Na2SO4掺杂含MgO铝酸钙熟料的结构表征及浸出性能

doi:10.11949/j.issn.0438-1157.20160586

化工学报 ›› 2017, Vol. 68 ›› Issue (1): 467-472.DOI: 10.11949/j.issn.0438-1157.20160586

• 材料化学工程与纳米技术 • 上一篇下一篇

Na₂SO₄掺杂含MgO铝酸钙熟料的结构表征及浸出性能

王波, 荣朔, 楚维钦, 郝圆亮, 孙会兰

河北科技大学材料科学与工程学院, 河北省材料近净成形技术重点实验室, 河北石家庄 050018

收稿日期:2016-05-03 修回日期:2016-10-04 出版日期:2017-01-05 发布日期:2017-01-05
通讯作者: 王波
基金资助:
国家自然科学基金项目（51104053）；河北省自然科学基金项目（E2016208107）；河北省高等学校科学技术研究项目（BJ2016023，QN2015002）。

Crystal structure and leaching performance of MgO-containing calcium aluminate clinkers doped with Na₂SO₄

WANG Bo, RONG Shuo, CHU Weiqin, HAO Yuanliang, SUN Huilan

School of Material Science and Engineering, Hebei Key Laboratory of Material Near-Net Forming Technology, Hebei University of Science and Technology, Shijiazhuang 050018, Hebei, China

Received:2016-05-03 Revised:2016-10-04 Online:2017-01-05 Published:2017-01-05
Contact: 10.11949/j.issn.0438-1157.20160586
Supported by:
supported by the National Natural Science Foundation of China (51104053), the Natural Science Foundation of Hebei Province (E2016208107) and the Science Foundation of University of Hebei Province (BJ2016023, QN2015002).

摘要/Abstract

摘要：

使用分析纯MgO、CaCO₃、SiO₂、Al₂O₃与Na₂SO₄在1350℃保温1 h合成了掺杂Na₂SO₄的含MgO铝酸钙熟料，在Na₂CO₃溶液体系下研究了其氧化铝浸出性能，通过XRD等分析手段对其晶体结构和自粉化性能进行了研究。结果表明，Na₂SO₄可以显著提升铝酸钙熟料的浸出性能，Na₂SO₄掺杂量由0%提高到4%，熟料的氧化铝浸出率由61.89%提高到92.01%，继续添加Na₂SO₄，浸出性能趋于稳定。由XRD结果可知，Na₂SO₄促使20CaO·13Al₂O₃·3MgO·3SiO₂（Q相）发生分解并使其转变为12CaO·7Al₂O₃（C₁₂A₇）。Na⁺进入C₁₂A₇晶格引起晶格畸变，从而提高C₁₂A₇的氧化铝浸出性能。Na₂SO₄的加入降低了熟料的自粉化性能，Na₂SO₄掺杂量由0%提高到6%，熟料的自粉率由97.46%下降到85.34%，当Na₂SO₄掺杂量达到10%后，熟料自粉率仅为36.3%。

关键词: 铝酸钙, 烧结, 氧化铝浸出, Q相, Na₂SO₄掺杂

Abstract:

MgO-containing calcium aluminate clinkers doped with Na₂SO₄ were synthesized using analytical grade reagents of MgO, CaCO₃, SiO₂, Al₂O₃, and Na₂SO₄ at 1350℃ for 1 h.The clinkers were studied for leaching performance in sodium carbonate solution, and for crystal structure and self-disintegrating performance by XRD and SEM.Doping Na₂SO₄ improved leaching performance of clinkers.When Na₂SO₄ content was raised from 0% to 4%, Al₂O₃ leaching ratio of clinkers increased from 61.89% to 92.01%.The leaching tended to be stabilized with further increase of Na₂SO₄ dopant.XRD results showed that doping Na₂SO₄ caused phase transformation from 20CaO·13Al₂O₃·3MgO·3SiO₂(Q-phase) to 12CaO·7Al₂O₃(C₁₂A₇).Na⁺ intrusion into C₁₂A₇ lattice forced lattice distortion, which probably promoted Al₂O₃ leaching.Na₂SO₄ dopant also deteriorated self-disintegration of clinkers.When Na₂SO₄ content increased from 0% to 6%, self-disintegrating ratio decreased from 97.46% to 85.34%, respectively.It further decreased to 36.3% for clinker with 10% Na₂SO₄ dopant.

