聚偏氟乙烯-b-聚乙烯基吡咯烷酮嵌段共聚物的制备和结构

doi:10.11949/j.issn.0438-1157.20171037

摘要/Abstract

摘要：

以C₆F₁₃I为链转移剂，通过碘转移乳液聚合制得碘封端的聚偏氟乙烯（PVDF-I），再以PVDF-I为大分子链转移剂进行N-乙烯基吡咯烷酮碘转移溶液聚合，得到聚偏氟乙烯-b-聚乙烯基吡咯烷酮（PVDF-b-PVP）两亲性嵌段共聚物；采用NMR、IR、XRD、DSC和AFM等对PVDF-b-PVP嵌段共聚物的分子和相态结构进行了表征。发现PVP能有效嵌入PVDF与末端碘之间，PVDF嵌段PVP后，PVDF分子链的有序度明显降低，产生γ晶型PVDF，同时结晶温度和结晶度降低。PVDF-b-PVP嵌段共聚物表现微相分离结构，相分离尺寸约20 nm，其亲水性也优于PVDF均聚物。

关键词: 聚合物, 合成, 结晶, 聚偏氟乙烯, 聚乙烯基吡咯烷酮, 嵌段共聚物

Abstract:

Iodine terminated poly(vinylidene fluoride) was prepared by iodine transfer emulsion polymerization using C₆F₁₃I as a chain transfer agent, and further employed to mediate the iodine transfer solution polymerizaton of N-vinylpyrrolidone to prepare amphiphilic poly(vinylidene fluoride)-b-poly(N-vinylpyrrolidone) (PVDF-b-PVP) block copolymers. The molecular and phase structures of PVDF-b-PVP copolymers were characterized by NMR, IR, XRD, DSC and AFM. It is confirmed that PVP block can be effectively inserted between PVDF block and terminated iodine. The order of PVDF chains in the block copolymers was decreased after the incorporation of PVP, resulting the formation of more γ phase PVDF crystals, and the decrease of crystallization temperature and crystallinity degree of PVDF. PVDF-b-PVP copolymers were microphase-separated with a domain size of about 20 nm, and exhibited better hydrophilicity than PVDF homopolymer.

Key words: polymer, synthesis, crystallization, poly (vinylidene fluoride), poly (N-vinylpyrrolidone), block copolymer

中图分类号:

TQ325.3

黄志辉, 刘进朝, 包永忠. 聚偏氟乙烯-b-聚乙烯基吡咯烷酮嵌段共聚物的制备和结构[J]. 化工学报, 2018, 69(2): 823-829.

HUANG Zhihui, LIU Jinchao, BAO Yongzhong. Synthesis and structure of amphiphilic poly(vinylidene fluoride)-b-poly(N-vinylpyrrolidone) block copolymers[J]. CIESC Journal, 2018, 69(2): 823-829.

