Effect of pre-contact temperature on performance of DQC spherical catalyst in propylene polymerization

doi:10.11949/j.issn.0438-1157.20161119

Abstract

Abstract:

The pre-contact temperature of DQC catalyst system on liquid bulk polymerization of propylene was studied using cyclohexyl methyl dimethoxy silane (C-donor) as external donor. The results indicated that increase of pre-contact temperature caused decrease of polymerization activity of DQC catalyst, which yielded polymers with decreased melt index but increased isotactic index and fine powder content. Gel permeation chromatography (GPC) results showed that increase of pre-contact temperature broadened molecular weight distributions and decreased both number and weight average molecular weights. Differential scanning calorimetry (DSC) results exhibited that melting temperature, melting enthalpy, crystallization enthalpy, and crystallinity of polypropylenes increased to various degrees. ¹³C NMR results showed an increase of stereoregular sequences of triad mm and pentad mmmm with increase of pre-contact temperature.

Key words: pre-contact temperature, DQC spherical catalyst, polypropylene, propylene polymerization

摘要：

使用甲基环己基二甲氧基硅烷（C-donor）作为外给电子体，对聚丙烯DQC球形催化剂进行了预接触温度液相本体聚合研究。实验结果表明，预接触温度升高，DQC球形催化剂的聚合活性降低，得到聚合物的等规指数升高，熔融指数下降，得到的聚合物细粉含量增加。GPC测试结果表明，预接触温度升高，聚合物的分子量分布变宽，数均分子量和重均分子量降低。DSC测试结果表明，聚合物的熔融温度、熔融焓和结晶焓数值均有不同程度的提高，聚合物的结晶度提高。¹³C NMR测试结果表明，预接触温度升高，得到的聚合物全同立构三单元组mm序列结构和五单元组mmmm序列结构含量均增加。

关键词: 预接触温度, DQC球形催化剂, 聚丙烯, 丙烯聚合

CLC Number:

TQ325.14

ZHANG Tianyi, XIA Xianzhi, LIU Yuexiang. Effect of pre-contact temperature on performance of DQC spherical catalyst in propylene polymerization[J]. CIESC Journal, 2017, 68(4): 1434-1441.

张天一, 夏先知, 刘月祥. 预接触温度对聚丙烯DQC球形催化剂聚合性能的影响[J]. 化工学报, 2017, 68(4): 1434-1441.

