SO2 corrosion resistance of composite ceramic coating for boiler heating surface

doi:10.11949/j.issn.0438-1157.20170273

Abstract

Abstract:

To address high-temperature corrosion at heating surface of coal-fired boilers, a composite ceramic coating on surface of 20G steel sheet was prepared by slurry method. After sintering, the composite ceramic coating had a relatively dense surface and good bonding to the substrate. Both uncoated and ceramic-coated steel sheets were studied for high-temperature corrosion resistance in sulfur dioxide (SO₂) by thermal kinetic analysis method. The results show that corrosion of the coated and uncoated steel sheets adheres to one dimensional diffusion reaction kinetic model at 400-500℃. Although activation energy of coated steel corrosion was lower than the uncoated one, the coating provided preferable high-temperature corrosion resistance. After exposure to SO₂, the appearance, element contents and phase structure of the sheets were characterized. Potassium sulfate (K₂SO₄) crystal grains were found to form on the coating surface. However, K₂SO₄ was not detected inside coating because relatively dense coating blocked sulfur diffusion.

Key words: boiler heating surface, flue gas, slurry method, composite ceramic coating, corrosion, reaction kinetics

摘要：

针对燃煤锅炉受热面存在的高温腐蚀问题，采用料浆法在20G钢材表面制备复合陶瓷涂层，烧结后的复合陶瓷涂层表面较为致密，涂层与基材具有良好的结合状态。对喷涂及未喷涂陶瓷涂层钢片在SO₂腐蚀气氛环境下的抗高温腐蚀性能进行试验，并采用热分析动力学方法对试验数据进行处理，结果表明，在400~500℃温度范围内，两种试样的腐蚀过程均符合一维扩散反应动力学模式，计算求得喷涂涂层钢片腐蚀反应活化能低于未喷涂涂层钢片，涂层具有较好的抗高温腐蚀性能。对腐蚀试验后试样的形貌、成分和物相分析结果显示，涂层在SO₂气氛下腐蚀后，表面生成K₂SO₄晶粒，但由于涂层较为致密，阻止了S的扩散，内部基本没有检测到K₂SO₄的存在。

关键词: 锅炉受热面, 烟道气, 料浆法, 复合陶瓷涂层, 腐蚀, 反应动力学

CLC Number:

TK08

WANG Jinqing, CHI Zuohe, YUAN Yichao, YU Jiahao, ZHANG Guangxue. SO₂ corrosion resistance of composite ceramic coating for boiler heating surface[J]. CIESC Journal, 2017, 68(11): 4221-4228.

王进卿, 池作和, 袁益超, 俞家豪, 张光学. 锅炉受热面复合陶瓷涂层抗高温SO₂腐蚀性能[J]. 化工学报, 2017, 68(11): 4221-4228.

