Synthesis and characterization of β-cyclodextrin polyurethane magnetic adsorbents and their adsorption on corilagin

doi:10.11949/j.issn.0438-1157.20160468

Abstract

Abstract:

Two magnetic adsorbents β-CDPU@Fe₃O₄ and β-CDPU@(SiO₂/Fe₃O₄) were synthesized by encapsulating Fe₃O₄ and SiO₂/Fe₃O₄ composite magnetic beads by β-cyclodextrin polyurethane polymer (β-CDPU), and adsorption and enrichment of polyphenolic natural product corilagin from Phyllanthus niruri L. herb plants by magnetic separation were studied. Both adsorbents were characterized by FTIR, XRD, SEM and TG/DTA techniques. The appearance of several new peaks in FTIR spectra around 1695, 1617, 1559, 1259 and 1033 cm^-1 was attributed to urethane and β-CD moiety. The adsorbent polymeric surface was rough with many protuberant lumps, folds and pores as observed by SEM. Both adsorbents were thermostable below 200℃, indicating suitability for separation usage at room temperature. Polymer content of the two adsorbents reached as high as 41.5% and 36.5%, respectively, based on the mass loss at high temperature in TG/DTA analysis. XRD showed that the crystal structure of Fe₃O₄ in both adsorbents was nearly the same as that of Fe₃O₄ and SiO₂/Fe₃O₄ composite beads. Hence, β-CDPU encapsulation did not alter crystal structure of Fe₃O₄. Adsorption of corilagin by both adsorbents followed Langmuir adsorption isotherm, which was expected from double adsorption sites in β-CDPU skeleton. But the special interaction between Fe₃O₄ magnetic-core and corilagin, probably due to the complex formation of Fe(Ⅲ) and phenolic hydroxyl groups in corilagin molecule, made it difficult to elute corilagin and resulted in low elution and recovery yield of corilagin at 17.0% and 10.5%, respectively. SiO₂ modification on Fe₃O₄ magnetic core was able to hinder such interaction and the adsorbent β-CDPU@(SiO₂/Fe₃O₄) exhibited more favorable performance for corilagin enrichment with the elution yield of 41.0% and recovery yield of 22.8%. The corilagin enrichment from Phyllanthus niruri L. showed the adsorbent β-CDPU@(SiO₂/Fe₃O₄) would find commercial application for recovery and enrichment of specific natural products from plant materials.

Key words: cyclodextrin polyurethane, magnetic, adsorbent, corilagin, Phyllanthus niruri L., adsorption, separation

摘要：

以环糊精聚氨酯β-CDPU包覆Fe₃O₄磁核及SiO₂/Fe₃O₄复合粒子，制备出两种磁性吸附剂β-CDPU@Fe₃O₄和β-CDPU@（SiO₂/Fe₃O₄）。考察了吸附剂对多酚类天然产物柯里拉京的吸附，并结合磁分离技术，从珠子草粗提液中直接富集柯里拉京。采用FTIR、XRD、SEM及热重分析法对两种磁性吸附剂进行了结构表征，表明两种吸附剂中聚合物含量分别为41.5%和36.5%，β-CDPU的包覆未改变Fe₃O₄的晶型。吸附机理研究表明，二者对柯里拉京的吸附均符合Langmuir型等温线，但Fe₃O₄磁核对柯里拉京具有特殊的相互作用，造成柯里拉京洗脱困难，总洗脱率和回收率仅17.0%和10.5%。而磁核经SiO₂修饰后，可以阻碍Fe₃O₄对柯里拉京的接触，提高柯里拉京的洗脱率（41.0%）和回收率（22.8%），实现珠子草中柯里拉京的初步富集。

关键词: 环糊精聚氨酯, 磁性, 吸附剂, 柯里拉京, 珠子草, 吸附, 分离

CLC Number:

O647.3
TB33

ZHAO Jun, MIN Shuxue, LIN Jiduan, CHEN Guo, WANG Xiaoqin. Synthesis and characterization of β-cyclodextrin polyurethane magnetic adsorbents and their adsorption on corilagin[J]. CIESC Journal, 2016, 67(10): 4246-4254.

