Photocatalytic degradation property of hemicellulose/TiO2 composite gel

doi:10.11949/j.issn.0438-1157.20151542

Abstract

Abstract:

Hemicellulose/TiO₂ composite gel was prepared using hemicellulose and TiO₂ nanoparticles. Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM) were used to study the structure and morphology of the hydrogel. Experimental analysis showed that the hemicellulose was successfully grafted with the polyacrylic acid and a porous hydrogel was observed. The pore size of the hydrogel decreased with the increase of the TiO₂ content. In addition, the swelling properties and photocatalytic degradation properties of the hydrogel were also investigated. Experimental results showed that the swelling ratio of the hydrogel increased at first and then decreased with the increase of pH while kept decreasing with the increase of the TiO₂ content. The degradation ratio of methylene blue increased at first and then decreased with the increase of the TiO₂ content or a rise of pH value of the methylene blue solution, and it also increased with the increase of the initial concentration of methylene blue solution.

Key words: polymer, nanoparticles, waste water, degradation

摘要：

以半纤维素和TiO₂纳米粒子为原料制得半纤维素/TiO₂复合凝胶。分别用红外光谱分析和扫描电镜对复合水凝胶进行了表征,分析表明半纤维素上成功接枝聚丙烯酸,凝胶呈现多孔结构,且随着TiO₂含量的增加凝胶孔径减小。考察了半纤维素/TiO₂复合凝胶的溶胀性能以及对亚甲基蓝的光催化降解性能,研究表明半纤维素/TiO₂复合凝胶的溶胀率随着TiO₂粒子含量的增加而减小,随着pH的增大先增大后减小;对亚甲基蓝染料的降解率随着TiO₂含量的增加先增大后减小,随着pH的增大先增大后减小,随着亚甲基蓝初始浓度的增大而增大。

关键词: 聚合物, 纳米粒子, 废水, 降解

CLC Number:

O648.17

SUN Xiaofeng, LI Chi, XIA Xiuyang, ZHOU Rui, WANG Yaxiong, FENG Yang. Photocatalytic degradation property of hemicellulose/TiO₂ composite gel[J]. CIESC Journal, 2016, 67(5): 2070-2077.

孙晓锋, 李驰, 夏修阳, 周睿, 王亚雄, 冯阳. 半纤维素/TiO₂复合凝胶的光催化降解性能[J]. 化工学报, 2016, 67(5): 2070-2077.

