V2O5-MoO3/TiO2催化滤袋的制备及中试应用

doi:10.11949/0438-1157.20210822

化工学报 ›› 2021, Vol. 72 ›› Issue (11): 5598-5606.DOI: 10.11949/0438-1157.20210822

• 催化、动力学与反应器 • 上一篇下一篇

V₂O₅-MoO₃/TiO₂催化滤袋的制备及中试应用

史玉婷^1,²(),皇甫林²,李长明³,王月⁴,高士秋²,伞晓广¹,韩振南¹,余剑²()

^1.沈阳化工大学化学工程学院，辽宁沈阳 110142
^2.中国科学院过程工程研究所多相复杂系统国家重点实验室，北京 100190
^3.北京工商大学生态环境学院，北京 100048
^4.浙江佰誉智能技术有限公司，浙江衢州 324000

收稿日期:2021-06-21 修回日期:2021-08-30 出版日期:2021-11-05 发布日期:2021-11-12
通讯作者: 余剑
作者简介:史玉婷（1995—），女，硕士研究生，shiyuting1107@163.com
基金资助:
国家重点研发计划项目(2019YFE0197200)

Preparation and pilot-scale test of V₂O₅-MoO₃/TiO₂ catalytic filter bag

Yuting SHI^1,²(),Lin HUANGFU²,Changming LI³,Yue WANG⁴,Shiqiu GAO²,Xiaoguang SAN¹,Zhennan HAN¹,Jian YU²()

^1.College of Chemical Engineering, Shenyang University of Chemical Technology, Shenyang 110142, Liaoning, China
^2.State Key Laboratory of Multi-phase Complex System, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China
^3.School of Ecology and Environment, Beijing Technology and Business University, Beijing 100048, China
^4.Zhejiang Baiyu Intelligent Technology Co. , Ltd. , Quzhou 324000, Zhejiang, China

Received:2021-06-21 Revised:2021-08-30 Online:2021-11-05 Published:2021-11-12
Contact: Jian YU

摘要/Abstract

摘要：

为解决现有Mn基催化滤袋SO₂中毒的问题，制备了基于V₂O₅-MoO₃/TiO₂的催化滤袋，用于在180~260℃范围内同时去除NO_x和粉尘。实验结果表明，双层滤袋在气体过滤面速度为0.2 m/min时具有良好的脱硝活性和抗硫抗水性能。在纯氧玻璃窑炉中试中采用制备的双层催化滤袋进行了试验，烟气量为2000~3000 m³/h、SO₂浓度在20~30 mg/m³范围内、水蒸气含量10%（体积分数）、NO_x浓度为400~550 mg/m³，在170~210℃范围内NO_x转化率可达到88.14%~95.06%，验证了催化滤袋的脱硝性能；连续运行1500 h后，活性出现5%左右的微弱衰减；在高硫烟气条件下（300~500 mg/m³）连续运行100 h发现催化滤袋失活，SEM-EDS和XPS表征证明催化剂失活是由于硫铵类物质在滤袋纤维表面沉积，部分活性位点被覆盖所致。

关键词: V₂O₅-MoO₃/TiO₂, 催化滤袋, 选择性催化还原, 抗硫抗水, 中试应用

Abstract:

In order to solve the SO₂ poisoning problem of the existing Mn-based catalytic filter bags, a catalytic filter bag based on V₂O₅-MoO₃/TiO₂ was prepared for the simultaneous removal of NO_x and dust in the range of 180—260℃. The experimental results displayed that the double-layer filter bags had excellent denitration activity and SO₂/H₂O-resistant stability when the gas filter surface velocity was 0.2 m/min. The double-layer catalytic filter bags were used in the pilot-scale test of pure oxygen glass kiln, when the flue gas volume was about 2000—3000 m³/h, SO₂ concentration in the range of 20—30 mg/m³, the water vapor content was 10%(vol) and NO_x concentration in the range of 400—550 mg/m³, the NO_x conversion reached 88.14%—95.06% from 170℃ to 210℃, and the good denitration performance of catalytic filter bags had been verified. After 1500 h of continuous operation, the activity showed a slight decay of about 5%. Under high-sulfur flue gas conditions (300—500 mg/m³) for 100 h continuous operation, the catalytic filter bag was found to be deactivated. SEM-EDS and XPS characterizations proved that the catalyst deactivation was due to the deposition of ammonium sulfate on the surface of the filter bag fiber and the part of active site is covered.

