硫铝酸钙的氧化铝溶出性能

doi:10.11949/j.issn.0438-1157.20160452

化工学报 ›› 2017, Vol. 68 ›› Issue (1): 460-466.DOI: 10.11949/j.issn.0438-1157.20160452

• 材料化学工程与纳米技术 • 上一篇下一篇

硫铝酸钙的氧化铝溶出性能

楚维钦, 张学政, 马东东, 孙会兰, 王波

河北科技大学材料科学与工程学院, 河北省材料近净成形技术重点实验室, 河北石家庄 050018

收稿日期:2016-04-07 修回日期:2016-10-22 出版日期:2017-01-05 发布日期:2017-01-05
通讯作者: 王波
基金资助:
国家自然科学基金项目（51104053）；河北省自然科学基金项目（E2016208107）；河北省高等学校科学技术研究项目（BJ2016023，QN2015002）。

Alumina leaching properties of calcium sulphoaluminate

CHU Weiqin, ZHANG Xuezheng, MA Dongdong, SUN Huilan, WANG Bo

School of Material Science and Engineering, Hebei Key Laboratory of Material Near-Net Forming Technology, Hebei University of Science and Technology, Shijiazhuang 050018, Hebei, China

Received:2016-04-07 Revised:2016-10-22 Online:2017-01-05 Published:2017-01-05
Contact: 10.11949/j.issn.0438-1157.20160452
Supported by:
supported by the National Natural Science Foundation of China (51104053), the Natural Science Foundation of Hebei Province (E2016208107) and the Science Foundation of University of Hebei Province (BJ2016023, QN2015002).

摘要/Abstract

摘要：

使用分析纯CaCO₃、Al₂O₃与CaSO₄·2H₂O配料，在1375℃、保温2 h的条件下合成了纯物相硫铝酸钙3CaO·3Al₂O₃·CaSO₄（C₄A₃S），对其物相组成和微观形貌进行了表征。并探究了碳碱浓度、苛碱浓度、溶出温度、溶出时间、粒度等因素对C₄A₃S氧化铝溶出性能的影响。结果表明：C₄A₃S的氧化铝溶出性能随着碳碱与苛碱浓度的增加先提高，之后趋于稳定。粒度越小，溶出率越高。与七铝酸十二钙12CaO·7Al₂O₃（C₁₂A₇）相比，C₄A₃S的孔洞状结构使其氧化铝更易溶出，在10 min时氧化铝溶出率即达到98%以上，且溶出所需的碳碱浓度与溶出温度均低于C₁₂A₇。在最佳条件：碳碱80 g·L^-1、苛碱10 g·L^-1、溶出温度80℃、溶出时间10 min下，C₄A₃S的氧化铝溶出率为98.76%。

关键词: 硫铝酸钙, 氧化铝, 溶出, 高硫铝土矿

Abstract:

Analytically pure carbonate calcium, alumina and dihydrate calcium sulfate were used to synthesize calcium sulphoaluminate(3CaO·3Al₂O₃·CaSO₄, C₄A₃S) at 1375℃ for 2 h.The phase compositions and microstructure were characterized.The effects of carbon alkali concentration, alkali concentration, leaching temperature, leaching time and particle sizes on the alumina leaching properties of C₄A₃S were explored.The results show that the alumina leaching ratio of C₄A₃S increases with the increase of concentration of sodium carbonate and alkali, then trends to stable.The leaching ratio becomes higher when the particle size of clinker decreases.Compared with 12CaO·7Al₂O₃(C₁₂A₇), the alumina of C₄A₃S is easier to be dissolved because of its porous structure, and the alumina leaching ratio is up to 98% under 10 min leaching.The concentration of sodium carbonate and the dissolution temperature of C₄A₃S is lower than that of C₁₂A₇.The alumina leaching ratio of C₄A₃S could reach 98.76% under the optimum conditions:sodium carbonate 80 g·L^-1, alkali 10 g·L^-1, dissolution temperature 80℃ and dissolution time 10 min.

