交联直写海藻酸盐水凝胶中空纤维的凝胶率与溶胀度

doi:10.3969/j.issn.0438-1157.2014.12.060

化工学报 ›› 2014, Vol. 65 ›› Issue (12): 5090-5096.DOI: 10.3969/j.issn.0438-1157.2014.12.060

• 材料化学工程与纳米技术 • 上一篇

交联直写海藻酸盐水凝胶中空纤维的凝胶率与溶胀度

李瑜^1,2, 刘媛媛¹, 李帅¹, 梁刚¹, 张亚男¹, 胡庆夕¹

1. 上海大学快速制造工程中心, 上海 200444;
2. 河南理工大学机械与动力工程学院, 河南焦作 454000

收稿日期:2014-05-16 修回日期:2014-06-30 出版日期:2014-12-05 发布日期:2014-12-05
通讯作者: 刘媛媛
基金资助:
国家自然科学基金项目(51475281,51375292,51105239).

Gel fraction and swelling degree of hollow alginate fiber fabricated by direct writing and crosslinking

LI Yu^1,2, LIU Yuanyuan¹, LI Shuai¹, LIANG Gang¹, ZHANG Yanan¹, HU Qingxi¹

1. Rapid Manufacturing Engineering Center, Shanghai University, Shanghai 200444, China;
2. School of Mechanical and Power Engineering, Henan Polytechnic University, Jiaozuo 454000, Henan, China

Received:2014-05-16 Revised:2014-06-30 Online:2014-12-05 Published:2014-12-05
Supported by:
supported by the National Natural Science Foundation of China (51475281,51375292,51105239).

摘要/Abstract

摘要： 以海藻酸钠为原料、氯化钙为交联剂,反应直写制备海藻酸钙水凝胶中空纤维及组织工程支架.纤维的凝胶率和溶胀度直接影响支架的成形质量与所装载细胞的存活率.浸取分离所直写中空纤维的未交联部分,分析材料浓度对凝胶率的影响;以滴注凝固浴制备的海藻酸钙微球为对照组,分析直写工艺的溶胀度表现.结果表明,以4%海藻酸钠与3%氯化钙材料交联直写的中空纤维凝胶率和纤维形貌较好地满足了直写工艺的要求;随着海藻酸钠浓度的增加,中空纤维的溶胀度先减小后小幅升高并趋于稳定;随着氯化钙浓度的增加,凝胶纤维的溶胀度逐渐减小;反应直写工艺由于较小的两相接触表面,其溶胀度比凝固浴制备凝胶微球高2～5倍,更高的含水率有利于保障所装载细胞的活性和传质.

关键词: 海藻酸钠, 聚合物加工, 中空纤维, 浸取, 凝胶, 凝胶率, 溶胀度

Abstract: With sodium alginate as raw material and calcium chloride as crosslinker, a hollow hydrogel fiber was fabricated by direct writing combined with crosslinking, and was used to construct tissue engineering scaffold. Fiber gel fraction and swelling degree directly affect the forming quality of scaffold and laden cell survival. The influence of materials concentration on gel fraction was analyzed by leaching the ungelled part from the fiber. As a control group, alginate beads were prepared with coagulating bath. The requirements of direct writing process, such as gel rate, gel fraction and fiber morphology were satisfied, when the concentration of sodium alginate and calcium chloride were 4% and 3% respectively. With increasing sodium alginate's concentration, equilibrium swelling degree of hollow fiber first decreased and then slightly increased and stabilized finally. With increasing calcium chloride's concentration, swelling degree gradually decreased. Due to smaller diffusion interface, swelling degree of hollow fiber was two to five times higher than the gelled beads, and higher moisture was in favor of the viability and mass transfer for cell laden.

Key words: sodium alginate, polymer processing, hollow fiber, leaching, gels, gel fraction, swelling degree

中图分类号:

TQ050.6

李瑜, 刘媛媛, 李帅, 梁刚, 张亚男, 胡庆夕. 交联直写海藻酸盐水凝胶中空纤维的凝胶率与溶胀度[J]. 化工学报, 2014, 65(12): 5090-5096.

LI Yu, LIU Yuanyuan, LI Shuai, LIANG Gang, ZHANG Yanan, HU Qingxi. Gel fraction and swelling degree of hollow alginate fiber fabricated by direct writing and crosslinking[J]. CIESC Journal, 2014, 65(12): 5090-5096.

