硬弹性HDPE流延基膜冷拉过程中显微结构的变化

doi:10.11949/j.issn.0438-1157.20151398

化工学报 ›› 2016, Vol. 67 ›› Issue (7): 3063-3070.DOI: 10.11949/j.issn.0438-1157.20151398

• 材料化学工程与纳米技术 • 上一篇下一篇

硬弹性HDPE流延基膜冷拉过程中显微结构的变化

沈鹏, 李娟, 杨兴成, 刘晶如, 俞强

常州大学材料科学与工程学院, 江苏省光伏科学与工程协同创新中心, 江苏常州 213164

收稿日期:2015-09-06 修回日期:2016-02-27 出版日期:2016-07-05 发布日期:2016-07-05
通讯作者: 俞强
基金资助:
江苏高校优势学科建设工程资助项目。

Change in microstructures of hard elastic HDPE cast film during cold-stretching process

SHEN Peng, LI Juan, YANG Xingcheng, LIU Jingru, YU Qiang

Jiansu Key Laboratory for Sollar Cell Materials &Technology, School of Materials Science &Engineering, Changzhou University, Changzhou 213164, Jiangsu, China

Received:2015-09-06 Revised:2016-02-27 Online:2016-07-05 Published:2016-07-05
Supported by:
supported by Priority Academic Program Development of Jiangsu Higher Education Institution.

摘要/Abstract

摘要：

以不同拉伸倍率和拉伸速度在室温下对硬弹性HDPE流延基膜施加冷拉作用，通过原子力显微镜、场发射扫描电镜、X射线衍射以及孔隙率和透气率测定来观察冷拉前后薄膜中片晶结构的变化，并且了解这些显微结构变化对微孔膜结构和性能的影响。研究发现，提高冷拉倍率可以增加拉伸膜中片晶分离程度，有利于形成具有较高孔隙率和透气率的微孔膜，但冷拉倍率过高会使片晶弯曲崩溃，部分微孔闭合；随冷拉速度增加，拉伸膜中片晶分离更加彻底，使得微孔膜中微孔数目增多且分布更加均匀；冷拉过程中拉伸应力下结晶的较长连接链和应力作用下破坏的片晶边缘的微次晶共同构成了拉伸膜中分离片晶间的初始桥结构。

关键词: 微孔膜, 聚合物加工, 高密度聚乙烯, 流延, 冷拉, 显微结构, 形态学

Abstract:

The hard elastic high density polyethylene(HDPE)cast film was cold-stretched uniaxially with different stretching ratios and rates in a process of preparing HDPE microporous membranes. AFM, FE-SEM and WAXD were used to observe the variations in the lamellar structure during the cold-stretching processes, and the microporous structure of resulting microporous membranes was evaluated with measurements of porosity and permeability. It was found that increasing cold-stretching ratio could promote the separation of row-nucleated lamellar structure in the films, and be beneficial to the increase of porosity and permeability in the microporous membranes. However, over high cold-stretching ratio led to the collapse of the lamellae, destroying the microporous structure. With the increase of stretching rates, the lamellae was separated to a greater extent, resulting in generation of more micropores and more uniform distribution. During the cold-stretching, the broken micro-second crystals at the lamellae edge and the crystallized long tie chains between lamellae converted to bridges connecting separated lamellae.

Key words: microporous membrane, polymer processing, high density polyethylene, casting, cold-stretching, microstructure, morphology

中图分类号:

TQ325.1⁺2

沈鹏, 李娟, 杨兴成, 刘晶如, 俞强. 硬弹性HDPE流延基膜冷拉过程中显微结构的变化[J]. 化工学报, 2016, 67(7): 3063-3070.

SHEN Peng, LI Juan, YANG Xingcheng, LIU Jingru, YU Qiang. Change in microstructures of hard elastic HDPE cast film during cold-stretching process[J]. CIESC Journal, 2016, 67(7): 3063-3070.