赵珺, 闵书学, 林集端, 陈国, 王晓琴. 环糊精聚氨酯磁性吸附剂制备、表征及对柯里拉京的吸附[J]. 化工学报, 2016, 67(10): 4246-4254.

References 37

[1]	廖鹏飞, 夏金兰, 聂珍媛, 等. 磁性微球的制备及在生物分离应用中的研究进展[J]. 生物磁学, 2005, 5(4):47-51. LIAO P F, XIA J L, NIE Z Y, et al. Progress in preparation and bio-separation application of magnetic microspheres[J]. Biomagnetism, 2005, 5(4):47-51.
[2]	FRANZREB M, SIEMANN-HERZBERG M, HOBLEY T J, et al. Protein purification using magnetic adsorbent particles[J]. Applied Microbiology and Biotechnology, 2006, 70(5):505-516.
[3]	ZHANG B, XING J M, LANG Y Q, et al. Synthesis of amino-silane modified magnetic silica adsorbents and application for adsorption of flavonoids from Glycyrrhiza uralensis Fisch[J]. Science in China Series B:Chemistry, 2008, 51(2):145-151.
[4]	徐秋生, 李文松. 超顺磁性吸附剂1步高效提取和纯化丹参中丹参酮[J]. 中草药, 2015, 46(24):3670-3674. XU Q S, LI W S. Superparamagnetic adsorbent for one-step efficient extraction and purification of tanshinones from Salvia miltiorrhiza[J]. Chinese Traditional and Herbal Drugs, 2015, 46(24):3670-3674.
[5]	李凯斌, 沈一丁, 费贵强, 等. 阴离子 β-环糊精/Fe3O4磁性微球对Cu2+的吸附[J]. 化工学报, 2014, 65(6):2148-2155. LI K B, SHEN Y D, FEI G Q, et al. Adsorption of Cu2+ by anionic β-cyclodextrin/Fe3O4 magnetic microspheres[J]. CIESC Journal, 2014, 65(6):2148-2155.
[6]	CONNORS K A. The stability of cyclodextrin complexes in solution[J]. Chemical Reviews, 1997, 97(5):1325-1357.
[7]	刘甜甜, 赵珺. 亲水作用色谱研究及环糊精固定相的应用[J]. 化学研究与应用, 2014, 26(5):615-622. LIU T T, ZHAO J. The application of hydrophilic interaction chromatography with cyclodextrin-stationary phase[J]. Chemical Research and Application, 2014, 26(5):615-622.
[8]	沈海民, 武宏科, 纪红兵, 等. β-环糊精-Fe3O4超分子体系的构筑及其应用研究进展[J]. 有机化学, 2014, 34(4):630-646. SHEN H M, WU H K, JI H B, et al. Progress in the construction of β-cyclodextrin-Fe3O4 supramolecular systems and their application[J]. Chinese Journal of Organic Chemistry, 2014, 34(4):630-646.
[9]	WANG M, LIU P, WANG Y, et al. Core-shell superparamagnetic Fe3O4@β-CD composites for host-guest adsorption of polychlorinated biphenyls (PCBs)[J]. Journal of Colloid and Interface Science, 2015, 447:1-7.
[10]	KIASAT A R, NAZARI S. Magnetic nanoparticles grafted with β-cyclodextrin-polyurethane polymer as a novel nanomagnetic polymer brush catalyst for nucleophilic substitution reactions of benzyl halides in water[J]. Journal of Molecular Catalysis A:Chemical, 2012, 365:80-86.
[11]	张欠欠, 彭延庆. 可磁回收的 β-环糊精聚氨酯纳米催化剂催化还原羰基化合物[J]. 化学世界, 2015, (11):649-652. ZHANG Q Q, PENG Y Q. Magnetically recoverable β-cyclodextrin polyurethane nano-catalyst for the reduction of carbonyl compounds[J]. Chemical World, 2015, (11):649-652.
[12]	WILSON L D, MOHAMED M H, HEADLEY J V. Surface area and pore structure properties of urethane-based copolymers containing β-cyclodextrin[J]. Journal of Colloid Interface Science, 2011, 357(1):215-222.