References 22

[1]	任南琪, 周显娇, 郭婉茜, 等. 染料废水处理技术研究进展 [J]. 化工学报, 2013, 64 (1): 84-94. REN N Q, ZHOU X J, GUO W Q, et al. A review on treatment methods of dye wastewater [J]. CIESC Journal, 2013, 64 (1): 84-94.
[2]	任健, 马宏瑞, 周杰, 等. 不同高级氧化体系处理染料废水的效果研究 [J]. 水处理技术, 2011, 37 (4): 60-63. REN J, MA H R,ZHOU J, et al. The comparison of treatment effect of dyeing wastewater with different advanced oxidation systems [J]. Technology of Water Treatment, 2011, 37 (4): 60-63.
[3]	PALMA C, CARVAJAL A, VASQUEZ C, et al. Wastewater treatment for removal of recalcitrant compounds: a hybrid process for decolorization and biodegradation of dyes [J]. Chinese Journal of Chemical Engineering, 2011, 19 (4): 621-625.
[4]	丛燕青,李哲,张轶,等. Fe2O3/TiO2纳米管的制备及其光电催化降解染料废水性能 [J]. 催化学报, 2012, 33 (8): 1402-1409. CONG Y Q, LI Z, ZHANG Y, et al. Fabrication of Fe2O3/TiO2 nanotube electrode and its photoelectrocatalytic performance in dye wastewater degradation [J]. Chinese Journal of Catalysis, 2012, 33 (8): 1402-1409.
[5]	高春涛, 蔡以兵, 王清清, 等. TiO2纳米纤维的制备及其对染料的光催化降解性能 [J]. 功能材料,2013, 44 (2): 240-243. GAO C T, CAI Y B, WANG Q Q, et al. Preparation and photocatalytic degradation properties on dyes of TiO2 nanofibers [J]. Journal of Functional Materials, 2013, 44 (2): 240-243.
[6]	林俊雄, 詹树林, 方明晖, 等. 聚丙烯酰胺/硅藻土复合材料处理染料废水 [J]. 稀有金属材料与工程, 2010, 39 (2): 418-421. LIN J X, ZHAN S L, FANG M H, et al. Treatment of dyeing wastewater by polyacrylamide/diatomite composite [J]. Rare Metal Materials and Engineering, 2010, 39 (2): 418-421.
[7]	李倩, 岳钦艳, 高宝玉, 等. 阳离子聚合物/膨润土纳米复合吸附材料的性能及对红色染料的脱色研究 [J]. 化工学报, 2006, 57 (2): 436-441. LI Q, YUE Q Y, GAO B Y, et al. Properties and decoloration of orcein dye on epichlorohydrin-dimethylamine cationic polymer/bentonite nanocomposite adsorption material [J]. Journal of Chemical Industry and Engineering (China), 2006, 57 (2): 436-441.
[8]	王巧巧, 倪哲明, 张峰, 等. 镁铝二元水滑石的焙烧产物对染料废水酸性红88的吸附 [J]. 无机化学学报, 2009, 25 (12): 2156-2162. WANG Q Q, NI Z M, ZHANG F, et al. Absorption of acid red 88 from aqueous solution by calcined layered double hydroxides [J]. Chinese Journal of Inorganic Chemistry, 2009, 25 (12): 2156-2162.
[9]	赵冰, 徐君. 臭氧-活性炭-过氧化氢法处理染料废水的研究 [J]. 中国资源综合利用, 2011, 29 (4): 27-30. ZHAO B, XU J. The research on treating dye wastewater by ozone-activated carbon-hydrogen peroxide [J]. China Resources Comprehensive Utilization, 2011, 29 (4): 27-30.
[10]	张烨, 郭健, 杨晓泉, 等. MTG酶诱导大豆11S球蛋白透明冷致水凝胶的制备 [J]. 化工学报, 2011, 62 (12): 3560-3568. ZHANG Y, GUO J, YANG X Q, et al. Preparation of microbial transglutaminase-induce soybean glycinin transparent cold-set hydrogels [J]. CIESC Journal, 2011, 62 (12): 3560-3568.
[11]	冯剑, 黄永民, 刘洪来. 凝胶网络中溶剂性质的分子动力学模拟 [J]. 化工学报, 2007, 58 (5): 1073-1076. FENG J, HUANG Y M, LIU H L. Molecular dynamics simulation of properties of solvent in gel network [J]. Journal of Chemical Industry and Engineering (China), 2007, 58 (5): 1073-1076.
[12]	张青松, 彭喆, 赵义平, 等. 不同种类水凝胶对结晶紫染料的吸附性能研究 [J]. 材料工程, 2011, (12): 20-24. ZHANG Q S, PENG Z, ZHAO Y P, et al. Absorption characteristics of crystal violet dye by different types of hydrogel [J]. Journal of Materials Engineering, 2011, (12): 20-24.
[13]	李亚婧, 孙晓锋, 叶青, 等. 新型半纤维素基磁性水凝胶的制备及性能 [J]. 物理化学学报, 2014, 30 (1): 111-120. LI Y J, SUN X F, YE Q, et al. Preparation and properties of a novel hemicellulose-based magnetic hydrogel [J]. Acta Physico-Chimica Sinica, 2014, 30 (1): 111-120.
[14]	余紫苹, 彭红, 林妲, 等. 植物半纤维素结构研究进展 [J]. 高分子通报, 2011, 40 (6): 48-54. YU Z P, PENG H, LIN D, et al. The structure characteristic of hemicellulose: a review [J]. Polymer Bulletin, 2011, 40 (6): 48-54.
[15]	黎新明, 尹国强, 崔英德. 基于半纤维素和木素的水凝胶研究进展 [J]. 化工新型材料, 2011, 39 (9): 21-25. LI X M, YIN G Q, CUI Y D. Progress of hydrogels based on hemicellulose and lignin [J]. New Chemical Materials, 2011, 39 (9): 21-25.
[16]	崔玉民, 韩金霞. 光催化降解水中有机污染物研究现状与展望 [J]. 染料化学学报, 2004, 32 (1): 123-128. CUI Y M, HAN J Y. Current status of research and prospect on photocatalytic degradation of organic pollutants in water [J]. Journal of Fuel Chemistry and Technology, 2004, 32 (1): 123-128.
[17]	郑华荣, 崔言娟, 张金水, 等. Pt助剂对N掺杂TiO2可见光光催化性能的影响 [J]. 催化学报, 2011, 32 (1): 100-105. ZHENG H R, CUI Y J, ZHANG J S, et al. Influence of Pt promoter on the visible light photocatalytic properties of N-doped TiO2 [J]. Chinese Journal of Catalysis, 2011, 32 (1): 100-105.
[18]	肖羽堂, 许双双, 杜勇超, 等. 新型TiO2光催化复合分离膜研究进展 [J]. 无机材料学报, 2011, 26 (4): 337-346. XIAO Y T, XU S S, DU Y C, et al. Progress of novel TiO2 photocatalytic separation membrane [J]. Journal of Inorganic Matericals, 2011, 26 (4): 337-346.
[19]	ZHAO K, FENG L, LI Z, et al. Preparation, characterization and photocatalytic degradation properties of TiO2/calcium alginate composite film and the recovery of TiO2 nanoparticle [J]. RSC Advances, 2014, 4 (93): 51321-51329.
[20]	XIAO C, FANG Y, ZHANG G. or TiO2/Fe3O4-containing PVA-based microgels for controlled photocatalytic degradation of methyl orange [J]. Polymer Composites, 2015, doi: 10.1002/pc.23568.
[21]	SUN X F, WANG H H, JING Z X, et al. Hemicellulose-based pH-sensitive and biodegradable hydrogel for controlled drug delivery [J]. Carbohydrate Polymers, 2013, 92: 1357-1366.
[22]	裴福云, 徐慎刚, 刘应良, 等. 染料敏化二氧化钛-石墨烯杂化材料光催化水分解制氢 [J]. 化工学报, 2013, 64 (8): 3062-3069. PEI F Y, XU S G, LIU Y L, et al. Photocatalytic hydrogen evolution from water by dye-sensitized titania/graphene nanocomposite [J]. CIESC Journal, 2013, 64 (8): 3062-3069.

