Al2O3/ACF复合电极材料的制备及性能表征

doi:10.11949/j.issn.0438-1157.20150440

化工学报 ›› 2015, Vol. 66 ›› Issue (11): 4703-4709.DOI: 10.11949/j.issn.0438-1157.20150440

• 材料化学工程与纳米技术 • 上一篇下一篇

Al₂O₃/ACF复合电极材料的制备及性能表征

李海红, 杨洁, 郭雅妮, 强雪妮

西安工程大学环境与化学工程学院, 陕西西安 710048

收稿日期:2015-04-10 修回日期:2015-07-28 出版日期:2015-11-05 发布日期:2015-11-05
通讯作者: 杨洁
基金资助:
陕西省科技厅工业公关项目(2014k10-08);陕西省教育厅产业化培育资助项目(2013JC15)。

Preparation and properties characterization of Al₂O₃/ACF compositeelectrode materials

LI Haihong, YANG Jie, GUO Yani, QIANG Xueni

College of Environmental and Chemical Engineering, Xi'an Polytechnic University, Xi'an 710048, Shaanxi, China

Received:2015-04-10 Revised:2015-07-28 Online:2015-11-05 Published:2015-11-05
Supported by:
supported by the Department of Industrial Public Relation Projects in Shaanxi Province (2014k10-08) and the Educational Industrialization Cultivation Projects in Shaanxi Province (2013JC15).

摘要/Abstract

摘要：

以H₃PO₄预处理后的活性炭纤维(ACF)毡为原料,采用浸渍煅烧法制备Al₂O₃/ACF复合电极材料;通过扫描电镜(SEM)、比表面积及孔径分析仪(BET)、X射线衍射(XRD)、X射线光电子能谱(XPS)、傅里叶红外光谱分析仪(FTIR)对负载Al₂O₃前后活性炭纤维的微观结构与电化学性能进行表征,利用自制的电吸附装置对NaCl模拟废水进行电吸附性能测试。结果表明,采用浸渍煅烧法成功制备了Al₂O₃/ACF复合电极材料,Al₂O₃/ACF复合体表面及孔道中有絮状或颗粒状的Al₂O₃存在,比表面积从1244.37 m²·g^-1降为974.59 m²·g^-1;同时,Al元素含量为1.06%,Al₂O₃以无晶相无定形态存在于纤维表面;Al₂O₃/ACF表面形成一些Al O键的官能团,其比电容比ACF提高76.5%。负载Al₂O₃后的ACF电极材料电吸附性能增强,除盐效率较ACF原样电极提升了2.3倍,且电极具有可再生性。Al₂O₃/ACF复合材料可以作为电极材料用于去除废水中的无机盐离子。

关键词: 浸渍煅烧法, 制备, 氧化铝, 复合材料, 电吸附

Abstract:

The activated carbon fiber (ACF) felt with H₃PO₄ pretreatment was used as raw materials, adopting dipping calcination method to prepare Al₂O₃/ACF composite electrode materials. The micro-structure and electrochemical performance of the activated carbon fiber before and after loaded with Al₂O₃ were characterized by using scanning electron microscopy (SEM), Brunauer-Emmett-Teller gas adsorption method (BET), X-ray diffraction (XRD), energy X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared spectroscopy (FTIR), respectively, and then using homemade improvised electric adsorption desalination device to test the electric adsorption performance for NaCl model wastewater. The results showed that Al₂O₃/ACF composite electrode materials were prepared with success by adopting the dipping calcination method. There was flocculent or granulate Al₂O₃ in the surface and pores of Al₂O₃/ACF complex, and the specific surface area was decreased from 1244.37 m²·g^-1 to 974.59 m²·g^-1. Meanwhile, the content of Al was 1.06% and Al₂O₃ with amorphous was existed on the surface of activated carbon fiber. The Al-O bonds were found on the surface of Al₂O₃/ACF electrode materials with increasing specific capacitance of 76.5% in comparison with the original activated carbon electrode. After loaded Al₂O_3, the electric double layer capacity of ACF electrode materials was increased, the electric adsorption performance was improved, the desalination efficiency was promoted more than 2.3 times as original and the electrode was reproducible. Al₂O₃/ACF composite materials can be used as the electrode materials for the removal of the inorganic ions in wastewater.

Key words: dipping calcination method, preparation, alumina, composites, electric adsorption

中图分类号:

TQ424.1

李海红, 杨洁, 郭雅妮, 强雪妮. Al₂O₃/ACF复合电极材料的制备及性能表征[J]. 化工学报, 2015, 66(11): 4703-4709.