[13]	YAMASAKI H, MAKIHATA Y, FUKUNAGA K. Preparation of crosslinked β-cyclodextrin polymer beads and their application as a sorbent for removal of phenol from wastewater[J]. Journal of Chemical Technology and Biotechnology, 2008, 83(7):991-997.
[14]	MOHAMED M H, WILSON L D, HEADLEY J V, et al. Investigation of the sorption properties of β-cyclodextrin-based polyurethanes with phenolic dyes and naphthenates[J]. Journal of Colloid and Interface Science, 2011, 356:217-226.
[15]	ZHAO J, LIU T T, CHEN G. An effective β-cyclodextrin polyurethane spherical adsorbent for the chromatographic enrichment of corilagin from Phyllanthus niruri L. extract[J]. Reactive and Functional Polymers, 2016, 102:119-129.
[16]	张树峰, 明艳林, 林毅, 等. 叶下珠属植物活性成分柯里拉京研究进展[J]. 亚热带植物科学, 2010, 39(4):79-83. ZHANG S F, MING Y L, LIN Y, et al. Research progress on corilagin of Phyllanthus[J]. Subtropical Plant Science, 2010, 39(4):79-83.
[17]	陈一燕, 陈崇宏. 柯里拉京药理活性研究进展[J]. 中国现代应用药学, 2010, 27(5):390-394. CHEN Y Y, CHEN C H. Advances in the pharmacological activity research on corilagin[J]. Chinese Journal of Modern Applied Pharmacy, 2010, 27(5):390-394.
[18]	HAU D K P, ZHU G Y, LEUNG A K M, et al. In vivo anti-tumour activity of corilagin on Hep3B hepatocellular carcinoma[J]. Phytomedicine, 2010, 18(1):11-15.
[19]	MARKOM M, HASAN M, DAUD W R W, et al. Extraction of hydrolysable tannins from Phyllanthus niruri Linn.:effects of solvents and extraction methods[J]. Separation and Purification Technology, 2007, 52(3):487-496.
[20]	PRASAD K N, YANG B, ZHAO M, et al. High pressure extraction of corilagin from longan (Dimocarpus longan Lour.) fruit pericarp[J]. Separation and Purification Technology, 2009, 70(1):41-45.
[21]	YANG Y C, LI J, ZU Y G, et al. Optimisation of microwave-assisted enzymatic extraction of corilagin and geraniin from Geranium sibiricum Linne and evaluation of antioxidant activity[J]. Food Chemistry, 2010, 122(1):373-380.
[22]	苏鹏飞, 陈国, 赵珺. 表面羧基化Fe3O4磁性纳米粒子的快捷制备及表征[J]. 高等学校化学学报, 2011, 32(7):1472-1477. SU P F, CHEN G, ZHAO J. Convenient preparation and characterization of surface carboxyl-functioned Fe3O4 magnetic nanoparticles[J]. Chemical Journal of Chinese Universities, 2011, 32(7):1472-1477.
[23]	陈佳璐, 陈国, 赵珺, 等. 羧基修饰的超顺磁纳米粒子直接固定化罗伊氏乳杆菌[J]. 化工学报, 2012, 63(4):1175-1181. CHEN J L, CHEN G, ZHAO J, et al. Direct immobilization of Lactobacillus reuteri using carboxyl-functional superparamagnetic nanoparticles[J]. CIESC Journal, 2012, 63(4):1175-1181.
[24]	黄丽珍, 李二冬, 李波, 等. β-环糊精/Fe3O4水基磁流体的制备表征及其对中性红的吸附行为[J]. 应用化学, 2014, 31(5):607-612. HUANG L Z, LI E D, LI B, et al. Preparation of water-based β-cyclodextrin/Fe3O4 magnetic fluid and its adsorption behavior for neutral red[J]. Chinese Journal of Applied Chemistry, 2014, 31(5):607-612.
