铁掺杂二氧化钛空心球的制备及性能

doi:10.11949/j.issn.0438-1157.20160443

摘要/Abstract

摘要：

以TiF₄为钛源、九水合硝酸铁为掺杂前体，采用水热法制备铁掺杂的TiO₂空心微球。采用SEM、TEM、XRD、BET、XPS等技术对样品的形貌、结构、晶型、比表面积、元素组成等进行表征，以亚甲基蓝（MB）的光催化降解为目标反应，评价其光催化活性。结果表明，160℃下水热反应生成的纳米TiO₂空心微球晶型为锐钛矿，少量掺铁并不影响微球的形貌及晶体结构。光催化实验表明，160℃下水热反应12 h生成的TiO₂空心微球样品均匀性好、光催化活性最佳；铁掺杂能显著提高TiO₂空心微球的催化活性，当铁钛比为1.5:100时，所得样品粒径最小，比表面积最大，光催化活性最高。

关键词: 氟化钛, 二氧化钛, 水热法, 铁掺杂, 光催化, 空心微球

Abstract:

Iron-doped titanium dioxide hollow microspheres were prepared hydrothermally using titanium tetrafluoride and ferric nitrate nonahydrate in aqueous solution as starting materials, and were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), surface area (BET) and X-ray photoelectron spectroscopy (XPS). Photocatalytic activity of the microspheres was evaluated on photocatalytic degradation of aqueous methylene blue (MB). TiO₂ in hollow microspheres created at 160℃ were anatase crystal and doping a relatively small amount of iron did not alter morphology and crystal structure of TiO₂. Iron doping could significantly improve the photocatalytic activity of TiO₂ hollow microspheres. The TiO₂ hollow microspheres obtained at a condition of 160℃ for 12 h had optimal dimensional uniformity and photocatalytic activity, which the best photocatalytic effect were observed on hollow microspheres with a 1.5% ratio of iron over titanium because of the smallest size and the highest surface area.

Key words: TiF₄, TiO₂, hydrothermal method, iron doping, photocatalytic, hollow microspheres

中图分类号:

TQ032

李雅泊, 郑玉婴, 刘阳龙. 铁掺杂二氧化钛空心球的制备及性能[J]. 化工学报, 2016, 67(10): 4493-4499.

LI Yabo, ZHENG Yuying, LIU Yanglong. Preparation and properties of iron doped TiO₂ hollow microspheres[J]. CIESC Journal, 2016, 67(10): 4493-4499.

