用于丙烷催化燃烧的PdxPty-ZSM-5/Cordierite整体式催化剂

doi:10.11949/j.issn.0438-1157.20181110

摘要/Abstract

摘要：

以ZSM-5分子筛、铝溶胶、硝酸钯、硝酸铂和水为原料制备分子筛浆料，采用真空抽提-一次涂覆法在堇青石蜂窝陶瓷载体表面制备出Pd_xPt_y-ZSM-5/Cordierite整体式催化剂，考察了Pd负载量、ZSM-5分子筛的硅铝比和Pd/Pt质量比对整体式催化剂的丙烷催化燃烧性能的影响，并用超声波振荡、SEM、XRD、H₂-TPR和C₃H₈-TPD等手段对整体式催化剂进行了表征。当球磨时间为60 min，分子筛浆料固含量为38%时，整体式催化剂的涂层上载量可达到178 g?L^-1，涂层脱落率低于0.5%。Pd₂Pt₃-ZSM-5/Cordierite整体式催化剂（贵金属总负载量为1.2 g?L^-1）对于丙烷的催化燃烧具有较好的催化活性（T₅₀=259℃，T₉₀=323℃）和稳定性，具有良好的工业应用前景，其中较低的ZSM-5分子筛硅铝比以及Pd和Pt之间的相互作用增加了对丙烷的吸附能力和表面活性氧物种的数量，从而提高了整体式催化剂的催化活性。

关键词: 丙烷, 催化燃烧, 真空抽提-一次涂覆法, 整体式催化剂, 分子筛浆料, 贵金属

Abstract:

Pd_xPt_y-ZSM-5/Cordierite monolithic catalysts were prepared on the surface of the cordierite honeycomb supports, via vacuum extraction and one coating method, in which ZSM-5 molecular sieve, alumina sol, platinum or palladium nitrates and water were used as raw materials to prepare molecular sieve slurry. Effects of Pd loading, Si/Al ratio of ZSM-5, the mass ratio of Pd/Pt on the catalytic performance of the monolithic catalysts for the catalytic combustion of propane were investigated. The monolithic catalysts were characterized by ultrasonic oscillation, SEM, XRD, H₂-TPR and C₃H₈-TPD. When the ball milling time is 60 min and the molecular sieve slurry solid content is 38%, the coating amount of the monolith catalyst can reach 178 g?L^-1, and the coating detachment rate is less than 0.5%. Pd₂Pt₃-ZSM-5/Cordierite catalyst (total loading of noble metals of 1.2 g?L^-1 ) exhibits better catalytic activity and stability (T₅₀=259℃, T₉₀=323℃) for the catalytic combustion of propane, which has better industrial application prospect. Lower Si/Al ratio of ZSM-5 and the interaction between Pd and Pt increase the amounts of adsorbed propane and surface active oxygen species, thus increases the catalytic performance of the monolithic catalyst.

Key words: propane, catalytic combustion, vacuum extraction and one coating method, monolithic catalyst, molecular sieves slurry, noble metals

中图分类号:

TE 991.1

唐铨, 郭杨龙, 詹望成, 郭耘, 王丽, 王筠松. 用于丙烷催化燃烧的Pd_xPt_y-ZSM-5/Cordierite整体式催化剂[J]. 化工学报, 2019, 70(3): 944-950.

Quan TANG, Yanglong GUO, Wangcheng ZHAN, Yun GUO, Li WANG, Yunsong WANG. Catalytic combustion of propane over Pd_xPt_y-ZSM-5/Cordierite monolithic catalyst[J]. CIESC Journal, 2019, 70(3): 944-950.

图/表 11

表1 不同球磨时间处理的浆料的涂覆效果比较

Table 1 Effect of milling time for slurry on washcoat performance

球磨时间/min	黏度/(mPa·s)	平均粒径/μm	上载量/(g?L^-1)	脱落率/%
0	84	5.6	73	3.6
30	264	3.3	168	0.2
60	378	3.2	178	0.5
90	439	3.5	198	3.5
150	523	3.4	210	5.3

