纳米CaCO3孔径调控及其对碳酸化反应性能的影响

doi:10.11949/j.issn.0438-1157.20171296

摘要/Abstract

摘要：

研究了纳米CaCO₃颗粒间孔径调控对CaO与CO₂碳酸化反应性能的影响。通过有机模板法制备得到一系列比表面积相近、孔径分布不同的纳米CaCO₃，并考察其再生和碳酸化反应性能差异。结果表明：增大平均孔径能促进纳米CaCO₃的热分解反应，并降低分解温度约15℃。将平均孔径由15 nm增大至113 nm可显著提高碳酸化反应速率和转化率。研究认为平均孔径和比表面积对碳酸化反应转化率的影响存在交互作用；比表面积小的纳米CaCO₃，表现出碳酸化反应转化率受扩散控制影响较大，而比表面积较大的表现为碳酸化反应转化率以表面反应影响控制为主的规律。

关键词: 纳米材料, 吸附剂, 二氧化碳, 氧化钙, 碳酸化反应

Abstract:

The pore size modulation of nano CaCO₃ particlesand its effect on the CaO carbonation with CO₂ have been studied. A series of nano CaCO₃ with similar surface area but different pore size distributions were prepared by organic templates, and their differences in regeneration and carbonation properties were tested. The results showed that enlarging the average pore diameter could accelerate the thermal decomposition of CaCO₃, and drop the regenerate temperature by 15℃. Analogously, increasing the pore diameter from 15 nm to 113 nm could promote the CaO carbonation rate and conversion. Additionally, researches revealed that the average pore diameter and surface area had a complex affection on CaO carbonation rate and conversion. The carbonation conversion of nano CaCO₃ with lower surface area is mostly affected by diffusion, while the conversion of nano CaCO₃ with greater surface area is mainly influenced by surface reaction.

Key words: nano materials, adsorbents, carbon dioxide, calcium oxide, carbonation

中图分类号:

TQ116.2

卢尚青, 吴素芳. 纳米CaCO₃孔径调控及其对碳酸化反应性能的影响[J]. 化工学报, 2018, 69(6): 2753-2758.

LU Shangqing, WU Sufang. Modulation of nano CaCO₃ pore size and effect on properties of carbonation reaction[J]. CIESC Journal, 2018, 69(6): 2753-2758.

