季铵盐型抗菌树脂合成及其漆膜的抗菌性能

doi:10.11949/j.issn.0438-1157.20150996

化工学报 ›› 2015, Vol. 66 ›› Issue (S2): 473-479.DOI: 10.11949/j.issn.0438-1157.20150996

• 材料化学工程与纳米技术 • 上一篇

季铵盐型抗菌树脂合成及其漆膜的抗菌性能

黄颖虹, 郑成, 毛桃嫣, 林璟, 陈鹏, 陈瑞兰

广州大学精细化工研究所, 广东广州 510006

收稿日期:2015-06-26 修回日期:2015-07-13 出版日期:2015-08-31 发布日期:2015-08-31
通讯作者: 郑成
基金资助:
广州市科技计划项目(2015)。

Synthesis of quaternary ammonium salt antibacterial resin and evaluation of antibacterial performance

HUANG Yinghong, ZHENG Cheng, MAO Taoyan, LIN Jing, CHEN Peng, CHEN Ruilan

Fine Chemical Research Institute, Guangzhou University, Guangzhou 510006, Guangdong, China

Received:2015-06-26 Revised:2015-07-13 Online:2015-08-31 Published:2015-08-31

摘要/Abstract

摘要：

采用聚合反应合成了一种季铵盐型抗菌树脂,通过漆膜的抑菌圈测试、抗菌率测试以及模拟不同环境对漆膜抗菌效果的影响测试对抗菌树脂的抗菌性能进行了评价,并考察了抗菌树脂漆膜的力学性能。结果表明:季铵盐抗菌剂的含量为6%时,漆膜对金黄色葡萄球菌及大肠杆菌的抗菌率均能达到99%以上。在此含量下,对漆膜的力学性能影响不大,且漆膜具有良好的抵抗恶劣环境的能力,漆膜被擦拭1000次后,其抗菌率仍能达到95%以上,具有良好的抗菌持效性能。

关键词: 季铵盐, 树脂, 抗菌性能, 漆膜

Abstract:

A quaternary ammonium salt type antibacterial resin was synthesized by the polymerization reaction. The antibacterial properties was evaluated by means of the bacteriostatic ring test, antibacterial rate test and the influence of different environment on the paint film antibacterial effect test, and the mechanical properties of antibacterial resin paint film were investigated. Results showed that the coating had good mechanical properties, when the content of quaternary ammonium salt was 6%, the antibacterial rate of paint film to the staphylococcus aureus and escherichia coli could reach more than 99%, and the coating had good resistance to bad environment, after wiping 1000 times, its antibacterial rate still more than 95%, and had good antibacterial effect performance.

Key words: quaternary ammonium salt, resin, antibacterial properties, paint film

中图分类号:

TQ317.4

黄颖虹, 郑成, 毛桃嫣, 林璟, 陈鹏, 陈瑞兰. 季铵盐型抗菌树脂合成及其漆膜的抗菌性能[J]. 化工学报, 2015, 66(S2): 473-479.

HUANG Yinghong, ZHENG Cheng, MAO Taoyan, LIN Jing, CHEN Peng, CHEN Ruilan. Synthesis of quaternary ammonium salt antibacterial resin and evaluation of antibacterial performance[J]. CIESC Journal, 2015, 66(S2): 473-479.

