Abstract: A series of waterborne polyurethanes (WPUs)with 50% solid content were prepared through a prepolymer process.The properties of the dispersion and its film were characterized by Fourier transform infrared spectroscopy (FT-IR), particle size analyzer, X-ray diffraction (XRD), differential scanning calorimetry (DSC)and tensile test machine.The influence of HDI/IPDI mole ratio on the properties of waterborne polyurethane dispersion, its film and the adhesive strength to EVA/PVC substrate were studied.The relationship between adhesive strength and time was analyzed.The results indicated that the WPU dispersion, crystallinities of soft segment and hard segment were improved with increasing HDI/IPDI mole ratio, while tensile strength of films significantly increased and then showed a small decrease, and the elongation at break increased first, then decreased.WPU films exhibited excellent waterproof performance, and the amount of water absorption was as low as 5.0%（mass）.The test result showed that all WPUs prepared exhibited outstanding adhesive strength to EVA/PVC substrate, and the joint failure of EVA/PVC substrates was all caused by the failure of interface after 24 h.With increasing mole ratio of HDI/IPDI,the adhesive strength of adhesive to EVA/PVC substrate increased, and when the mole ratio of HDI/IPDI was 7∶1, the performance of WPU adhesive was the best.

Key words: waterborne polyurethane, crystallinity, mechanical property, adhesive property

摘要： 采用预聚体分散法制备了一系列固含量为50%的水性聚氨酯(WPU)，并通过傅里叶红外光谱(FT-IR)、粒径分析仪、X射线衍射(XRD)、差示扫描量热分析(DSC)、拉力试验机等仪器进行表征，研究了HDI/IPDI摩尔比对WPU的乳液性能和胶膜结晶性能、力学性能、耐水性能，以及基材EVA/PVC粘接性能的影响，分析了不同摩尔比的HDI/IPDI和粘接时间与WPU胶黏剂对EVA/PVC粘接性能的关系。研究发现，随着HDI/IPDI摩尔比增加，水性聚氨酯的乳液性能、软硬段的结晶性都得到提高，而胶膜拉伸强度呈先增大后减小的趋势，断裂伸长率则先减小后增大。所有WPU胶膜都有很好耐水性，胶膜吸水率都在5.0%（质量）以下。粘接实验结果表明，WPU胶黏剂对EVA/PVC具有优异的粘接性能，24 h后可对基材产生界面破坏，随着HDI/IPDI摩尔比增加，胶黏剂的粘接强度增大。当HDI/IPDI=7∶1时，水性聚氨酯的综合性能最好。

关键词: 水性聚氨酯, 结晶性能, 力学性能, 粘接性能