基于石墨烯纳米材料的水质Cr(Ⅵ)电化学传感器

doi:10.11949/j.issn.0438-1157.20170587

化工学报 ›› 2017, Vol. 68 ›› Issue (12): 4816-4823.DOI: 10.11949/j.issn.0438-1157.20170587

• 材料化学工程与纳米技术 • 上一篇下一篇

基于石墨烯纳米材料的水质Cr(Ⅵ)电化学传感器

李玥琪¹, 胡敬芳², 邹小平², 高国伟^1,2

1 北京信息科技大学自动化学院, 北京 100192;
2 北京信息科技大学传感器重点实验室, 北京 100101

收稿日期:2017-05-09 修回日期:2017-08-21 出版日期:2017-12-05 发布日期:2017-12-05
通讯作者: 胡敬芳
基金资助:
国家自然科学基金项目（9011610902）；北京市教育委员会科技专项基金项目（KM201611232021）。

Graphene nanomaterial based electrochemical sensor for Cr(Ⅵ) detection in water

LI Yueqi¹, HU Jingfang², ZOU Xiaoping², GAO Guowei^1,2

1 Detectation Technology & Autodevicement, Beijing Information Science & Technology University, Beijing 100192, China;
2 Key Laboratory of Sensor, Beijing Information Science & Technology University, Beijing 100101, China

Received:2017-05-09 Revised:2017-08-21 Online:2017-12-05 Published:2017-12-05
Supported by:
supported by the National Natural Science Foundation of China (9011610902) and the Science and Technology Project of Beijing Educational Committee (KM201611232021).

摘要/Abstract

摘要：

针对我国水质重金属六价铬（Cr（Ⅵ））污染问题突出，提出了一种基于石墨烯纳米材料的水质Cr（Ⅵ）电化学传感器。采用电化学方法还原氧化石墨烯，构建石墨烯纳米材料修饰金电极（rGO/Au）。采用扫描电子显微镜（SEM）和透射电子显微镜（TEM）技术表征了rGO/Au的表面形貌和结构；采用方波伏安法、循环伏安法和线性扫描伏安法等电化学方法研究了Cr（Ⅵ）在rGO/Au表面的直接电催化还原行为，优化了氧化石墨烯的电化学还原电位和还原时间，以及支持电解质pH、浓度和检测电位等实验参数；采用计时电流法，在无须预富集的条件下，考察了Cr（Ⅵ）浓度与rGO/Au响应电流之间的线性关系。实验结果表明，石墨烯纳米材料对Cr（Ⅵ）有明显的电催化还原活性，计时电流响应值与Cr（Ⅵ）浓度呈良好的线性关系，线性范围为5～2000μg·L^-1，最低检测限为0.5 μA·L^-1（S/N≥3）。所制备的rGO/Au具有对常见其他重金属干扰离子（Cr（Ⅲ）、Ni（Ⅱ）、Cu（Ⅱ）、Mg（Ⅱ）和Mn（Ⅱ））较好的抗干扰性能，11次连续测定后，响应值相对初始值下降幅度小于10%，表明该修饰电极具有较好的稳定性。本研究提出的电化学传感器具有检测方法简单、快速、环保以及可重复使用的优点，能够应用于水质重金属Cr（Ⅵ）的快速测定。

关键词: 石墨烯, 纳米材料, 重金属Cr(Ⅵ), 电催化还原, 电化学, 传感器

Abstract:

