化工学报 ›› 2012, Vol. 63 ›› Issue (7): 2258-2265.DOI: 10.3969/j.issn.0438-1157.2012.07.039

• 材料化学工程与纳米技术 • 上一篇    下一篇

HDI/IPDI对水性聚氨酯及胶膜性能的影响

颜财彬,傅和青,陈焕钦   

  1. 华南理工大学化学与化工学院
  • 收稿日期:2011-12-14 修回日期:2012-02-22 出版日期:2012-07-05 发布日期:2012-07-05
  • 通讯作者: 傅和青

Effect of HDI/IPDI mole ratio on properties of waterborne polyurethane and its film

YAN Caibin,FU Heqing,CHEN Huanqin   

  • Received:2011-12-14 Revised:2012-02-22 Online:2012-07-05 Published:2012-07-05

摘要: 采用预聚体分散法制备了一系列固含量为50%的水性聚氨酯(WPU),并通过傅里叶红外光谱(FT-IR)、粒径分析仪、X射线衍射(XRD)、差示扫描量热分析(DSC)、拉力试验机等仪器进行表征,研究了HDI/IPDI摩尔比对WPU的乳液性能和胶膜结晶性能、力学性能、耐水性能,以及基材EVA/PVC粘接性能的影响,分析了不同摩尔比的HDI/IPDI和粘接时间与WPU胶黏剂对EVA/PVC粘接性能的关系。研究发现,随着HDI/IPDI摩尔比增加,水性聚氨酯的乳液性能、软硬段的结晶性都得到提高,而胶膜拉伸强度呈先增大后减小的趋势,断裂伸长率则先减小后增大。所有WPU胶膜都有很好耐水性,胶膜吸水率都在5.0%(质量)以下。粘接实验结果表明,WPU胶黏剂对EVA/PVC具有优异的粘接性能,24 h后可对基材产生界面破坏,随着HDI/IPDI摩尔比增加,胶黏剂的粘接强度增大。当HDI/IPDI=7∶1时,水性聚氨酯的综合性能最好。

关键词: 水性聚氨酯, 结晶性能, 力学性能, 粘接性能

Abstract: A series of waterborne polyurethanes (WPUs)with 50% solid content were prepared through a prepolymer process.The properties of the dispersion and its film were characterized by Fourier transform infrared spectroscopy (FT-IR), particle size analyzer, X-ray diffraction (XRD), differential scanning calorimetry (DSC)and tensile test machine.The influence of HDI/IPDI mole ratio on the properties of waterborne polyurethane dispersion, its film and the adhesive strength to EVA/PVC substrate were studied.The relationship between adhesive strength and time was analyzed.The results indicated that the WPU dispersion, crystallinities of soft segment and hard segment were improved with increasing HDI/IPDI mole ratio, while tensile strength of films significantly increased and then showed a small decrease, and the elongation at break increased first, then decreased.WPU films exhibited excellent waterproof performance, and the amount of water absorption was as low as 5.0%(mass).The test result showed that all WPUs prepared exhibited outstanding adhesive strength to EVA/PVC substrate, and the joint failure of EVA/PVC substrates was all caused by the failure of interface after 24 h.With increasing mole ratio of HDI/IPDI,the adhesive strength of adhesive to EVA/PVC substrate increased, and when the mole ratio of HDI/IPDI was 7∶1, the performance of WPU adhesive was the best.

Key words: waterborne polyurethane, crystallinity, mechanical property, adhesive property