Key words: calcium aluminate, sintering, alumina leaching, Q-phase, Na₂SO₄ doping

中图分类号:

TF803.21

王波, 荣朔, 楚维钦, 郝圆亮, 孙会兰. Na₂SO₄掺杂含MgO铝酸钙熟料的结构表征及浸出性能[J]. 化工学报, 2017, 68(1): 467-472.

WANG Bo, RONG Shuo, CHU Weiqin, HAO Yuanliang, SUN Huilan. Crystal structure and leaching performance of MgO-containing calcium aluminate clinkers doped with Na₂SO₄[J]. CIESC Journal, 2017, 68(1): 467-472.

参考文献 23

[1]	YUE Q, WANG H M, GAO C K, et al. Resources saving and emissions reduction of the aluminum industry in China[J]. Resources, Conservation and Recycling, 2015, 104:68-75.
[2]	顾松青. 我国的铝土矿资源和高效低耗的氧化铝生产技术[J]. 中国有色金属学报, 2004, 14(S1):91-97. GU S Q. Alumina production technology with high efficiency and low consumption from Chinese bauxite resource[J]. The Chinese Journal of Nonferrous Metals, 2004, 14(S1):91-97.
[3]	谢武明, 楼匡宇, 张文治, 等. 高铁铝土矿的强化还原焙烧-磁选除铁[J]. 有色金属(选矿部分), 2016, (1):26-30. XIE W M, LOU K Y, ZHANG W Z, et al. Reinforce reduction roasting-magnetic separation in removing ferrum of high iron content bauxite[J]. Nonferrous Metals (Mineral Processing Section), 2016, (1):26-30.
[4]	张佰永, 王鹏. 低铝硅比时代的中国氧化铝工艺选择[J]. 轻金属, 2011, (7):36-39. ZHANG B Y, WANG P. Selection for Chinese alumina process in the times of low A/S ratio[J]. Light Metals, 2011, (7):36-39.
[5]	URÍK M, BUJDOŠ M, MILOVÁ-?IAKOVÁ B, et al. Aluminum leaching from red mud by filamentous fungi[J]. Journal of Inorganic Biochemistry, 2015, 152:154-159.
[6]	YAO Z T, XIA M S, SARKER P K, et al. A review of the alumina recovery from coal fly ash, with a focus in China[J]. Fuel, 2014, 120:74-85.
[7]	李来时, 翟玉春, 秦晋国, 等. 以粉煤灰为原料制备高纯氧化铝[J]. 化工学报, 2006, 57(9):2189-2193. LI L S, ZHAI Y C, QIN J G, et al. Extracting high-purity alumina from fly ash[J]. Journal of Chemical Industry and Engineering (China), 2006, 57(9):2189-2193.
[8]	纪利春, 相亚军. 电石渣烧结法从赤泥回收氧化铝[J]. 无机盐工业, 2016, 48(2):68-70. JI L C, XIANG Y J. Alumina recovery from red mud by sintering method of carbide slag[J]. Inorganic Chemicals Industry, 2016, 48(2):68-70.
[9]	YANG Q C, MA S H, ZHENG S L, et al. Recovery of alumina from circulating fluidized bed combustion Al-rich fly ash using mild hydrochemical process[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(4):1187-1195.
[10]	BAI G H, TENG W X G, WANG X G, et al. Alkali desilicated coal fly ash as substitute of bauxite in lime-soda sintering process for aluminum production[J]. Transactions of Nonferrous Metals Society of China, 2010, 20(s1):169-175.
[11]	ZHANG D, PAN X L, YU H Y, et al. Mineral transition of calcium aluminate clinker during high-temperature sintering with low-lime dosage[J]. Journal of Materials Science & Technology, 2015, 31(12):1244-1250.