The heavy metal ion pollution of hexavalent chromium (Cr(Ⅵ)) in water is serious in China. An electrochemical sensor for hexavalent chromium (Cr(Ⅵ)) detection is proposed based on graphene nanomaterial. The graphene nanomaterial modified gold electrode (rGO/Au) was prepared by using the method of electrochemical reduction of graphene oxide (GO). The surface morphology and structure of rGO/Au were characterized by scanning electron microscope (SEM) and transmission electron microscope (TEM) technologies. The direct electrocatalytic reduction of Cr(Ⅵ) on the surface of rGO/Au was studied by using electrochemical methods such as square wave voltammetry (SWV), cyclic voltammetry (CV) and linear sweep voltammetry (LSV), etc. The preparation conditions were optimized which include GO reduction potential and reduction time, as well as the detection parameters, such as detection potential, pH and concentration of electrolyte. Without preconcentration step, the linear relationship between Cr(Ⅵ) concentrations and current responses on the rGO/Au was investigated by using amperometry method. The experimental results showed that graphene nanomaterial has electrocatalytic activity for Cr(Ⅵ) reduction. A good linear relationship between Cr(Ⅵ) concentrations and current responses was obtained from 5 to 2000 μg·L^-1, with a low detection limit of 0.5 μg·L^-1 (S/N ≥ 3). The modified electrode was resistant to some common metal interference ions, such as Cr(Ⅲ), Ni(Ⅱ), Cu(Ⅱ), Mg(Ⅱ) and Mn(Ⅱ). And the response current decreased less than 10% compared to the initial value after 11 successive measures, which showed a relative good stability. The advantages of the proposed electrochemical sensor are simple, fast, friendly environmental and reusable, which made it possible to apply the sensor for rapid detection of Cr(Ⅵ) in water.

Key words: graphene, nanomaterial, heavy metal ion Cr(Ⅵ), electrocatalytic reduction, electrochemistry, sensor

中图分类号:

TP212.2

李玥琪, 胡敬芳, 邹小平, 高国伟. 基于石墨烯纳米材料的水质Cr(Ⅵ)电化学传感器[J]. 化工学报, 2017, 68(12): 4816-4823.

LI Yueqi, HU Jingfang, ZOU Xiaoping, GAO Guowei. Graphene nanomaterial based electrochemical sensor for Cr(Ⅵ) detection in water[J]. CIESC Journal, 2017, 68(12): 4816-4823.

