Adsorption equilibrium and mechanism of ethanol on MIL-101(Cr)

doi:10.11949/j.issn.0438-1157.20151052

Abstract

Abstract:

The adsorption performance and adsorption mechanism of ethanol on MIL-101(Cr) were investigated. MIL-101(Cr) was synthesized using a hydrothermal synthesis method, and characterized using N₂ adsorption measurements, powder X-ray diffraction, and Fourier transform infrared spectroscopy. The adsorption isotherms of ethanol and water vapor were measured by static adsorption method at different temperatures, and ethanol adsorption mechanisms on four types of adsorptive sites in MIL-101 were discussed. The isosteric heats of ethanol and water adsorption were calculated according to these isotherms. The adsorption and desorption of ethanol on MIL-101 were evaluated. Results show that adsorption capacity of MIL-101(Cr) for ethanol is up to 20.3 mmol·g^-1 at 298 K, much higher than those of some traditional adsorbents. At low pressure, the adsorption capacity of MIL-101 for ethanol is higher than that for water vapor, which could be ascribed to larger dipole moment and dynamic diameter of ethanol compared to water molecule. In addition, the isosteric heat of ethanol adsorption on MIL-101 is higher than that of water vapor adsorption. At high pressure, multilayer adsorption or cage filling occurs, so the molecule with large dynamic size will fill within MOFs with less moles than that with small dynamic size due the limitation of pore volume of MOFs. As a consequence, the adsorption capacity of MIL-101 for ethanol is lower than that for water vapor because the dynamic diameter of ethanol (0.45 nm) is larger than that of water molecule (0.268 nm). The ethanol adsorption and desorption isotherms show that ethanol adsorption on MIL-101 is highly reversible.

Key words: MIL-101(Cr), ethanol, water vapor, adsorption equilibrium, adsorption, heat of adsorption

摘要：

主要研究了MIL-101材料对乙醇的吸附性能和吸附机理。采用水热合成法制备了MIL-101(Cr),并分别应用N₂静态吸附、X射线粉末衍射(PXRD)、傅里叶红外光谱(FTIR)等分析手段对MIL-101晶形结构、孔隙结构参数进行分析表征。应用静态吸附法测定乙醇和水蒸气在不同温度下的吸附等温线,并讨论乙醇吸附在MIL-101(Cr) 4种吸附位的机理,根据吸附等温线估算出乙醇和水蒸气在MIL-101上的等量吸附热,并测试了乙醇在MIL-101上的吸附循环性能。研究表明,在298 K下,MIL-101的乙醇吸附容量为20.3 mmol·g^-1,远高于传统吸附材料。在低压下MIL-101对乙醇的吸附量高于水蒸气的吸附量,这是由于乙醇的偶极矩和分子动力学直径均比水大,使得乙醇分子在孔道中受到更大吸附力场作用;在低吸附量范围,乙醇在MIL-101上的等量吸附热要高于水蒸气的等量吸附热。在较高吸附压力条件下,主要发生多层吸附或孔填充,受吸附剂的孔容限制效应,尺寸越大的分子被吸附的物质的量会越少,由于乙醇的动力学直径(0.45 nm)大于水分子的动力学直径(0.268 nm),所以在较高吸附压力下乙醇在MIL-101上吸附量要小于水蒸气的吸附量。多次吸附脱附等温线测试显示MIL-101具有良好的乙醇吸附循环性能。

关键词: MIL-101(Cr), 乙醇, 水蒸气, 吸附平衡, 吸附, 吸附热

CLC Number:

TB383
O647

YU Ying, SUN Xuejiao, YAN Jian, XIAO Jing, XI Hongxia, LI Zhong. Adsorption equilibrium and mechanism of ethanol on MIL-101(Cr)[J]. CIESC Journal, 2016, 67(1): 300-308.

余颖, 孙雪娇, 颜健, 肖静, 奚红霞, 李忠. 乙醇在MIL-101上的吸附相平衡及其吸附机理[J]. 化工学报, 2016, 67(1): 300-308.

