碱式碳酸镁微球的反应结晶过程

doi:10.3969/j.issn.0438-1157.2013.02.042

化工学报 ›› 2013, Vol. 64 ›› Issue (2): 718-724.DOI: 10.3969/j.issn.0438-1157.2013.02.042

• 材料化学工程与纳米技术 • 上一篇下一篇

碱式碳酸镁微球的反应结晶过程

杨晨¹, 宋兴福¹, 汪瑾^1,2, 孙泽¹, 于建国^1,2

1. 华东理工大学,国家盐湖资源综合利用工程技术研究中心,上海 200237;
2. 化学工程联合国家重点实验室(华东理工大学),上海 200237

收稿日期:2012-07-16 修回日期:2012-11-13 出版日期:2013-02-05 发布日期:2013-02-05
通讯作者: 宋兴福
作者简介:杨晨(1984—),男,博士研究生。
基金资助:
新世纪优秀人才项目(NCET-08-0776)。

Reactive crystallization process of hydromagnesite microspheres

YANG Chen¹, SONG Xingfu¹, WANG Jin^1,2, SUN Ze¹, YU Jianguo^1,2

1. National Engineering Research Center for Integrated Utilization of Salt Lake Resource, East China University of Science and Technology, Shanghai 200237, China;
2. State Key Laboratory of Chemical Engineering (East China University of Science and Technolagy), Shanghai 200237, China

Received:2012-07-16 Revised:2012-11-13 Online:2013-02-05 Published:2013-02-05
Supported by:
supported by the Program for New Century Excellent Talents in University (NCET-08-0776).

摘要/Abstract

摘要： 碱式碳酸镁是一种重要的化工产品和原料。实验提供一种反应结晶直接制备碱式碳酸镁微球的方法,考察了搅拌时间、反应温度和反应物浓度对产物形貌和粒度的影响,分析了其形成机制。结果表明,采用控制搅拌时间的方法,制备出粒度在10～43 μm、变异系数为28%～43%的尺寸可控、形态良好的碱式碳酸镁微球。通过对结晶过程晶型晶貌研究发现,氯化镁和碳酸钠反应首先生成无定形物,逐步相转移为结晶相。研究表明,搅拌作用对无定形物相转移具有显著影响。在搅拌过程中,以产生晶核过程为主,在静置状态下,以无定形物生长在已有晶体过程为主,搅拌时间对晶体粒度和形貌起到调控作用。

关键词: 反应结晶, 碱式碳酸镁, 无定形物, 形貌

Abstract: Hydromagnesite is an important chemical raw material and product.A reactive crystallization method was provided to prepare hydromagnesite microspheres directly in experiments.The effects of stirring time, reactive temperature and reactant concentrations on the morphology and particle size were studied.The formation mechanism of hydromagnesite microspheres was analyzed.The results show that hydromagnesite microspheres with controllable size and good shape can be obtained by controlling the stirring time.The size of particles is 10—43 μm with the coefficient of variation of 28%—43%.It is found that the amorphous substance is first generated by the reaction of magnesium chloride and sodium carbonate in the crystallization process.The amorphous substance gradually transfers to crystal phase.The study shows that the stirring has a significant impact on the phase transfer of amorphous substance.Crystal nuclei form during the stirring process.Under the static condition, the growth process of amorphous substance onto the pre-existed crystals is dominant.As a result, the crystal size and morphology can be regulated by the stirring time.

Key words: reactive crystallization, hydromagnesite, amorphous substance, morphology

中图分类号:

杨晨, 宋兴福, 汪瑾, 孙泽, 于建国. 碱式碳酸镁微球的反应结晶过程[J]. 化工学报, 2013, 64(2): 718-724.

YANG Chen, SONG Xingfu, WANG Jin, SUN Ze, YU Jianguo. Reactive crystallization process of hydromagnesite microspheres[J]. CIESC Journal, 2013, 64(2): 718-724.