[12]	孙会兰, 于海燕, 齐铭, 等. 12CaO·7Al2O3和γ-2CaO·SiO2混合物相的合成和溶出性能研究[J]. 轻金属, 2009, (1):9-12. SUN H L, YU H Y, QI M, et al. Synthesis and leaching properties of 12CaO·7Al2O3 and γ-2CaO·SiO2 mixture[J]. Light Metals, 2009, (1):9-12.
[13]	WANG B, CHU W Q, ZHANG J X, et al. Kinetics and mechanism of formation of 20CaO·13Al2O3·3MgO·3SiO2[J]. Mineral Processing and Extractive Metallurgy Imm Transactions Section C, 2015, 124(3):151-156.
[14]	EREMIN N I. Investigations on the complex processing of bauxites[C]//Symposium of ICSOBA. Budapest:Research Institute for Non-ferrous Metals, 1971:329-335.
[15]	王波, 于海燕, 孙会兰, 等. MgO对12CaO·7Al2O3晶体结构及其氧化铝浸出性能的影响[J]. 矿冶工程, 2008, 28(5):68-71. WANG B, YU H Y, SUN H L, et al. Effect of MgO on the crystal structure and alumina leaching property of 12CaO·7Al2O3[J]. Mining and Metallurgical Engineering, 2008, 28(5):68-71.
[16]	田勇攀, 涂赣峰, 潘晓林, 等. Na2O掺杂铝酸钙化合物物相转化与浸出性能[J]. 化工学报, 2015, 66(4):1551-1556. TIAN Y P, TU G F, PAN X L, et al. Phase transformation and leaching performance of Na2O-doping calcium aluminate compounds[J]. CIESC Journal, 2015, 66(4):1551-1556.
[17]	WANG B, SUN H L, GUO D, et al. Effect of Na2O on alumina leaching property and phase transformation of MgO-containing calcium aluminate slags[J]. Transactions of Nonferrous Metals Society of China, 2011, 21(12):2752-2757.
[18]	HOSONO H, HAYASHI K, KAJIHARA K, et al. Oxygen ion conduction in 12CaO·7Al2O3:O2-conduction mechanism and possibility of O-fast conduction[J]. Solid State Ionics, 2009, 180(6/7/8):550-555.
[19]	潘晓林, 于海燕, 田勇攀, 等. 钙空位12CaO·7Al2O3晶体稳定性的计算机模拟[J]. 中国有色金属学报, 2014, 24(11):2914-2920. PAN X L, YU H Y, TIAN Y P, et al. Computer simulation of crystal stability of 12CaO·7Al2O3 with calcium vacancy[J]. The Chinese Journal of Nonferrous Metals, 2014, 24(11):2914-2920.
[20]	沈岳松, 纵宇浩, 眭国荣, 等. Ti-Al-Si-Ox脱硝催化剂载体的组分优化及性能研究[J]. 无机材料学报, 2015, 30(5):542-548. SHEN Y S, ZONG Y H, SUI G R, et al. Component optimization and performance of Ti-Al-Si-Ox deNOx catalyst carrier[J]. Journal of Inorganic Materials, 2015, 30(5):542-548.
[21]	MATSUISHI S, TODA Y, MIYAKAWA M, et al. High-density electron anions in a nanoporous single crystal:[Ca24Al28O64]4+(4e-)[J]. Science, 2003, 301(44):626-630.
[22]	严非男, 杨晨星, 陈俊. 掺杂Rh离子SrTiO3晶体缺陷形成能和电子结构的研究[J]. 人工晶体学报, 2016, 45(1):279-284. YAN F N, YANG C X, CHEN J. Study on the formation energies and electronic structures of Rh doped SrTiO3[J]. Journal of Synthetic Crystals, 2016, 45(1):279-284.
[23]	王波, 宗书凤, 孙会兰, 等. 钙铝比对11.3CaO·7Al2O3微观结构及其溶出性能的影响[J]. 化工学报, 2014, 65(10):4183-4190. WANG B, ZONG S F, SUN H L, et al. Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al2O3[J]. CIESC Journal, 2014, 65(10):4183-4190.