参考文献 22

[1]	Goldberg S, Doyle R J, Rosenberg M. Mechanism of enhancement of microbial cell hydrophobicity by cationic polymers[J]. J. Bacteriol.,1990,172(10):5650-5654.
[2]	Joerger R D. Antimicrobial films for food applications a quantitative analysis of their effectiveness[J]. Packag. Technol. Sci., 2007,20:231-273.
[3]	Yudovin-Farber I, Beyth N, Weiss E I, Domb A J. Antibacterial effect of composite resins containing quaternary ammonium polyethyleneimine nanoparticles[J]. Journal of Nanoparticle Research, 2010,12(2):591-603.
[4]	Jampala S N, Sarmadi M, Somers E B, Wong A C L, Denes F S. Plasma-enhanced synthesis of bactericidal quaternary ammonium thin layers on stainless steel and cellulose surfaces[J]. Langmuir, 2008,24:8583-8591.
[5]	Tyagi M, Singh H. Preparation and antibacterial evaluation of urinary balloon catheter[J]. Biomed. Sci. Instrum., 1997,33:240-245.
[6]	Eva H Hansen, Mark A Schembri, Per Klemm, Thomas Schafer, Soren Molin, Lone Gram. Elucidation of the antibacterial mechanism of the curvularia haloperoxidase system by DNA microarray profiling[J]. Applied and Environmental Microbiology, 2004,70(3):1749-1757.
[7]	Lambert P A, Hammond S M. Potassium fluxes, first indication of membrane damage in microorganisms[J]. Biochem. Biophys. Acta,1973,54:796-799.
[8]	Salt W D, Wiseman D. Relationship between uptake of cetyltrimethylammonium bromide by Escherichia coli and its effects on cell growth and viability[J]. Pharm. Pharmacol.,1970,22:261-264.
[9]	Salton M R J. The adsorption of cetyltrimethylammonium bromide by bacteria, its action in releasing cellular constituents and its bactericidal effects[J]. Gen. Microbiol.,1951,5:391-404.
[10]	Salton M R J. Lytic agents, cell permeability and monolayer permeability[J]. Gen. Physiology,1968,52:227-252.
[11]	Daoud N N D, Dickinson N A, Gilbert P. Antibacterial activity and physicoche-mical properties of some alkyl-dimethylbenzyl ammonium chlorides[J]. Microbios., 1983,37:75-85.
[12]	Gilbert P, Al-Taae A N A. Aatimicrobial activity of some alkyl-trimethyl ammonium bromides[J]. Lett. Appl. Microbiol.,1985,1:101-105.
[13]	Balgavy P, Devínsky F. Cut-off effects in biological activities of surfactants[J]. Adv. Colloid. Interface Sci., 1996,66:23-63.
[14]	Seda Tigh R, Vural Evren. Synthesis and characterization of a novel antistatic poly(vinyl cgloride)/quaternary ammonium based ion-conductive acrylate copolymer composites[J]. Journal of Electrostatics,2013,71:987-993.
[15]	Yang Baoping(杨保平),Tan Sheng(潭生),Guo Junhong(郭军红),et al. Preparation of acrylic antibaterial coatings[J].Point & Coatings Industry, 2011,41(8):43-53.
[16]	Daoud N N D, Dickinson N A, Gilbert P. Antibacterial activity and physico-chemical properties of some alkyl-dimethylbenzyl ammonium chlorides[J]. Microbios., 1983,37:75-85.
[17]	Gen L, Neoh K G, Kang E T. Surface fictionalization technique for conferring antibacterial properties to polymeric and cellulosic surfaces[J]. Langmuir,2007,19:10295-10303.
[18]	Hadi Bakhshi, Hamid yeganeh, Shanhran Mehdipour-Ataei, et al. Synthesis and characterization of antibacterial po;yurethane coatings from quaternary ammonium salts functiomalized soybean oil based polyols[J]. Materials Science and Engineering C, 2013,33:153-168.
[19]	何经纬,刘芳,梁晓旭.含季铵盐结构的抗菌性甲基丙烯酸酯单体及其制法和应用[P]:CN,102807510A.2012-12-05.
[20]	Kugler R, Bouloussa O, Rondelez F. Evidence of a charge-density threshold for optimum efficiency of biocidal cationic surfaces[J]. Microbiology,2005,151:1341-1348.
[21]	Murata H, Koepsel R R, Matyjaszewski K, Russell A J. Permanent, non-leaching antibacterial surface:how high density cationic surfaces kill bacterial cells[J]. Biomaterials, 2007,28:4870-4879.
[22]	Shan Jiang, Li Wang, Haojie Yu, et al. Preparation of crosslinked polystyrenes with qyaternary ammonium and their antibacterial behavior[J]. Reactive & Functional Polymers,2005,62:209-213.