Photocatalytic degradation property of hemicellulose/TiO₂ composite gel

半纤维素/TiO₂复合凝胶的光催化降解性能

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References 22

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Baiyu YANG, Yue KOU, Juntao JIANG, Yali ZHAN, Qinghong WANG, Chunmao CHEN. Chemical conversion of dissolved organic matter in petrochemical spent caustic along a wet air oxidation pretreatment process [J]. CIESC Journal, 2023, 74(9): 3912-3920.
[2]	Rubin ZENG, Zhongjie SHEN, Qinfeng LIANG, Jianliang XU, Zhenghua DAI, Haifeng LIU. Study of the sintering mechanism of Fe₂O₃ nanoparticles based on molecular dynamics simulation [J]. CIESC Journal, 2023, 74(8): 3353-3365.
[3]	Xin YANG, Xiao PENG, Kairu XUE, Mengwei SU, Yan WU. Preparation of molecularly imprinted-TiO₂ and its properties of photoelectrocatalytic degradation of solubilized PHE [J]. CIESC Journal, 2023, 74(8): 3564-3571.
[4]	Ao ZHANG, Yingwu LUO. Low modulus, high elasticity and high peel adhesion acrylate pressure sensitive adhesives [J]. CIESC Journal, 2023, 74(7): 3079-3092.
[5]	Jie WANG, Xiaolin QIU, Ye ZHAO, Xinyang LIU, Zhongqiang HAN, Yong XU, Wenhan JIANG. Preparation and properties of polyelectrolyte electrostatic deposition modified PHBV antioxidant films [J]. CIESC Journal, 2023, 74(7): 3068-3078.
[6]	Jie LIU, Lisheng WU, Jinjin LI, Zhenghong LUO, Yinning ZHOU. Preparation and properties of polyether-based vinylogous urethane reversible crosslinked polymers [J]. CIESC Journal, 2023, 74(7): 3051-3057.
[7]	Yong LI, Jiaqi GAO, Chao DU, Yali ZHAO, Boqiong LI, Qianqian SHEN, Husheng JIA, Jinbo XUE. Construction of Ni@C@TiO₂ core-shell dual-heterojunctions for advanced photo-thermal catalytic hydrogen generation [J]. CIESC Journal, 2023, 74(6): 2458-2467.
[8]	Juhui CHEN, Qian ZHANG, Lingfeng SHU, Dan LI, Xin XU, Xiaogang LIU, Chenxi ZHAO, Xifeng CAO. Study on flow characteristics of nanoparticles in a rotating fluidized bed based on DEM method [J]. CIESC Journal, 2023, 74(6): 2374-2381.
[9]	Zhen LONG, Jinhang WANG, Junjie REN, Yong HE, Xuebing ZHOU, Deqing LIANG. Experimental study on inhibition effect of natural gas hydrate formation by mixing ionic liquid with PVCap [J]. CIESC Journal, 2023, 74(6): 2639-2646.
[10]	Yanmei ZHANG, Tao YUAN, Jiang LI, Yajie LIU, Zhanxue SUN. Study on the construction of high-efficient SRB mixed microflora and its performance under acid stress [J]. CIESC Journal, 2023, 74(6): 2599-2610.
[11]	Qin YANG, Chuanjian QIN, Mingzi LI, Wenjing YANG, Weijie ZHAO, Hu LIU. Fabrication and properties of dual shape memory MXene based hydrogels for flexible sensor [J]. CIESC Journal, 2023, 74(6): 2699-2707.
[12]	Ruikang LI, Yingying HE, Weipeng LU, Yuanyuan WANG, Haodong DING, Yongming LUO. Study on the electrochemical enhanced cobalt-based cathode to activate peroxymonosulfate [J]. CIESC Journal, 2023, 74(5): 2207-2216.
[13]	Jianhua ZHANG, Mengmeng CHEN, Yawen SUN, Yongzhen PENG. Efficient nitrogen and phosphorus removal from domestic wastewater via simultaneous partial nitritation and phosphorus removal combined Anammox [J]. CIESC Journal, 2023, 74(5): 2147-2156.
[14]	Shaoyun CHEN, Dong XU, Long CHEN, Yu ZHANG, Yuanfang ZHANG, Qingliang YOU, Chenglong HU, Jian CHEN. Preparation and adsorption properties of monolayer polyaniline microsphere arrays [J]. CIESC Journal, 2023, 74(5): 2228-2238.
[15]	Laiming LUO, Jin ZHANG, Zhibin GUO, Haining WANG, Shanfu LU, Yan XIANG. Simulation and experiment of high temperature polymer electrolyte membrane fuel cells stack in the 1—5 kW range [J]. CIESC Journal, 2023, 74(4): 1724-1734.