参考文献 30

[1]	JIN W, ZHANG Z, WU G, et al. Integrated lignin-mediated adsorption-release process and electrochemical reduction for the removal of trace Cr(Ⅵ)[J]. RSC Advances, 2014, 4(53):27843-27849.
[2]	COSTA M. Potential hazards of hexavalent chromate in our drinking water.[J]. Toxicology & Applied Pharmacology, 2003, 188(1):1-5.
[3]	ORGANIZATION W H. Guidelines for drinking-water quality. Vol1, Recommendations:addendum[J]. Guidelines for Drinking-water Quality, 2006, 38(3):104-108.
[4]	康新平, 刘洪海, 陈坚. 液体样品中铬的价态和微量分析方法的研究进展[J]. 理化检验(化学分册), 1999, 35(3):139-142. KANG X P, LIU H H, CHEN J. On the valency and progress of analytical method of chromium in water solution[J].PTCA(PART B:Chemical Analysis), 1999, 35(3):139-142.
[5]	KREUZ B. Separation and determination of Cr(Ⅲ) and Cr(Ⅵ) with cation-exchange chromatography and atomic absorption spectroscopy. An experiment for quantitative methods of analysis[J]. Journal of Chemical Education, 2005, 82(3):435-438.
[6]	WILLIAMS T, JONES P, EBDON L. Simultaneous determination of Cr(Ⅲ) and Cr(Ⅵ) at ultratrace levels using ion chromatography with chemiluminescence detection[J]. Journal of Chromatography A, 1989, 482(2):361-366.
[7]	WANG L, XIA T, LIU J, et al. Preparation and application of a novel core/shell organic nanoparticle as a fluorescence probe in the selective determination of Cr(Ⅵ)[J]. Spectrochimica Acta Part A Molecular &Biomolecular Spectroscopy, 2005, 62(1/2/3):565-569.
[8]	LEVITSKAIA T G, O'HAR M J, SINKOV S I, et al. Direct spectrophotometric analysis of Cr(Ⅵ) using a liquid waveguide capillary cell[J]. Applied Spectroscopy, 2008, 62(1):107.
[9]	AND S M B, BRODBELT J S, MARCHAND A P, et al. Evaluation of binding selectivities of caged crown ligands toward heavy metals by electrospray ionization/quadrupole ion trap mass spectrometry[J]. Analytical Chemistry, 2000, 72(11):2433-2445.
[10]	BARD A J, FAULKNER L R. Electrochemical Methods:Fundamentals and Applications[M]. Wiley, 1980.
[11]	WANG J, BIAN C, TONG J, et al. Microsensor chip integrated with gold nanoparticles-modified ultramicroelectrode array for improved electroanalytical measurement of copper ions[J]. Electroanalysis, 2013, 25(7):1713-1721.
[12]	LI J, ZHANG J, WEI H, et al. Combining chemical reduction with an electrochemical technique for the simultaneous detection of Cr(Ⅵ), Pb(Ⅱ) and Cd(Ⅱ)[J]. Analyst, 2009, 134(2):273-277.
[13]	JIN W, WU G, CHEN A. Sensitive and selective electrochemical detection of chromium (Ⅵ) based on gold nanoparticle-decorated titania nanotube arrays[J]. Analyst, 2014, 139(1):235-241.
[14]	LIN L, LAWRENCE N S, THONGNGAMDEE S, et al. Catalytic adsorptive stripping determination of trace chromium (Ⅵ) at the bismuth film electrode[J]. Talanta, 2005, 65(1):144-148.
[15]	SVANCARA I, FORET P, VYTRAS K. A study on the determination of chromium as chromate at a carbon paste electrode modified with surfactants[J]. Talanta, 2004, 64(4):844.
[16]	MISCORIA S A, JACQ C, MAEDER T, et al. Screen-printed electrodes for electroanalytical sensing, of chromium Ⅵ in strong acid media[J]. Sensors & Actuators B Chemical, 2014, 195(5):294-302.
[17]	CARRINGTON N A, YONG L, XUE Z L. Electrochemical deposition of sol-gel films for enhanced chromium (Ⅵ) determination in aqueous solutions[J]. Analytica Chimica Acta, 2006, 572(1):17-24.
[18]	KACHOOSANGI R T, COMPTON R G. Voltammetric determination of chromium (Ⅵ) using a gold film modified carbon composite electrode[J]. Sensors & Actuators B Chemical, 2013, 178(178):555-562.
[19]	HE X, ZHENG Q L, PING Y, et al. Electrochemical synthesis of silver nanoparticles-coated gold nanoporous film electrode and its application to amperometric detection for trace Cr(Ⅵ)[J]. Science China:Chemistry, 2011, 54(6):1004-1010.
[20]	YANG Y, DIAO M, GAO M, et al. Facile preparation of graphene/polyaniline composite and its application for electrocatalysis hexavalent chromium reduction[J]. Electrochimica Acta, 2014, 132(19):496-503.
[21]	SANTHOSH C, SARANYA M, RAMACHANDRAN R, et al. Graphene/gold nanocomposites-based thin films as an enhanced sensing platform for voltammetric detection of Cr(Ⅵ) ions[J]. Journal of Nanotechnology, 2014, DOI:org/10.1155/2014/304526.
[22]	NOVOSELOV K S, JIANG D, SCHEDIN F, et al. Two-dimensional atomic crystals[J]. Proceedings of the National Academy of Sciences of the United States of America, 2005, 102(30):10451-10453.
[23]	CHARRIER A, COATI A, ARGUNOVA T, et al. Solid-state decomposition of silicon carbide for growing ultra-thin heteroepitaxial graphite films[J]. Journal of Applied Physics, 2002, 92(5):2479.
[24]	LI X, CAI W, AN J, et al. Large-area synthesis of high-quality and uniform graphene films on copper foils[J]. Science, 2009, 324(5932):1312.
[25]	EIGLER S, ENZELBERGERHEIM M, GRIMM S, et al. Wet chemical synthesis of graphene[J]. Advanced Materials, 2013, 25(26):3583-3587.
[26]	DENG S, LEI J, CHENG L, et al. Amplified electrochemiluminescence of quantum dots by electrochemically reduced graphene oxide for nanobiosensing of acetylcholine[J]. Biosensors & Bioelectronics, 2011, 26(11):4552-4558.
[27]	GUO H L, WANG X F, QIAN Q Y, et al. A green approach to the synthesis of graphene nanosheets.[J]. ACS Nano, 2009, 3(9):2653-2659.
[28]	CHEN K, CHEN L, CHEN Y, et al. Three-dimensional porous graphene-based composite materials:electrochemical synthesis and application[J]. Journal of Materials Chemistry, 2012, 22(39):20968-20976.
[29]	WELCH C M, NEKRASSOVA O, COMPTON R G. Reduction of hexavalent chromium at solid electrodes in acidic media:reaction mechanism and analytical applications[J]. Talanta, 2005, 65(1):74-80.
[30]	HALLAM P M, KAMPOUTIS D K, KADARA R O, et al. Graphite screen printed electrodes for the electrochemical sensing of chromium(Ⅵ)[J]. Analyst, 2010, 135(8):1947.