Key words: calcium sulphoaluminate, alumina, leaching, high-sulfur bauxite

中图分类号:

TF803.21

楚维钦, 张学政, 马东东, 孙会兰, 王波. 硫铝酸钙的氧化铝溶出性能[J]. 化工学报, 2017, 68(1): 460-466.

CHU Weiqin, ZHANG Xuezheng, MA Dongdong, SUN Huilan, WANG Bo. Alumina leaching properties of calcium sulphoaluminate[J]. CIESC Journal, 2017, 68(1): 460-466.

参考文献 21

[1]	张佰永, 姜跃华, 郭沈, 等. 中国铝土矿资源变化对世界氧化铝工业格局的影响[J]. 轻金属, 2014, (7):1-5. ZHANG B Y, JIANG Y H, GUO S, et al. The influence of bauxite resource change in China on layout of world alumina industry[J]. Light Metal, 2014, (7):1-5.
[2]	朱妍, 霍云波, 郭秋影. 氧化铝市场分析与展望[J]. 中国金属通报, 2013, (4):27-29. ZHU Y, HUO Y B, GUO Q Y. Analysis and prospect of alumina market[J]. China Metal Bulletin, 2013, (4):27-29.
[3]	顾松青. 我国的铝土矿资源和高效低耗的氧化铝生产技术[J]. 中国有色金属学报, 2004, 14(S1):91-97. GU S Q. Alumina production technology with high efficiency and low consumption from Chinese bauxite resource[J]. The Chinese Journal of Nonferrous Metals, 2004, 14(S1):91-97.
[4]	杨静, 蒋周青, 马鸿文, 等. 中国铝资源与高铝粉煤灰提取氧化铝研究进展[J]. 地学前缘, 2014, 21(5):313-324. YANG J, JIANG Z Q, MA H W, et al. The bauxite resource in China and advances in the techniques of extracting alumina from high-alumina coal fly ash[J]. Earth Science Frontiers, 2014, 21(5):313-324.
[5]	王祝堂. 浅析中国氧化铝工业技术发展方向[J]. 中国有色建设, 2013, (3):40-41. WANG Z T. Analysis on the development trend of Chinese alumina industry[J]. China Nonferrous Construction, 2013, (3):40-41.
[6]	李来时, 翟玉春, 秦晋国, 等. 以粉煤灰为原料制备高纯氧化铝[J]. 化工学报, 2006, 57(9):2189-2193. LI L S, ZHAI Y C, QIN J G, et al. Extracting high-purity alumina from fly ash[J]. Journal of Chemical Industry and Engineering(China), 2006, 57(9):2189-2193.
[7]	MOLDOVEANU G A, PAPANGELAKIS V G. Recovery of rare earth elements adsorbed on clay minerals(Ⅱ):Leaching with ammonium sulfate[J]. Hydrometallurgy, 2013, 131/132:158-166.
[8]	YAO Z T, XIA M S, SARKER P K, et al. A review of the alumina recovery from coal fly ash, with a focus in China[J]. Fuel, 2014, 120:74-85.
[9]	鲁桂林, 迟松江, 毕诗文. 赤泥中氧化铝和氧化铁的浸出[J]. 材料与冶金学报, 2010, 9(1):31-34. LU G L, CHI S J, BI S W. Leachiing of alumina and iron oxide from red mud[J]. Journal of Materals and Metallurgy, 2010, 9(1):31-34.
[10]	王佳东, 翟玉春, 申晓毅. 碱石灰烧结法从脱硅粉煤灰中提取氧化铝[J]. 轻金属, 2009, (6):14-16. WANG J D, ZHAI Y C, SHEN X Y. Extracting Al2O3 from desiliconized fly ash with alkali lime sintering process[J]. Light Metal, 2009, (6):14-16.