References 31

[1]	王为术, 赵鹏飞, 陈刚, 等. 超超临界锅炉垂直水冷壁水动力特性[J]. 化工学报, 2013, 64(9):3213-3219. WANG W S, ZHAO P F, CHEN G, et al. Hydrodynamic characteristics of vertical water-wall in ultra-supercritical pressure boiler[J]. CIESC Journal, 2013, 64(9):3213-3219.
[2]	SHIM H S, VALENTINE J R, DAVIS K, et al. Development of fireside waterwall corrosion correlations using pilot-scale test furnace[J]. Fuel, 2008, 87(15/16):3353-3361.
[3]	CHATHA S S, SIDHU H S, SIDHU B S. High temperature hot corrosion behaviour of NiCr and Cr3C2-NiCr coatings on T91 boiler steel in an aggressive environment at 750℃[J]. Surface and Coatings Technology, 2012, 206(19/20):3839-3850.
[4]	SIDHU T S, AGRAWAL R D, PRAKASH S. Hot corrosion of some superalloys and role of high-velocity oxy-fuel spray coatings-a review[J]. Surface and Coatings Technology, 2005, 198(1-3):441-446.
[5]	SOMASUNDARAM B, KADOLI R, RAMESH M R. Evaluation of thermocyclic oxidation behavior of HVOF sprayed (Cr3C2-35% NiCr)+5% Si coatings on boiler tube steels[J]. Procedia Materials Science, 2014, 5:398-407.
[6]	SZYMA?SKI K, HERNAS A, MOSKAL G, et al. Thermally sprayed coatings resistant to erosion and corrosion for power plant boilers-a review[J]. Surface and Coatings Technology, 2015, 268:153-164.
[7]	WANG B Q, SEITZ M W. Comparison in erosion behavior of iron-base coatings sprayed by three different arc-spray processes[J]. Wear, 2001, 250(1-12):755-761.
[8]	LI X F. Corrosion behaviours of two nickel-based coatings in H2S-containing environments[J]. Surface and Coatings Technology, 2004, 183(2/3):212-215.
[9]	赵双群, 谢锡善, D. SMITH G. 新型镍基高温合金在模拟燃煤锅炉环境中的腐蚀[J]. 金属学报, 2004, 40(6):659-663. ZHAO S Q, XIE X S, D.SMITH G. Corrosion of a new nickel base superalloy in coal-fired boiler environments[J].Acta Metallurgica Sinica, 2004, 40(6):659-663.
[10]	李学锋, 杨中元, 秦颢, 等. 新型高铬镍基合金涂层在H2S气氛中抗高温腐蚀性能的研究[J]. 稀有金属, 2001, 25(6):440-443. LI X F, YANG Z Y, QIN H, et al. High temperature corrosion behavior of a new-type high-Cr-content coating exposured to H2S-containing environments[J]. Chinese Journal of Rare Metals, 2001, 25(6):440-443.
[11]	蒋建敏, 董娜, 贺定勇, 等. 电弧喷涂NiCrMo涂层耐蚀性能研究[J]. 稀有金属, 2006, 30(1):34-38. JIANG J M, DONG N, HE D Y, et al. Corrosion resistance properties of arc sprayed NiCrMo coatings[J]. Chinese Journal of Rare Metals, 2006, 30(1):34-38.
[12]	UUSITALO M A, VUORISTO P M J, MÄNTYLÄ T A. High temperature corrosion of coatings and boiler steels in oxidizing chlorine-containing atmosphere[J]. Materials Science & Engineering A, 2003, 346(1/2):168-177.
[13]	SIDHU T S, PRAKASH S, AGRAWAL R D. Hot corrosion studies of HVOF NiCrBSi and Stellite-6 coatings on a Ni-based superalloy in an actual industrial environment of a coal fired boiler[J]. Surface & Coatings Technology, 2006, 201(3/4):1602-1612.
[14]	丁彰雄, 陈江涛, 王群. FeCrAl合金涂层抗高温氧化及热腐蚀性能研究[J]. 武汉理工大学学报(交通科学与工程版), 2003, 27(4):513-516. DING Z X, CHEN J T, WANG Q. Performance of high temperature oxidation and hot corrosion resistance of FeCrAl alloy coating[J]. Journal of Wuhan University of Technology (Transportation Science & Engineering), 2003, 27(4):513-516.
[15]	HUSSAIN T, SIMMS N J, NICHOLLS J R, et al. Fireside corrosion degradation of HVOF thermal sprayed FeCrAl coating at 700-800℃[J]. Surface & Coatings Technology, 2015, 268:165-172.
[16]	FORMANEK B, SZYMA?SKI K, SZCZUCKA-LASOTA B, et al. New generation of protective coatings intended for the power industry[J]. Journal of Materials Processing Technology, 2005, 164-165:850-855.
