Effects of various factors on adsorption of MIL-101(Cr) for dyes in aqueous solutions

doi:10.11949/j.issn.0438-1157.20140942

Abstract

Abstract:

Under various conditions, the adsorption capacity of metal-organic framework, MIL-101(Cr), was measured for cationic dyes (methylene blue (MB), rhodamine B) and anionic dyes (helianthine B (HB), acid chrome blue K) in aqueous solutions. The effect of various factors on the adsorption selectivity of MIL-101(Cr) was studied for HB and MB in mixed solutions. The results show that the adsorption capacity to anionic dyes is higher than that to cationic dyes when the dyes exist solely or coexist. The selection coefficient b is 5.9 at T=300 K and pH=3, and it decreases obviously with the increase of pH value, while temperature has a little effect on adsorption selectivity. The mechanism for adsorption selectivity is that MIL-101(Cr) has positive surface potential, so there exist electrostatic attractive interactions between MIL-101(Cr) and anionic dye molecules while it is repulsion interaction for cationic dyes. Moreover, modification with ethyl diamine increases the adsorption selectivity of MIL-101(Cr) for anionic dyes, whereas with oxalic acid the selectivity decreases.

Key words: absorbent, adsorption selectivity, cationic dye, anionic dye, kinetics, stability

摘要：

在多种条件下研究了金属有机框架MIL-101(Cr)对阳离子型染料(亚甲基蓝、罗丹明B)和阴离子型染料(甲基橙、酸性铬蓝K)的吸附性质,主要研究了MIL-101(Cr)对亚甲基蓝和甲基橙的选择性吸附作用。结果表明,中性环境下无论在单组分还是双组分体系中MIL-101(Cr)对阴离子型染料的吸附能力均大于对阳离子型的吸附能力。在pH=3,T=300 K的条件下,选择性系数β可达5.9,但随着pH的增加,选择性系数逐渐降低。相比之下,温度对吸附的选择性影响不大。选择性吸附的机理可以解释为:由于表面带正电荷,MIL-101(Cr)对阴离子型染料产生静电吸引作用;相反,对阳离子型染料的排斥作用而降低了其吸附能力。另外,乙二胺改性提高了MIL-101(Cr)对阴离子型染料的选择吸附性能,而草酸改性降低了选择吸附性。

关键词: 吸附剂, 选择性吸附, 阳离子型染料, 阴离子型染料, 动力学, 稳定性

CLC Number:

TQ136.1⁺1

XU Yanli, YANG Hanbiao, LÜ Mengmeng, CHEN Qi, LIU Xueting, WEI Fengyu. Effects of various factors on adsorption of MIL-101(Cr) for dyes in aqueous solutions[J]. CIESC Journal, 2015, 66(10): 4025-4031.

徐艳丽, 杨汉标, 吕盟盟, 陈琪, 刘雪霆, 魏凤玉. 多种因素对MIL-101(Cr)选择性吸附水溶液中染料的影响[J]. 化工学报, 2015, 66(10): 4025-4031.