References 25

[1]	洪定一. 聚丙烯——原理、工艺与技术[M]. 北京:中国石化出版社, 2002:15-49.HONG D Y. Polypropylene-Principle, Process and Technology[M]. Beijing:China Petrochemical Press, 2002:15-49.
[2]	毛炳权, 杨霭春, 郑莹, 等. 用于烯烃聚合和共聚合的催化剂体系:85100997A[P]. 1987.01.10.MAO B Q, YANG A C, ZHENG Y, et al. Catalyst system used for alkene poly-and copolymerization:85100997A[P]. 1987.01.10.
[3]	张天一, 夏先知, 刘月祥, 等. 外给电子体对DQC催化剂聚合性能的影响[J]. 石油化工, 2011, 40(4):381-386.ZHANG T Y, XIA X Z, LIU Y X, et al. Effects of external electron donors on performance of DQC catalyst in propylene polymerization[J]. Petrochemical Technology, 2011, 40(4):381-386.
[4]	夏先知, 杜宏斌, 王新生, 等. DQ型高效催化剂在环管PP装置上的应用[J]. 合成树脂及塑料, 2002, 19(1):20-22.XIA X Z, DU H B, WANG X S, et al. The application of DQ high efficiency catalyst in polypropylene loop reactor[J]. China Synthetic Resin and Plastics, 2002, 19(1):20-22.
[5]	李刚, 赵唤群, 于建明, 等. NG催化剂在气相法聚丙烯装置上的工业化应用[J]. 石油化工, 2004, 33(3):252-257.LI G, ZHAO H Q, YU J M, et al. Application of NG catalyst in an existing gas phase polypropylene plant[J]. Petrochemical Technology, 2004, 33(3):252-257.
[6]	王志武, 李天益, 高明智, 等. 用于丙烯气相聚合工艺的NG催化剂的研究[J]. 石油化工, 2003, 32(9):759-762.WANG Z W, LI T Y, GAO M Z, et al. Study on NG catalyst for propylene gas phase polymerization process[J]. Petrochemical Technology, 2003, 32(9):759-762.
[7]	郭正阳, 杨岭, 谭忠. NA-Ⅱ型催化剂生产BOPP专用树脂的工业应用[J]. 合成树脂及塑料, 2008, 25(5):1-4.GUO Z Y, YANG L, TAN Z. Industrial application of NA-Ⅱ catalyst in production of speciality BOPP resin[J]. China Synthetic Resin and Plastics, 2008, 25(5):1-4.
[8]	杨岭, 谭忠, 郭正阳, 等.新型聚丙烯催化剂的性能研究[J]. 石油化工, 2008, 37(1):39-43.YANG L, TAN Z, GUO Z Y, et al. Study on property of new polypropylene catalyst[J]. Petrochemical Technology, 2008, 37(1):39-43.
[9]	高明智, 刘海涛, 李珠兰, 等. 用于烯烃聚合的固体催化剂组分和含该催化剂组分的催化剂及其应用:1436796A[P]. 2003.08.20.GAO M Z, LIU H T, LI Z L, et al. Solid catalyst component for olefine polymerization, catalyst with the component and its application:1436796A[P]. 2003.08.20.
[10]	刘海涛, 马晶, 丁春敏, 等. 1,3-二醇酯为内给电子体的丙烯聚合催化剂[J]. 石油化工, 2006, 35(2):127-131.LIU H T, MA J, DING C M, et al. Propylene polymerization catalyst with 1,3-diol dibenzoate as internal donor[J]. Petrochemical Technology, 2006, 35(2):127-131.
[11]	高富堂, 夏先知, 毛炳权. 复配内给电子体对TiCl4 MgCl2丙烯聚合催化剂性能的影响[J]. 高分子材料科学与工程, 2010, 26(7):1-4.GAO F T, XIA X Z, MAO B Q. Effect of novel mixed internal donors on the properties of MgCl2-supported Ziegle-Natta catalysts for propylene polymerization[J]. Polymer Materials Science and Engineering, 2010, 26(7):1-4.
[12]	罗志强, 刘月祥, 夏先知. 复配内给电子体催化剂催化丙烯聚合[J]. 石油化工, 2007, 36(3):221-226.LUO Z Q, LIU Y X, XIA X Z. Propylene polymerization catalyzed by internal electron donor campound catalyst[J]. Petrochemical Technology, 2007, 36(3):221-226.
[13]	刘月祥, 王新生, 张天一, 等. NDQ催化剂催化丙烯聚合[J]. 合成树脂及塑料, 2009, 26(5):1-3.LIU Y X, WANG X S, ZHANG T Y, et al. Propylene polymerization with NDQ catalyst[J]. China Synthetic Resin and Plastics, 2009, 26(5):1-3.
[14]	秦金来, 夏先知, 刘月祥, 等. DQC催化剂的性能表征及工业应用[J]. 石油化工, 2011, 40(6):650-654.QIN J L, XIA X Z, LIU Y X, et al. Characterization and industrial application of DQC catalyst for propylene polymerization[J]. Petrochemical Technology, 2011, 40(6):650-654.
[15]	赵瑾, 刘月祥, 夏先知, 等. 一种用于烯烃聚合的催化剂组分及其催化剂:101724102B[P]. 2011-11-02.ZHAO J, LIU Y X, XIA X Z, et al. Catalyst component for olefin polymerization and catalyst thereof:101724102B[P]. 2011-11-02.
[16]	赵瑾, 夏先知, 刘月祥, 等. 用于烯烃聚合的催化剂组分及其制备方法:102234339B[P]. 2013-02-27.ZHAO J, XIA X Z, LIU Y X, et al. Catalyst components for olefin polymerization and preparation method thereof:102234339B[P]. 2013-02-27.
[17]	谭扬, 姜涛, 刘月祥, 等. 预络合对TiCl4/SiO2-MgCl2催化剂活性及聚丙烯颗粒形态的影响[J]. 石油化工, 2007, 36(8):780-783.TAN Y, JIANG T, LIU Y X, et al. Effects of precomplexation on activity of TiCl4/SiO2-MgCl2 catalyst in propylene polymerization and polymer particle morphology[J]. Petrochemical Technology, 2007, 36(8):780-783.
[18]	陈旭, 慕雪梅, 张长军, 等. 75 kg·h-1聚丙烯中试装置预接触工艺管路的优化设计计算[J]. 化学工程师, 2011, (10):25-27.CHEN X, MU X M, ZHANG C J, et al. Optimized design and calculation of 75 kg·h-1 polypropylene pilot-plant test pre-compounding[J]. Chemical Engineer, 2011, (10):25-27.
[19]	周浪屿, 孙涛, 韩章远. 聚丙烯催化剂三剂预接触罐D201运行分析[J]. 当代化工, 2010, 39(4):455-457.ZHOU L Y, SUN T, HAN Z Y. Operation analysis of polypropylene catalyst pre-contact pot D201[J]. Contemporary Chemical Industry, 2010, 39(4):455-457.
[20]	杨伟, 史炜, 谢邦互. 玻璃微珠改性聚丙烯的熔融、结晶与形态[J]. 高分子材料科学与工程, 2005, 21(2):249-252.YANG W, SHI W, XIE B H. Melting crystallization and morphology of glass bead filled PP and LLDPE composites[J]. Polymer Materials Science and Engineering, 2005, 21(2):249-252.
[21]	FORTE M C, COUTINHO F M B. The influence of catalyst system and polymerization conditions on polypropylene properties[J]. Eur. Polym. J., 1996, 32(5):605-611.
[22]	ZUCCHINI U, CECCHIN G. Control of molecular weight distribution for polypropylene obtained by commercial Ziegler-Natta catalyst:effect of temperature[J]. Adv. Polym. Sci., 1983, 51:101-153.
[23]	FAN Z Q, FENG L X, YANG S L. Distribution of active centers on TiCl4/MgCl2 catalyst for olefin polymerization[J]. J. Polym. Sci., Part A:Polym. Chem., 1996, 34(16):3329-3335.
[24]	CHENG H N, KAKUGO M. Carbon-13 NMR analysis of compositional heterogeneity in ethylene-propylene copolymers[J]. Macromolecules, 1991, 24(8):1724-1726.
[25]	MATSUOKA H, LIU B P, NAKATANI H, et al. Variation in the isospecific active sites of internal donor-free MgCl2-supported Ziegler catalysts:effect of external electron donors[J]. Macromol. Rapid Commu., 2001, 22(22):326-328.