[17]	SHAN X, WEI L Q, ZHANG X M, et al. A protective ceramic coating to improve oxidation and thermal shock resistance on CrMn alloy at elevated temperatures[J]. Ceramics International, 2015, 41(3):4706-4713.
[18]	MUROYA Y, MOTOKI A, SHIMANOE K, et al. Densification of SiO2-Al2O3-TiO2 based ceramic film coated on steel for high thermal stabilty and mechanical properties[J]. Surface and Coatings Technology, 2006, 201(3/4):880-885.
[19]	SHAN X, WEI L Q, ZHANG X M, et al. A protective ceramic coating to improve oxidation and thermal shock resistance on CrMn alloy at elevated temperatures[J]. Ceramics International, 2015, 41(3, Part B):4706-4713.
[20]	戴民, 汤杰, 樊占国, 等. SiO2-BaO-Al2O3-Cr2O3陶瓷保护涂层的制备及性能[J]. 材料保护, 2009, 42(8):66-68. DAI M, TANG J, FAN Z G, et al. Preparation and performance of SiO2-BaO-Al2O3-Cr2O3 ceramic protective coating on austenitis stainless steel[J]. Materials Protection, 2009, 42(8):66-68.
[21]	马国强, 李友芬. SiO2-B2O3-ZrO2陶瓷涂层的制备及性能[J]. 北京化工大学学报(自然科学版), 2013, 40(6):50-55. MA G Q, LI Y F. Preparation and properties of SiO2-B2O3-ZrO2 ceramic coating[J].Journal of Beijing University of Chemical Technology (Natural Science), 2013, 40(6):50-55.
[22]	NIU X, ZHANG H, HU X, et al. Synthesis of well-adhered SiO2-Al2O3 glass-ceramic coating on NiCrFe alloy supports[J]. Applied Surface Science, 2013, 268:265-269.
[23]	黄敏, 李克智, 王宇. 料浆法制备碳/碳复合材料Al-Si合金抗氧化涂层[J]. 热加工工艺, 2010, 39(18):87-89. HUANG M, LI K Z, WANG Y. Oxidation resistance of Al-Si alloy coating prepared by slurry[J]. Material & Heat Treatment, 2010, 39(18):87-89.
[24]	肖来荣, 蔡志刚, 易丹青, 等. 料浆烧结法制备改性Si-Cr-Ti高温抗氧化涂层的研究[J]. 稀有金属与硬质合金, 2005, 33(2):23-27. XIAO L R, CAI Z G, YI D Q, et al. Study of preparation of high-temperature and anti-oxidized modified Si-Cr-Ti coating by slurry sintering[J]. Rare Metals and Cemented Carbides, 2005, 33(2):23-27.
[25]	赵虹, 章勤, 吴广君, 等. 锅炉水冷壁在不同浓度SO2气氛下高温腐蚀的热分析动力学研究[J]. 电站系统工程, 2005, 21(6):32-34. ZHAO H, ZHANG Q, WU G J, et al. A study of thermal analysis kinetics for high temperature corrosion of water wall tube 20 g at different density SO2[J]. Power System Engineering, 2005, 21(6):32-34.
[26]	姜介炜. 炉膛受热面防护复合陶瓷涂层性能及提升传热效果研究[D]. 杭州:中国计量学院, 2016. JIANG J W. Study of composite ceramic coating characteristics for protecting heating surface and improving heat transfer performance[D]. Hangzhou:China Jiliang University, 2016.
[27]	LI X Z, LIU Z D, LI H C, et al. Investigations on the behavior of laser cladding Ni-Cr-Mo alloy coating on TP347H stainless steel tube in HCl rich environment[J]. Surface and Coatings Technology, 2013, 232:627-639.
[28]	YAN Z Q, XIONG X, XIAO P, et al. Si-Mo-SiO2 oxidation protective coatings prepared by slurry painting for C/C-SiC composites[J]. Surface and Coatings Technology, 2008, 202(19):4734-4740.
[29]	华隽石, 王进卿, 池作和, 等. 锅炉受热面复合陶瓷涂层抗高温腐蚀性能试验研究[J]. 电站系统工程, 2016, (1):9-11. HUA J S, WANG J Q, CHI Z H, et al. Experimental study on corrosion resistance of high temperature composite ceramic coating used in boiler heating surface[J]. Power System Engineering, 2016, (1):9-11.
[30]	胡荣祖. 热分析动力学[M]. 第2版. 北京:科学出版社, 2008:1-16. HU R Z. Thermal Analysis Kinetics[M]. 2nd ed, Beijing:Science Press, 2008:1-16.
[31]	印佳敏, 丁艳军, 吴占松. 生物质锅炉过热器气相HCl腐蚀试验的动力学研究[J]. 热力发电, 2009, 38(1):10-13. YIN J M, DING Y J, WU Z S. Dynamic study on corrosion test in gas-phase HCl for superheaters of biomass boilers[J]. Thermal Power Generation, 2009, 38(1):10-13.

