液滴界面可控导入沉淀剂制备单分散均匀微球

李春林, 解华, 刘娜, 林柄承, 刘中民

中国科学院大连化学物理研究所, 辽宁大连 116023

收稿日期:2015-06-12 修回日期:2015-06-20 出版日期:2015-09-05 发布日期:2015-09-05
通讯作者: 刘中民
基金资助:
国家自然科学基金项目(21376233,21176233)。

Preparation of monodisper microsphere by controlled droplet solidification

LI Chunlin, XIE Hua, LIU Na, LIN Bingcheng, LIU Zhongmin

Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, Liaoning, China

Received:2015-06-12 Revised:2015-06-20 Online:2015-09-05 Published:2015-09-05
Supported by:
supported by the National Natural Science Foundation of China (21376233, 21176233).

摘要/Abstract

摘要：

均一尺寸微米功能材料在诸如高分子化学、医药化工、催化以及高效分离等领域都受到普遍关注。现有常规方法很难满足制备单分散、均一性的微米材料的要求。采用微流控技术,在微流控芯片内先生成液滴,然后再在线固化液滴的方法,制备了各种单分散、尺寸均一的微球。通过液滴界面受控导入沉淀剂到液滴中,当所含溶质为固化慢的硅溶胶时,生成实心微球,制备得到表面积达572 m²·g^-1、直径变异系数约为2%的纳米孔道二氧化硅微球;当液滴内含沉淀固化较快的溶质,如Zn、Fe、Cu,则可形成水合氧化物或者混合氧化物空心球微球;当含快沉淀也含慢速固化物质时,如含可溶性Fe的硅溶胶时,通过调控沉淀剂进入液滴的速度,也成功了制备了Fe均匀分散在氧化硅内的混合氧化物微球。

关键词: 介尺度, 界面, 制备, 微流控, 液滴, 微球, 单分散

Abstract:

Uniform size micromeres functional material gets a lot of attention in the fields of polymer chemistry, medicine and chemical industry, catalysis and separation. It is incovenient to prepare monodisperse and uniformity micrometer material by current conventional technology. With microfluidic technology, the droplet was generated in the chip and following to solidify the droplet online to prepare various of monodisperse and size uniformity microsphere. Since the droplet was a Si sol of slow-solidified, the nonporous SiO₂ microsphere with a BET surface area of 572 m²·g^-1 and a variance coefficient of microsphere diameters of about 2% were produced by introducing precipitator from the interface of droplet. Because the droplets were a material of fast-precipited, such as Zn, Fe, or Cu ion, a hollow microsphere consisted of hydrate oxide or mixed oxide was produced. As the droplet contains both materials of fast-precipitated and flow-solidified, such as Si sol containing of Fe ion, SiO₂ microsphere with a homogeneous dispersed Fe in it was obtained by adjusting the introducing velocity of precipitator into the droplet.

Key words: mesoscale, interface, preparation, microfluidic, droplet, microsphere, monodisperse

中图分类号:

TQ028.8

李春林, 解华, 刘娜, 林柄承, 刘中民. 液滴界面可控导入沉淀剂制备单分散均匀微球[J]. 化工学报, 2015, 66(9): 3654-3660.

LI Chunlin, XIE Hua, LIU Na, LIN Bingcheng, LIU Zhongmin. Preparation of monodisper microsphere by controlled droplet solidification[J]. CIESC Journal, 2015, 66(9): 3654-3660.

