay J, Nagy I, Banyai I, et al. High temperature copolymerization of styrene and maleic anhydride in propagating polymerization front[J]. Macromol.Rapid Commun., 1999, 20: 315-318
[5]	Hu Ting, Chen Su, Tian Yuan, et al. Frontal free-radical copolymerization of urethane-acrylates[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2006,44(9): 3018-3024
[6]	Michael F P, Vladimir A V, Lydia L L, et al. Free-radical frontal copolymerization: the dependence of the front velocity on the monomer feed composition and reactivity ratios[J]. Macromol.Theory Simul., 2003, 12: 276-286
[7]	Fang Yuan, Chen Li, Chen Su. Facile and quick synthesis of poly(N-methylolacrylamide)/polyhedral oligomeric silsesquioxane graft copolymer hybrids via frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2009, 47(4): 1136-1147
[8]	Hu Ting, Fang Yuan, Yu Huan, et al. Synthesis of poly(N-methylolacrylamide)/polymethylacrylamide hybrids via frontal free-radical polymerization[J]. Colloid and Polymer Science, 2007, 285(8): 891-898
[9]	Chen Su, Sui Jianjun,Chen Li, et al. Polyurethane-nanosilica hybrid nanocomposites synthesized by frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2005, 43(8): 1670-1680
[10]	Fang Yuan, Chen Li, Wang Caifeng, et al. Facile synthesis of fluorescent quantum dot-polymer nanocomposites via frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2010,48(10): 2170-2177
[11]	Alzari Valeria, Nuvoli Daniele, Mariani Alberto, et al. Graphene-containing thermoresponsive nanocomposite hydrogels of poly(N-isopropylacrylamide) prepared by frontal polymerization[J]. Journal of Materials Chemistry, 2011, 21(24): 8727
[12]	Zhou Jin, Tang Wenqi, Chen Su, et al.In situ access to white light-emitting fluorescent polymer nanocomposites via plasma-ignited frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2012, 50(18): 3736-3742
[13]	Scognamillo Sergio, Alzari Valeria, Mariani Alberto. Thermoresponsive super water absorbent hydrogels prepared by frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2010, 48(11): 2486-2490
[14]	Zhou Jin, Chen Li, Chen Su, et al. Available plasma-ignited frontal polymerization approach toward facile fabrication of functional polymer hydrogels[J]. Chemistry of Materials, 2010, 22(19): 5653-5659
[15]	Guo Xin, Chen Li, Chen Su, et al. Fast synthesis of versatile nanocrystal-embedded hydrogels toward the sensing of heavy metal ions and organoamines[J]. Journal of Materials Chemistry, 2011, 21(4): 1124-1129
[16]	Scognamillo Sergio, Alzari Valeria, Mariani Alberto. Thermoresponsive super water absorbent hydrogels prepared by frontal polymerization of N-isopropyl acrylamide and 3-sulfopropyl acrylate potassium salt[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2011, 49(5): 1228-1234
[17]	Feng Qiao, Yan Qingzhi, Ge Changchun. Frontal polymerization synthesis and characterization of temperature-and pH-sensitive hydrogels[J]. Colloid and Polymer Science, 2012, 291(5): 1163-1170
[18]	Sanna Roberta, Alzari Valeria, Mariani Alberto. Polymer hydrogels of 2-hydroxyethyl acrylate and acrylic acid obtained by frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2012, 50(8): 1515-1520
[19]	Zhou Zhenfang, Yu Chao, Chen Su. Facile access to poly(NMA-co-VCL) hydrogels via long range laser ignited frontal polymerization[J]. Journal of Materials Chemistry A, 2013, 1(25): 7326
[20]	Wu Xiaobin(吴校彬), Fu Heqing(傅和青), Huang Hong(黄洪), Chen Huanqin(陈焕钦). Frontal free-radical polymerization of urethane-acrylate [J]. Journal of Chemical Industry and Engineering(China) (化工学报),2007, 58(6): 1581-1586
[21]	Yan Qingzhi(燕青芝), Su Xintai(宿新泰), Zhang Wenfeng(张文峰), Ge Changchun(葛昌纯). Preparation of starch-g-sodium acrylate/acrylamide superabsorbent via frontal polymerization [J]. Chemical Journal of Chinese Universities (高等学校化学学报), 2005, 26(7): 1363-1365
[22]	Chen Su(陈苏), Feng Cang(丰沧), Sui Jianjun(眭建军). Study on frontal polymerization of polyurethanepnanosilica sol hybrids[J]. Acta Polymerica Sinica(高分子学报), 2005(1):1-3
[23]	Feng Qiao(冯巧), Lu Guodong(卢国冬), Liu Yuqiong(刘玉琼), Yan Qingzhi(燕青芝), Ge Changchun(葛昌纯). Frontal polymerization of acrylamide for preparing porous polyacrylamide hydrogel[J]. Acta Polymerica Sinica(高分子学报),2009(7): 674-679
[24]	Chekanov Y, Arrington D, Brust G, Pojman J A. Frontal curing of epoxy resins: comparison of mechanical and thermal properties to batch-cured materials[J]. Journal of Applied Polymer Science, 1997, 66:1209-1216
[25]	Frulloni E, Salinas M M, Torre L, Mariani A, Kenny J M. Numerical modeling and experimental study of the frontal polymerization of the diglycidyl ether of bisphenol A/diethylenetriamine epoxy system[J]. Journal of Applied Polymer Science, 2005,96(5): 1756-1766
[26]	Mariani Alberto, Bidali Simone, Caria Giuseppe, et al. Synthesis and characterization of epoxy resin-montmorillonite nanocomposites obtained by frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2007, 45(11): 2204-2211
[27]	Scognamillo Sergio, Alzari Valeria, Nuvoli Daniele, Mariani Alberto. Hybrid organic/inorganic epoxy resins prepared by frontal polymerization[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2010, 48: 4721-4725
[28]	Zhao Haifang (赵海芳). Investigation of frontal polymerization of epoxy resin [D]. Nanchang: Nanchang Hangkong University, 2012
[29]	Mervin Bazile J R, Archie Nichols H, Pojman J A, et al. Effect of orientation on thermoset frontal polymerization[J].Journal of Polymer Science Part A: Polymer Chemistry, 2002, 40: 3504-3508