LI Haihong, YANG Jie, GUO Yani, QIANG Xueni. Preparation and properties characterization of Al₂O₃/ACF compositeelectrode materials[J]. CIESC Journal, 2015, 66(11): 4703-4709.

参考文献 23

[1]	Nghiem L D, Scher A I. Critical risk points of nanofiltration and reverse osmosis process in water recycling applications [J]. Desalination, 2006, 187 (1): 303-312.
[2]	Banasiak L J, Kruttschnitt T W, Schafer A I. Desalination using electrodialysis as a function of voltage and salt concentration [J]. Desalination, 2007, 205 (1): 38-46.
[3]	Soldatov V S, Sokolova V I, Medyak G V, et al. Binary ion exchange equilibria in systems containing, Cl- and on fibrous anion exchangers with tetraalky lammomium groups [J]. Reactive and Functional Polymers, 2007, 67 (12): 1530-1539.
[4]	Kim C. Electrochemical characterization of activated carbon nanofibers as an electrode in supercapacitors [J]. Journal of Power Sources, 2005, 142 (3): 382-388.
[5]	Zhang Lezhong (张乐忠), Hu Jiapeng (胡家朋), Zhao Shengyun (赵生云), et al. Recent advances of research on modified activated carbon [J]. Materials Review (材料导报), 2009, 11 (23): 435-438.
[6]	Ahn H J, Lee J H, Jeong Y, et al. Nanostructured carbon cloth electrode for desalination from aqueous solutions [J]. Materials Science and Engineering A, 2007, 449 (2): 841-845.
[7]	Mohammad A S, Hisham E. Developments in thermal desalination processes: design, energy, and costing aspects [J]. Desalination, 2007, 214 (1/2/3): 227-240.
[8]	Yang C M, Choi W H, Na B K, et al. Capacitive deionization of NaCl solution with carbon aerogel-silica gel composite electrodes [J]. Desalination, 2005, 174 (2):125-133.
[9]	Feng Lajun (冯拉俊), Cao Kaibo (曹凯博), Lei Ali (雷阿利). Preparation of α-Al2O3 ultrafine powder by pyrolytic process [J]. China Powder Science and Technology (中国粉体技术), 2006, 40 (4): 8-10.
[10]	Carrott P J M, Nabais J M V, Ribeiro M M L, et al. Microwave heating as a novel method for introducing molecular sieve properties into activate carbon fibers [J]. Carbon, 2004, 42 (1): 227-229.
[11]	Zhao Yan, Hu Xiaomin, Shan Shiliang. Renovated electroabsorptive desalination by using activated carbon coating electrodes [J]. Journal of Safety and Environment, 2012, 32 (3): 28-32.
[12]	Ottiger S, Pini R, Storti G, Mazzotti M. Competitive adsorption equilibria of CO2 and CH4 on a dry coal [J]. Adsorption. 2008, 14 (4): 539-556.
[13]	Laura J B, Thomas W J, Andrea I. Desalination using electrodialysis as a function of voltage and salt concentration [J]. Desalination, 2007, 205 (1/2/3): 38-46.
[14]	LI Haihong (李海红), LI Hongyan (李红艳). Preparation and electrochemical performance of activated carbon coated electrodes [J]. Journal of Materials Science & Engineering (材料科学与工程学报), 2014, 32 (1):101-106.
[15]	Bouhidel K E, Lakehal A. Infulence of voltage and flow rate on elecdeionization (EDI) process efficiency [J]. Desalination, 2006, 188: 411-421.
[16]	Li Quanming, Qiu Fagui, Zhang Mei, et al. Study on preparation and property of PAN-based activate carbon fiber felt [J]. Acta Scientiarum Naturalium Universitatis Sunyatseni, 2007, 46 (6): 267-268.
[17]	Egashira M, Takatsuji H, Okada S, et al. Properties of containing Sn nano- particles activated carbon fiber for a negative electrode in lithium batteries [J]. Journal of Power Sources, 2002,107: 56-60.
[18]	Li Haihong (李海红), Li Hongyan (李红艳). Effects of different pretreatment methods on structure and adsorption properties of activated carbon [J]. Materials Science and Engineering of Powder Metallurgy (粉末冶金材料科学与工程), 2014, 19 (4): 647-653.
[19]	Han Yanhe (韩严和), Quan Xie (全燮), Zhao Huimin (赵慧敏), et al. Kinetics of enhanced adsorption by polarization for organic pollutants onactivated carbon fiber [J]. Environmental Science (环境科学), 2006, 27 (6): 1111-1116.
[20]	Wang S, Wang D Z, Ji L J, et al. Equilibrium and kinetic studies on the removal of NaCl from aqueous solutions by electrosorption on carbon nanotube electrodes [J]. Separation and Purification Technology, 2007, 58 (1): 12-16.
[21]	Zhang Qianxian (张钱献), Zheng Guoqu (郑国渠), Cai Chao (蔡超), et al. Research on the anodic aluminum oxide as anodic foil of aluminum electrolytic capacitor [J]. Journal of Functional Materials (功能材料), 2011, 42 (6): 1071-1074.
[22]	Hou Qingyu (侯清玉), Wuyun Gerile (乌云格日乐), Zhao Chunwang (赵春旺). Effects of the concentration of heavily oxygen vacancy of rutile TiO2 on electric conductivity performance from first principles study [J]. Acta Physica Sinica (物理学报), 2013, 62 (16): 320-325.
[23]	Moehida I, Korai Y, Shirhama M, et al. Removal of SOx and NOx over activated carbon fibers [J]. Carbon, 2010, 38 (1): 227-239.