基于石墨烯纳米材料的水质Cr(Ⅵ)电化学传感器

Graphene nanomaterial based electrochemical sensor for Cr(Ⅵ) detection in water

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 30

相关文章 15

编辑推荐

Metrics

本文评价

[1]	刘远超, 关斌, 钟建斌, 徐一帆, 蒋旭浩, 李耑. 单层XSe₂（X=Zr/Hf）的热电输运特性研究[J]. 化工学报, 2023, 74(9): 3968-3978.
[2]	程业品, 胡达清, 徐奕莎, 刘华彦, 卢晗锋, 崔国凯. 离子液体基低共熔溶剂在转化CO₂中的应用[J]. 化工学报, 2023, 74(9): 3640-3653.
[3]	胡亚丽, 胡军勇, 马素霞, 孙禹坤, 谭学诣, 黄佳欣, 杨奉源. 逆电渗析热机新型工质开发及电化学特性研究[J]. 化工学报, 2023, 74(8): 3513-3521.
[4]	陈佳起, 赵万玉, 姚睿充, 侯道林, 董社英. 开心果壳基碳点的合成及其对Q235碳钢的缓蚀行为研究[J]. 化工学报, 2023, 74(8): 3446-3456.
[5]	张蒙蒙, 颜冬, 沈永峰, 李文翠. 电解液类型对双离子电池阴阳离子储存行为的影响[J]. 化工学报, 2023, 74(7): 3116-3126.
[6]	邢美波, 张中天, 景栋梁, 张洪发. 磁调控水基碳纳米管协同多孔材料强化相变储/释能特性[J]. 化工学报, 2023, 74(7): 3093-3102.
[7]	余娅洁, 李静茹, 周树锋, 李清彪, 詹国武. 基于天然生物模板构建纳米材料及集成催化剂研究进展[J]. 化工学报, 2023, 74(7): 2735-2752.
[8]	张琦钰, 高利军, 苏宇航, 马晓博, 王翊丞, 张亚婷, 胡超. 碳基催化材料在电化学还原二氧化碳中的研究进展[J]. 化工学报, 2023, 74(7): 2753-2772.
[9]	葛加丽, 管图祥, 邱新民, 吴健, 沈丽明, 暴宁钟. 垂直多孔碳包覆的FeF₃正极的构筑及储锂性能研究[J]. 化工学报, 2023, 74(7): 3058-3067.
[10]	屈园浩, 邓文义, 谢晓丹, 苏亚欣. 活性炭/石墨辅助污泥电渗脱水研究[J]. 化工学报, 2023, 74(7): 3038-3050.
[11]	张谭, 刘光, 李晋平, 孙予罕. Ru基氮还原电催化剂性能调控策略[J]. 化工学报, 2023, 74(6): 2264-2280.
[12]	董茂林, 陈李栋, 黄六莲, 吴伟兵, 戴红旗, 卞辉洋. 酸性助水溶剂制备木质纳米纤维素及功能应用研究进展[J]. 化工学报, 2023, 74(6): 2281-2295.
[13]	杨琴, 秦传鉴, 李明梓, 杨文晶, 赵卫杰, 刘虎. 用于柔性传感的双形状记忆MXene基水凝胶的制备及性能研究[J]. 化工学报, 2023, 74(6): 2699-2707.
[14]	刘远超, 蒋旭浩, 邵钶, 徐一帆, 钟建斌, 李耑. 几何尺寸及缺陷对石墨炔纳米带热输运特性的影响[J]. 化工学报, 2023, 74(6): 2708-2716.
[15]	李瑞康, 何盈盈, 卢维鹏, 王园园, 丁皓东, 骆勇名. 电化学强化钴基阴极活化过一硫酸盐的研究[J]. 化工学报, 2023, 74(5): 2207-2216.