参考文献 22

[1]	Giannakopoulos G, Masania K, Taylor A C. Toughening of epoxy using core-shell particles [J]. J. Mater. Sci., 2011, 46(2): 327-338
[2]	Lu Lingang(卢林刚), Li Ling(李铃), Shu Zhongjun(舒仲俊), Dong Xilin(董希琳), Gao Weiying(高维英), Yu Baogang(于宝刚). Preparation and property of halogen-free phosphorous flame retardant epoxy resin [J]. Polym. Mater. Sci. Eng.(高分子材料科学与工程), 2010, 26(5): 158-161
[3]	Ching H L, Sheng L C, Tsai P W. High-Tg transparent poly(ether sulfone)s based on phosphinated bisphenols [J]. Chem. Phys., 2011, 212: 455-464
[4]	Yuan Q X, Xu Y Z, Jia L. Synthesis of novel phosphorus-containing epoxy hardeners and thermal stability and flame-retardant properties of cured products [J]. J. Appl. Polym. Sci., 2012, 125: 1219-1225
[5]	Wu Qingyu(伍清浴). Synthesis and Application Study on Several Reactive Flame Retardant of Diphenylphosphine Oxide Derivatives [D]. Shandong: Shandong University of Science and Technology, 2013
[6]	Huang Nianhua(黄年华), Zhang Qiang(张强), Li Zhihua(李治华), Xiong Qi(熊奇). Flame retardant and thermal degradation kinetics of novel copolyester containing phosphorus linked pendant groups [J]. Chem. J. Chinese University(高等学校化学学报), 2007, 28(11): 2219-2224
[7]	Wang Q F, Shi W F. Kinetics study of thermal decomposition of epoxy resins containing flame retardant components [J]. Polym. Degra. Stab., 2006, 91: 1747-1754
[8]	Li Q, Guan C X, Zhang A Q, Chen D H, Qing Z B. Thermal stabilities and the thermal degradation kinetics of polyimides [J]. Polym. Degra. Stab., 2004, 84: 369-373
[9]	Wang Dandan(王丹丹), Wang Peng(王鹏). Thermal degradation kinetics of poly(benzobisoxazole imide) [J]. Acta Polymerica Sinica(高分子学报), 2013(2): 154-158
[10]	Wu B, Wang Y Z, Wang X L, Yang K K, Jin Y D, Zhao H. Kinetics of thermal oxidative degradation of phosphorus-containing flame retardant copolyesters [J]. Polym. Degra. Stab., 2002, 76: 401-409
[11]	Lu Liming(陆立明). Thermal Analysis in Practice(热分析应用基础)[M]. Shanghai: Donghua University Press, 2010: 89-92
[12]	Li Heng(李恒), Wang Dehai(王德海), Qian Xiaqing(钱夏青). Curing kinetics of epoxy resin by non-isothermal DSC method [J]. Journal of Solid Rocket Technology(固体火箭技术), 2013, 36(2): 266-284
[13]	Gan Li(甘丽), Sun Zhijie(孙志杰), Gu Yizhuo(顾轶卓). Epoxy resin curing reaction studied by dynamic and isothermal model free kinetics [J]. Acta Polymerica Sinica(高分子学报), 2010(8): 1016- 1022
[14]	Flynm J H. The "temperature integral"—its use and abuse [J]. Thermochim Acta, 1997, 300: 83-92
[15]	Coats A W, Redern J P. Kinetic parameters from the thermogravimetric data [J]. Nature (Lond), 1964, 201: 68-69
[16]	Liu Xiaodong(刘晓东),Cheng Yu(程珏),Lin Xin(林欣),Zhang Junying(张军营). Curing kinetics of epoxy resins/amine system and epoxy/episulfide resin/amine system [J]. CIESC Journal(化工学报), 2013, 64(11): 4046-4052
[17]	Liaw D J. Synthesis of polyphosphates by the polyaddition of bisphenol-S diglycidyl ether and aryl phosphorodichloridates [J]. J. Polym. Sci., Part A: Polym. Chem., 1997, 35:2365-2375
[18]	Wang L S, Wang X L, Yan G L. Synthesis, characterization and flame retardance behaviour of poly(ethylene terephthalate) copolymer containing triaryl phosphine oxide [J]. Polym. Degr. Stab., 2000, 69(1): 127-130
[19]	Balabanovich A I, Levchik G F, Levchiky S V, Engelmann J. Fire retardant synergism between cyclic diphosphonate ester and melamine in poly(butylene terephthalate) [J]. J. Fire Sci., 2003, 1(20): 71-83
[20]	Olive Fischer, Doris Pospiech, Andreas Korwitz, Karin Share, Liane Häußler, Peter Fridel, Dieter Fischer, Christina Harnisch, Yana Bykov, Manfred Döring. Synthesis and properties of phosphorus polyesters with systematically altered phosphorus environment [J]. Polym. Degr. Stab., 2011, 96: 2198-2208
[21]	Zhu H M, Yan J H, Jiang X G, Lai Y E, Cen K F. Study on pyrolysis of typical medical waste materials by using TG-FTIR analysis [J]. J. Hazard. Mater., 2008, 153: 670-676
[22]	Tang Yuanwang(唐远旺). Evolved Gas Analysis (逸出气体分析)[M].Shanghai: Donghua University Press, 2009: 12-22