Al₂O₃/ACF复合电极材料的制备及性能表征

Preparation and properties characterization of Al₂O₃/ACF compositeelectrode materials

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献 23

相关文章 15

编辑推荐

Metrics

本文评价

[1]	胡兴枝, 张皓焱, 庄境坤, 范雨晴, 张开银, 向军. 嵌有超小CeO₂纳米粒子的碳纳米纤维的制备及其吸波性能[J]. 化工学报, 2023, 74(8): 3584-3596.
[2]	吴文涛, 褚良永, 张玲洁, 谭伟民, 沈丽明, 暴宁钟. 腰果酚生物基自愈合微胶囊的高效制备工艺研究[J]. 化工学报, 2023, 74(7): 3103-3115.
[3]	王志龙, 杨烨, 赵真真, 田涛, 赵桐, 崔亚辉. 搅拌时间和混合顺序对锂离子电池正极浆料分散特性的影响[J]. 化工学报, 2023, 74(7): 3127-3138.
[4]	张澳, 罗英武. 低模量、高弹性、高剥离强度丙烯酸酯压敏胶[J]. 化工学报, 2023, 74(7): 3079-3092.
[5]	王杰, 丘晓琳, 赵烨, 刘鑫洋, 韩忠强, 许雍, 蒋文瀚. 聚电解质静电沉积改性PHBV抗氧化膜的制备与性能研究[J]. 化工学报, 2023, 74(7): 3068-3078.
[6]	朱风, 陈凯琳, 黄小凤, 鲍银珠, 李文斌, 刘嘉鑫, 吴玮强, 高王伟. KOH改性电石渣脱除羰基硫的性能研究[J]. 化工学报, 2023, 74(6): 2668-2679.
[7]	蔡斌, 张效林, 罗倩, 党江涛, 左栗源, 刘欣梅. 导电薄膜材料的研究进展[J]. 化工学报, 2023, 74(6): 2308-2321.
[8]	崔张宁, 胡紫璇, 吴雷, 周军, 叶干, 刘田田, 张秋利, 宋永辉. 可降解纤维素基材料的耐水性能研究进展[J]. 化工学报, 2023, 74(6): 2296-2307.
[9]	李振, 张博, 王丽伟. PEG-EG固-固相变材料的制备和性能研究[J]. 化工学报, 2023, 74(6): 2680-2688.
[10]	陈韶云, 徐东, 陈龙, 张禹, 张远方, 尤庆亮, 胡成龙, 陈建. 单层聚苯胺微球阵列结构的制备及其吸附性能[J]. 化工学报, 2023, 74(5): 2228-2238.
[11]	代佳琳, 毕唯东, 雍玉梅, 陈文强, 莫晗旸, 孙兵, 杨超. 热物性对混合型CPCMs固液相变特性影响模拟研究[J]. 化工学报, 2023, 74(5): 1914-1927.
[12]	吴学红, 栾林林, 陈亚南, 赵敏, 吕财, 刘勇. 可降解柔性相变薄膜的制备及其热性能[J]. 化工学报, 2023, 74(4): 1818-1826.
[13]	刘瑞琪, 周栖桐, 张悦, 贺莹, 高静, 马丽. 基于金纳米颗粒修饰二氧化硅纳米花的生物传感器构建及应用[J]. 化工学报, 2023, 74(3): 1247-1259.
[14]	徐东, 田杜, 陈龙, 张禹, 尤庆亮, 胡成龙, 陈韶云, 陈建. 聚苯胺/二氧化锰/聚吡咯复合纳米球的制备及其电化学储能性[J]. 化工学报, 2023, 74(3): 1379-1389.
[15]	陈瑞哲, 程磊磊, 顾菁, 袁浩然, 陈勇. 纤维增强树脂复合材料化学回收技术研究进展[J]. 化工学报, 2023, 74(3): 981-994.