Key words: V₂O₅-MoO₃/TiO₂, catalytic filter bag, SCR, SO₂/H₂O resistant, pilot-scale test

中图分类号:

X 511

史玉婷, 皇甫林, 李长明, 王月, 高士秋, 伞晓广, 韩振南, 余剑. V₂O₅-MoO₃/TiO₂催化滤袋的制备及中试应用[J]. 化工学报, 2021, 72(11): 5598-5606.

Yuting SHI, Lin HUANGFU, Changming LI, Yue WANG, Shiqiu GAO, Xiaoguang SAN, Zhennan HAN, Jian YU. Preparation and pilot-scale test of V₂O₅-MoO₃/TiO₂ catalytic filter bag[J]. CIESC Journal, 2021, 72(11): 5598-5606.

图/表 11

图1 烟气净化中试工艺流程

Fig.1 Pilot-scale test process flow chart of flue gas purification

图2 不同配方颗粒催化剂的脱硝性能

Fig.2 The denitration performance of granular catalysts with different formulations

图3 V10Mo10颗粒催化剂的表征结果

Fig.3 Characterization of V10Mo10 granular catalyst

图4 不同过滤面速度下的滤袋脱硝性能

Fig.4 Denitrification performance of filter bags at different filtration velocity on catalytic performance

图5 不同层数滤袋的脱硝性能

Fig.5 Denitrification performance of filter bags with different layers

图6 双层滤袋的抗硫抗水性能

Fig.6 SO2/H2O-resistant stability of double layer filter bags

图7 催化滤袋的中试应用性能

Fig.7 Pilot-scale test denitrification performance of catalytic filter bags

图8 不同催化滤袋的SEM-EDS图

Fig.8 SEM-EDS images of different catalytic filter bags

表1 不同催化滤袋的EDS元素含量

Table 1 The percentage of EDS elements in different catalytic filter bags

样品	Content/%(mass)
样品	C	O	F	S	V
新鲜-内侧	17.26	6.81	57.94	0.49	4.43
1500 h-外侧	13.17	30.37	20.33	12.59	1.13
1500 h-内侧	15.22	18.34	42.17	2.64	4.34
失活-外侧	12.37	47.59	8.20	31.18	0.66
失活-内侧	16.96	15.86	43.72	7.60	1.69

图9 新鲜滤袋和失活滤袋的脱硝性能对比

Fig.9 Comparison of denitrification performance between fresh filter bag and deactivated filter bag