Na₂SO₄掺杂含MgO铝酸钙熟料的结构表征及浸出性能

Crystal structure and leaching performance of MgO-containing calcium aluminate clinkers doped with Na₂SO₄

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 23

相关文章 15

编辑推荐

Metrics

本文评价

[1]	曾如宾, 沈中杰, 梁钦锋, 许建良, 代正华, 刘海峰. 基于分子动力学模拟的Fe₂O₃纳米颗粒烧结机制研究[J]. 化工学报, 2023, 74(8): 3353-3365.
[2]	葛泽峰, 吴雨青, 曾名迅, 查振婷, 马宇娜, 侯增辉, 张会岩. 灰化学成分对生物质气化特性的影响规律[J]. 化工学报, 2023, 74(5): 2136-2146.
[3]	李亚芾, 付亮亮, 白浩隆, 白丁荣, 许光文. 菱镁矿浮选尾矿直接合成同时制备镁橄榄石和镁砂研究[J]. 化工学报, 2022, 73(8): 3679-3687.
[4]	郭志强, 燕可洲, 张吉元, 柳丹丹, 高阳艳, 郭彦霞. 煤矸石/粉煤灰对赤泥钠化还原焙烧反应的影响机制[J]. 化工学报, 2022, 73(5): 2194-2205.
[5]	孙雄康, 李强. 多级复合芯结构的强化沸腾传热研究[J]. 化工学报, 2022, 73(3): 1127-1135.
[6]	王晓蓉, 曾玺, 王芳, 张光义, 许德平, 许光文. 温度和气氛对高K高S糠醛渣灰分的烧结特性研究[J]. 化工学报, 2022, 73(1): 411-424.
[7]	周剑, 江倩, 杨怡, 冯厦厦, 仲兆祥, 邢卫红. 烧结助剂对低温制备碳化硅多孔陶瓷性能的影响[J]. 化工学报, 2021, 72(4): 2293-2299.
[8]	李浩然, 邱彤. 基于因果分析的烧结生产状态预测模型[J]. 化工学报, 2021, 72(3): 1438-1446.
[9]	朱有健, 张显显, 陈奕名, 吴学红, 杨海平, 陈汉平. 磷酸二氢钙对玉米秆灰熔融烧结特性的影响研究[J]. 化工学报, 2020, 71(7): 3313-3321.
[10]	王永胜, 兰小林, 邱天, 张新平, 吴莹莹, 陈莉, 徐伟祥, 郭栋杰, 段正康. 铜基石墨烯复合催化剂的合成与表征[J]. 化工学报, 2020, 71(6): 2889-2899.
[11]	王康, 张扬, 胡丽琳, 张海, 吕俊复, 岳光溪. 高分压水蒸气对石灰石脱硫过程的影响作用[J]. 化工学报, 2019, 70(8): 3188-3195.
[12]	毛燕东, 李克忠, 刘雷, 辛峰. 添加剂对催化气化工艺中煤灰结渣性及气化性能影响研究[J]. 化工学报, 2019, 70(5): 1951-1963.
[13]	朱明汉, 白鹏飞, 胡艳鑫, 黄金. 烧结多孔槽道吸液芯超薄平板热管的传热性能[J]. 化工学报, 2019, 70(4): 1349-1357.
[14]	曲江源, 刘霄龙, 关彦军, 齐娜娜, 滕阳, 徐文青, 朱廷钰, 张锴. 基于CFD模拟的臭氧低温氧化烧结烟气中NO过程分析[J]. 化工学报, 2019, 70(11): 4387-4396.
[15]	张路平, 杨晓凤, 郑海康, 王倩, 蒙真真, 武志红. 多孔Al₂O₃/SiC、MoSi₂/SiC复合材料的制备及吸波性能[J]. 化工学报, 2019, 70(11): 4478-4485.