Tensile properties of ICM polycarbonate part under low temperature

doi:10.11949/j.issn.0438-1157.20150292

CIESC Journal ›› 2015, Vol. 66 ›› Issue (10): 4268-4274.DOI: 10.11949/j.issn.0438-1157.20150292

Previous Articles Next Articles

Tensile properties of ICM polycarbonate part under low temperature

JIANG Jing^1,2,3, WANG Xiaofeng^2,3,4, HOU Jianhua^2,3,4, LI Qian^2,3, XU Yiyang^2,3,4

1 School of Material Science and Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China;
2 National Centre for International Joint Research of Micro-Nano Moulding Technology, Zhengzhou 450001, Henan, China;
3 Key Laboratory of Micro Molding Technology at Henan Province, Zhengzhou 450001, Henan, China;
4 School of Mechanics and Engineering Science, Zhengzhou University, Zhengzhou 450001, Henan, China

Received:2015-03-10 Revised:2015-05-26 Online:2015-10-05 Published:2015-10-05
Supported by:
supported by the National Natural Science Foundation of China (11372286) and the Specialized Research Fund for the Doctoral Program of Higher Education of China (20124101110007).

注射压缩成型聚碳酸酯制品的低温拉伸力学性能

蒋晶^1,2,3, 王小峰^2,3,4, 侯建华^2,3,4, 李倩^2,3, 徐轶洋^2,3,4

1 郑州大学材料科学与工程学院, 河南郑州 450001;
2 微纳成型技术国际联合研究中心, 河南郑州 450001;
3 河南省微成型技术重点实验室, 河南郑州 450001;
4 郑州大学力学与工程科学学院, 河南郑州 450001

通讯作者: 李倩
基金资助:
国家自然科学基金项目(11372286);高等学校博士学科点专项科研联合资助基金项目(20124101110007)。

Abstract

Abstract:

Tensile properties of conventional injection molding (IM) PC (polycarbonate) and injection-compression molding (ICM) parts in room and low temperature were compared. The effect of five process parameters (melt and mold temperature, compression distance, delay time and compression force) on residual stress and tensile properties of ICM parts under low temperature was investigated systematically. The results showed that higher tensile yield stress and Modulus were found for ICM parts compared with IM part. Tensile properties of ICM or IM parts were improved under low temperature. Secondary transition were discovered around -40℃ for PC. As the most influenced morphology, the residual stress of ICM parts has the opposite variation as the function of process parameters. Higher melt and molding temperature, bigger compression distance, shorter delay time and smaller compression force can be helpful to give lower residual stress value, and thus to improve the tensile properties.

Key words: polymers, polycarbonate, injection-compression molding, viscosity, residual stress, mechanical properties

摘要：

以聚碳酸酯为材料,利用自行设计带有压缩功能的模具,采用常规注塑成型(IM)和注射压缩成型方法(ICM)对比研究制品在常温和低温环境下的拉伸力学性能;基于单因素实验方法,研究熔体温度、模具温度、模板压缩距离、延迟时间和压缩力对ICM制品残余应力和低温拉伸性能的影响规律。结果表明:在相同的环境温度下,ICM制品较IM制品有较大的屈服应力和弹性模量;低温环境下样品的拉伸性能有所提升,并在-40℃附近出现了聚碳酸酯分子的次级玻璃化转变;残余应力是影响ICM制品低温拉伸性能的主要因素,较高的熔体温度、模具温度、模板压缩距离,以及较短的延迟时间,较小的压缩力会减小ICM制品的残余应力,提高制品的低温拉伸性能。

关键词: 聚合物, 聚碳酸酯, 注射压缩成型, 黏度, 残余应力, 机械性能

CLC Number:

TQ028.8

JIANG Jing, WANG Xiaofeng, HOU Jianhua, LI Qian, XU Yiyang. Tensile properties of ICM polycarbonate part under low temperature[J]. CIESC Journal, 2015, 66(10): 4268-4274.

蒋晶, 王小峰, 侯建华, 李倩, 徐轶洋. 注射压缩成型聚碳酸酯制品的低温拉伸力学性能[J]. 化工学报, 2015, 66(10): 4268-4274.