图10 新鲜滤袋和失活滤袋的XPS光谱

Fig.10 XPS spectrum of fresh and deactivated filter bags

参考文献 34

1	宁汝亮, 刘霄龙, 朱廷钰. 低温SCR脱硝催化剂研究进展 [J].过程工程学报, 2019, 19(2): 223-234.
	Ning R L, Liu X L, Zhu T Y. Research progress of low-temperature SCR denitration catalysts[J]. The Chinese Journal of Process Engineering, 2019, 19(2): 223-234.
2	Li J H, Chang H Z, Ma L, et al. Low-temperature selective catalytic reduction of NO_x with NH₃ over metal oxide and zeolite catalysts—a review[J]. Catalysis Today, 2011, 175(1): 147-156.
3	Liu J X, Zhao Z, Xu C M, et al. Structure, synthesis, and catalytic properties of nanosize cerium-zirconium-based solid solutions in environmental catalysis[J]. Chinese Journal of Catalysis, 2019, 40(10): 1438-1487.
4	刘芳琪, 于敦喜, 吴建群, 等. 燃煤锅炉SCR对颗粒物排放特性影响[J]. 化工学报, 2018, 69(9): 4051-4057.
	Liu F Q, Yu D X, Wu J Q, et al. Effect of SCR on particulate matter emissions from a coal-fired boiler[J]. CIESC Journal, 2018, 69(9): 4051-4057.
5	Pio F. Present status and perspectives in de-NO_x SCR catalysis[J]. Applied Catalysis A: General, 2001, 222(1/2): 221-236.
6	王响, 薛友祥, 程之强, 等. 除尘脱硝一体化陶瓷膜材料的研究[J]. 现代技术陶瓷, 2019, 40(5): 345-353.
	Wang X, Xue Y X, Cheng Z Q, et al. On the ceramic membrane material for SCR and dust removal[J]. Advanced Ceramics, 2019, 40(5): 345-353.
7	Qiu Y, Liu B, Du J, et al. The monolithic cordierite supported V₂O₅-MoO₃/TiO₂ catalyst for NH₃-SCR[J]. Chemical Engineering Journal, 2016, 294: 264-272.
8	Kwon B C, Kang D, Lee S W, et al. Synthesis of macro-porous de-NO_x catalysts for poly-tetra-fluoro-ethylene membrane bag filter[J]. Journal of Nanoscience and Nanotechnology, 2021, 21(8): 4537-4543.
9	Li W M, Liu H D, Chen Y F. Fabrication of MnO_x-CeO₂-based catalytic filters and their application in low-temperature selective catalytic reduction of NO with NH₃[J]. Industrial & Engineering Chemistry Research, 2020, 59(28): 12657-12665.
10	张先龙, 彭真, 刘鹏, 等. 基于PPS的锰基催化脱硝-除尘功能一体化滤料的制备及其低温SCR脱硝[J]. 功能材料, 2015, 46(S2): 160-164.
	Zhang X L, Peng Z, Liu P, et al. Preparation of PPS filter loaded with MnO_x for dust elimination and de-NO by low-temperature SCR[J]. Journal of Functional Materials, 2015, 46(S2): 160-164.
11	Liu J X, Wang L, Okejiri F, et al. Deep understanding of strong metal interface confinement: a journey of Pd/FeO_x catalysts[J]. ACS Catalysis, 2020, 10(15): 8950-8959.
12	陈雪红, 郑玉婴, 付彬彬, 等. 原位聚合MnO₂/PoPD@PPS复合滤料及其NH₃-SCR脱硝性能研究[J]. 燃料化学学报, 2017, 45(12): 1514-1521.
	Chen X H, Zheng Y Y, Fu B B, et al. Preparation of MnO₂/PoPD@PPS functional composites for low-temperature NO reduction with NH₃[J]. Journal of Fuel Chemistry and Technology, 2017, 45(12): 1514-1521.
13	Yang B, Shen Y S, Su Y, et al. Removal characteristics of nitrogen oxides and particulates of a novel Mn-Ce-Nb-O_x/P84 catalytic filter applied for cement kiln[J]. Journal of Industrial and Engineering Chemistry, 2017, 50: 133-141.
14	Park Y O, Lee K W, Rhee Y W. Removal characteristics of nitrogen oxide of high temperature catalytic filters for simultaneous removal of fine particulate and NO_x[J]. Journal of Industrial and Engineering Chemistry, 2009, 15(1): 36-39.
15	Gao F Y, Tang X L, Yi H H, et al. A review on selective catalytic reduction of NO_x by NH₃ over Mn-based catalysts at low temperatures: catalysts, mechanisms, kinetics and DFT calculations[J]. Catalysts, 2017, 7(7): 199.
16	Liu C, Shi J W, Gao C, et al. Manganese oxide-based catalysts for low-temperature selective catalytic reduction of NO_x with NH₃: a review[J]. Applied Catalysis A: General, 2016, 522: 54-69.
17	郭凤, 余剑, Tuyet-Suong Tran, 等. 溶胶-凝胶原位合成钒钨钛催化剂及NH₃-SCR性能[J]. 化工学报, 2017, 68(10): 3747-3754.
