燃煤电厂真实烟气条件下SCR催化剂脱硝性能

doi:10.3969/j.issn.0438-1157.2013.07.041

化工学报 ›› 2013, Vol. 64 ›› Issue (7): 2611-2618.DOI: 10.3969/j.issn.0438-1157.2013.07.041

燃煤电厂真实烟气条件下SCR催化剂脱硝性能

高岩, 栾涛, 彭吉伟, 吕涛

山东大学能源与动力工程学院, 山东济南 250061

收稿日期:2012-11-05 修回日期:2012-12-16 出版日期:2013-07-05 发布日期:2013-07-05
通讯作者: 栾涛
作者简介:高岩(1984- ),男,博士研究生。
基金资助:
山东省科技发展计划项目(2011GSF11716)。

DeNO_x performance of SCR catalyst for exhaust gas from coal-fired power plant

GAO Yan, LUAN Tao, PENG Jiwei, LÜ Tao

School of Energy and Power Engineering, Shandong University, Jinan 250061, Shandong, China

Received:2012-11-05 Revised:2012-12-16 Online:2013-07-05 Published:2013-07-05
Supported by:
supported by the Science and Technology Development Planning of Shandong Province (2011GSF11716).

摘要/Abstract

摘要： 制备了具有工业应用价值的V₂O₅/TiO₂负载WO₃与MoO₃的蜂窝状SCR催化剂,并在某燃煤电厂烟气环境下,对其催化性能进行了测试,结果表明:增大催化剂体积能够提高脱硝效率,但活性增量逐步下降,当脱硝效率达到80%以上时,继续增大催化剂体积其活性提高不显著。催化剂的脱硝活性随着积灰时间的延长而降低,脱硝系统运行4 h后,催化剂脱硝活性减少9.4%。在燃煤电厂尾气飞灰浓度约为0.031 kg·m^-3环境下,为满足尾气中NO_x浓度排放要求(<200 mg·m^-3),每连续运行6 h需进行一次吹灰。催化剂的脱硝性能随着运行时间的延长,先急剧下降,后缓慢降低。在连续运行48~168 h范围内,脱硝活性下降值小于1%,SO₂氧化率下降值小于0.1%。在12个月内,平均每连续运行700 h,脱硝活性降低1%。

关键词: SCR, NO_x, SO₂, NH₃, 燃煤电厂

Abstract: A honeycomb SCR catalyst of V₂O₅/TiO₂ with WO₃ and MoO₃ was prepared and its deNO_x performance was investigated in a pilot plant test using flue gas of a coal-fired power plant.The results show that the larger catalyst volume is,the higher deNO_x efficiency,and SO₂ oxidation increases too,but increase ratio becomes smaller.When deNO_x efficiency is above 80%,the outlet NO_x concentration met the emission standards,and the efficiency improvement is not significant by further enlarging catalyst volume which led to higher construct cost.In order to obtain the best ratio of deNO_x efficiency to catalyst volume and avoid resources waste for single requirement of higher deNO_x efficiency,SCR catalyst volume should be adjusted for different boiler types,according to flue gas component of coal-fired power plant and national emission standards.The deNO_x efficiency reduces with soot increase deposited,and drops about 9.4% within 4 h of soot depositing.The outlet NO_x concentration can be at 198 mg·m^-3 after 8 h of soot depositing.At 0.031 kg·m^-3 of fly ash concentration,the soot deposited needed to be blown each 6 h to obtain a satisfied deNO_x efficiency (>80%).When run time prolongs,the deNO_x efficiency falls sharply first,and then reaches a relative stable level.Within 48—168 h,the deNO_x efficiency and SO₂ oxidation decline less than 1% and 0.1%,respectively.After continuous run for 3 months (2160 h),the NO_x concentration at outlet of SCR tower is 196 mg·m^-3.The deNO_x efficiency declines at a rate of 1% per 700 h for continuous 12 month run.

Key words: SCR, NO_x, SO₂, NH₃, coal-fired power plant

中图分类号:

X511

高岩, 栾涛, 彭吉伟, 吕涛. 燃煤电厂真实烟气条件下SCR催化剂脱硝性能[J]. 化工学报, 2013, 64(7): 2611-2618.

GAO Yan, LUAN Tao, PENG Jiwei, LÜ Tao. DeNO_x performance of SCR catalyst for exhaust gas from coal-fired power plant[J]. CIESC Journal, 2013, 64(7): 2611-2618.