参考文献 22

[1]	Rasenack N, Müller B W.Crystal habit and tableting behavior[J].Int.J.Pharm., 2002,244:45-57
[2]	Yan C, Xue D, Zou L, Yan X, Wang W.Preparation of magnesium hydroxide nanoflowers[J].J.Cryst.Growth, 2005,282:448-454
[3]	Mann S.The chemistry of form[J].Angew. Chem. Int. Ed., 2000,39:3392-3406
[4]	Zhang Z, Zheng Y, Chen J, Zhang Q.Facile synthesis of monodisperse magnesium oxide microspheres via seed-induced precipitation and their applications in high-performance liquid chromatography[J].Adv. Funct. Mater., 2007,17:2447-2454
[5]	Mitsuhashi K, Tagami N, Tanabe K, Tanabe K, Ohkubo T, Sakai H, Koishi M,Abe M.Synthesis of microtubes with a surface of "house of cards" structure via needlelike particles and control of their pore size[J].Langmuir,2005,21:3659-3663
[6]	Li Q, Ding Y, Yu G, Li C, Li F, Qian Y.Fabrication of light-emitting porous hydromagnesite with rosette-like architecture[J].Solid State Commun.,2003,125:117-120
[7]	Yan C L, Xue D F, Zou L.Fabrication of hexagonal MgO and its precursors by a homogeneous precipitation method[J].J.Mater.Res.Bul., 2006,41(12):2341-2348
[8]	Cheng W T, Li Z B.Controlled supersaturation precipitation of hydromagnesite for the MgCl2-Na2CO3 system at elevated temperatures:chemical modeling and experiment[J].Ind.Eng.Chem.Res., 2010, 49(4):1964-1974
[9]	Song Xingfu(宋兴福),Yang Chen(杨晨),Wang Jin(汪瑾), Sun Shuying(孙淑英), Yu Jianguo(于建国).Synthesis of porous hydromagnesite microspheres with rosette-like morphology[J].Chinese J.Inorg.Chem.(无机化学学报), 2011,27(5):1008-1014
[10]	Zhang Lili(张黎黎), Liu Jiaxiang(刘家祥), Li Min(李敏).Effect of different pyrogenation conditions on crystal morphology of basic magnesium carbonate [J].J. Chin. Chem.Soc.(硅酸盐学报), 2008,36(9):1310-1314
[11]	Hopkinson L, Rutt K, Gressey G.The transformation of nesquehonite to hydromagnesite in the system CaO-MgO-H2O-CO2 CaO-MgO-H2O-CO2:an experimental spectroscopic study[J].The Journal of Geology, 2008,116:387-400
[12]	Hao Z, Pan J, Du F.Synthesis of basic magnesium carbonate microrods with a surface of "house of cards" structure[J].Mater.Lett., 2009,63:985-988
[13]	Ohkubo T, Suzuki S, Mitsuhashi K, Ogura T, Iwanaga S, Sakai H, Koishi M, Abe M.Preparation of petaloid microspheres of basic magnesium carbonate[J].Langmuir,2007,23:5872-5874
[14]	Liu F, Sun C, Yan C, Xue D.Solution-based chemical strategies to purposely control the microstructure of functional materials[J].J.Mater.Sci.Technol., 2008,24:641-648
[15]	Zhang Z,Y Zheng, Zhang J, Zhang Q,Chen J, Liu Z, Liang X.Synthesis and shape evolution of monodisperse basic magnesium carbonate microspheres[J].Cryst. Growth Des.,2007,7:337-342
[16]	Zhou Xiangting(周相廷), Liu Liyan(刘丽艳), Zhai Xueliang(翟学亮).Preceding state of basic magnesium carbonate[J].Chemical Reagents (化学世界), 1999,21(3):135-137
[17]	Cheng Wenting(程文婷),Li Zhibao(李志宝),Ke Jiajun(柯家骏).Effect factors of crystal growth and morphology of MgCO3·3H2O[J].The Chinese Journal of Nonferrous Metals(中国有色金属学报),2008,18(1):230-235
[18]	Zhang Z P, Zheng Y J, Ni Y W, Liu Z, Chen J, Liang X.Temperature- and pH-dependent morphology and FT-IR analysis of magnesium carbonate hydrates[J].J. Phys. Chem.B,2006,110(26):12969-12973
[19]	Lanas J, Alvarez J I.Dolomitic limes:evolution of the slaking process under different conditions[J].Thermochim. Acta, 2004,423(1/2):1-12
[20]	Botha A, Strydom C A.DTA and FT-IR analysis of the rehydration of basic magnesium carbonate[J].J.Therm.Anal.Calorim., 2003,71(3):987-995
[21]	Chen Jianfeng(陈建峰), Chen Gantang(陈甘棠).Mixing-precipitation process(Ⅰ):Experimental[J].Journal of Chemical Industry and Engineering (China)(化工学报), 1994,45(2):176-182
[22]	Chen Jianfeng(陈建峰), Chen Gantang(陈甘棠).Mixing-precipitation process(Ⅱ):Model and its verification by experiments[J].Journal of Chemical Industry and Engineering (China)(化工学报), 1994,45(2):183-190