[25]	HU H, WANG Z, PAN L, et al. Ag-coated Fe3O4@SiO2 three-ply composite microspheres:synthesis, characterization, and application in detecting melamine with their surface-enhanced Raman scattering[J]. Journal of Physical Chemistry C, 2010, 114(17):7738-7742.
[26]	杜雪岩, 马芬, 李芳, 等. Fe3O4@SiO2磁性纳米粒子的制备及表征[J]. 兰州理工大学学报, 2011, 37(2):22-25. DU X Y, MA F, LI F, et al. Preparation and characterization of Fe3O4@SiO2 magnetic nanoparticles[J]. Journal of Lanzhou University of Technology, 2011, 37(2):22-25.
[27]	JIANG Y J, JIANG J H, GAO Q M, et al. A novel nanoscale catalyst system composed of nanosized Pd catalysts immobilized on Fe3O4@SiO2-PAMAM[J]. Nanotechnology, 2008, 19(7):369-381.
[28]	徐芳, 王军涛, 韩朝晖. 正癸酸修饰磁性纳米Fe3O4对溶菌酶的吸附研究[J]. 化学研究与应用, 2013, 25(9):1251-1257. XU F, WANG J T, HAN Z H. Adsorption of lysozyme by Fe3O4 magnetic nanoparticles modified by the capric acid[J]. Chemical Research and Application, 2013, 25(9):1251-1257.
[29]	TANG B, CUI J, WANG Y, et al. Facile synthesis and performances of PEG/SiO2 composite form-stable phase change materials[J]. Solar Energy, 2013, 97:484-492.
[30]	张笛, 邓满凤, 赵赫, 等. 多巴胺包埋磁性SiO2固定化漆酶催化去除4-氯酚[J]. 化工学报, 2015, 66(9):3705-3711. ZHANG D, DENG M F, ZHAO H, et al. Immobilization of laccase on magnetic SiO2 through dopamine self-polymerization for 4-CP removal[J]. CIESC Journal, 2015, 66(9):3705-3711.
[31]	MOHAMED M H, WILSON L D, HEADLEY J V. Tuning the physicochemical properties of β-cyclodextrin based polyurethanes via cross-linking conditions[J]. Microporous and Mesoporous Materials, 2015, 214:23-31.
[32]	HEDGES A R, SHIEH W J, SIKORSKI C T. Use of cyclodextrins for encapsulation in the use of treatment of food products[J]. ACS Symposium Series, 1995, 590:60-71.
[33]	WEI Y, CHENG F, LI H, et al. Thermal properties and micromorphology of polyurethane resins based on liquefied benzylated wood[J]. Journal of Scientific and Industrial Research, 2005, 64:435-439.
[34]	AMSTAD E, GILLICH T, BILECKA I, et al. Ultrastable iron oxide nanoparticle colloidal suspensions using dispersants with catechol-derived anchor groups[J]. Nano Letters, 2009, 9(12):4042-4048.
[35]	AMSTAD E, GEHRING A U, FISCHER H, et al. Influence of electronegative substituents on the binding affinity of catechol-derived anchors to Fe3O4 nanoparticles[J]. Journal of Physical Chemistry C, 2011, 115(3):683-691.
[36]	李媛, 肖乐辉, 周乃元, 等. 在茶叶农药残留测定中用四氧化三铁纳米粒子去除样品中的色素[J]. 分析化学, 2013, 41(1):63-68. LI Y, XIAO L H, ZHOU N Y, et al. Purification of pigments by iron oxide nanoparticles for analysis of pesticide residues in tea[J]. Chinese Journal of Analytical Chemistry, 2013, 41(1):63-68.
[37]	李凯, 孙蕊, 彭羽, 等. Fe3O4磁性分子印迹聚合物的研究进展[J]. 化学研究与应用, 2015, 27(12):1790-1795. LI K, SUN R, PENG Y, et al. Research progress of Fe3O4 magnetic molecularly imprinted polymers[J]. Chemical Research and Application, 2015, 27(12):1790-1795.