参考文献 30

[1]	RIDHA F N, LU D Y, SYMONDS R T, et al. Attrition of CaO-based pellets in a 0.1 MWth dual fluidized bed pilot plant for post-combustion CO2 capture[J]. Powder Technology, 2016, 291:60-65.
[2]	VALVERDE J M, SANCHEZ-JIMENZ P E, PEREZ-MAQUEDA L A. Ca-looping for postcombustion CO2 capture:a comparative analysis on the performances of dolomite and limestone[J]. Applied Energy, 2015, 138:202-215.
[3]	BATINI C, BURRA K R G, GUPTA A K. Sorption enhanced steam reforming of methane using calcium looping[C]//55th AIAA Aerospace Sciences Meeting, 2017:1610.
[4]	MACDOWELL N, FLORIN N, BUCHARD A, et al. An overview of CO2 capture technologies[J]. Energy & Environmental Science, 2010, 3(11):1645-1669.
[5]	MARKEWITZ P, KUCKSHINRICHS W, LEITNER W, et al. Worldwide innovations in the development of carbon capture technologies and the utilization of CO2[J]. Energy & Environmental Science, 2012, 5(6):7281-7305.
[6]	VALVERDE J M. Ca-based synthetic materials with enhanced CO2 capture efficiency[J]. Journal of Materials Chemistry A, 2013, 1(3):447-468.
[7]	ERANS M, MANOVIC V, ANTHONY E J. Calcium looping sorbents for CO2 capture[J]. Applied Energy, 2016, 180:722-742.
[8]	BIASIN A, SEGRE C U, SALYVIULO G, et al. Investigation of CaO-CO2 reaction kinetics by in-situ XRD using synchrotron radiation[J]. Chemical Engineering Science, 2015, 127:13-24.
[9]	SANCHEZ-JIMENZ P E, PEREZ-MAQUEDA L A, VALVERDE J M. Nano-silica supported CaO:a regenerable and mechanically hard CO2 sorbent at Ca-looping conditions[J]. Applied Energy, 2014, 118:92-99.
[10]	ZHAO C, ZHOU Z, CHENG Z. Sol-gel-derived synthetic CaO-based CO2 sorbents incorporated with different inert materials[J]. Industrial & Engineering Chemistry Research, 2014, 53(36):14065-14074.
[11]	REDDY G K, QUILLIN S, SMIRNIOTIS P. Influence of the synthesis method on the structure and CO2 adsorption properties of Ca/Zr sorbents[J]. Energy & Fuels, 2014,28(5):3292-3299.
[12]	MANOVIC V, ANTHONY E J. Thermal activation of CaO-based sorbent and self-reactivation during CO2 capture looping cycles[J]. Environmental Science & Technology, 2008, 42(11):4170-4174.
[13]	BLAMEY J, MANOVIC V, ANTHONY E J, et al. On steam hydration of CaO-based sorbent cycled for CO2 capture[J]. Fuel, 2015, 150:269-277.
[14]	LIU W Q, AN H, QIN C L, et al. Performance enhancement of calcium oxide sorbents for cyclic CO2 capture-a review[J]. Energy & Fuels, 2012, 26(5):2751-2767.
[15]	RADFAMIA H R, ILIUTA M C. Metal oxide-stabilized calcium oxide CO2 sorbent for multicycle operation[J]. Chemical Engineering Journal, 2013, 232:280-289.
[16]	WEI S, MAHULI S K, AGNIHOTRI R, et al. High surface area calcium carbonate:pore structural properties and sulfation characteristics[J]. Industrial & Engineering Chemistry Research, 1997, 36(6):2141-2148.
[17]	FLORIN N H, HARRIS A T. Reactivity of CaO derived from nano-sized CaCO3 particles through multiple CO2 capture-and-release cycles[J]. Chemical Engineering Science, 2009, 64(2):187-191.
[18]	WU S F, LI Q H, KIM J N, et al. Properties of a nano CaO/Al2O3 CO2 sorbent[J]. Industrial & Engineering Chemistry Research, 2008, 47(1):180-184.
[19]	WANG S, FAN L, LI C, et al. Porous spherical CaO-based sorbents via PSS-assisted fast precipitation for CO2 capture[J]. ACS Applied Materials & Interfaces, 2014, 6(20):18072-18077.
[20]	LUO C, SHEN Q, DING N, et al. Morphological changes of pure micro-and nano-sized CaCO3 during a calcium looping cycle for CO2 capture[J]. Chemical Engineering & Technology, 2012, 35(3):547-554.
[21]	SANTOS E T, ALFONSIN C, CHAMBEL A, et al. Investigation of a stable synthetic sol-gel CaO sorbent for CO2 capture[J]. Fuel, 2012, 94:624-628.
[22]	KIERZKOWSKA A M, PACCIANI R, MULLER C R. CaO-based CO2 sorbents:from fundamentals to the development of new, highly effective materials[J]. ChemSusChem, 2013, 6(7):1130-1148.
[23]	CHEN C, YANG S, AHN W. Calcium oxide as high temperature CO2 sorbent:effect of textural properties[J]. Materials Letters, 2012, 75:140-142.
[24]	SAKADJIAN B B, IYER M V, GUPTA H, et al. Kinetics and structural characterization of calcium-based sorbents calcined under subatmospheric conditions for the high-temperature CO2 capture process[J]. Industrial & Engineering Chemistry Rhesearch, 2007, 46(1):35-42.
[25]	陈彰旭,郑炳云,李先学,等. 模板法制备纳米材料研究进展[J]. 化工进展, 2010, 29(1):94-99. CHEN Z X, ZHENG B Y, LI X X, et al. Progress in the preparation of nanomaterials employing template method[J]. Chemical Industry & Engineering Progress, 2010, 29(1):94-99.
[26]	ZHAO D, FENG J, HUO Q, et al. Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores[J]. Science, 1998, 279(5350):548-552.
[27]	ABEBE M, HEDIN N, BACSIK Z. Spherical and porous particles of calcium carbonate synthesized with food friendly polymer additives[J]. Crystal Growth & Design, 2015, 15(8):3609-3616.
[28]	ZHAO Z, ZHANG L, DAI H, et al. Surfactant-assisted solvo-or hydrothermal fabrication and characterization of high-surface-area porous calcium carbonate with multiple morphologies[J]. Microporous & Mesoporous Materials, 2011, 138(1):191-199.
[29]	COENEN A, CHURCH T L, HARRIS A T. Biological versus synthetic polymers as templates for calcium oxide for CO2 capture[J]. Energy & Fuels, 2011, 26(1):162-168.
[30]	卢尚青,吴素芳. 碳酸钙热分解进展[J]. 化工学报, 2015, 66(8):2895-2902. LU S Q, WU S F. Advances in calcium carbonate thermal decomposition[J]. CIESC Journal, 2015, 66(8):2895-2902.