参考文献 16

[1]	Alemany L J,Berti F,Busca G,et al.Characterization and composition of commercial V2O5-WO3-TiO2 SCR catalysts[J].Applied Catalysis B:Environmental,1996,10(4):299-311
[2]	Kim M H,An T H.A commercial V2O5-WO3/TiO2 catalyst used at an NH3-SCR deNOx process in an oil-fired power plant:cause of an increase in deNOxing and NH3 oxidation performances at low temperatures//13th Korean-Japan Symposium on Catalysis[C].Springer,2011
[3]	Xu H,Yan Z Y,Xu X,et al.Experiment study of the pilot ammonia SCR system in a coal-fired power plant//2011 Asia-Pacific Power and Energy Engineering Conference[C].IEEE,2011
[4]	Khodayari R,Odenbrand C U I.Regeneration of commercial TiO2-V2O5-WO3 SCR catalysts used in biofuel plants[J].Applied Catalysis B:Environmental,2001,30(1/2):87-99
[5]	Chen J P,Yang R T.Mechanism of poisoning of the V2O5/TiO2 catalyst for the reduction of NO by NH3[J].Journal of Catalysis,1990,125(2):411-420
[6]	Alemany L J,Lietti L,Ferlazzo N,et al.Reactivity and physicochemical characterization of V2O5-WO3/TiO2 de-NOx catalysts[J].Journal of Catalysis,1995,155(1):117-130
[7]	Huang Haifeng (黄海凤),Zhang Feng (张峰),Lu Hanfeng (卢晗锋),Chen Yinfei (陈银飞).Effect of preparation methods on structures and performance of MnOx/TiO2 catalyst for low-temperature NH3-SCR[J].CIESC Journal (化工学报),2010,61(1):80-85
[8]	Wu Bijun (吴碧君),Xiao Ping (肖萍),Liu Xiaoqin (刘晓勤).Performance and kinetic study on selective catalytic reduction of NOx with NH3 of MnOx-WO3/TiO2 catalyst[J].CIESC Journal (化工学报),2011,62(4):940-946
[9]	Dang Shuai (党帅),Zhong Beijing (钟北京),Yuan Zhen (袁振).Reduction mechanism of NOx by coal gas produced in a 130 t powder coal burner and coupling CFD calculation[J].CIESC Journal (化工学报),2012,63(8):2544-2550
[10]	Yang Juan (杨娟),Wang Yin(汪印),Yu Jian (余剑),Xu Guangwen (许光文).Removal of low concentration NO at room temperature using metal oxide supported on activated carbon[J].CIESC Journal (化工学报),2012,63(8):2538-2543
[11]	Zheng Y,Jensen A D,Johnsson J E,et al.Deactivation of V2O5-WO3-TiO2 SCR catalyst at biomass fired power plants:elucidation of mechanisms by lab-and pilot-scale experiments[J].Applied Catalysis B:Environmental,2008,83(3/4):186-194
[12]	Zheng Y,Jensen A D,Johnsson J E.Deactivation of V2O5-WO3-TiO2 SCR catalyst at a biomass-fired combined heat and power plant[J].Applied Catalysis B:Environmental,2005,60(3/4):253-264
[13]	Gao X,Du X S,Fu Y C,et al.Theoretical and experimental study on the deactivation of V2O5 based catalyst by lead for selective catalytic reduction of nitric oxides[J].Catalysis Today,2011,175(1):625-630
[14]	Gao Y,Luan T,Lü T,et al.The Mo loading effect on thermo stability and SO2 oxidation of SCR catalyst[J].Advanced Materials Research,2012,573:58-62
[15]	Gao Y,Luan T,Lü T,et al.The Mo loading effect on SCR deNOx performance for V-W-Mo/TiO2 catalyst[J].Applied Mechanics and Materials,2012,229:126-129
[16]	Gao Yan (高岩),Luan Tao (栾涛),Cheng Kai (程凯),et al.Industrial experiment on selective catalytic reduction honeycomb catalyst[J].Proceedings of the Chinese Society of Electrical Engineering (中国电机工程学报),2011,31(35):21-28