参考文献 34

[1]	ZHANG Q H, FAN W G, GAO L. Anatase TiO2 nanoparticles immobilized on ZnO tetrapods as a highly efficient and easily recyclable photocatalyst[J]. Applied Catalysis B:Environmental, 2007, 76(12):168-173.
[2]	陈建新, 张娜, 李银辉, 等. 氮掺杂TiO2/壳聚糖复合膜吸附和光降解染料[J]. 化工学报, 2015, 66(9):3746-3752. CHEN J X, ZHANG N, LI Y H, et al. Adsorption and photocatalytic degradation of dye by N-doped TiO2/chitosan composited films[J]. CIESC Journal, 2015, 66(9):3746-3752.
[3]	ZHAO D L, SHENG G D, CHEN C L, et al. Enhanced photocatalytic degradation of methylene blue under visible irradiation on graphene@TiO2 dyade structure[J]. Applied Catalysis B:Environmental, 2012, 111/112:303-308.
[4]	LIAO Y C, XIE C S, LIU Y, et al, Comparison on photocatalytic degradation of gaseous formaldehyde by TiO2, ZnO and their composite[J]. Ceramics International, 2012, 6(38):4437-4444.
[5]	SUN B, VORONTSOV A V, SMIRNIOTIS P G. Role of platinum deposited on TiO2 in phenol photocatalytic oxidation[J]. Langmuir, 2003, 19(8):3151-3156.
[6]	MONA S, ABDEL M. Titanium dioxide nanomaterial doped with trivalent lanthanide ions of Tb, Eu and Sm:preparation, characterization and potential applications[J]. Inorganica Chimica Acta, 2007, 360(9):2863-2874.
[7]	KARTHIK K, VICTOR J N. High pressure electrical resistivity studies on Ni-doped TiO2 nanoparticles[J]. Journal of Alloys and Compounds, 2011, 509(16):5173-5176.
[8]	AO Y H, XU J J, FU D G, et al. A simple method to prepare N-doped titania hollow spheres with high photocatalytic activity under visible light[J]. Journal of Hazardous Materials, 2009, 167:413-417.
[9]	WEI F Y, ZENG H L, SHI L, et al. Effect of sulphur and iron co-doping on photocatalytic activity of titanium dioxide[J]. Journal of the Chinese Ceramic Society, 2008, 36(9):1272-1276.
[10]	RANJIT K T, WILLNER I, BOSSMANN S H, et al. Lanthanide oxide doped titanium dioxide photocatalysts:effective photocatalysts for the enhanced degradation of salicylic acid and t-cinnamic acid[J]. Journal of Catalysis, 2001, 204(2):305-310.
[11]	BAE E, CHOI W. Highly enhanced photoreductive degradation of perchlorinated compounds on dye-sensitized metal/TiO2 under visible light[J]. Environmental Science and Technology, 2003, 37(1):147-152.
[12]	杨秋文, 刘素琴, 黄可龙, 等. Fe(Ⅲ)掺杂介孔TiO2的溶剂热法合成与表征[J]. 湘潭大学自然科学学报, 2009, 31(1):71-76. YANG Q W, LIU S Q, HUANG K L, et al. Solvothermal fabrication and characterization of iron doped mesoporous TiO2[J]. Natural Science Journal of Xiangtan University, 2009, 31(1):71-76.
[13]	高远, 徐安武, 刘汉钦. 掺铁TiO2用于NO2-光催化降解研究[J]. 中山大学学报, 2000, 30(5):1-5. GAO Y, XU A W, LIU H Q. The photocatalysis of iron doped TiO2 used in the degradation of NO2-[J]. Acta Scientiarum Naturalium Universitatis Sunyatseni, 2000, 30(5):1-5.
[14]	LI W Q, LIU X, LI H X. Hydrothermal synthesis of graphene/Fe3+-doped TiO2 nanowire composites with highly enhanced photocatalytic activity under visible light irradiation[J]. Journal of Materials Chemistry A, 2015, 3:15214-15223.
[15]	LI G C, ZHANG Z K. Preparation and characterization of hollow titania microspheres[J]. Journal of Functional Materials Contents, 2004, 35(1):2786-2791.
[16]	SYOUFIAN A, NAKASHIMA K. Degradation of methylene blue in aqueous dispersion of hollow titania photocatalyst:optimization of reaction by peroxydisulfate electron scavenger[J]. Journal of Colloid and Interface Science, 2007, 313(1):213-218.
[17]	LIANG Y C, WANG C C, KEI C C, et al. Photocatalysis of Ag-loaded TiO2 nanotube arrays formed by atomic layer deposition[J]. The Journal of Physical Chemistry C, 2011, 115(19):9498-9502.
[18]	钟永辉, 周琪, 刘家琴, 等. 氟化改性TiO2空心微球的制备及光催化性能[J].无机化学学报, 2013, 29(10):2133-2139. ZHONG Y H, ZHOU Q, LIU J Q, et al. Preparation of fluorizated TiO2 hollow microspheres and their photocatalytic activity[J]. Chinese Journal of Inorganic Chemistry, 2013, 29(10):2133-2139.
[19]	XU J J, AO Y H, CHEN M D. Preparation of B-doped titania hollow sphere and its photocatalytic activity under visible light[J]. Materials Letters, 2009, 28(63):2442-2444.
[20]	JAE H J, DONG H K, SUN J K, et al. Synthesis and photocatalytic property of a mixture of anatase and rutile TiO2 doped with Fe by mechanical alloying process[J]. Journal of Alloys and Compounds, 2008, 459:386-389.
[21]	LIN F, JIANG D M, LIN Y, et al. Magnetism of Fe-doped TiO2 milled in different milling atmospheres[J]. Physica B, 2008, 403:2193-2196.
[22]	YANG P, LU C, HUA N P, et al. Titanium dioxide nanoparticles co-doped with Fe3+ and Eu3+ ions for photocatalysis[J]. Materials Letters, 2002, 57(4):794-801.
[23]	TU Y F, HUANG S Y, SANG J P, et al. Preparation of Fe-doped TiO2 nanotube arrays and their photocatalytic activities under visible light[J]. Materials Research Bulletin, 2010, 45:224-229.
[24]	LI J, ZENG C H. Hollowing Sn-doped TiO2 nanospheres via Ostwald ripening[J]. American Chemical Society, 2007, 129(51):15839-15847.
[25]	YANG H G, ZENG H C. Preparation of hollow anatase TiO2 nanospheres via Ostwald ripening[J]. The Journal of Physical Chemistry B, 2004, 11(108):3492-3495.
[26]	REGINLDO S S, GUILHERME A F, CARLOS G, et al. Iron insertion and hematite segregation on Fe-doped TiO2 nanoparticles obtained from sol-gel and hydrothermal methods[J]. Applied Materials, 2012, 4:5555-5561.
[27]	DONG H K, HYUN S H, SUN J K, et al. Photocatalytic behaviors and structural characterization of nanocrystalline Fe-doped TiO2 synthesized by mechanical alloying[J]. Journal of Alloys and Compounds, 2004, 375:259-264.
[28]	NASRALLA N, YEGANEH M, ASTUTI Y, et al. Structural and spectroscopic study of Fe-doped TiO2 nanoparticles prepared by sol-gel method[J]. Scientia Iranica, 2013, 20:1018-1022.
[29]	MOHAMED S H, EIHAGARY M, ALTHOYAIB S. Growth of undoped and Fe doped TiO2 nanostructures and their optical and photocatalytic properties[J]. Applied Physics A, 2013, 111:1207-1212.
[30]	KITIROTE W, LAKSANA L, PONGTANAWAT K, et al. Calcination temperature effect on solvothermal Fe-TiO2 and its performance under visible light irradiation[J]. Journal of the Taiwan Institute of Chemical Engineers, 2010, 41:612-616.
[31]	VIJAYALASHMI K, JEREIL S D. Influence of Fe catalytic doping on the properties of TiO2 nanoparticles synthesized by microwave method[J]. Materials in Electronics, 2014, 25:5089-5094.
[32]	WU Q P, ZHENG Q, ROEL K. Creating oxygen vacancies as a novel strategy to form tetrahedrally coordinated Ti4+ in Fe/TiO2 nanoparticles[J]. The Journal of Physical Chemistry, 2012, 116:7219-7226.
[33]	ZOLTAN A, NANDOR B, TUNDE A. Synthesis, structure and photocatalytic properties of Fe(Ⅲ)-doped TiO2 prepared from TiCl3[J]. Applied Catalysis B:Environmental, 2008, 81:27-37.
[34]	ZHU J, REN J, HUO Y N, et al. Nanocrystalline Fe/TiO2 visible photocatalyst with a mesoporous structure prepared via a nonhydrolytic sol-gel route[J]. The Journal of Chemical Physics, 2007, 111:18965-18969.