图1 浆料固含量对涂层上载量和脱落率的影响

Fig.1 Effect of solid content of slurry on loading and mass loss of washcoat

图2 Pd负载量对整体式催化剂催化活性的影响

Fig.2 Effect of Pd loading on catalytic activity of monolith catalysts

图3 ZSM-5硅铝比对整体式催化剂催化活性的影响

Fig.3 Effect of Si/Al ratio of ZSM-5 on catalytic activity of monolith catalysts

图4 Pd/Pt质量比对整体式催化剂催化活性的影响

Fig.4 Effect of mass ratio of Pd/Pt on catalytic activity of monolithic catalysts

表2 Pd/Pt质量比对整体式催化剂催化活性的影响

Table 2 Effect of mass ratio of Pd/Pt on catalytic activity of monolithic catalysts

催化剂	T₅₀/℃	T₉₀ /℃
Pd-ZSM-5/Cordierite	302	342
Pd₄Pt₁-ZSM-5/Cordierite	337	383
Pd₂Pt₃-ZSM-5/Cordierite	259	323
Pd₃Pt₂-ZSM-5/Cordierite	293	337
Pd₁Pt₄-ZSM-5/Cordierite	301	374
Pt-ZSM-5/Cordierite	319	403

图5 整体式催化剂的XRD谱图

Fig.5 XRD patterns of monolith catalysts

图6 整体式催化剂H2-TPR谱图

Fig.6 H2-TPR profiles of monolith catalysts

图7 整体式催化剂的C3H8-TPD谱图

Fig.7 C3H8-TPD profiles of monolith catalysts

图8 堇青石载体和分子筛涂层的SEM图

Fig.8 SEM images of cordierite support and ZSM-5 washcoat

图9 在400℃下整体式催化剂的稳定性

Fig.9 Stability of monolith catalyst at 400℃

参考文献 32

1	DuanJ C, TanJ H, YangL, et al. Concentration, sources and ozone formation potential of volatile organic compounds (VOCs) during ozone episode in Beijing[J]. Atmospheric Research, 2008, 88(1): 25-35.
2	HuangB B, LeiC, WeiC H, et al. Chlorinated volatile organic compounds (Cl-VOCs) in environment-sources, potential human health impacts, and current remediation technologies[J]. Environment International, 2014, 71(4): 118-138.
3	LiottaL F. Catalytic oxidation of volatile organic compounds on supported noble metals[J]. Applied Catalysis B: Environmental, 2010, 100(3/4): 403-412.
4	LiW B, WangJ X, GongH. Catalytic combustion of VOCs on non-noble metal catalysts[J]. Catalysis Today, 2009, 148(1/2): 81-87.
5	ZhangZ, JiangZ, ShangguanW. Low-temperature catalysis for VOCs removal in technology and application: a state-of-the-art review[J]. Catalysis Today, 2016, 264: 270-278.
6	KamalM S, RazzakS A, HossainM M. Catalytic oxidation of volatile organic compounds (VOCs) — a review[J]. Atmospheric Environment, 2016, 140: 117-134.
7	XieY J, YuY Y, GongX Q, et al. Effect of the crystal plane figure on the catalytic performance of MnO₂ for the total oxidation of propane[J]. CrystEngComm, 2015, 17(15): 3005-3014.
8	XieY J, GuoY, GuoY L, et al. A highly effective Ni-modified MnO_x catalyst for total oxidation of propane: the promotional role of nickel oxide[J]. RSC Advances, 2016, 6(55): 50228-50237.
9	XieY J, GuoY, GuoY L, et al. A highly-efficient La-MnO_x catalyst for propane combustion: the promotional role of La and the effect of the preparation method[J]. Catalysis Science & Technology, 2016, 6(23): 8222-8233.
10	HuZ, QiuS, YouY, et al. Hydrothermal synthesis of NiCeO_x nanosheets and its application to the total oxidation of propane[J]. Applied Catalysis B: Environmental, 2018, 225: 110-120.
11	HuZ, WangZ, GuoY, et al. Total oxidation of propane over a Ru/CeO₂ catalyst at low temperature[J]. Environmental Science & Technology, 2018, 52(16): 9531-9541.
12	OkalJ, ZawadzkiM, TylusW. Microstructure characterization and propane oxidation over supported Ru nanoparticles synthesized by the microwave-polyol method[J]. Applied Catalysis B: Environmental, 2011, 101(3/4): 548-559.
13	OkalJ, ZawadzkiM. Combustion of propane over novel zinc aluminate-supported ruthenium catalysts[J]. Applied Catalysis B: Environmental, 2011, 105(1/2): 182-190.
14	ZhuZ Z, LuG Z, ZhangZ G, et al. Highly active and stable Co₃O₄/ZSM-5 catalyst for propane oxidation: effect of the preparation method[J]. ACS Catalysis, 2013, 3(6): 1154-1164.
