渗透汽化-结晶耦合分离稀溶液中的香兰素

doi:10.11949/j.issn.0438-1157.20161828

摘要/Abstract

摘要：

以聚醚嵌段共聚酰胺（PEBA2533）为膜材料，采用干法相转化法制备性能优异的高分子膜，用于渗透汽化-结晶耦合（PVCC）分离系统中回收稀水溶液中的香兰素。采用扫描电子显微镜（SEM）对PEBA2533膜的形貌进行表征。考察原料液浓度、温度对膜渗透汽化性能的影响。结果表明：随着溶液浓度的增加，PEBA2533膜溶胀性能增加，说明PEBA2533能够优先吸附香兰素；随原料液浓度增加，香兰素渗透通量增加，分离因子略微下降；原料液温度增加，香兰素渗透通量和分离因子都增加；并通过Arrhenius方程计算得到香兰素比水对温度更加敏感。PVCC系统中控制一级冷凝器温度为2℃时，一级冷凝器中结晶态香兰素通量为39.52 g·m^-2·h^-1，纯度在99%以上。

关键词: 香兰素, 渗透汽化, 渗透汽化-结晶耦合, 聚醚嵌段共聚酰胺

Abstract:

The high performance poly(ether-block-amide) (PEBA2533) membrane was prepared by dry phase inversion method, and then used for separation of vanillin from dilute aqueous solutions in the pervaporation-crystallization coupling (PVCC) system. The structural morphology of PEBA2533 membranes were characterized by SEM. The effects of feed concentration and operating temperature on the pervaporation performances of membrane were investigated. The results showed that the swelling degree of PEBA2533 membrane increased with the increase of concentration. This indicated that PEBA2533 could preferentially adsorb vanillin. With the increase of the feed concentration, the flux of vanillin increased while the separation factor decreased slightly. The vanillin permeation flux and separation factor both increased as the operating temperature increased. The equation of Arrhenius indicated that vanillin was more sensitive to temperature than water. When the temperature of first condenser was controlled at 2℃ in the PVCC system, the flux of crystal vanillin in the first condenser was 39.52 g·m^-2·h^-1 and the purity was more than 99%.

Key words: vanillin, pervaporation, pervaporation-crystallization coupling, poly (ether-block-amide)

中图分类号:

TQ028.8

王倩, 张新儒, 王永洪, 侯蒙杰, 张桃, 李龙, 刘成岑. 渗透汽化-结晶耦合分离稀溶液中的香兰素[J]. 化工学报, 2017, 68(8): 3126-3132.

WANG Qian, ZHANG Xinru, WANG Yonghong, HOU Mengjie, ZHANG Tao, LI Long, LIU Chengcen. Separation of vanillin from dilute aqueous solutions by pervaporation-crystallization coupling[J]. CIESC Journal, 2017, 68(8): 3126-3132.