参考文献 20

[1]	Bai C L, Liu M H. From chemistry to nanoscience: not just a matter of size [J]. Angewandte Chemie-International Edition, 2013, 52: 2678-2683.
[2]	Zhao Y C, Chen G W, Ye C B, Yuan Q. Gas-liquid two-phase flow in microchannel at elevated pressure [J]. Chemical Engineering Science, 2013, 87: 122-132.
[3]	Garstecki P, Stone H A, Whitesides G M. Mechanism for flow-rate controlled breakup in confined geometries: a route to monodisperse emulsions [J]. Physical Review Letters, 2005, 94: 164501-164504.
[4]	Lee I, Yoo Y, Cheng Z, Jeong H-K. Generation of monodisperse mesoporous silica microspheres with controllable size and surface morphology in a microfluidic device [J]. Advanced Functional Materials, 2008, 18: 4014-4021.
[5]	Luo Guangsheng (骆广生),Wang Kai (王凯),Wang Peijian (王佩坚), Lü Yangchen (吕阳成). Advances in polymer synthesis in microreactors [J]. CIESC Journal (化工学报), 2014, 65: 2563-2574.
[6]	Wang Wei (汪伟),Xie Rui (谢锐), Ju Xiaojie (巨晓洁),Chu Liangyin (褚良银).Recent progress of microfluidic fabrication of novel functional microparticles [J]. CIESC Journal (化工学报), 2014, 65: 2555-2562.
[7]	Zhang Yan (张艳),Lei Jiandu (雷建都), Lin Hai (林海),Ge Liyuan (耿立媛),Su Haijia (苏海佳),Ma Guanhui (马光辉),Su Zhiguo (苏志国). Progress in preparation of microspheres using microfluidic devices [J]. The Chinese Journal of Process Engineering (过程工程学报), 2009, 9: 1028-1034.
[8]	Li D, Guan Z, Zhang W, Zhou X, Zhang W Y, Zhuang Z, Wang X, Yang C J. Synthesis of uniform-size hollow silica microspheres through interfacial polymerization in monodisperse water-in-oil droplets [J]. Acs Applied Materials & Interfaces, 2010, 2:2711-2714.
[9]	Yano K, Fukushima Y. Particle size control of mono-dispersed super-microporous silica spheres [J]. Journal of Materials Chemistry, 2003, 13:2577-2581.
[10]	Wan J, Stone H A. Coated gas bubbles for the continuous synthesis of hollow inorganic particles [J]. Langmuir, 2012, 28:37-41.
[11]	Jeong W C, Choi M, Lim C H, Yang S M. Microfluidic synthesis of atto-liter scale double emulsions toward ultrafine hollow silica spheres with hierarchical pore networks [J]. Lab on a Chip, 2012, 12: 5262-5271.
[12]	Wang Peng (王澎),Chen Bin (陈斌). Numerical simulation of micro-droplet breakup in T-shaped micro-fluidic chip [J].CIESC Journal (化工学报), 2012, 63:999-1003.
[13]	Liu Y, Ju M H, Wang C Q, Zhang L X, Liu X Q. Preparation of monodisperse mesoporous carbon microspheres from poly(furfuryl alcohol)-silica composite microspheres produced in a microfluidic device [J]. Journal of Materials Chemistry, 2011, 21: 15049-15056.
[14]	Pan Y C, Ju M H, Wang C Q, Zhang L X, Xu N P. Versatile preparation of monodisperse poly (furfuryl alcohol) and carbon hollow spheres in a simple microfluidic device [J]. Chemical Communications, 2010, 46: 3732-3734.
[15]	Wang J T, Wang J, Han J J. Fabrication of advanced particles and particle-based materials assisted by droplet-based microfluidics [J]. Small, 2011, 7:1728-1754.
[16]	Panizza P, Engl W, Hany C, Backov R. Controlled production of hierarchically organized large emulsions and particles using assemblies on line of co-axial flow devices [J]. Colloids and Surfaces A-Physicochemical and Engineering Aspects, 2008, 312: 24-31.
[17]	Carroll N J, Rathod S B, Derbins E, Mendez S, Weitz D A, Petsev D N. Droplet-based microfluidics for emulsion and solvent evaporation synthesis of monodisperse mesoporous silica microspheres [J]. Langmuir, 2008, 24: 658-661.
[18]	Chokkalingam V, Weidenhof B, Kramer M, Maier W F, Herminghaus S, Seemann R. Optimized droplet-based microfluidics scheme for sol-gel reactions [J]. Lab on a Chip, 2010, 10:1700-1705.
[19]	Chen Y, Wang Y J, Yang L A, Luo G S. Micrometer-sized monodispersed silica spheres with advanced adsorption properties [J]. AIChE Journal, 2008, 54: 298-309.
[20]	Ma Jingyun (马静云), Jiang Lei (姜雷), Qin Jianhua (秦建华). Synthesis of hollow titania microspheres by using microfluidic droplet-template [J]. Chinese Journal of Chromatography (色谱), 2011, 29: 890-895.