SO₂ corrosion resistance of composite ceramic coating for boiler heating surface

锅炉受热面复合陶瓷涂层抗高温SO₂腐蚀性能

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References 31

Related Articles 15

Recommended Articles 0

Metrics

Comments

[1]	Cheng CHENG, Zhongdi DUAN, Haoran SUN, Haitao HU, Hongxiang XUE. Lattice Boltzmann simulation of surface microstructure effect on crystallization fouling [J]. CIESC Journal, 2023, 74(S1): 74-86.
[2]	Fei KANG, Weiguang LYU, Feng JU, Zhi SUN. Research on discharge path and evaluation of spent lithium-ion batteries [J]. CIESC Journal, 2023, 74(9): 3903-3911.
[3]	Linzheng WANG, Yubing LU, Ruizhi ZHANG, Yonghao LUO. Analysis on thermal oxidation characteristics of VOCs based on molecular dynamics simulation [J]. CIESC Journal, 2023, 74(8): 3242-3255.
[4]	Jiaqi CHEN, Wanyu ZHAO, Ruichong YAO, Daolin HOU, Sheying DONG. Synthesis of pistachio shell-based carbon dots and their corrosion inhibition behavior on Q235 carbon steel [J]. CIESC Journal, 2023, 74(8): 3446-3456.
[5]	Jing ZHAO, Chengwen GU, Xigao JIAN, Zhihuan WENG. Preparation and performance evaluation of magnolol-based epoxy resin anti-corrosion coatings [J]. CIESC Journal, 2023, 74(7): 3010-3017.
[6]	Mengmeng ZHANG, Dong YAN, Yongfeng SHEN, Wencui LI. Effect of electrolyte types on the storage behaviors of anions and cations for dual-ion batteries [J]. CIESC Journal, 2023, 74(7): 3116-3126.
[7]	Yanhui LI, Shaoming DING, Zhouyang BAI, Yinan ZHANG, Zhihong YU, Limei XING, Pengfei GAO, Yongzhen WANG. Corrosion micro-nano scale kinetics model development and application in non-conventional supercritical boilers [J]. CIESC Journal, 2023, 74(6): 2436-2446.
[8]	Guohua SHI, Linshen HE, Xiling ZHAO, Shigang ZHANG. Study of removal characteristics of particulate matters within flue gas by spray tower for waste-heat recovery [J]. CIESC Journal, 2023, 74(4): 1735-1745.
[9]	Jin YU, Binbin YU, Xinsheng JIANG. Study on quantification methodology and analysis of chemical effects of combustion control based on fictitious species [J]. CIESC Journal, 2023, 74(3): 1303-1312.
[10]	Shaozhuang WANG, Dunxi YU, Jiayi LI, Jingkun HAN, Xin YU, Fangqi LIU. Effects of torrefaction with flue gas on grindability of corn stalk [J]. CIESC Journal, 2023, 74(2): 861-870.
[11]	Yujun MA, Xiangjun LIU. Theoretical studies of water recovery from flue gas by using ceramic membrane [J]. CIESC Journal, 2022, 73(9): 4103-4112.
[12]	Chen CHEN, Qian YANG, Yun CHEN, Rui ZHANG, Dong LIU. Chemical kinetic study on coal volatiles combustion for various oxygen concentrations [J]. CIESC Journal, 2022, 73(9): 4133-4146.
[13]	Jiaming WANG, Xuehua RUAN, Gaohong HE. Research progress of membrane separation materials for different industrial CO₂-containing mixtures [J]. CIESC Journal, 2022, 73(8): 3417-3432.
[14]	Xiaolan WEI, Wenjie QI, Jing DING, Jianfeng LU, Weilong WANG, Shule LIU. Effect of valence state of chromium in molten chloride salt on corrosivity of nickel-based alloy [J]. CIESC Journal, 2022, 73(7): 3182-3192.
[15]	Cong HE, Wenqi ZHONG, Guanwen ZHOU, Xi CHEN. Study on decomposition characteristics of cement raw meal in suspension furnace at high altitude [J]. CIESC Journal, 2022, 73(5): 2120-2129.