Phase transformation and leaching performance of Na₂O-doping calcium aluminate compounds

TIAN Yongpan, TU Ganfeng, PAN Xiaolin, YU Haiyan

School of Materials & Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China

Received:2014-08-20 Revised:2015-01-04 Online:2015-04-05 Published:2015-04-05
Supported by:
supported by the National Natural Science Foundation of China (51174054, 51374065).

摘要/Abstract

摘要：

以分析纯试剂CaCO₃、Al₂O₃和Na₂CO₃为原料,在1350℃烧结1 h合成了Na₂O掺杂铝酸钙熟料,并采用XRD、SEM和EDS等方法研究了Na₂O掺杂CaO-Al₂O₃体系铝酸钙化合物的物相演变规律及熟料浸出性能。结果表明:当CaO和Al₂O₃的摩尔比为1.0时,CaO-Al₂O₃体系铝酸钙由CaO·Al₂O₃和12CaO·7Al₂O₃组成,而Na₂O掺杂铝酸钙熟料由CaO·Al₂O₃、12CaO·7Al₂O₃、Na₂O·Al₂O₃和Na₄Ca₃(AlO₂)₁₀组成。除形成含Na₂O化合物外,熟料中掺杂的Na₂O固溶于12CaO·7Al₂O₃中,而CaO·Al₂O₃中几乎不含Na₂O。随着熟料中Na₂O掺杂量的升高,12CaO·7Al₂O₃和Na₄Ca₃(AlO₂)₁₀的含量逐渐增加,CaO·Al₂O₃的含量逐渐降低;12CaO·7Al₂O₃和Na₄Ca₃(AlO₂)₁₀的结晶度逐渐降低,CaO·Al₂O₃的结晶度逐渐升高。Na₂O的掺杂提高了熟料在碳酸钠溶液中的浸出性能,并且使浸出渣中CaCO₃的空间群由R-3CH、P63/MMC两种转变为只含有R-3CH一种。

关键词: Na₂O掺杂, 烧结, 铝酸钙, 浸取, 物相转化

Abstract:

Calcium aluminate clinkers doped with Na₂O were synthesized using analytically pure reagents CaCO_3, Al₂O₃, and Na₂CO₃ at 1350℃ for 1 h. XRD, SEM and EDS were used to study the phase transformation of calcium aluminates and the leaching performance of clinkers from CaO-Al₂O₃ system doped with Na₂O. The results show that the main phases of clinkers from CaO-Al₂O₃ system are CaO·Al₂O₃ and 12CaO·7Al₂O₃, while those of clinkers from CaO-Al₂O₃ system doped with Na₂O are CaO·Al₂O₃, 12CaO·7Al₂O₃, Na₂O·Al₂O₃ and Na₄Ca₃(AlO₂)₁₀, when the molar ratio of CaO to Al₂O₃ is 1.0. Some of the Na₂O forms compounds containing Na₂O, the rest is doped in 12CaO·7Al₂O₃, meanwhile nearly none of Na₂O is doped in CaO·Al₂O₃. With the increasing of the Na₂O content in clinkers, the amounts of 12CaO·7Al₂O₃ and Na₄Ca₃(AlO₂)₁₀ increase while the amount of CaO·Al₂O₃ decreases, and the crystallinity of 12CaO·7Al₂O₃ and Na₄Ca₃(AlO₂)₁₀ decrease while that of CaO·Al₂O₃ increases. Due to the doping of Na₂O, the leaching performance of alumina in the clinkers using the sodium carbonate solution is improved and the space groups of CaCO₃ in the leached residues are changed from R-3CH and P63/MMC to only R-3CH.

Key words: Na₂O doping, sintering, calcium aluminate, leaching, phase transformation

中图分类号:

TF803.21

田勇攀, 涂赣峰, 潘晓林, 于海燕. Na₂O掺杂铝酸钙化合物物相转化与浸出性能[J]. 化工学报, 2015, 66(4): 1551-1556.

TIAN Yongpan, TU Ganfeng, PAN Xiaolin, YU Haiyan. Phase transformation and leaching performance of Na₂O-doping calcium aluminate compounds[J]. CIESC Journal, 2015, 66(4): 1551-1556.