碱式碳酸镁微球的反应结晶过程

Reactive crystallization process of hydromagnesite microspheres

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 22

相关文章 15

编辑推荐

Metrics

本文评价

[1]	李盼, 马俊洋, 陈志豪, 王丽, 郭耘. Ru/α-MnO₂催化剂形貌对NH₃-SCO反应性能的影响[J]. 化工学报, 2023, 74(7): 2908-2918.
[2]	苏伟怡, 丁佳慧, 李春利, 王洪海, 姜艳军. 酶促反应结晶研究进展[J]. 化工学报, 2023, 74(2): 617-629.
[3]	陆勇, 刘对平, 李晨阳, 周吉彬, 叶茂. 光纤内窥图像法测量MTO催化剂表观形貌及其积炭量的实验研究[J]. 化工学报, 2022, 73(6): 2662-2668.
[4]	唐翠萍, 张雅楠, 梁德青, 李祥. 聚乙烯己内酰胺链端改性及其对甲烷水合物形成的抑制作用研究[J]. 化工学报, 2022, 73(5): 2130-2139.
[5]	葛世轶, 杨遥, 黄正梁, 孙婧元, 王靖岱, 阳永荣. 基于静电分选解析聚乙烯颗粒生长与形貌演变[J]. 化工学报, 2022, 73(4): 1585-1596.
[6]	殷海青, 马祎明, 万旭兴, 董伟兵, 张玉龙, 吴送姑. 碳酸锂气液固三相反应结晶过程研究[J]. 化工学报, 2022, 73(3): 1207-1220.
[7]	王之豪, 宋欣, 殷亚然, 张先明. 微流控纺丝中凝胶速率对螺旋纤维形貌的调控机制[J]. 化工学报, 2022, 73(11): 5158-5166.
[8]	李闯, 张扬, 刘小娟, 王学重. 添加剂作用下阿司匹林结晶模拟和实验研究[J]. 化工学报, 2021, 72(9): 4796-4807.
[9]	周石杰, 任祯, 杨宇森, 卫敏. 不同形貌金属氧化物的制备及其在工业催化反应中的应用[J]. 化工学报, 2021, 72(6): 2972-3001.
[10]	朱慧红, 茆志伟, 杨涛, 冯翔, 金浩, 彭冲, 杨朝合, 王继锋, 方向晨. 催化剂形貌对沸腾床渣油加氢Ni-Mo/Al₂O₃ 催化剂活性位的影响机制[J]. 化工学报, 2021, 72(4): 2076-2085.
[11]	胥永辉, 陈道梁, 孙东科, 李金兵, 韩永生. 微观浓度场对银生长形貌的调控作用[J]. 化工学报, 2020, 71(S2): 281-288.
[12]	李冠男, 贺高红, 姜晓滨. 膜结晶处理高浓度Na⁺、Mg²⁺//Cl^--H₂O溶液的结晶调控[J]. 化工学报, 2019, 70(9): 3412-3420.
[13]	尚良超, 陈晓东, 肖杰. 喷雾干燥颗粒表面形貌形成过程粗粒化模拟[J]. 化工学报, 2019, 70(6): 2153-2163.
[14]	杜占. 颗粒表面金属铁析出规律的热力学研究[J]. 化工学报, 2019, 70(11): 4143-4152.
[15]	陈宇飞, 耿成宝, 楚洪月, 汪波涛, 郭红缘, 岳春艳. 蒙脱土/聚醚砜-双马来酰亚胺复合材料微观形貌及性能[J]. 化工学报, 2018, 69(S1): 148-154.