15	HuZ, LiuX F, MengD M, et al. Effect of ceria crystal plane on the physicochemical and catalytic properties of Pd/ceria for CO and propane oxidation[J]. ACS Catalysis, 2016, 6(4): 2265-2279.
16	ZhuZ Z, LuG Z, GuoY, et al. High performance and stability of the Pt-W/ZSM-5 catalyst for the total oxidation of propane: the role of tungsten[J]. Chemcatchem, 2013, 5(8): 2495-2503.
17	AvilaM S, VignattiC R, ApesteguíaC R, et al. Effect of support on the deep oxidation of propane and propylene on Pt-based catalysts[J]. Chemical Engineering Journal, 2014, 241: 52-59.
18	ParkJ E, KimK B, SeoK W, et al. Propane combustion over supported Pt catalysts[J]. Research on Chemical Intermediates, 2011, 37(9): 1135-1143.
19	MailletT, SolleauC, J JrBarbier, et al. Oxidation of carbon monoxide, propene, propane and methane over a Pd/Al₂O₃ catalyst. Effect of the chemical state of Pd[J]. Applied Catalysis B Environmental, 1997, 14(1/2): 85-95.
20	MailletT, J JrBarbier, DuprezD. Reactivity of steam in exhaust gas catalysis(Ⅲ): Steam and oxygen/steam conversions of propane on a Pd/Al₂O₃ catalyst[J]. Applied Catalysis B Environmental, 1996, 9(1/2/3/4): 251-266.
21	YazawaY, TakagiN, YoshidaH, et al. The support effect on propane combustion over platinum catalyst: control of the oxidation-resistance of platinum by the acid strength of support materials[J]. Applied Catalysis A General, 2002, 233(1/2): 103-112.
22	GarettoT F, RincónE, ApesteguíaC R. Deep oxidation of propane on Pt-supported catalysts: drastic turnover rate enhancement using zeolite supports[J]. Applied Catalysis B: Environmental, 2004, 48(3): 167-174.
23	单学蕾, 关乃佳, 曾翔, 等. 不同硅铝比的Cu-ZSM-5/堇青石整体式催化剂的NO分解反应性能[J]. 催化学报, 2001, 22(3): 242-244.
	ShanX L, GuanN J, ZengX, et al. NO decomposition on Cu-ZSM-5/cordierite monolithic catalyst samples with different Si/Al ratios[J]. Chinese Journal of Catalysis, 2001, 22(3): 242-244.
24	WangS N, CuiY J, LanL, et al. A new monolithic Pt-Pd-Rh motorcycle exhaust catalyst to meet future emission standards[J]. Chinese Journal of Catalysis, 2014, 35(9): 1482-1491.
25	DeugdR M D, KapteijnF, MoulijnJ A. Using monolithic catalysts for highly selective Fischer-Tropsch synthesis[J]. Catalysis Today, 2003, 79/80(3): 495-501.
26	SchneiderR, KießlingD, WendtG. Cordierite monolith supported perovskite-type oxides — catalysts for the total oxidation of chlorinated hydrocarbons[J]. Applied Catalysis B: Environmental, 2000, 28(3/4): 187-195.
27	Colman-LernerE, PelusoM A, SambethJ, et al. Cerium, manganese and cerium/manganese ceramic monolithic catalysts. Study of VOCs and PM removal[J]. Journal of Rare Earths, 2016, 34(7): 675-682.
28	江浩, 郭杨龙, 张志刚, 等. Ni对单Pd型挥发性有机废气净化催化剂的助催化作用[J]. 无机化学学报, 2006, 22(7): 1210-1214.
	JiangH, GuoY L, ZhangZ G, et al. Promotion of Ni on performance of Pd-only catalyst for destractive removal of volatile organic wastes[J]. Chinese Journal of Inorganic Chemistry, 2006, 22(7): 1210-1214.
29	MitraB, KunzruD. Washcoating of different zeolites on cordierite monoliths[J]. Journal of the American Ceramic Society, 2008, 91(1): 64-70.
30	CarvalhoL S, PieckC L, RangelM C, et al. Trimetallic naphtha reforming catalysts(I):Properties of the metal function and influence of the order of addition of the metal precursors on Pt-Re-Sn/γ-Al₂O₃-Cl[J]. Applied Catalysis A: General, 2004, 269(1/2): 91-103.
31	ZhuZ Z, LuG Z, GuoY, et al. Influences of Pd precursors and preparation method on the catalytic performances of Pd-only close-coupled catalysts[J]. Journal of Industrial and Engineering Chemistry, 2012, 18(6): 2135-2140.
32	ElangovanS P, OguraM, ErnstS, et al. A comparative study of zeolites SSZ-33 and MCM-68 for hydrocarbon trap applications[J]. Microporous & Mesoporous Materials, 2006, 96(1/2/3): 210-215.