References 19

[1]	Wu Zuquan (吴祖铨), Wu Nian (吴念). Polycarbonate Resin and Application (聚碳酸酯树脂及其应用) [M]. Beijing: Chemical Industry Press, 2009: 1-8.
[2]	Lee S H, Kim S Y, et al. Warpage of a large-sized orthogonal stiffened plate produced by injection molding and injection compression molding [J]. Journal of Applied Polymer Science, 2010, 116 (6): 3460-3467.
[3]	Materials World Group. Living it large injection moulding aircraft canopies [J]. Materials World, 2003, 11 (8): 19-20.
[4]	Wu C H, Chen W S. Injection molding and injection compression molding of three-beam grating of DVD pickup lens [J]. Sensor. Actuat A: Phys., 2006, 125 (2): 367-375.
[5]	Huang M S, Chung C F. Injection molding and injection compression molding of thin-walled light-guided plates with V-grooved micro features [J]. J. Appl. Polym. Sci., 2011, 121 (2): 1151-1159.
[6]	Huang Hanxiong, Li Kun, Li Sha. Injection-compression molded part shrinkage uniformity comparison between semicrystalline and amorphous plastics [J]. Polymer—Plastics Technology and Engineering, 2009, 48: 64-68.
[7]	Guan Weisheng, Huang Hanxiong. Manipulation and online monitoring of micro-replication quality during injection-compression molding [J]. Micromech. Microeng, 2012, (22): 1-10.
[8]	Hopmann Ch, Michaeli W, Hessner S, Walach P. Determination and comparison of process-and quality-characteristics of injection-compression moulded polymer optics [J]. Nanosystems, 2011, 3 (3): 174-179.
[9]	Chen Yuhong (陈宇宏), Yuan Yuan (袁渊), Zhang Yisheng (张毅生), Li Xi (李曦), Zhan Maosheng (詹茂盛). Residual stress,warpage and shrinkage analysis of injection molded transparent panel based on optical distortion [J]. Journal of Aeronautical Materials (航空材料学报), 2008, 28 (6): 82-87.
[10]	Chen Yuhong (陈宇宏), Yuan Yuan (袁渊), Liu Xiaoyan (刘小艳), Guo Dandan (郭丹丹), Bai Yifeng (白一峰). Comparison on optical properties of injection molded and injection-compression molded transparencies [J]. Journal of Aeronautical Materials (航空材料学报), 2011, 31 (2): 55-60.
[11]	He Manjun (何曼君), Chen Weixiao (陈维孝), Dong Xixia (董西侠). Polymer Physics (高分子物理) [M]. Shanghai: Fudan University Press, 2000: 315-332.
[12]	Khondker O, Yang X, Usui N, et al. Mechanical properties of textile-inserted PP/PP knitted composites using injection-compression molding [J]. Compos. Part A: Appl Sci Manufac., 2006, 37 (12): 2285-2299.
[13]	Starkweather H W, Brooks R E. Effect of spherulites on the mechan-ical properties of nylon 66 [J]. J. Appl. Polym. Sci., 1959, 1 (2): 236-239.
[14]	Chen S C, Peng H S, Huang L T, Chung M S. Investigations of the tensile properties on polycarbonate thin-wall injection molded parts [J]. J. Reinf. Plast. Compos., 2003, 22 (5): 479-494.
[15]	Zhang Guo (张果). Research on the influence of process parameters on the properties of injection compression molded product based on numerical simulation [D]. Zhengzhou: Zhengzhou University, 2013.
[16]	Xie Chunwen (谢春稳). Residual stress formation mechanism and optical property of injection compression-molded product [D]. Beijing: Beijing University of Chemical Technology, 2013.
[17]	Menard K P. Dynamic Mechanical Analysis [M]. 2nd ed. New York: CRC Press, 2008: 95-118.
[18]	Denizart O, Vincent M, Agassant J F.Thermal stresses and strains in injection moulding: experiments and computations [J]. Journal of Materials Science, 1995, 30 (2): 552-560.
[19]	Guan Weisheng, Huang Hanxiong, Wang Bin. Poiseuille_squeeze flow induced crystallization in microinjection compression molded isotactic polypropylene [J]. Journal of Polymer Science, Part B: Polymer Physics, 2013, 51: 358-367.