References 43

[1]	HENNING H-M. Solar assisted air conditioning of buildings—an overview [J]. Applied Thermal Engineering, 2007, 27 (10): 1734-1749.
[2]	FROEHLICH J F, DOMINIK J C, HENNINGER S K. Advancement of sorption-based heat transformation by a metal coating of highly-stable, hydrophilic aluminium fumarate MOF [J]. RSC Advances, 2014, 4 (46): 24073-24082.
[3]	ARISTOV Y I. Optimal adsorbent for adsorptive heat transformers: dynamic considerations [J]. International Journal of Refrigeration-Revue Internationale Du Froid, 2009, 32 (4): 675-686.
[4]	SAHA B B, CHAKRABORTY A, KOYAMA S, et al. A new generation cooling device employing CaCl2-in-silica gel-water system [J]. International Journal of Heat and Mass Transfer, 2009, 52 (1/2): 516-524.
[5]	TAMAINOT-TELTO Z, METCALF S J, CRITOPH R E, et al. Carbon-ammonia pairs for adsorption refrigeration applications: ice making, air conditioning and heat pumping [J]. International Journal of Refrigeration-Revue Internationale Du Froid, 2009, 32 (6): 1212-1229.
[6]	VESELOVSKAYA J V, CRITOPH R E, THORPE R N, et al. Novel ammonia sorbents "porous matrix modified by active salt" for adsorptive heat transformation (Ⅲ): Testing of "BaCl2/vermiculite" composite in a lab-scale adsorption chiller [J]. Applied Thermal Engineering, 2010, 30 (10): 1188-1192.
[7]	EL-SHARKAWY I I, SAHA B B, KOYAMA S, et al. Experimental investigation on activated carbon-ethanol pair for solar powered adsorption cooling applications [J]. International Journal of Refrigeration-Revue Internationale Du Froid, 2008, 31 (8): 1407-1413.
[8]	ROMERO-ANAYA A J, LILLO-RODENAS M A, LINARES-SOLANO A. Factors governing the adsorption of ethanol on spherical activated carbons [J]. Carbon, 2015, 83: 240-249.
[9]	ZHANG Ke, LIVELY R P, NOEL J D, et al. Adsorption of water and ethanol in MFI-type zeolites [J]. Langmuir, 2012, 28 (23): 8664-8673.
[10]	FARHA O K, YAZAYDIN A O, ERYAZICI I, et al. De novo synthesis of a metal-organic framework material featuring ultrahigh surface area and gas storage capacities [J]. Nature Chemistry, 2010, 2 (11): 944-948.
[11]	FURUKAWA H, KO N, GO Y B, et al. Ultrahigh porosity in metal-organic frameworks [J]. Science, 2010, 329 (5990): 424-428.
[12]	YOON M, SRIRAMBALAJI R, KIM K. Homochiral metal-organic frameworks for asymmetric heterogeneous catalysis [J]. Chemical Reviews, 2012, 112 (2): 1196-1231.
[13]	HORCAJADA P, GREF R, BAATI T, et al. Metal-organic frameworks in biomedicine [J]. Chemical Reviews, 2012, 112 (2): 1232-1268.
[14]	BETARD A, FISCHER R A. Metal-organic framework thin films: from fundamentals to applications [J]. Chemical Reviews, 2012, 112 (2): 1055-1083.
[15]	李亮莎, 王可可, 黄宏亮, 等. 高稳定铪金属-有机骨架材料的合成及二氧化碳捕获性能 [J]. 化工学报, 2014, 65 (5): 1706-1715.LI L S, WANG K K, HUANG H L, et al. Synthesis of exceptional stable Hf-based metal-organic frameworks: characterization, stability and CO2 adsorption performance [J]. CIESC Journal, 2014, 65 (5): 1706-1715.
[16]	乔智威, 杨仁党, 王海辉, 等. 面向生物甲烷分离的不同金属配位金属-有机骨架材料的分子设计 [J]. 化工学报, 2014, 65 (5): 1729-1735.QIAO Z W, YANG R D, WANG H H, et al. Molecular design of metal-organic frameworks with different metal ligands for bio-methane separation [J]. CIESC Journal, 2014, 65 (5): 1729-1735.
[17]	王可可, 李亮莎, 黄宏亮, 等. 铪金属-有机骨架材料的孔尺寸调控及其吸附性能 [J]. 化工学报, 2014, 65 (5): 1696-1705.WANG K K, LI L S, HUANG H L, et al. Control of pore size in Hf-based metal-organic frameworks and exploration of their adsorption properties [J]. CIESC Journal, 2014, 65 (5): 1696-1705.
[18]	杨琰, 王莎, 张志娟, 等. 氨气改性的NH3@MIL-53(Cr)吸附CO2和CH4的性能 [J]. 化工学报, 2014, 65 (5): 1759-1763.YANG Y, WANG S, ZHANG Z J, et al. CO2 and CH4 adsorption performance of modified MIL-53(Cr) via ammonia vapor [J]. CIESC Journal, 2014, 65 (5): 1759-1763.
[19]	REZK A, AL-DADAH R, MAHMOUD S, et al. Characterisation of metal organic frameworks for adsorption cooling [J]. International Journal of Heat and Mass Transfer, 2012, 55 (25/26): 7366-7374.
[20]	JEREMIAS F, KHUTIA A, HENNINGER S K, et al. MIL-100(Al, Fe) as water adsorbents for heat transformation purposes—a promising application [J]. Journal of Materials Chemistry, 2012, 22 (20): 10148-10151.
[21]	KÜSGENS P, ROSE M, SENKOVSKA I, et al. Characterization of metal-organic frameworks by water adsorption [J]. Microporous and Mesoporous Materials, 2009, 120 (3): 325-330.