[11]	张佰永, 周凤禄. 粉煤灰石灰石烧结法生产氧化铝的机理探讨[J]. 轻金属, 2007, (6):17-18, 27. ZHANG B Y, ZHOU F L. The limestone sintering process to produce alumina with fly ash[J]. Light Metal, 2007, (6):17-18, 27.
[12]	李殷泰, 毕诗文, 段振瀛, 等. 关于广西贵港三水铝石型铝土矿综合利用工艺方案的探讨[J]. 轻金属, 1992, (9):6-14. LI Y T, BI S W, DUAN Z Y, et al. Discussion on the comprehensive process of gibbsite bauxite in Guangxi[J]. Light Metal, 1992, (9):6-14.
[13]	孙会兰, 涂赣峰, 毕诗文, 等. 七铝十二钙的合成及其在高碳钠铝酸钠溶液中的溶出性能[J]. 轻金属, 2007, (11):17-19. SUN H L, TU G F, BI S W, et al. Synthesizati on of C12A7 and its leaching property in sodium aluminate solution with high-Na2OC[J]. Light Metal, 2007, (11):17-19.
[14]	王波, 宗书凤, 孙会兰, 等. 钙铝比对11.3CaO·7Al2O3微观结构及其溶出性能的影响[J]. 化工学报, 2014, 65(10):4183-4190. WANG B, ZONG S F, SUN H L, et al. Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al2O3[J]. CIESC Journal, 2014, 65(10):4183-4190.
[15]	GOODBOY K P. Investigation of a sinter process for extraction of Al2O3 from coal wastes[J]. Metallurgical and Materials Transactions B, 1976, 7(4):716-718.
[16]	马素花, 沈晓冬, 黄叶平, 等. 无水硫铝酸钙的合成及形成机制[J]. 硅酸盐学报, 2008, 36(1):78-81. MA S H, SHEN X D, HUANG Y P, et al. Preparation and formation mechanism of calcium sulphoaluminate[J]. Journal of the Chinese Ceramic Society, 2008, 36(1):78-81.
[17]	杨天华, 李润东, 周俊虎, 等. 高温固硫物相硫铝酸钙生成反应热力学研究[J]. 热力发电, 2006, (6):6-9. YANG T H, LI R D, ZHOU J H, et al. Formation thermodynamics of high-temperature phase sulphoaluminate[J]. Thermal Power Generation, 2006, (6):6-9.
[18]	杨天华, 李润东, 周俊虎, 等. 高温固硫物相硫铝酸钙生成动力学[J]. 化工学报, 2006, 57(10):2327-2331. YANG T H, LI R D, ZHOU J H, et al. Formation kinetics of high-temperature phase sulphoaluminate[J]. Journal of Chemical Industry and Engineering(China), 2006, 57(10):2327-2331.
[19]	王丽, 李金洪, 杨静. 高温固硫物相硫铝酸钙在不同气氛下的动力学实验研究[J]. 矿物岩石, 2009, 29(3):23-28. WANG L, LI J H, YANG J. Study on the kinetics of high temperature solid phase calcium aluminate under different atmosphere[J]. Journal of Mineral and Petrology, 2009, 29(3):23-28.
[20]	于海燕, 王波, 潘晓林, 等. 12CaO·7Al2O3晶体结构及其氧化铝浸出性能[J]. 工程科学学报, 2015, 37(1):30-34. YU H Y, WANG B, PAN X L, et al. Crystal structure and Al2O3 leaching properties of 12CaO·7Al2O3[J]. Chinese Journal of Engineering, 2015, 37(1):30-34.
[21]	孙会兰, 于海燕, 王波, 等. 12CaO·7Al2O3溶出动力学[J]. 中国有色金属学报, 2008, 18(10):1920-1925. SUN H L, YU H Y, WANG B, et al. Leaching dynamics of 12CaO·7Al2O3[J]. The Chinese Journal of Nonferrous Metals, 2008, 18(10):1920-1925.