燃煤电厂真实烟气条件下SCR催化剂脱硝性能

DeNO_x performance of SCR catalyst for exhaust gas from coal-fired power plant

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 16

相关文章 15

编辑推荐

Metrics

本文评价

[1]	周微, 王福烨, 贺宁, 于海斌, 马新宾, 刘家旭. Cu/SSZ-13催化剂脱硝活性中心与催化性能构效关系的研究[J]. 化工学报, 2022, 73(2): 672-680.
[2]	黄顺进, 张丽, 颜井冲, 王志刚, 雷智平, 李占库, 任世彪, 王知彩, 水恒福. 高碱煤与煤矸石掺烧SO₂和NO减排及结渣抑制研究[J]. 化工学报, 2022, 73(12): 5581-5591.
[3]	谢玉仙, 刘涛, 苏胜, 刘利军, 钟毓秀, 马智伟, 许凯, 汪一, 胡松, 向军. 工业窑炉烟气氧含量对钒钛系催化剂NH₃-SCR脱硝反应的影响[J]. 化工学报, 2022, 73(10): 4410-4418.
[4]	陈尔健, 代彦军. 使用NH₃-LiNO₃工质对的增压型回热吸收循环性能分析[J]. 化工学报, 2021, 72(S1): 445-452.
[5]	尹子骏, 苏胜, 卿梦霞, 赵志刚, 王中辉, 王乐乐, 江龙, 汪一, 胡松, 向军. 一种典型钒钛系SCR催化剂SO₃生成特性研究[J]. 化工学报, 2021, 72(5): 2596-2603.
[6]	王东亮, 谢江鹏, 周怀荣, 孟文亮, 杨勇, 李德磊. 基于MDEA的烟气SO₂捕集过程工艺参数和能量集成分析[J]. 化工学报, 2021, 72(3): 1521-1528.
[7]	张盈盈, 郭淑娜, 宋帅龙, 杨许召, 吴诗德, 田俊峰, 韩光鲁, 张静静, 李亚坤, 张建强. 离子液体/低共熔溶剂用于NH₃分离过程的热力学分析[J]. 化工学报, 2021, 72(3): 1264-1274.
[8]	杨润农,余林,赵向云,杨晓波,高梓寒,傅广赢,姜久兴,练纬琳,刘武源,范群. 无模板法合成的Phi分子筛在NO选择性催化还原中的应用[J]. 化工学报, 2020, 71(12): 5578-5588.
[9]	刘应书,孙宁起,李子宜,杨雄,魏进超,杨本涛,吴倩倩,刘佳欣. 冷凝法回收烟气吸附脱硫解吸气中SO₂工艺参数的影响规律研究[J]. 化工学报, 2020, 71(12): 5620-5627.
[10]	肖俏欣, 林文俊, 李浩然, 王从敏. 含醚阴离子功能化离子液体高效捕集SO₂[J]. 化工学报, 2020, 71(1): 361-367.
[11]	李向阳, 李扬, 靳立军, 杨赫, 王德超, 胡浩权. MnO_x改性活性炭用于模拟烟气中Hg⁰的脱除[J]. 化工学报, 2019, 70(8): 3078-3085.
[12]	焦坤灵, 赵阳国, 武文斐, 王振峰, 龚志军. SO₂对稀土精矿催化剂NH₃-SCR脱硝催化性能的影响[J]. 化工学报, 2019, 70(12): 4645-4653.
[13]	朱丽, 邓芸, 宋宇鹏, 王月娟, 鲁继青, 罗孟飞. MnO_x对Pt/CeZrO₂催化剂在水汽和CO₂环境下CO氧化的影响[J]. 化工学报, 2018, 69(4): 1484-1492.
[14]	张文静, 吴烨, 蔡天意, 刘道银, 马吉亮, 梁财, 陈晓平. 胺基CO₂固体吸附剂脱碳特性及SO₂的影响[J]. 化工学报, 2018, 69(4): 1586-1594.
[15]	刘慧, 张林, 杨晓晰, 李东刚. 缝式低NO_x燃烧器结构的优化模拟[J]. 化工学报, 2018, 69(4): 1723-1730.

燃煤电厂真实烟气条件下SCR催化剂脱硝性能

DeNOx performance of SCR catalyst for exhaust gas from coal-fired power plant

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 16

相关文章 15

编辑推荐

Metrics

本文评价

DeNO_x performance of SCR catalyst for exhaust gas from coal-fired power plant