参考文献 20

[1]	胡继文, 沈家瑞, 黄勇. 硬弹性聚丙烯的排状堆积片晶[J]. 应用化学, 2003, 20(5): 466-469. HU J W, SHEN J R, HUANG Y. Piled lamellae rows in hard elastic polypropylene[J]. Chinese Journal of Applied Chemistry, 2003, 20(5): 466-469.
[2]	高昆, 胡信国, 伊廷锋. 锂离子电池聚烯烃隔膜的特性及发展现状[J]. 电池工业, 2007, 12(2): 122-126. GAO K, HU X G, YI Y F. Characteristics and development situation of the polyolefin separators for Li-ion battery[J]. Chinese Battery Industry, 2007, 12(2): 122-126.
[3]	LEE S Y, PARK S Y, SONG H S. Lamellar crystalline structure of hard elastic HDPE films and its influence on microporous membrane formation[J]. Polymer, 2006, 47(10): 3540-3547.
[4]	LEE S Y, PARK S Y, SONG H S. Effects of melt-extension and annealing on row-nucleated lamellar crystalline structure of HDPE films[J]. Journal of Applied Polymer Science, 2007, 103(5): 3326-3333.
[5]	刘葭, 丁治天, 刘正英, 等. 辊速辊温对高密度聚乙烯拉伸微孔膜及其片晶结构的影响[J]. 高分子学报, 2010, (11): 1278-1283. LIU J, DING Z T, LIU Z Y, et al. Effect of roller rates and temperatures on the structure of HDPE stretched microporous membranes and lamellae[J]. Acta Polymerica Sinica, 2010, (11): 1278-1283.
[6]	丁治天, 刘正英, 刘葭, 等. 高分子量级分含量对熔体挤出拉伸法制备聚丙烯微孔膜的影响[J]. 高分子学报, 2011, (4): 462-468. DING Z T, LIU Z Y, LIU J, et al. Effect of the content of high molecular weight component on PP microporous membranes obtained by melt-extrusion-stretching method[J]. Acta Polymerica Sinica, 2011, (4): 462-468.
[7]	SADEGHI F, AJJI A, CARREAU P J. Analysis of row nucleated lamellar morphology of polypropylene obtained from the cast film process: effect of melt rheology and process conditions[J]. Polymer Engineering & Science, 2007, 47(7): 1170-1178.
[8]	TABATABAEI S H, CARREAU P J, AJJI A. Effect of processing on the crystalline orientation, morphology, and mechanical properties of polypropylene cast films and microporous membrane formation[J]. Polymer, 2009, 50(17): 4228-4240.
[9]	沈鹏, 杨兴成, 朱梦冰, 等. 流延工艺条件对聚乙烯流延基膜取向片晶结构和拉伸成孔性的影响[J]. 高分子材料科学与工程, 2015, 35(5): 129-134. SHEN P, YANG X C, ZHU M B, et al. Effects of casting technique on oriented lamellar structure of HDPE casting film and its micropore-forming performance by uniaxial stretching[J]. Polymeric Materials Science and Engineering, 2015, 35(5): 129-134.
[10]	SAFFAR A, CARREAU P J, AJJI A, et al. Development of polypropylene microporous hydrophilic membranes by blending with PP-g-MA and PP-g-AA[J]. Journal of Membrane Science, 2014, 462: 50-61.
[11]	TABATABAEI S H, CARREAU P J, AJJI A. Microporous membranes obtained from PP/HDPE multilayer films by stretching[J]. Journal of Membrane Science, 2009, 345(1): 148-159.
[12]	SHI Q, YU M, ZHOU X, et al. Structure and performance of porous polymer electrolytes based on P(VDF-HFP) for lithium ion batteries[J]. Journal of Power Sources, 2002, 103(2): 286-292.
[13]	LEI C H, WU S Q, XU R J, et al. A study of plastic plateau disappearance in stress-strain curve of annealed polypropylene films during stretching[J]. Advance in Materials Research, 2013, 2(2): 111-118.
[14]	WU S, LEI C, CAI Q, et al. Study of structure and properties of polypropylene microporous membrane by hot stretching[J]. Polymer Bulletin, 2014, 71(9):2205-2217.
[15]	YU T H. Processing and structure-property behavior of microporous polyethylene: from resin to final film[D]. Virginia: Dissertation, Virginia Polytechnic Institute and State University, 1996.
[16]	ZUO F, KEUM J K, CHEN X, et al. The role of interlamellar chain entanglement in deformation-induced structure changes during uniaxial stretching of isotactic polypropylene[J]. Polymer, 2007, 48(23): 6867-6880.
[17]	NITTA K H, TAKAYANAGI M. Tensile yield of isotactic polypropylene in terms of a lamellar-cluster model[J]. Journal of Polymer Science Part B: Polymer Physics, 2000, 38(8): 1037-1044.
[18]	KIM J, KIM S S, PARK M, et al. Effects of precursor properties on the preparation of polyethylene hollow fiber membranes by stretching[J]. Journal of Membrane Science, 2008, 318(1): 201-209.
[19]	LEI C H, HUANG W L, XU R J, et al. The correlation between the lower temperature melting plateau endotherm and the stretching- induced pore formation in annealed polypropylene films[J]. Journal of Plastic Film and Sheeting, 2012, 28(2): 151-164.
[20]	HOSEMANN R, CAOKOVIC H. Adhasive reibungse alastizitat von hard elastischem polypropylene (HEPP)[J]. Colloid & Polymer Science, 1981, 259(1): 15-21.28(2): 151-164.
	HOSEMANN R, CAOKOVIC H. Adhasive reibungse alastizitat von hard elastischem polypropylene (HEPP). Colloid & Polymer Science, 1981,259(1): 15-21.