参考文献 30

[1]	ALBUQUERQUE I D, MAZZOTTI M. Crystallization process design using thermodynamics to avoid oiling out in a mixture of vanillin and water[J]. Crystal Growth & Design, 2014, 14(11):5617-5625.
[2]	SON G E, SUGARTSEREN N, YOON W B, et al. Phase behavior of ternary mixtures of water-vanillin-ethanol for vanillin extraction via dissipative particle dynamics[J]. Journal of Chemical & Engineering Data, 2014, 59(10):3036-3040.
[3]	PLAGGENBORG R, OVERHAGE J, LOOS A, et al. Potential of rhodococcus strains for biotechnological vanillin production from ferulic acid and eugenol[J]. Applied Microbiology and Biotechnology, 2006, 72(4):745.
[4]	FARGUES C, MATHIAS Á, RODRIGUES A. Kinetics of vanillin production from kraft lignin oxidation[J]. Industrial & Engineering Chemistry Research, 1996, 35(1):28-36.
[5]	杨晓慧, 周永红, 胡丽红, 等. 木质素制备香草醛的研究进展[J]. 纤维素科学与技术, 2010, 18(4):49-54. YANG X H, ZHOU Y H, HU L H, et al. Research advances in preparation of vanillin from lignin[J]. Journal of Cellulose Science and Technology, 2010, 18(4):49-54.
[6]	DI GIOIA D, SCIUBBA L, SETTI L, et al. Production of biovanillin from wheat bran[J]. Enzyme and Microbial Technology, 2007, 41(4):498-505.
[7]	BRAZINHA C, BARBOSA D S, CRESPO J G. Sustainable recovery of pure natural vanillin from fermentation media in a single pervaporation step[J]. Green Chemistry, 2011, 13(8):2197.
[8]	DONG Z Z, GU F L, XU F, et al. Comparison of four kinds of extraction techniques and kinetics of microwave-assisted extraction of vanillin from vanilla planifolia andrews[J]. Food Chemistry, 2014, 149:54-61.
[9]	MOTA M I F, RODRIGUES PINTO P C, LOUREIRO J M, et al. Recovery of vanillin and syringaldehyde from lignin oxidation:a review of separation and purification processes[J]. Separation & Purification Reviews, 2015, 45(3):227-259.
[10]	葛业超. 香兰素的合成与分离的研究现状及发展趋势[J]. 当代经理人, 2006:127-128. GE Y C. Study on the synthesis and separation of vanillin and development trend[J]. Contemporary Managers, 2006:127-128.
[11]	刘礼旺. 香兰素的合成与分离提取研究进展[J]. 农技服务, 2010, 27(8):1038-1039. LIU L W. Research advances in synthesis and separation of vanillin[J]. Agricultural Technology Service, 2010, 27(8):1038-1039.
[12]	MOTA M I F, PINTO P C R, LOUREIRO J M, et al. Successful recovery and concentration of vanillin and syringaldehyde onto a polymeric adsorbent with ethanol/water solution[J]. Chemical Engineering Journal, 2016, 294:73-82.
[13]	MOTA M I F, PINTO P C R, LOUREIRO J M, et al. Adsorption of vanillin and syringaldehyde onto a macroporous polymeric resin[J]. Chemical Engineering Journal, 2016, 288:869-879.
[14]	LIU F F, LIU L, FENG X S. Separation of acetone-butanol-ethanol (ABE) from dilute aqueous solutions by pervaporation[J]. Separation and Purification Technology, 2005, 42(3):273-282.
[15]	BÖDDEKER K W, GATFIELD I L, JÄHNIG J, et al. Pervaporation at the vapor pressure limit:vanillin[J]. Journal of Membrane Science, 1997, 137(1):155-158.
[16]	CAMERA-RODA G, AUGUGLIARO V, CARDILLO A, et al. A pervaporation photocatalytic reactor for the green synthesis of vanillin[J]. Chemical Engineering Journal, 2013, 224:136-143.
[17]	ZHANG X R, LI C C, HAO X G, et al. Recovering phenol as high purity crystals from dilute aqueous solutions by pervaporation[J]. Chemical Engineering Science, 2014, 108:183-187.
[18]	LI C C, ZHANG X R, HAO X G, et al. Thermodynamic and mechanistic studies on recovering phenol crystals from dilute aqueous solutions using pervaporation-crystallization coupling (PVCC) system[J]. Chemical Engineering Science, 2015, 127:106-114.
[19]	HAO X, PRITZKER M, FENG X. Use of pervaporation for the separation of phenol from dilute aqueous solutions[J]. Journal of Membrane Science, 2009, 335(1/2):96-102.
[20]	DING C, ZHANG X R, LI C C, et al. ZIF-8 incorporated polyether-block-amide membrane for phenol permselective pervaporation with high efficiency[J]. Separation and Purification Technology, 2016, 166:252-261.
[21]	LI C C, ZHANG X R, HAO X G, et al. Efficient recovery of high-purity aniline from aqueous solutions using pervaporation-fractional condensation system[J]. AIChE Journal, 2015, 61(12):4445-4455.
[22]	HAYAHA G O. Separation of phenol from aqueous streams by a composite hollow fiber based pervaporation process using polydimethyl siloxane (PDMS) polyether-block-amide (PEBA) as two-layer membranes[J]. Journal of Separation Science and Technology, 2009, 44(12):2894-2914.
[23]	MINHAS B S, CHUBA M R, SAXTON R J. Membrane process for separating sulfur compounds from FCC light naphtha:WO2002053253A1[P]. 2003.
[24]	HASANO?LU A, SALT Y, KELE?ER S, et al. Pervaporation separation of organics from multicomponent aqueous mixtures[J]. Chemical Engineering and Processing:Process Intensification, 2007, 46(4):300-306.
[25]	杨超. 聚醚共聚乙酰胺膜的溶胀及渗透汽化性能研究[D]. 广西:广西大学, 2008. YANG C. Swelling of poly-ether block amide membrane and its pervaporation[D]. Guangxi:Guangxi University, 2008.