	Guo F, Yu J, Tuyet-Suong T, et al. In situ preparation of mesoporous V₂O₅-WO₃/TiO₂ catalyst by sol-gel method and its performance for NH₃-SCR reaction[J]. CIESC Journal, 2017, 68(10): 3747-3754.
18	Alemany L J, Lietti L, Ferlazzo N, et al. Reactivity and physicochemical characterization of V₂O₅-WO₃/TiO₂ de-NO_x catalysts[J]. Journal of Catalysis, 1995, 155(1): 117-130.
19	Gan L N, Guo F, Yu J, et al. Improved low-temperature activity of V₂O₅-WO₃/TiO₂ for denitration using different vanadium precursors[J]. Catalysts, 2016, 6(2): 25.
20	Abubakar A, Li C M, Huangfu L, et al. Simultaneous removal of particulates and NO by the catalytic bag filter containing V₂O₅-MoO₃/TiO₂[J]. Korean Journal of Chemical Engineering, 2020, 37(4): 633-640.
21	单良, 尹荣强, 王慧, 等. VMoTi/玻纤复合催化滤布制备及其除尘协同脱硝性能研究[J]. 化工学报, 2021,72(9): 4892-4899.
	Shan L, Yin R Q, Wang H, et al. Preparation of VMoTi/glass fiber catalytic filter-cloth and research on its dust and NO_x synergistic removal performance[J]. CIESC Journal, 2021,72(9): 4892-4899.
22	Yu J, Li C M, Guo F, et al. The pilot demonstration of a honeycomb catalyst for the DeNO_x of low-temperature flue gas from an industrial coking plant[J]. Fuel, 2018, 219: 37-49.
23	Ma Z R, Wu X D, Feng Y, et al. Low-temperature SCR activity and SO₂ deactivation mechanism of Ce-modified V₂O₅-WO₃/TiO₂ catalyst[J]. Progress in Natural Science: Materials International, 2015, 25(4): 342-352.
24	Jeon S W, Song I, Lee H, et al. Enhanced activity of vanadia supported on microporous titania for the selective catalytic reduction of NO with NH₃: effect of promoters[J]. Chemosphere, 2021, 275: 130105.
25	Han L, Cai S, Gao M, et al. Selective catalytic reduction of NO_x with NH₃ by using novel catalysts: state of the art and future prospects[J]. Chemical Reviews, 2019, 119(19): 10916-10976.
26	Apostolescu N, Geiger B, Hizbullah K, et al. Selective catalytic reduction of nitrogen oxides by ammonia on iron oxide catalysts[J]. Applied Catalysis B: Environmental, 2006, 62(1/2): 104-114.
27	Amiridis M D, Wachs I E, Deo G, et al. Reactivity of V₂O₅ catalysts for the selective catalytic reduction of NO by NH₃: influence of vanadia loading, H₂O, and SO₂[J]. Journal of Catalysis, 1996, 161(1): 247-253.
28	Turco M, Lisi L, Pirone R, et al. Effect of water on the kinetics of nitric oxide reduction over a high-surface-area V₂O₅/TiO₂ catalyst[J]. Applied Catalysis B: Environmental, 1994, 3(2/3): 133-149.
29	Kwon D W, Park K H, Hong S C. Enhancement of SCR activity and SO₂ resistance on VO_x/TiO₂ catalyst by addition of molybdenum[J]. Chemical Engineering Journal, 2016, 284: 315-324.
30	尹子骏, 苏胜, 卿梦霞, 等. 一种典型钒钛系SCR催化剂SO₃生成特性研究[J]. 化工学报, 2021, 72(5): 2596-2603.
	Yin Z J, Su S, Qing M X, et al. Study on SO₃ formation characteristics of a typical vanadium titanium SCR catalyst[J]. CIESC Journal, 2021, 72(5): 2596-2603.
31	Guo X Y, Bartholomew C, Hecker W, et al. Effects of sulfate species on V₂O₅/TiO₂ SCR catalysts in coal and biomass-fired systems[J]. Applied Catalysis B: Environmental, 2009, 92(1/2): 30-40.
32	刘亭, 沈伯雄, 朱国营, 等. 抗水、抗SO₂的低温选择性催化还原催化剂研究进展[J]. 环境污染与防治, 2008, 30(11): 80-83.
	Liu T, Shen B X, Zhu G Y, et al. A review of research in H₂O and SO₂ resistant low-temperature SCR catalysts[J]. Environmental Pollution & Control, 2008, 30(11): 80-83.
33	Cornaglia L M, Lombardo E A. XPS studies of the surface oxidation states on vanadium-phosphorus-oxygen (VPO) equilibrated catalysts[J]. Applied Catalysis A: General, 1995, 127(1/2): 125-138.
34	Romano E J, Schulz K H. A XPS investigation of SO₂ adsorption on ceria-zirconia mixed-metal oxides[J]. Applied Surface Science, 2005, 246(1/2/3): 262-270.