[1]	汤晓玲, 王嘉瑞, 朱玄烨, 郑仁朝. 基于Pickering乳液的卤醇脱卤酶催化合成手性环氧氯丙烷[J]. 化工学报, 2023, 74(7): 2926-2934.
[2]	李治东, 万佳琪, 刘莹, 唐艺溪, 刘威, 宋忠贤, 张学军. 一步法合成α-MnO₂/β-MnO₂催化剂及其对甲苯催化氧化的性能研究[J]. 化工学报, 2022, 73(8): 3615-3624.
[3]	王婵, 肖国锡, 郭小雪, 徐人威, 岳源源, 鲍晓军. 基于介尺度结构解聚-重组装的Beta分子筛的绿色合成及应用[J]. 化工学报, 2022, 73(6): 2690-2697.
[4]	叶枫, 李刚, 付鑫, 郎雪梅, 王燕鸿, 王盛龙, 张建利, 樊栓狮. 多孔膜反应器中丙烷催化脱氢制丙烯的模拟研究[J]. 化工学报, 2022, 73(5): 2008-2019.
[5]	王结祥, 李洪国, 叶松寿, 郑进保, 陈秉辉. 卤素负载锌-腺嘌呤骨架材料的构建及无助剂催化CO₂环加成反应[J]. 化工学报, 2021, 72(7): 3686-3695.
[6]	张志华, 杜威, 段学志, 周兴贵. 表面改性未焙烧TS-1固载金催化丙烯氢氧环氧化反应性能研究[J]. 化工学报, 2021, 72(7): 3613-3625.
[7]	王刚,段学志,袁渭康,周兴贵. 钛硅分子筛TS-1催化环氧丙烷异构反应的机理探究[J]. 化工学报, 2021, 72(10): 5150-5158.
[8]	杜威, 张志华, 段学志, 周兴贵. 丙烯氢氧环氧化动力学与反应器概念设计研究进展[J]. 化工学报, 2021, 72(1): 116-131.
[9]	邹树平, 姜镇涛, 王志才, 柳志强, 郑裕国. 环氧化物水解酶交联细胞聚集体催化合成(R)-环氧氯丙烷[J]. 化工学报, 2020, 71(9): 4238-4245.
[10]	胡松, 李进龙, 杨卫胜. 环氧丙烷尾气甲醇吸收及纯化工艺[J]. 化工学报, 2020, 71(4): 1657-1665.
[11]	胡松, 李进龙, 李木金, 杨卫胜. 萃取精馏生产高纯度环氧丙烷的工艺研究[J]. 化工学报, 2019, 70(2): 670-677.
[12]	万星晨, 林文胜. 螺旋管丙烷流动沸腾换热特性[J]. 化工学报, 2018, 69(S2): 135-140.
[13]	田雅洁, 林文胜. 船用绕管式LNG气化器方案对比[J]. 化工学报, 2018, 69(S2): 141-146.
[14]	姜玉良, 刘元伟, 韩波, 阮慧敏, 沈江南, 高从堦. PEI交联的PECH/nylon复合阴离子交换膜的制备及性能研究[J]. 化工学报, 2018, 69(6): 2744-2752.
[15]	丁超, 胡海涛, 丁国良, 陈杰, 密晓光, 余思聪. 运行工况对LNG绕管式换热器壳侧换热特性的影响[J]. 化工学报, 2018, 69(6): 2417-2423.