References 23

[1]	Jain A K, Gupta V K, Bhatnagar A. Utilization of industrial waste products as adsorbents for the removal of dyes [J]. J. Hazard. Mater., 2003, 101:31-42.
[2]	Gupta V K, Mittal A, Krishnan L, Gajbe V. Adsorption kinetics and column operations for the removal and recovery of malachite green from wastewater using bottom ash [J]. Sep. Purif. Technol., 2004, 40:87-96.
[3]	Gupta V K, Mittal A, Krishnan L, Mittal J. Adsorption treatment and recovery of the hazardous dye, Brilliant Blue FCF, over bottom ash and de-oiled soya [J]. J. Sci., 2006, 293:16-26.
[4]	Lee J Y, Farha O K, Roberts J, Scheidt K A, Nguyen S T, Hupp J T. Metal-organic framework materials as catalysts [J]. Chem. Soc. Rev., 2009, 38:1418-1429.
[5]	Zhou Hongcai, Long J R, Yaghi O M. Introduction to metal-organic frameworks [J]. Chem. Rev., 2012, 112:673-674.
[6]	Meek S T, Greathouse J A, Allendorf M D. Metal-organic frameworks: a rapidly growing class of versatile nanoporous materials [J]. Adv. Mater., 2011, 23: 249-267.
[7]	Jhung S H, Lee J H, Yoon J W, Serre C, Férey G, Chang J S. Microwave synthesis of chromium terephthalate MIL-101 and its benzene sorption ability [J]. Adv. Mater., 2007, 19: 121-124.
[8]	Yang Shaolei, Chen Chunyan, Yan Zhihong, Cai Qingyun, Yao Shouzhuo. Evaluation of metal-organic framework 5 as a new SPE material for the determination of polycyclic aromatic hydrocarbons in environmental waters [J]. J. Sep. Sci., 2013, 36(7):1283-1290.
[9]	Haque E, Lee J E, Jang I T, Hwang Y K, Chang J S, Jegal J, Jhung S H, Adsorptive removal of methyl orange from aqueous solution with metal-organic frameworks, porous chromium-benzenedicarboxylates [J]. J. Hazard. Mater., 2010, 181:535-542.
[10]	Li Jianrong, Sculley J, Zhou Hongcai. Metal-organic frameworks for separations [J]. Chem. Rev., 2012, 112:869-932.
[11]	Huang Kang, Liu Sainan, Li Qianqian, Jin Wanqin. Preparation of novel metal-carboxylate system MOF membrane for gas separation [J]. Sep. Purif. Technol., 2013,119: 94-101.
[12]	Seoane B, Téllez C, Coronas J, Staudt C. NH2-MIL-53(Al) and NH2-MIL-101(Al) in sulfur-containing copolyimide mixed matrix membranes for gas separation [J]. Sep. Purif. Technol., 2013, 111: 72-81.
[13]	Ribeiro A M, Campo M C, Narin G, Santos J C, Ferreira A, Chang J S, Hwang Y K, Seo Y K, Lee U H, Loureiro J M, Rodrigues A E. Pressure swing adsorption process for the separation of nitrogen and propylene with a MOF adsorbent MIL-100(Fe) [J]. Sep. Purif. Technol., 2013, 110: 101-111.
[14]	Crini G. Non-conventional low-cost adsorbents for dye removal: a review [J]. Bioresour. Technol., 2006, 97:1061-1085.
[15]	Al-Degs Y S, El-Barghouthi M I, Khraisheh M A, Ahmad M N, Allen S J. Effect of surface area, micropores, secondary micropores, and mesopores volumes of activated carbons on reactive dyes adsorption from solution [J]. Sep. Sci. Technol., 2004, 39:97-111.
[16]	Wang Shaobin, Boyjoo Y, Choueib A, Zhu Z H. Removal of dyes from aqueous solution using fly ash and red mud [J]. Water Res., 2005, 39: 129-138.
[17]	Ferey G. A chromium terephthalate-based solid with unusually large pore volumes and surface area [J]. Science, 2005, 309:2040-2042.
[18]	Haque E, Khan N A, Lee J E, Jhung S H. Facile purification of porous metal terephthalates with ultrasonic treatment in the presence of amides [J]. Chem. Eur. J., 2009, 15: 11730-11736.
[19]	Chen Chen, Zhang Meng, Guan Qingxin, Li Wei. Kinetic and thermodynamic studies on the adsorption of xylenol orange onto MIL-101(Cr) [J]. Chemical Engineering Journal, 2012,183: 60-67.
[20]	Wang Shaobin, Zhu Z H. Characterisation and environmental application of an Australian natural zeolite for basic dye removal from aqueous solution [J]. J. Hazard. Mater., 2006, 136: 946-952.
[21]	Alpat S K, Ozbayrak O, Alpat S, Akcay H. The adsorption kinetics and removal of cationic dye, Toluidine Blue O, from aqueous solution with Turkish zeolite [J]. J. Hazard. Mater., 2008, 151: 213-220.
[22]	Rauf M A, Qadri S M, Ashraf S, Al-Mansoori K M. Adsorption studies of toluidine blue from aqueous solutions onto gypsum [J]. Chem. Eng. J., 2009, 150: 90-95.
[23]	Singh K P, Mohan D, Sinha S, Tondon G S, Gosh D. Color removal from wastewater using low-cost activated carbon derived from agricultural waste material [J]. Ind. Eng. Chem. Res., 2003,42: 1965-1976.