硫铝酸钙的氧化铝溶出性能

Alumina leaching properties of calcium sulphoaluminate

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 21

相关文章 15

编辑推荐

Metrics

本文评价

[1]	吴学红, 栾林林, 陈亚南, 赵敏, 吕财, 刘勇. 可降解柔性相变薄膜的制备及其热性能[J]. 化工学报, 2023, 74(4): 1818-1826.
[2]	何金峰, 李秀珍, 寇建耀, 陶庭杰, 余灿, 刘欢, 陈永元, 赵豪健, 江大好, 李小年. 乙醇制高级醇有序介孔氧化铝负载铜基催化剂研究[J]. 化工学报, 2023, 74(3): 1082-1091.
[3]	袁妮妮, 郭拓, 白红存, 何育荣, 袁永宁, 马晶晶, 郭庆杰. 化学链燃烧过程Fe₂O₃/Al₂O₃载氧体表面CH₄反应：ReaxFF-MD模拟[J]. 化工学报, 2022, 73(9): 4054-4061.
[4]	朱慧红, 茆志伟, 杨涛, 冯翔, 金浩, 彭冲, 杨朝合, 王继锋, 方向晨. 催化剂形貌对沸腾床渣油加氢Ni-Mo/Al₂O₃ 催化剂活性位的影响机制[J]. 化工学报, 2021, 72(4): 2076-2085.
[5]	魏强, 黄文斌, 周亚松. 硫氮化合物在磷改性NiW/Al₂O₃加氢催化剂上的吸附行为研究[J]. 化工学报, 2021, 72(3): 1372-1381.
[6]	李凡, 姜奥林, 杨浩林, 曾小军, 蒋利桥, 汪小憨. 氧化锆基涂层壁面改善火焰稳定性研究[J]. 化工学报, 2021, 72(11): 5883-5892.
[7]	刘华, 彭佳杰, 余凯, 倪毅, 王芳, 潘权稳, 葛天舒, 王如竹. 活性氧化铝基质新型复合吸附剂的制备和储热性能[J]. 化工学报, 2020, 71(7): 3354-3361.
[8]	靳红旺, 郑立刚, 朱小超, 于水军, 潘荣锟, 杜德朋, 窦增果. 竖直管道中氧化铝抑制铝粉爆炸特性研究[J]. 化工学报, 2020, 71(4): 1929-1939.
[9]	郭玉梅, 曹丽琼, 郭彦霞, 燕可洲. 煤矸石和赤泥协同提取氧化铝过程矿相转变研究[J]. 化工学报, 2019, 70(4): 1542-1549.
[10]	王耀武, 彭建平, 狄跃忠, 蒿鹏程. 铝电解槽干式防渗料在电解过程中的反应机理探讨[J]. 化工学报, 2019, 70(3): 1035-1041.
[11]	凌忠钱, 周超, 曾宪阳, 凌波, 钱炯杰. 多孔介质内低热值乙烯燃烧的污染物排放特性试验研究[J]. 化工学报, 2019, 70(11): 4346-4355.
[12]	金铭, 胡定华, 李强, 范德松. Al₂O₃纳米流体液滴蒸发特性的数值模拟研究[J]. 化工学报, 2019, 70(11): 4199-4206.
[13]	万艳春, 王玉军, 骆广生. 并流滴加法制备大孔容纤维状γ-氧化铝[J]. 化工学报, 2018, 69(11): 4840-4847.
[14]	赵国冰, 张琪, 程飞, 王天宇. Na改性Pt/AlOOH对甲醛催化氧化反应活性的影响[J]. 化工学报, 2018, 69(11): 4722-4727.
[15]	聂玉娟, 王二东, 王许云. 制备高纯超细氧化铝粉体新方法[J]. 化工学报, 2017, 68(9): 3616-3622.