季铵盐型抗菌树脂合成及其漆膜的抗菌性能

Synthesis of quaternary ammonium salt antibacterial resin and evaluation of antibacterial performance

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 22

相关文章 15

编辑推荐

Metrics

本文评价

[1]	徐文杰, 贾献峰, 王际童, 乔文明, 凌立成, 王任平, 余子舰, 张寅旭. 有机硅/酚醛杂化气凝胶的制备和性能研究[J]. 化工学报, 2023, 74(8): 3572-3583.
[2]	赵婧, 顾程文, 蹇锡高, 翁志焕. 厚朴酚基环氧树脂防腐涂层的制备及性能评价[J]. 化工学报, 2023, 74(7): 3010-3017.
[3]	陈瑞哲, 程磊磊, 顾菁, 袁浩然, 陈勇. 纤维增强树脂复合材料化学回收技术研究进展[J]. 化工学报, 2023, 74(3): 981-994.
[4]	张娜, 潘鹤林, 牛波, 张亚运, 龙东辉. 酚醛树脂热裂解反应机理的密度泛函理论研究[J]. 化工学报, 2023, 74(2): 843-860.
[5]	郑杰元, 张先伟, 万金涛, 范宏. 丁香酚环氧有机硅树脂的制备及其固化动力学研究[J]. 化工学报, 2023, 74(2): 924-932.
[6]	王建, 雷子萱, 姚家钰, 李建, 刘育红. 对苯二甲醛酚醛树脂的制备及其固化动力学研究[J]. 化工学报, 2022, 73(3): 1403-1415.
[7]	王哲, 祖愿, 胡方圆, 蹇锡高. 含杂萘联苯结构的环氧树脂固化动力学分析[J]. 化工学报, 2022, 73(2): 681-688.
[8]	徐力, 吴谦秋, 雷子萱, 李嘉玄, 刘育红. 硅氧烷预聚体改性热塑性酚醛树脂的交联结构及其力学性能[J]. 化工学报, 2022, 73(10): 4734-4744.
[9]	胡慧慧, 杨亮, 刘道平, 张柯. 低剂量超吸水树脂溶液微滴中甲烷水合物生成动力学[J]. 化工学报, 2022, 73(10): 4659-4667.
[10]	韩维辰, 王佳铭, 贺曼罗, 贺高红, 焉晓明, 阮雪华. 潜伏型环氧固化剂甲基异丁基酮二亚胺的合成及工艺优化[J]. 化工学报, 2021, 72(7): 3832-3838.
[11]	王湘阳, 年永乐, 刘娜, 程文龙. 考虑C-SiO₂反应的新型硅基材料烧蚀分析模型[J]. 化工学报, 2021, 72(6): 3270-3277.
[12]	杜娟, 龚志强, 黄曹兴, 梁辰, 姚双全, 刘杨. 树脂吸附-超滤协同分离甘蔗渣碱法半纤维素[J]. 化工学报, 2021, 72(4): 2139-2147.
[13]	倪佳, 孙雪艳, 税子怡, 贺飞鸿, 惠小敏, 朱亮亮, 陈曦. 湿法再生CO₂空气捕集材料的能耗与性能优化[J]. 化工学报, 2021, 72(3): 1409-1418.
[14]	肖覃, 曾旭, 黄健涵, 刘又年. 富氧功能化超交联树脂的合成及其对苯胺的吸附[J]. 化工学报, 2021, 72(3): 1742-1750.
[15]	金晶, 安秋凤, 杨博文, 史书源, 田华鹏. 环氧基POSS改性环氧树脂的研制与性能研究[J]. 化工学报, 2020, 71(5): 2432-2439.