[1]	范孝雄, 郝丽芳, 范垂钢, 李松庚. LaMnO₃/生物炭催化剂低温NH₃-SCR催化脱硝性能研究[J]. 化工学报, 2023, 74(9): 3821-3830.
[2]	李泽严, 樊星, 李坚. 非热等离子体强化TiO₂催化尿素分解副产物水解性能的研究[J]. 化工学报, 2021, 72(9): 4698-4707.
[3]	邱爽, 肖永厚, 刘建辉, 贺高红. 一步法制备高活性NH₃-SCR催化剂Cu-SAPO-34：Si含量的影响[J]. 化工学报, 2021, 72(5): 2578-2585.
[4]	刘涛, 张书廷. Ba、Co共掺MnO_x复合氧化物低温选择性催化还原NO研究[J]. 化工学报, 2020, 71(7): 3106-3113.
[5]	王晨,陈泽翔,王建强,沈美庆,王军. 基于NH₃-SCR反应铜基小孔分子筛催化剂Na中毒对比研究[J]. 化工学报, 2020, 71(12): 5551-5560.
[6]	张霄玲,鲍佳宁,李运甲,皇甫林,李文松,高士秋,许光文,李长明,余剑. 工业MnO_x颗粒催化剂的制备及其低温脱硝应用研究[J]. 化工学报, 2020, 71(11): 5169-5177.
[7]	汤常金,孙敬方,董林. 超低温（< 150℃）SCR脱硝技术研究进展[J]. 化工学报, 2020, 71(11): 4873-4884.
[8]	陈潇雪, 宋敏, 孟凡跃, 卫月星. Fe _x MnCe₁-AC低温SCR催化剂SO₂中毒机理研究[J]. 化工学报, 2019, 70(8): 3000-3010.
[9]	李萍, 李长明, 段正康, 高士秋, 许光文, 余剑. 低温烟气脱硝催化剂适用条件与动力学[J]. 化工学报, 2019, 70(8): 2981-2990.
[10]	张涛, 刘琪英, 张彩红, 张琦, 马隆龙. Ni/La₂O₂CO₃催化剂对山梨醇氢解产物的选择性调控[J]. 化工学报, 2017, 68(6): 2359-2367.
[11]	戚春萍, 武文粉, 王晨晔, 李会泉. 燃煤电厂废旧SCR脱硝催化剂中TiO₂载体的回收与再利用[J]. 化工学报, 2017, 68(11): 4239-4248.
[12]	石建伟, 吴威, 杨荟楠, 苏明旭, 蔡小舒. 基于激光光谱法的尿素水溶液液膜多参数测量[J]. 化工学报, 2017, 68(1): 79-86.
[13]	刘建华, 杨晓博, 张琛, 吴凡, 李忠, 夏启斌. Fe₂O₃对V₂O₅-WO₃/TiO₂催化剂表面性质及其性能的影响[J]. 化工学报, 2016, 67(4): 1287-1293.
[14]	李倩, 谷华春, 辛颖, 李壮壮, 张昭良. V₂O₅-WO₃/TiO₂脱硝催化剂机械强度和孔隙率的响应曲面模型[J]. 化工学报, 2015, 66(9): 3496-3503.
[15]	李洋1，2，陈敏东1，薛志钢2，支国瑞2，马京华2，刘妍2，高炜2. 燃煤电厂协同脱汞研究进展及强化措施[J]. 化工进展, 2014, 33(08): 2187-2191.

V₂O₅-MoO₃/TiO₂催化滤袋的制备及中试应用

Preparation and pilot-scale test of V₂O₅-MoO₃/TiO₂ catalytic filter bag

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 11

参考文献 34

相关文章 15

编辑推荐

Metrics

本文评价