参考文献 21

[1]	Li Laishi(李来时), Zhai Yuchun(翟玉春), Qin Jinguo(秦晋国), Wu Yan(吴艳), Liu Yingying(刘瑛瑛). Extracting high purity alumina from fly ash [J]. Journal of Chemical Industry and Engineering (China)(化工学报), 2006, 57(9): 2189-2193
[2]	Di Yuezhong(狄跃忠), Wang Zhihui(王智慧), Wang Yaowu(王耀武), Peng Jianping(彭建平), Feng Naixiang(冯乃祥). Extract of high-whiteness aluminum hydroxide from residues of novel process of magnesium production by aluminothermy reduction [J]. CIESC Journal (化工学报), 2013, 64(3): 1106-1111
[3]	Seeley F G, Mcdowell W J, Felker L K, Kelmers A D, Egan B Z. Determination of extraction equilibria for several metals in the development of a process designed to recover aluminum and other metals from coal combustion ash [J]. Hydrometallurgy, 1981, 6(3/4): 277-290
[4]	Zhang Wu(张武). Research on the phase compositions and leaching properties of sintering products in CaO-Al2O3-SiO2 system[D]. Shenyang: Northeastern University, 2011
[5]	Yu Haiyan, Pan Xiaolin, Wang Bo, Zhang Wu, Sun Huilan,Bi Shiwen. Effect of Na2O on formation of calcium aluminates in CaO-Al2O3-SiO2 system [J]. Transaction of Nonferrous Metals Society of China, 2012, 22(12): 3108-3112
[6]	Wang Bo(王波), Yu Haiyan(于海燕), Sun Huilan(孙会兰), Bi Shiwen(毕诗文). Effects of sintering process parameters on physicochemical properties of calcium aluminate slag system [J]. The Chinese Journal of Process Engineering(过程工程学报), 2008, 8(5): 949-952
[7]	Tong Zhifang(佟志芳), Bi Shiwen(毕诗文), Li Huili(李惠莉), Yang Yihong(杨毅宏). Leaching kinetics of calcium aluminate slag [J]. The Chinese Journal of Process Engineering(过程工程学报), 2005, 5(4): 399-402
[8]	Xiao Wei(肖玮), Liu Wei(刘卫), Zhang Nianbing(张念炳), Li Zhiying(黎志英). Study on the process of extracting alumina from the middling grade bauxite using lime sinter [J]. Journal of Guizhou University of Technology:Natural Science Edition(贵州工业大学学报:自然科学版), 2008, 37(5): 41-43
[9]	Sui Huilan(孙会兰), Yu Haiyan(于海燕), Wang Bo(王波), Miao Yu(苗瑜), Tu Ganfeng(涂赣峰), Bi Shiwen(毕诗文). Leaching dynamics of 12CaO·7Al2O3 [J]. The Chinese Journal of Nonferrous Metals(中国有色金属学报), 2008, 18(10): 1920-1925
[10]	Palacios L, ángeles G, Torre D L, Bruque S, Jose L, Santiago G G, Sheptyakov D, Miguel A G. Crystal structures and in-situ formation study of mayenite electrides [J]. Inorganic Chemistry, 2007, 46(10): 4167-4176
[11]	Nishioa Y, Nomurab K, Yanagia H, Kamiya T, Hirano M, Hosono H. Short-channel nanowire transistor using a nanoporous crystal semiconductor 12CaO·7Al2O3 [J]. Materials Science and Engineering:B, 2010, 173(1/2/3): 37-40
[12]	Miyakawa M, Toda Y, Hayashi K, Hirano M, Kamiya T, Matsunami N, Hosono H. Formation of inorganic electride thin films via site-selective extrusion by energetic inert gas ions [J]. Journal of Applied Physics, 2005, 97(2): 023510(1-6)
[13]	Kim S W, Shimoyama T, Hosono H. Solvated electrons in high-temperature melts and glasses of the room-temperature stable electride [Ca24Al28O64]4+·4e- applied [J]. Science, 2011, 1: 71-74
[14]	Hayashi K, Matsuishi S, Kamiya T, Hirano M, Hosono H. Light-induced conversion of an insulating refractory oxide into a persistent electronic conductor [J]. Nature, 2002, 419: 462-465
[15]	Tong Zhifang (佟志芳), Xie Senlin(谢森林), Zhang Liheng(张立恒), Chen Tao(陈涛), Liu Wei(刘卫). Preparation and application of the 12CaO·7Al2O3 material [J]. The Chinese Journal of Nonferrrous Metals(有色金属科学与工程), 2011, 2(6): 16-21
[16]	Toda Y, Miyakawa M, Hayashi K, Kamiya T, Hirano M, Hosono H. Thin film fabrication of nanoporous 12CaO·7Al2O3 crystal and its conversion into transparent conductive films by light illumination [J]. Thin Solid Films, 2003, 445(2): 309-312
[17]	Tõldsepp E, Avarmaa T, Denks V, Feldbach E, Kirm M, Maaroos A, Mändar H, Vielhauer S. Synthesis and luminescence properties of Ce3+ doped nanoporous 12CaO·7Al2O3 powders and ceramics [J]. Optical Materials, 2010, 32(8): 784-788
[18]	Shen Jing(沈静), Gong Lu(宫璐), Li Quanxin(李全新). Structure and antibacterial property of Na2O doped C12A7 [J]. Chinese Journal of Inorganic Chemistry(中国无机化学学报), 2011, 27(2): 353-360
[19]	Ostrowski C, Zelazny J. Solid solutions of calcium aluminates C3A, C12A7 and CA with sodium oxide [J]. Journal of Thermal Analysis and Calorimetry, 2004, 75(3): 867-885
[20]	Taylor J C, Hinczak I, Matulis C E. Rietveld full-profile quantification of Portland cement clinker: the importance of including a full crystallography of the major phase polymorphs [J]. Powder Diffraction, 2000, 15(1): 7-18
[21]	Torre A G, Bruque S, Aranda A G. Rietveld quantitative amorphous content analysis [J]. Journal of Applied Crystallography, 2001, 34(2): 196-202