参考文献

[1] AMEDURI B. From vinylidene fluoride(VDF) to the applications of VDF-containing polymers and copolymers:recent developments and future trends[J]. Chemical Reviews, 2009, 109(12):6632-6686.
[2] BHAVANI P, SANGEETHA D. Blend membranes for direct methanol and proton exchange membrane fuel cells[J]. Chinese Journal of Polymer Science, 2012, 30(4):548-560.
[3] LI X, CHERUVALLY G, KIM J K, et al. Polymer electrolytes based on an electrospun poly(vinylidene fluoride-co-hexafluoropropylene) membrane for lithium batteries[J]. Journal of Power Sources, 2007, 167(2):491-498.
[4] BOUTEVIN G, TIFFES D, LOUBAT C, et al. New fluorinated surfactants based on vinylidene fluoride telomers[J]. Journal of Fluorine Chemistry, 2012, 134:77-84.
[5] SPREAFICO M A, COJOCARU P, MAGAGNIN L, et al. PVDF latex as a binder for positive electrodes in lithium-ion batteries[J]. Industrial & Engineering Chemistry Research, 2014, 53(22):9094-9100.
[6] LEE B O, WOO W J, PARK H S, et al. Influence of aspect ratio and skin effect on EMI shielding of coating materials fabricated with carbon nanofiber/PVDF[J]. Journal of Materials Science, 2002, 37(9):1839-1843.
[7] WANG H, LIU Z, WANG E, et al. A robust superhydrophobic PVDF composite coating with wear/corrosion-resistance properties[J]. Applied Surface Science, 2015, 332:518-524.
[8] LI J H, LI M Z, MIAO J, et al. Improved surface property of PVDF membrane with amphiphilic zwitterionic copolymer as membrane additive[J]. Applied Surface Science, 2012, 258(17):6398-6405.
[9] CHEN Y, YING L, YU W, et al. Poly(vinylidene fluoride) with grafted poly(ethylene glycol) side chains via the RAFT-mediated process and pore size control of the copolymer membranes[J]. Macromolecules, 2003, 36(25):9451-9457.
[10] VALADE D, BOYER C, AMEDURI B, et al. Poly(vinylidene fluoride)-b-poly(styrene) block copolymers by iodine transfer polymerization(ITP):synthesis, characterization, and kinetics of ITP[J]. Macromolecules, 2006, 39(25):8639-8651.
[11] GELIN M P, AMEDURⅡ B. Radical solution copolymerisation of vinylidene fluoride with hexafluoropropene[J]. Journal of Fluorine Chemistry, 2005, 126(4):577-585.
[12] KOSTOV G, BOSCHET F, BRANDSTADTER S, et al. Random and sequential radical cotelomerizations of 3,3,3-trifluoropropene (H₂C=CHCF₃) with vinylidene fluoride (F₂C=CH₂)[J]. Journal of Polymer Science:Part A:Polymer Chemistry, 2009, 47(16):3964-3981.
[13] LARUELLE G, NICOL E, AMEDURI B, et al. Synthesis of poly(vinylidene fluoride)-b-poly(styrene sulfonate) block copolymers by controlled radical polymerizations[J]. Journal of Polymer Science:Part A:Polymer Chemistry, 2011, 49(18):3960-3969.
[14] MESKINI A, RAIHANE M, STEVENSON-ROYAUD I, et al. Dielectric properties of block copolymers based on vinylidene fluoride and cyano comonomers[J]. Journal of Non-Crystalline Solids, 2010, 356(11-17):688-694.
[15] GELIN M P, AMEDURⅡ B. Fluorinated block copolymers containing poly(vinylidene fluoride) or poly(vinylidene fluoride-co-hexafluoropropylene) blocks from perfluoropolyethers:synthesis and thermal properties[J]. Journal of Polymer Science:Part A:Polymer Chemistry, 2003, 41(1):160-171.
[16] ASANDEI A D, ADEBOLU O I, SIMPSON C P. Mild-temperature Mn₂(CO)₁₀-photomediated controlled radical polymerization of vinylidene fluoride and synthesis of well-defined poly(vinylidene fluoride) block copolymers[J]. Journal of the American Chemical Society, 2012, 134(14):6080-6083.
[17] ASANDEI A D. Photomediated controlled radical polymerization and block copolymerization of vinylidene fluoride[J]. Chemical Reviews, 2016, 116(4):2244-2274.
[18] JO S M, LEE W S, AHN B S, et al. New AB or ABA type block copolymers:atom transfer radical polymerization(ATRP) of methyl methacrylate using iodine-terminated PVDFs as(macro)initiators[J]. Polymer Bulletin, 2000, 44(1):1-8.
[19] ZHANG Z B, YING S K, SHI Z Q. Synthesis of fluorine-containing block copolymers via ATRP 1. Synthesis and characterization of PSt-PVDF-PSt triblock copolymers[J]. Polymer, 1999, 40(5):1341-1345.
[20] DESTARAC M, MATYJASZEWSKI K, SILVEMAN E, et al. Atom transfer radical polymerization initiated with vinylidene fluoride telomers[J]. Macromolecules, 2000, 33(13):4613-4615.
[21] XU K, LI K, KHANCHAITIT P, WANG Q. Synthesis and characterization of self-assembled sulfonated poly(styrene-b-vinylidene fluoride-b-styrene) triblock copolymers for proton conductive membranes[J]. Chemistry of Materials, 2007, 19(24):5937-5945.
[22] KOSTOV G, BOSCHET F, BULLER J, et al. First amphiphilic poly(vinylidene fluoride-co-3,3,3-trifluoropropene)-b-oligo(vinyl alcohol) block copolymers as potential nonpersistent fluorosurfactants from radical polymerization controlled by xanthate[J]. Macromolecules, 2011, 44(7):1841-1855.
[23] GIRARD E, MARTY J D, AMEDURI B, et al. Direct synthesis of vinylidene fluoride-based amphiphilic diblock copolymers by RAFT/MADIX polymerization[J]. ACS Macro Letters, 2012, 1(2):270-274.
[24] KOSTOV G, BOSCHET F, BULLER J, et al. First amphiphilic poly(vinylidene fluoride-co-3,3,3-trifluoropropene)-b-oligo(vinyl alcohol) block copolymers as potential nonpersistent fluorosurfactants from radical polymerization controlled by xanthate[J]. Macromolecules, 2011, 44(7):1841-1855.
[25] GUERRE M, CAMPAGNE B, GIMELLO O, et al. Deeper insight into the MADIX polymerization of vinylidene fluoride[J]. Macromolecules, 2015, 48(21):7810-7822.
[26] LANG W Z, GUO Y J, CHU L F. Evolution of the precipitation kinetics, morphologies, permeation performances, and crystallization behaviors of polyvinylidenefluoride(PVDF) hollow fiber membrane by adding different molecular weight polyvinylpyrrolidone(PVP)[J]. Polymers for Advanced Technologies, 2011, 22(12):1720-1730.
[27] XU C Q, HUANG W, LU X, et al. Preparation of PVDF porous membranes by using PVDF-g-PVP powder as an additive and their antifouling property[J]. Radiation Physics and Chemistry, 2012, 81(11):1763-1769.
[28] KANG G D, CAO Y M. Application and modification of poly(vinylidene fluoride)(PVDF) membranes-a review[J]. Journal of Membrane Science, 2014, 463(0):145-165
[29] JAMES C S. Refractive Indices of Polymers[M]. New York:Wiley, 2003:571-590.
[30] MARTINS P, LOPES A C, LANCEROS-MENDEZ S. Electroactive phases of poly(vinylidene fluoride):determination, processing and applications[J]. Progress in Polymer Science, 2014, 39(4):683-706.
[31] CHENG J, WANG S C, CHEN S J, et al. Crystallization behavior and hydrophilicity of poly(vinylidene fluoride)/poly(methyl methacrylate)/poly(vinyl pyrrolidone) ternary blends[J]. Polymer International, 2012, 61(3):477-484.
[32] LI L, JIANG Z, XU J, et al. Predicting poly(vinyl pyrrolidone)'s solubility parameter and systematic investigation of the parameters of electrospinning with response surface methodology[J]. Journal of Applied Polymer Science, 2014, 131(11):40304.
[33] CUI Z, HASSANKIADEH N T, LEE S Y, et al. Poly(vinylidene fluoride) membrane preparation with an environmental diluent via thermally induced phase separation[J]. Journal of Membrane Science, 2013, 444:223-236.