Preparation and coal pyrolysis performance of magnetic MgFe2O4 and its core-shell catalysts

Yong’an CHEN1,2(),Anning ZHOU1,2(),Yunlong LI1,3,Zhiwei SHI1,2,Xinfu HE1,2,Weihong JIAO1,2   

  1. 1.School of Chemistry and Chemical Engineering, Xi’an University of Science and Technology, Xi’an 710054, Shaanxi, China
    2.Key Laboratory of Coal Resources Exploration and Comprehensive Utilization, MNR, Xi’an 710021, Shaanxi, China
    3.Shaanxi Coal Industry Chemical Group, Shenmu Tianyuan Chemical Co. , Yulin 719319, Shaanxi, China
  • Received:2022-03-06 Revised:2022-04-24 Online:2022-08-01 Published:2022-07-05
  • Contact: Anning ZHOU

磁性MgFe2O4及其核壳催化剂制备与煤热解性能研究

陈永安1,2(),周安宁1,2(),李云龙1,3,石智伟1,2,贺新福1,2,焦卫红1,2   

  1. 1.西安科技大学化学与化工学院,陕西 西安 710054
    2.自然资源部煤炭资源勘探与综合利用重点实验室,陕西 西安 710021
    3.陕西煤业化工集团神木天元化工有限公司,陕西 榆林 719319
  • 通讯作者: 周安宁
  • 作者简介:陈永安(1997—),男,硕士研究生, 2920452554@qq.com
  • 基金资助:
    陕西省煤炭联合基金项目(2019JPL-10)

Abstract:

The MgFe2O4 precursor was prepared by the sol-gel method, the MgFe2O4 catalyst was obtained by calcination, and the core-shell structure catalyst MgFe2O4@SiO2 and MgFe2O4@SiO2@HZSM-5 (MSH) were prepared by the St?ber method. The magnetic properties and structural characteristics of the catalysts were investigated by VSM, XRD, SEM, FT-IR, and N2 physical adsorption. In a fixed bed reactor, under an N2 atmosphere, the magnetic catalysts were investigated for the catalytic properties and recovery and regeneration of tar-rich coal from the Bulianta (BLT). The results show that the MgFe2O4 has a cubic spinel structure with a saturation magnetization of 181.50 emu/g and good thermal stability. The above series of magnetic catalysts all show good catalytic activity, among which MSH has the best catalytic activity. Compared with non-catalytic pyrolysis, the tar yield of MSH catalytic pyrolysis increased by 57.7%, the content of aliphatic hydrocarbons and benzene in the tar increased by about 2 times, and the content of polycyclic aromatic hydrocarbons decreased by 8.6%—9.8%. The magnetic separation method can effectively realize the recovery of the catalyst, and regeneration of the catalyst can be realized by roasting in 700℃. The SiO2 coating helps to improve the magnetocaloric stability and catalytic lifetime of the core-shell catalyst.

Key words: catalytic pyrolysis, magnetic MgFe2O4, coating, tar, recovery, regeneration

摘要:

采用溶胶-凝胶法制得MgFe2O4前体,经焙烧得到MgFe2O4催化剂,再经St?ber法制得核壳结构催化剂MgFe2O4@SiO2和MgFe2O4@SiO2@HZSM-5(MSH),利用VSM、XRD、SEM、FT-IR、N2物理吸附等手段研究了催化剂的磁性能和结构特征;在固定床反应器上,考察了N2气氛下磁性催化剂对补连塔富油煤的催化热解特性及回收再生性能。结果表明:MgFe2O4为立方尖晶石结构,饱和磁化强度达到181.50 emu/g,具有良好热稳定性能。上述系列磁性催化剂均呈现出良好的催化活性,其中MSH催化活性最好。与非催化热解相比,MSH催化热解焦油产率提高了57.7%,焦油中脂肪烃和苯类含量增加约2倍,稠环芳烃含量下降8.6%~9.8%。采用磁选方法可有效实现催化剂回收,经700℃下焙烧处理,可实现回收催化剂的再生。SiO2包覆有助于提高核壳结构催化剂的磁热稳定性和催化寿命。

关键词: 催化热解, 磁性MgFe2O4, 包覆, 焦油, 回收, 再生