交联直写海藻酸盐水凝胶中空纤维的凝胶率与溶胀度

Gel fraction and swelling degree of hollow alginate fiber fabricated by direct writing and crosslinking

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献 22

相关文章 15

编辑推荐

Metrics

本文评价

[1]	高燕, 伍鹏, 尚超, 胡泽君, 陈晓东. 基于双流体喷嘴的磁性琼脂糖微球的制备及其蛋白吸附性能探究[J]. 化工学报, 2023, 74(8): 3457-3471.
[2]	徐文杰, 贾献峰, 王际童, 乔文明, 凌立成, 王任平, 余子舰, 张寅旭. 有机硅/酚醛杂化气凝胶的制备和性能研究[J]. 化工学报, 2023, 74(8): 3572-3583.
[3]	刘杰, 吴立盛, 李锦锦, 罗正鸿, 周寅宁. 含乙烯基胺酯键聚醚类可逆交联聚合物的制备及性能研究[J]. 化工学报, 2023, 74(7): 3051-3057.
[4]	韩奎奎, 谭湘龙, 李金芝, 杨婷, 张春, 张永汾, 刘洪全, 于中伟, 顾学红. 四通道中空纤维MFI分子筛膜用于二甲苯异构体分离[J]. 化工学报, 2023, 74(6): 2468-2476.
[5]	谢诗婷, 刘壮, 谢锐, 巨晓洁, 汪伟, 潘大伟, 褚良银. 聚（N-异丙基丙烯酰胺-共聚-烯丙基硫脲）智能微凝胶的制备及其Hg²⁺响应性能的研究[J]. 化工学报, 2023, 74(6): 2689-2698.
[6]	杨琴, 秦传鉴, 李明梓, 杨文晶, 赵卫杰, 刘虎. 用于柔性传感的双形状记忆MXene基水凝胶的制备及性能研究[J]. 化工学报, 2023, 74(6): 2699-2707.
[7]	王蕾, 王磊, 白云龙, 何柳柳. SA膜状锂离子筛的制备及其锂吸附性能[J]. 化工学报, 2023, 74(5): 2046-2056.
[8]	范坤阳, 杨景兴, 许海波, 连兴容, 何凤梅, 陈聪慧, 李增耀. 遮光剂掺杂SiO₂气凝胶传热的统一格子Boltzmann模型研究[J]. 化工学报, 2023, 74(5): 1974-1981.
[9]	饶纤纤, 杜淼, 单国荣, 潘鹏举. 不同金属盐破乳对丁基橡胶硫化行为的影响[J]. 化工学报, 2023, 74(2): 756-765.
[10]	高端辉, 肖卫强, 高峰, 夏倩, 汪曼秋, 卢昕博, 詹晓力, 张庆华. 聚酰亚胺基气凝胶材料的制备与应用[J]. 化工学报, 2022, 73(7): 2757-2773.
[11]	李文涛, 林慧娟, 钟海. 原位构建富氟SEI的凝胶电解质用于金属锂二次电池[J]. 化工学报, 2022, 73(7): 3240-3250.
[12]	赵希强, 张健, 孙爽, 王文龙, 毛岩鹏, 孙静, 刘景龙, 宋占龙. 生物质炭改性微球去除化工废水中无机磷的性能研究[J]. 化工学报, 2022, 73(5): 2158-2173.
[13]	钟国栋, 邓超和, 王洋, 王佳韵, 王如竹. 蜂窝状水凝胶吸附床传热传质特性数值模拟及验证[J]. 化工学报, 2022, 73(3): 1083-1092.
[14]	万丽, 梁德青. 一种可生物降解水合物动力学抑制剂的研究[J]. 化工学报, 2022, 73(2): 894-903.
[15]	牛卉芳, 闫伦靖, 吕鹏, 张旭峰, 王美君, 孔娇, 鲍卫仁, 常丽萍. 煤焦油沥青基碳气凝胶微球的制备及分析[J]. 化工学报, 2022, 73(12): 5605-5614.