纳米CaCO₃孔径调控及其对碳酸化反应性能的影响

Modulation of nano CaCO₃ pore size and effect on properties of carbonation reaction

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 30

相关文章 15

编辑推荐

Metrics

本文评价

[1]	宋瑞涛, 王派, 王云鹏, 李敏霞, 党超镔, 陈振国, 童欢, 周佳琦. 二氧化碳直接蒸发冰场排管内流动沸腾换热数值模拟分析[J]. 化工学报, 2023, 74(S1): 96-103.
[2]	张义飞, 刘舫辰, 张双星, 杜文静. 超临界二氧化碳用印刷电路板式换热器性能分析[J]. 化工学报, 2023, 74(S1): 183-190.
[3]	杨学金, 杨金涛, 宁平, 王访, 宋晓双, 贾丽娟, 冯嘉予. 剧毒气体PH₃的干法净化技术研究进展[J]. 化工学报, 2023, 74(9): 3742-3755.
[4]	刘远超, 关斌, 钟建斌, 徐一帆, 蒋旭浩, 李耑. 单层XSe₂（X=Zr/Hf）的热电输运特性研究[J]. 化工学报, 2023, 74(9): 3968-3978.
[5]	程业品, 胡达清, 徐奕莎, 刘华彦, 卢晗锋, 崔国凯. 离子液体基低共熔溶剂在转化CO₂中的应用[J]. 化工学报, 2023, 74(9): 3640-3653.
[6]	盛冰纯, 于建国, 林森. 铝基锂吸附剂分离高钠型地下卤水锂资源过程研究[J]. 化工学报, 2023, 74(8): 3375-3385.
[7]	杨菲菲, 赵世熙, 周维, 倪中海. Sn掺杂的In₂O₃催化CO₂选择性加氢制甲醇[J]. 化工学报, 2023, 74(8): 3366-3374.
[8]	洪瑞, 袁宝强, 杜文静. 垂直上升管内超临界二氧化碳传热恶化机理分析[J]. 化工学报, 2023, 74(8): 3309-3319.
[9]	陈佳起, 赵万玉, 姚睿充, 侯道林, 董社英. 开心果壳基碳点的合成及其对Q235碳钢的缓蚀行为研究[J]. 化工学报, 2023, 74(8): 3446-3456.
[10]	邢美波, 张中天, 景栋梁, 张洪发. 磁调控水基碳纳米管协同多孔材料强化相变储/释能特性[J]. 化工学报, 2023, 74(7): 3093-3102.
[11]	余娅洁, 李静茹, 周树锋, 李清彪, 詹国武. 基于天然生物模板构建纳米材料及集成催化剂研究进展[J]. 化工学报, 2023, 74(7): 2735-2752.
[12]	葛加丽, 管图祥, 邱新民, 吴健, 沈丽明, 暴宁钟. 垂直多孔碳包覆的FeF₃正极的构筑及储锂性能研究[J]. 化工学报, 2023, 74(7): 3058-3067.
[13]	刘春雨, 周桓宇, 马跃, 岳长涛. CaO调质含油污泥干燥特性及数学模型[J]. 化工学报, 2023, 74(7): 3018-3027.
[14]	张琦钰, 高利军, 苏宇航, 马晓博, 王翊丞, 张亚婷, 胡超. 碳基催化材料在电化学还原二氧化碳中的研究进展[J]. 化工学报, 2023, 74(7): 2753-2772.
[15]	董茂林, 陈李栋, 黄六莲, 吴伟兵, 戴红旗, 卞辉洋. 酸性助水溶剂制备木质纳米纤维素及功能应用研究进展[J]. 化工学报, 2023, 74(6): 2281-2295.