[26]	HANSEN C M. Hansen Solubility Parameters:A User's Handbook[M]. CRC Press, 2007.
[27]	MANDAL M K, BHATTACHARYA P. Poly (ether-block-amide) membrane for pervaporative separation of pyridine present in low concentration in aqueous solution[J]. Journal of Membrane Science, 2006, 286(1):115-124.
[28]	GARCÍA V, PONGRÁCZ E, MUURINEN E, et al. Pervaporation of dichloromethane from multicomponent aqueous systems containing n-butanol and sodium chloride[J]. Journal of Membrane Science, 2009, 326(1):92-102.
[29]	JANG M, KAMENS R M, LEACH K B, et al. A thermodynamic approach using group contribution methods to model the partitioning of semivolatile organic compounds on atmospheric particulate matter[J]. Environmental Science & Technology, 1997, 31(10):2805-2811.
[30]	范仲元. 水和水蒸气热力性质图表[M]. 北京:中国电力出版社, 1996:118. FAN Z Y. The Thermodynamic Properties of Water and Steam[M]. Beijing:China Electric Power Press, 1996:118.n & Purification Reviews, 2015, 45(3):227-259.
[10]	葛业超. 香兰素的合成与分离的研究现状及发展趋势[J]. 当代经理人, 2006:127-128. GE Y C, Study on the synthesis and separation of vanillin and development trend[J]. Contemporary Managers, 2006:127-128.
[11]	刘礼旺. 香兰素的合成与分离提取研究进展[J]. 农技服务, 2010, 27(8):1038-1039. LIU L W. Research Advances in synthesis and separation of vanillin[J]. Agricultural Technology Service, 2010, 27(8):1038-1039.
[12]	MOTA M I F, PINTO P C R, LOUREIRO J M, et al. Successful recovery and concentration of vanillin and syringaldehyde onto a polymeric adsorbent with ethanol/water solution[J]. Chemical Engineering Journal, 2016, 294:73-82.
[13]	MOTA M I F, PINTO P C R, LOUREIRO JM, et al. Adsorption of vanillin and syringaldehyde onto a macroporous polymeric resin[J]. Chemical Engineering Journal, 2016, 288:869-879.
[14]	LIU F, LIU L, FENG X. Separation of acetone-butanol-ethanol (ABE) from dilute aqueous solutions by pervaporation[J]. Separation and Purification Technology, 2005, 42(3):273-282.
[15]	BÖDDEKER K W, GATFIELD I L, JÄHNIG J, et al. Pervaporation at the vapor pressure limit:Vanillin[J]. Journal of Membrane Science, 1997, 137(1):155-158.
[16]	CAMERA-RODA G, AUGUGLIARO V, CARDILLO A, et al. A pervaporation photocatalytic reactor for the green synthesis of vanillin[J]. Chemical Engineering Journal, 2013, 224:136-143.
[17]	ZHANG X, LI C, HAO X, et al. Recovering phenol as high purity crystals from dilute aqueous solutions by pervaporation[J]. Chemical Engineering Science, 2014, 108:183-187.
[18]	LI C, ZHANG X, HAO X, et al. Thermodynamic and mechanistic studies on recovering phenol crystals from dilute aqueous solutions using pervaporation-crystallization coupling (PVCC) system[J]. Chemical Engineering Science, 2015, 127:106-114.
[19]	HAO X, PRITZKER M, FENG X. Use of pervaporation for the separation of phenol from dilute aqueous solutions[J]. Journal of Membrane Science, 2009, 335(1-2):96-102.
[20]	DING C, ZHANG X, LI C, et al. ZIF-8 incorporated polyether block amide membrane for phenol permselective pervaporation with high efficiency[J]. Separation and Purification Technology, 2016, 166:252-261.
[21]	LI C, ZHANG X, HAO X, et al. Efficient recovery of high-purity aniline from aqueous solutions using pervaporation-fractional condensation system[J]. AIChE Journal, 2015, 61(12):4445-4455.
[22]	HAYAHA G O. Separation of phenol from aqueous streams by a composite hollow fiber based pervaporation process using polydimethyl siloxane (PDMS)polyether-block-amide (PEBA) as two-layer membranes[J]. Journal of Separation Science and Technology, 2009, 44(12):2894-2914.
[23]	MINHAS B S, CHUBA M R, SAXTON R J. Membrane process for separating sulfur compounds from FCC light naphtha[P]. Google Patents, 2003.
[24]	HASANO?LU A, SALT Y, KELE?ER S, et al. Pervaporation separation of organics from multicomponent aqueous mixtures[J]. Chemical Engineering and Processing:Process Intensification, 2007, 46(4):300-306.
[25]	杨超, 聚醚共聚乙酰胺膜的溶胀及渗透汽化性能研究[D]. 广西:广西大学, 2008. YANG C. Swelling of poly-ether block amide membrane and its pervaporation[D]. Guangxi:Guangxi University, 2008.
[26]	Hansen CM. A user's handbook[M]. 2007.
[27]	MANDAL M K, BHATTACHARYA P. Poly (ether-block-amide) membrane for pervaporative separation of pyridine present in low concentration in aqueous solution[J]. Journal of Membrane Science, 2006, 286(1):115-124.
[28]	GARCÍA V, PONGRÁCZ E, MUURINEN E, et al. Pervaporation of dichloromethane from multicomponent aqueous systems containing n-butanol and sodium chloride[J]. Journal of Membrane Science, 2009, 326(1):92-102.
[29]	JANG M, KAMENS R M, LEACH K B,et al. A thermodynamic approach using group contribution methods to model the partitioning of semivolatile organic compounds on atmospheric particulate matter[J]. Environmental Science & Technology, 1997, 31(10):2805-2811.
[30]	范仲元. 水和水蒸气热力性质图表[M]. 北京:中国电力出版社, 1996:118. FAN Z Y. The Thermodynamic properties of water and steam[M]. Beijing:China Electric Power Press, 1996:118.