[22]	SEO Y K, YOON J W, LEE J S, et al. Energy-efficient dehumidification over hierachically porous metal-organic frameworks as advanced water adsorbents [J]. Advanced Materials, 2012, 24 (6): 806-810.
[23]	SUIB S L. Handbook of zeolite science and technology [J]. Science, 2003, 302 (5649): 1335-1336.
[24]	DENOYEL R, BEURROIES I, VINCENT D. Microcalorimetric methods for studying vapour adsorption and wetting of powders [J]. Journal of Thermal Analysis and Calorimetry, 2002, 70 (2): 483-492.
[25]	WESTON M H, DELAQUIL A A, SARJEANT A A, et al. Tuning the hydrophobicity of zinc dipyridyl paddlewheel metal-organic frameworks for selective sorption [J]. Crystal Growth & Design, 2013, 13 (7): 2938-2942.
[26]	VAN ASSCHE T R C, DUERINCK T, GUTIERREZ SEVILLANO J J, et al. High adsorption capacities and two-step adsorption of polar adsorbates on copper benzene-1,3,5-tricarboxylate metal-organic framework [J]. Journal of Physical Chemistry C, 2013, 117 (35): 18100-18111.
[27]	REZK A, AL-DADAH R, MAHMOUD S, et al. Investigation of ethanol/metal organic frameworks for low temperature adsorption cooling applications [J]. Applied Energy, 2013, 112: 1025-1031.
[28]	KHUTIA A, RAMMELBERG H U, SCHMIDT T, et al. Water sorption cycle measurements on functionalized MIL-101Cr for heat transformation application [J]. Chemistry of Materials, 2013, 25 (5): 790-798.
[29]	MAKSIMCHUK N V, TIMOFEEVA M N, MELGUNOV M S, et al. Heterogeneous selective oxidation catalysts based on coordination polymer MIL-101 and transition metal-substituted polyoxometalates [J]. Journal of Catalysis, 2008, 257 (2): 315-323.
[30]	WU T B, ZHANG P, MA J, et al. Catalytic activity of immobilized Ru nanoparticles in a porous metal-organic framework using supercritical fluid [J]. Chinese Journal of Catalysis, 2013, 34 (1): 167-175.
[31]	HONG D Y, HWANG Y K, SERRE C, et al. Porous chromium terephthalate MIL-101 with coordinatively unsaturated sites: surface functionalization, encapsulation, sorption and catalysis [J]. Advanced Functional Materials, 2009, 19 (10): 1537-1552.
[32]	LI Y W, Yang R T. Hydrogen storage in metal-organic and covalent-organic frameworks by spillover [J]. AIChE Journal, 2008, 54 (1): 269-279.
[33]	SENKOVSKA I, KASKEL S. High pressure methane adsorption in the metal-organic frameworks Cu-3(btc)(2), Zn-2(bdc)(2)dabco, and Cr3F(H2O)(2)O(bdc)(3) [J]. Microporous and Mesoporous Materials, 2008, 112 (1/2/3): 108-115.
[34]	LIU Y Y, ZENG J L, ZHANG J, et al. Improved hydrogen storage in the modified metal-organic frameworks by hydrogen spillover effect [J]. International Journal of Hydrogen Energy, 2007, 32 (16): 4005-4010.
[35]	LEBEDEV O I, MILLANGE F, SERRE C, et al. First direct imaging of giant pores of the metal-organic framework MIL-101 [J]. Chemistry of Materials, 2005, 17 (26): 6525-6527.
[36]	LIU D F, Lin Y S, LI Z, et al. Adsorption and separation of CH4/H2 in MIL-101s by molecular simulation study [J]. Chemical Engineering Science, 2013, 98: 246-254.
[37]	WU Y, LIU D F, CHEN H Y, et al. Enhancement effect of lithium-doping functionalization on methanol adsorption in copper-based metal-organic framework [J]. Chemical Engineering Science, 2015, 123: 1-10.
[38]	NGUYEN C, SONWANE C G, BHATIA S K, et al. Adsorption of benzene and ethanol on MCM-41 material [J]. Langmuir, 1998, 14 (17): 4950-4952.
[39]	YAN J, YU Y, MA C, et al. Adsorption isotherms and kinetics of water vapor on novel adsorbents MIL-101(Cr)@GO with super-high capacity [J]. Applied Thermal Engineering, 2015, 84: 118-125.
[40]	YANG R T. Adsorbents: Fundamentals and Applications [M]. New York: John Wiley & Sons; 2003: 8-13.
[41]	SUN X J, XIA Q B, ZHAO Z X, et al. Synthesis and adsorption performance of MIL-101(Cr)/graphite oxide composites with high capacities of n-hexane [J]. Chemical Engineering Journal, 2014, 239: 226-232.
[42]	JOVANOVI? D. Physical adsorption of gases [J]. Kolloid-Zeitschrift und Zeitschrift für Polymere, 1969, 235 (1): 1214-1225.
[43]	SHEN D M, BÜLOW M, SIPERSTEIN F, et al. Comparison of experimental techniques for measuring isosteric heat of adsorption [J]. Adsorption-Journal of the International Adsorption Society, 2000, 6 (4): 275-286.