硬弹性HDPE流延基膜冷拉过程中显微结构的变化

Change in microstructures of hard elastic HDPE cast film during cold-stretching process

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 20

相关文章 15

编辑推荐

Metrics

本文评价

[1]	刘杰, 吴立盛, 李锦锦, 罗正鸿, 周寅宁. 含乙烯基胺酯键聚醚类可逆交联聚合物的制备及性能研究[J]. 化工学报, 2023, 74(7): 3051-3057.
[2]	刘春雨, 周桓宇, 马跃, 岳长涛. CaO调质含油污泥干燥特性及数学模型[J]. 化工学报, 2023, 74(7): 3018-3027.
[3]	饶纤纤, 杜淼, 单国荣, 潘鹏举. 不同金属盐破乳对丁基橡胶硫化行为的影响[J]. 化工学报, 2023, 74(2): 756-765.
[4]	郑少杰, 王建斌, 胡激江, 李伯耿, 袁文博, 王宗, 姚臻. 单体组成切换法调控聚丙烯/丁烯合金的结构与性能[J]. 化工学报, 2023, 74(2): 904-915.
[5]	郭祥, 乔金硕, 王振华, 孙旺, 孙克宁. 碳燃料固体氧化物燃料电池结构研究进展[J]. 化工学报, 2023, 74(1): 290-302.
[6]	王之豪, 宋欣, 殷亚然, 张先明. 微流控纺丝中凝胶速率对螺旋纤维形貌的调控机制[J]. 化工学报, 2022, 73(11): 5158-5166.
[7]	周东一, 肖湘华, 肖飚, 刘益才. 脂肪类复合相变储能材料中脂肪酸最佳质量含量的确定方法[J]. 化工学报, 2021, 72(S1): 560-566.
[8]	陈婷婷, 韩恺忻, 陈翠雪, 凌雪萍, 沈亮, 卢英华. 铁还原菌Shewanella xiamenensis BC01的有机溶剂应激研究[J]. 化工学报, 2021, 72(7): 3747-3756.
[9]	高姣丽, 李恩泽, 康锦, 成怀刚. 盐湖老卤动态变温分离高纯结晶硫酸镁[J]. 化工学报, 2021, 72(6): 3022-3030.
[10]	田锐, 王沛力, 吕超, 段雪. 有机-无机复合材料中无机相分散度三维荧光分析[J]. 化工学报, 2021, 72(6): 3002-3013.
[11]	牟新竹, 陈振乾. 污泥厚度对超声波辅助热风干燥污泥特性的影响[J]. 化工学报, 2020, 71(S2): 241-252.
[12]	郭飞,张兆想,宋炜,贾晓红. 橡胶硫化过程数值模拟研究进展[J]. 化工学报, 2020, 71(8): 3393-3402.
[13]	赵云, 向中华. 微流控制备金属/共价有机框架功能材料研究进展[J]. 化工学报, 2020, 71(6): 2547-2563.
[14]	代晓玉, 马远恩, 许志明, 张霖宙, 赵锁奇, 徐春明. 催化裂化油浆组成分布对中间相沥青光学织构的影响[J]. 化工学报, 2020, 71(6): 2678-2687.
[15]	贺彦林, 田业, 顾祥柏, 徐圆, 朱群雄. 基于正则化的函数连接神经网络研究及其复杂化工过程建模应用[J]. 化工学报, 2020, 71(3): 1072-1079.