Na₂O掺杂铝酸钙化合物物相转化与浸出性能

Phase transformation and leaching performance of Na₂O-doping calcium aluminate compounds

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 21

相关文章 15

编辑推荐

Metrics

本文评价

[1]	曾如宾, 沈中杰, 梁钦锋, 许建良, 代正华, 刘海峰. 基于分子动力学模拟的Fe₂O₃纳米颗粒烧结机制研究[J]. 化工学报, 2023, 74(8): 3353-3365.
[2]	葛泽峰, 吴雨青, 曾名迅, 查振婷, 马宇娜, 侯增辉, 张会岩. 灰化学成分对生物质气化特性的影响规律[J]. 化工学报, 2023, 74(5): 2136-2146.
[3]	李亚芾, 付亮亮, 白浩隆, 白丁荣, 许光文. 菱镁矿浮选尾矿直接合成同时制备镁橄榄石和镁砂研究[J]. 化工学报, 2022, 73(8): 3679-3687.
[4]	郭志强, 燕可洲, 张吉元, 柳丹丹, 高阳艳, 郭彦霞. 煤矸石/粉煤灰对赤泥钠化还原焙烧反应的影响机制[J]. 化工学报, 2022, 73(5): 2194-2205.
[5]	孙雄康, 李强. 多级复合芯结构的强化沸腾传热研究[J]. 化工学报, 2022, 73(3): 1127-1135.
[6]	王晓蓉, 曾玺, 王芳, 张光义, 许德平, 许光文. 温度和气氛对高K高S糠醛渣灰分的烧结特性研究[J]. 化工学报, 2022, 73(1): 411-424.
[7]	谢昭明, 陈庚, 刘仁龙, 刘作华, 岑少斗, 陶长元, 郭胜惠. 刚柔组合桨强化软锰矿浸出过程的反应动力学特性[J]. 化工学报, 2021, 72(5): 2586-2595.
[8]	周剑, 江倩, 杨怡, 冯厦厦, 仲兆祥, 邢卫红. 烧结助剂对低温制备碳化硅多孔陶瓷性能的影响[J]. 化工学报, 2021, 72(4): 2293-2299.
[9]	李浩然, 邱彤. 基于因果分析的烧结生产状态预测模型[J]. 化工学报, 2021, 72(3): 1438-1446.
[10]	王曰杰, 李玲玲, 何春宏. 炼油废催化剂生物淋滤脱金属研究进展[J]. 化工学报, 2021, 72(2): 901-912.
[11]	吴玉花,丁欣,李小露,高红凤,冯炜,白红存,郭庆杰. 离子液体-微波辅助从黄连提取小檗碱的实验与分子模拟[J]. 化工学报, 2020, 71(7): 3123-3131.
[12]	朱有健, 张显显, 陈奕名, 吴学红, 杨海平, 陈汉平. 磷酸二氢钙对玉米秆灰熔融烧结特性的影响研究[J]. 化工学报, 2020, 71(7): 3313-3321.
[13]	方俊华,唐琦,李杨,李遥瑶,吕秋颖,范准,周健,许劲. 污泥水热碳化中磷的形态变化及金属浸出行为[J]. 化工学报, 2020, 71(7): 3288-3295.
[14]	王永胜, 兰小林, 邱天, 张新平, 吴莹莹, 陈莉, 徐伟祥, 郭栋杰, 段正康. 铜基石墨烯复合催化剂的合成与表征[J]. 化工学报, 2020, 71(6): 2889-2899.
[15]	马密霞, 秦宁, 闵清, 胡文祥. 微波超声波联用萃取白藜芦醇及其苷的HPLC测定[J]. 化工学报, 2019, 70(S1): 124-129.