液滴界面可控导入沉淀剂制备单分散均匀微球

Preparation of monodisper microsphere by controlled droplet solidification

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 20

相关文章 15

编辑推荐

Metrics

本文评价

[1]	吴馨, 龚建英, 靳龙, 王宇涛, 黄睿宁. 超声波激励下铝板表面液滴群输运特性的研究[J]. 化工学报, 2023, 74(S1): 104-112.
[2]	周晓庆, 李春煜, 杨光, 蔡爱峰, 吴静怡. 液滴撞击不同曲率过冷波纹面结冰动力学行为及机理研究[J]. 化工学报, 2023, 74(S1): 141-153.
[3]	毕丽森, 刘斌, 胡恒祥, 曾涛, 李卓睿, 宋健飞, 吴翰铭. 粗糙界面上纳米液滴蒸发模式的分子动力学研究[J]. 化工学报, 2023, 74(S1): 172-178.
[4]	陆俊凤, 孙怀宇, 王艳磊, 何宏艳. 离子液体界面极化及其调控氢键性质的分子机理[J]. 化工学报, 2023, 74(9): 3665-3680.
[5]	林典, 江国梅, 徐秀彬, 赵波, 刘冬梅, 吴旭. 硅基类液防原油黏附涂层的研制及其减阻性能研究[J]. 化工学报, 2023, 74(8): 3438-3445.
[6]	傅予, 刘兴翀, 王瀚雨, 李海敏, 倪亚飞, 邹文静, 雷月, 彭永姗. F₃EACl修饰层对钙钛矿太阳能电池性能提升的研究[J]. 化工学报, 2023, 74(8): 3554-3563.
[7]	吴文涛, 褚良永, 张玲洁, 谭伟民, 沈丽明, 暴宁钟. 腰果酚生物基自愈合微胶囊的高效制备工艺研究[J]. 化工学报, 2023, 74(7): 3103-3115.
[8]	王志龙, 杨烨, 赵真真, 田涛, 赵桐, 崔亚辉. 搅拌时间和混合顺序对锂离子电池正极浆料分散特性的影响[J]. 化工学报, 2023, 74(7): 3127-3138.
[9]	何宣志, 何永清, 闻桂叶, 焦凤. 磁液液滴颈部自相似破裂行为[J]. 化工学报, 2023, 74(7): 2889-2897.
[10]	张贲, 王松柏, 魏子亚, 郝婷婷, 马学虎, 温荣福. 超亲水多孔金属结构驱动的毛细液膜冷凝及传热强化[J]. 化工学报, 2023, 74(7): 2824-2835.
[11]	朱风, 陈凯琳, 黄小凤, 鲍银珠, 李文斌, 刘嘉鑫, 吴玮强, 高王伟. KOH改性电石渣脱除羰基硫的性能研究[J]. 化工学报, 2023, 74(6): 2668-2679.
[12]	李正涛, 袁志杰, 贺高红, 姜晓滨. 疏水界面上的NaCl液滴蒸发过程内环流调控机制研究[J]. 化工学报, 2023, 74(5): 1904-1913.
[13]	尹驰, 张正国, 凌子夜, 方晓明. 含石蜡@二氧化硅纳米胶囊和碳纤维的相变热界面材料及其散热性能[J]. 化工学报, 2023, 74(4): 1795-1804.
[14]	邓璐, 巨晓洁, 张文杰, 谢锐, 汪伟, 刘壮, 潘大伟, 褚良银. 微流控法可控制备放射性壳聚糖栓塞微球[J]. 化工学报, 2023, 74(4): 1781-1794.
[15]	贾露凡, 王艺颖, 董钰漫, 李沁园, 谢鑫, 苑昊, 孟涛. 微流控双水相贴壁液滴流动强化酶促反应研究[J]. 化工学报, 2023, 74(3): 1239-1246.