Tensile properties of ICM polycarbonate part under low temperature

注射压缩成型聚碳酸酯制品的低温拉伸力学性能

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

References 19

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Shuang LIU, Linzhou ZHANG, Zhiming XU, Suoqi ZHAO. Study on molecular level composition correlation of viscosity of residual oil and its components [J]. CIESC Journal, 2023, 74(8): 3226-3241.
[2]	Jie LIU, Lisheng WU, Jinjin LI, Zhenghong LUO, Yinning ZHOU. Preparation and properties of polyether-based vinylogous urethane reversible crosslinked polymers [J]. CIESC Journal, 2023, 74(7): 3051-3057.
[3]	Qin YANG, Chuanjian QIN, Mingzi LI, Wenjing YANG, Weijie ZHAO, Hu LIU. Fabrication and properties of dual shape memory MXene based hydrogels for flexible sensor [J]. CIESC Journal, 2023, 74(6): 2699-2707.
[4]	Bowen LEI, Jianhua WU, Qihang WU. Research on high injection superheat cycle for R290 low pressure ratio heat pump [J]. CIESC Journal, 2023, 74(5): 1875-1883.
[5]	Bimao ZHOU, Shisen XU, Xiaoxiao WANG, Gang LIU, Xiaoyu LI, Yongqiang REN, Houzhang TAN. Effect of burner bias angle on distribution characteristics of gasifier slag layer [J]. CIESC Journal, 2023, 74(5): 1939-1949.
[6]	Shaoyun CHEN, Dong XU, Long CHEN, Yu ZHANG, Yuanfang ZHANG, Qingliang YOU, Chenglong HU, Jian CHEN. Preparation and adsorption properties of monolayer polyaniline microsphere arrays [J]. CIESC Journal, 2023, 74(5): 2228-2238.
[7]	Xuehong WU, Linlin LUAN, Yanan CHEN, Min ZHAO, Cai LYU, Yong LIU. Preparation and thermal properties of degradable flexible phase change films [J]. CIESC Journal, 2023, 74(4): 1818-1826.
[8]	Yongquan ZHANG, Weiwei XUAN. Mechanism of alkali metal/(FeO+CaO+MgO) influence on the structure and viscosity of silicate ash slag [J]. CIESC Journal, 2023, 74(4): 1764-1771.
[9]	Haiqin LIU, Bowen LI, Zhe LING, Liang LIU, Juan YU, Yimin FAN, Qiang YONG. Facile preparation and properties of chemically modified galactomannan films via mild hydroxy-alkyne click reaction [J]. CIESC Journal, 2023, 74(3): 1370-1378.
[10]	Shuai WANG, Fukai YANG, Xinyu XU. Preparation and characterization of flame retardant bio-based polyols polyurethane foam [J]. CIESC Journal, 2023, 74(3): 1399-1408.
[11]	Dong XU, Du TIAN, Long CHEN, Yu ZHANG, Qingliang YOU, Chenglong HU, Shaoyun CHEN, Jian CHEN. Preparation and electrochemical energy storage of polyaniline/manganese dioxide/polypyrrole composite nanospheres [J]. CIESC Journal, 2023, 74(3): 1379-1389.
[12]	Yue HU, Shoujun MA, Xigao JIAN, Zhihuan WENG. Study on curing phthalonitrile resin with novel poly(phthalazinone ether nitrile) [J]. CIESC Journal, 2023, 74(2): 871-882.
[13]	Zhiyuan JIN, Guorong SHAN, Pengju PAN. Preparation and heat and salt resistance of AM/AMPS/SSS terpolymer [J]. CIESC Journal, 2023, 74(2): 916-923.
[14]	Jiaqing ZHANG, Rongpei JIANG, Weikang SHI, Boxiang WU, Chao YANG, Zhaohui LIU. Study on viscosity-temperature characteristics and component characteristics of rocket kerosene [J]. CIESC Journal, 2023, 74(2): 653-665.
[15]	Shaojie ZHENG, Jianbin WANG, Jijiang HU, Bo-Geng LI, Wenbo YUAN, Zong WANG, Zhen YAO. Regulation of structure and mechanical properties of poly(propylene-butene) alloys by monomer composition switching [J]. CIESC Journal, 2023, 74(2): 904-915.